A simple triggered vacuum gap has previously been described by the authors in this journal (see ibid., vol.5, 415, 1972). Further studies have resulted in improvement of the performance with regard to sensitivity and consistency of the trigger characteristics and immunity from bridging due to metal particles eroded from the arc. The earlier design suffered from rather frequent bridging of the auxiliary gap and showed rather wide scatter in its trigger characteristics. In the present design thermally stable materials like fused quartz, machinable ceramic 'Supramica 500' (Mycalex Corporation of America), lead titanate, barium titanate (LCC HTD) and silicon carbide have been used to insulate the trigger electrode from the cathode. Consistent triggerings free from bridging, at relatively low voltages of 200-400 V have been obtained.

Delay characteristics of a simple triggered vacuum gap

Firing delays of a simple triggered vacuum gap are reported in this paper. The effects of insulating materials in the auxiliary gap, auxiliary gap current, main gap current and electrode separation on the delay have been investigated. The presence of insulating material in the auxiliary gap having low auxiliary gap resistance appears to exhibit large delay. Delay decreases considerably with increase of current in the auxiliary and the main gaps, but it increases with increase of electrode separation. The scatter in the delay is less than 25 ps and 500 ps with supramica (Mycalex Corporation of America) and silicon carbide respectively at lower values of auxiliary gap current and it becomes negligible for supramica at auxiliary gap currents greater than 6A. This investigation appears to indicate that the simple device can be used as a fast switch.

High vacuum tribology of polycrystalline diamond coatings

Polycrystalline diamond coatings have been grown on unpolished side of Si(100) wafers by hot filament chemical vapour deposition process. The morphology of the grown coatings has been varied from cauliflower morphology to faceted morphology by manipulation of the growth temperature from 700 degrees C to 900 degrees C and methane gas concentration from 3% to 1.5%. It is found that the coefficient of friction of the coatings under high vacuum of 133.32 x 10(-7) Pa (10(-7) torr) with nanocrystalline grains can be manipulated to 0.35 to enhance tribological behaviour of bare Si substrates.

Triggered vacuum gap for initiating electric arcs in vacuum

Describes a simple triggered vacuum gap developed for initiating electric arcs in vacuum which uses the property that the voltage required to breakdown a gap in vacuum in the presence of a solid insulating material is considerably less than the voltage required in the absence of such material. In this triggered vacuum gap a solid insulating material is used in the angular space between the main cathode and the concentric trigger electrode forming the auxiliary gap. Different materials like epoxy resin, Teflon (PTFE) and mica have been used. The trigger voltage was found to vary in the range 560-1840 V. The results with epoxy and Teflon were unsatisfactory because the trigger voltages showed wide scatter and the auxiliary gap was soon bridged by metal particles eroded from the electrodes. Though the trigger voltages required with mica were relatively high, consistent triggering could be obtained for a large number of trials before the auxiliary gap was bridged. This was probably due to better thermal stability of mica as compared with either epoxy or Teflon.

Numerical estimation of hotspot temperatures in electrodes subjected to pulsed electron beam heating in vacuum

A numerical solution for the transient temperature distribution in a cylindrical disc heated on its top surface by a circular source is presented. A finite difference form of the governing equations is solved by the Alternating Direction Implicit (ADI) time marching scheme. This solution has direct applications in analyzing transient electron beam heating of target materials as encountered in the prebreakdown current enhancement and consequent breakdown in high voltage vacuum gaps stressed by alternating and pulsed voltages. The solution provides an estimate of the temperature for pulsed electron beam heating and the size of thermally activated microparticles originating from anode hot spots. The calculated results for a typical 45kV (a.c.) electron beam of radius 2.5 micron indicate that the temperature of such spots can reach melting point and could give rise to microparticles which could initiate breakdown.

Matched thermochemical diagram for vacuum decarburization of ferroalloys

The carbon content of high carbon ferroalloy melts can be reduced by a vacuum treatment. Carbon and oxygen dissolved in the melt react to form CO. Although this process has been suggested in the literature, no comprehensive analysis of the equilibrium partial pressure of CO over an alloy melt with a given carbon and oxygen content has been reported. In this paper, a new type of matched thermochemical diagram is introduced, from which the feasibility of decarburization at reduced CO pressure and the minimum achievable carbon level can be graphically evaluated for any alloy composition and temperature. Carbon and oxygen potentials of different alloys are plotted as functions of temperature on two terminal diagrams. By projecting information from these plots onto a central diagram, containing data on the Gibbs' energy of mixing for the C-O system, equilibrium partial pressures of CO and CO2 are obtained. Nomograms on the central diagram give a direct indication of the equilibrium partial pressures at any given temperature. The carbon and oxygen activities in ferrochromium alloys have been assessed and the results are presented to illustrate the construction and use of the matched thermochemical diagrams.

Studies on thin film materials on acrylics for optical applications

Deposition of durable thin film coatings by vacuum evaporation on acrylic substrates for optical applications is a challenging job. Films crack upon deposition due to internal stresses and leads to performance degradation. In this investigation, we report the preparation and characterization of single and multi-layer films of TiO2, CeO2, Substance2 (E Merck, Germany), Al2O3, SiO2 and MgF2 by electron beam evaporation on both glass and PMMA substrates. Optical micrographs taken on single layer films deposited on PMMA substrates did not reveal any cracks. Cracks in films were observed on PMMA substrates when the substrate temperature exceeded 80degreesC. Antireflection coatings of 3 and 4 layers have been deposited and characterized. Antireflection coatings made on PMMA substrate using Substance2 (H2) and SiO2 combination showed very fine cracks when observed under microscope. Optical performance of the coatings has been explained with the help of optical micrographs.

Fluid dynamics study of a new vacuum degassing process

Recently, the demand of the steel having superior chemical and physical properties has increased for which the content of carbon must be in ultra low range. There are many processes which can produce low carbon steel such as Tank degasser and RH (Rheinstahl-Heraeus) processes. It has been claimed that using a new process, called REDA (Revolutionary Degassing Activator), one can achieve the carbon content below 10ppm in less time. REDA process in terms of installment cost is in between tank degasser and RH processes. As such, REDA process has not been studied thoroughly. Fluid flow phenomena affect the decarburization rate the most besides the chemical reaction rate. Therefore, momentum balance equations along with k-ε turbulent model have been solved for gas and liquid phases in two-dimension (2D) for REDA process. The fluid flow phenomena have been studied in details for this process by varying gas flow rate, depth of immersed snorkel in the steel, diameter of the snorkel and change in vacuum pressure. It is found that design of snorkel affects the mixing process of the bath significantly.

Physical chemistry of the reduction of calcium oxide with aluminium in vacuum

The physical chemistry of "aluminothermic" reduction of calcium oxide in vacuum is analyzed. Basic thermodynamic data required for the analysis have been generated by a variety of experiments. These include activity measurements in liquid AI-Ca alloys and determination of the Gibbs energies of formation of calcium aluminates. These data have been correlated with phase relations in the Ca-AI-0 system at 1373 K. The various stages of reduction, the end products and the corresponding equilibrium partial pressures of calcium have been established from thermodynamic considerations. In principle, the recovery of calcium can be improved by reducing the pressure in the reactor. However,, the cost of a high vacuum system and the enhanced time for reduction needed to achieve higher yields makes such a practice uneconomic. Aluminum contamination of calcium also increases at low pressures. The best compromise is to carry the reduction up to the stage where 3CaO-Al,O, is formed as the product. This corresponds to an equilibrium calcium partial pressure of 31.3 Pa at 1373 K and 91.6 Pa at 1460 K. Calcium can be extracted at this pressure using mechanical pumps in approximately 8 to 15 hr, depending on the size and the fill ratio of the retort and porosity of the charge briquettes.

A new matched thermochemical diagram for vacuum refining of nickel and cupronickel alloys

Sulfur and oxygen dissolved in nickel and cupronickel melts can be remwed as gaseous oxides of sulfur by a vacuum treatment. Presented in this paper is a new matched thermcxhemical disgran~ that permit.. direct evaluation of the equilibrium partial pressure of SO, as a function of temperature wer an alloy of specified compition. The matched thermochemical diagram consists of a central plot which shows the integral Gibbs' energy of mixing for the binary system SO, at different temperatures. The central plot is flanked on either side by terminal plots of the chemical potentials of oxygen and sulfur, as functions of temperature, for different alloy compositions. By projecting the chemical wtentials of oxygen and sulfur from the terminal lots on to the central diagram, ihe equilibrium partial pressure of S0,can be directly ;cad on the nomograms on the central plot at different temperatures. The matched therrnochemical diagrams are useful in assuring the efficiency of vacuum refining.

Study of Fluid Flow and Mixing Behaviour of a Vacuum Degasser

In recent times the demand of ultra-low carbon steel (ULCS) with improved mechanical properties such as good ductility and good workability has been increased as it is used to produce cold-rolled steel sheets for automobiles. For producing ULCS efficiently, it is necessary to improve the productivity of the vacuum degassers such as RH, DH and tank degasser. Recently, it has been claimed that using a new process, called REDA (revolutionary degassing activator), one can achieve the carbon content below 10 ppm in less time. As such, REDA process has not been studied thoroughly in terms of fluid flow and mass transfer which is a necessary precursor to understand and design this process. Therefore, momentum and mass transfer of the process has been studied by solving momentum and species balance equations along with k-epsilon turbulent model in two-dimension (2D) for REDA process. Similarly, computational fluid dynamic studies have been made in 2D for tank and RH degassers to compare them with REDA process. Computational results have been validated with published experimental and theoretical data. It is found that REDA process is the most efficient among all these processes in terms of mixing efficiency. Fluid flow phenomena have been studied in details for REDA process by varying gas flow rate, depth of immersed snorkel in the steel, diameter of the snorkel and change in vacuum pressure. It is found that design of snorkel affects the melt circulation in the bath significantly.

Non-destructive evaluation of porosity and its effect on mechanical properties of carbon fiber reinforced polymer composite materials

In this work, an attempt is made to induce porosity of varied levels in carbon fiber reinforced epoxy based polymer composite laminates fabricated using prepregs by varying the fabrication parameters such as applied vacuum, autoclave pressure and curing temperature. Different NDE tools have been utilized to evaluate the porosity content and correlate with measurable parameters of different NDE techniques. Primarily, ultrasonic imaging and real time digital X-ray imaging have been tried to obtain a measurable parameter which can represent or reflect the amount of porosity contained in the composite laminate. Also, effect of varied porosity content on mechanical properties of the CFRP composite materials is investigated through a series of experimental investigations. The outcome of the experimental approach has yielded interesting and encouraging trend as a first step towards developing an NDE tool for quantification of effect of varied porosity in the polymer composite materials.

Performances of single and two-stage pulse tube cryocoolers under different vacuum levels with and without thermal radiation shields

Single and two-stage Pulse Tube Cryocoolers (PTC) have been designed, fabricated and experimentally studied. The single stage PTC reaches a no-load temperature of similar to 29 K at its cold end, the two-stage PTC reaches similar to 2.9 K in its second stage cold end and similar to 60 K in its first stage cold end. The two-stage Pulse Tube Cryocooler provides a cooling power of similar to 250 mW at 4.2 K. The single stage system uses stainless steel meshes along with Pb granules as its regenerator materials, while the two-stage PTC uses combinations of Pb along with Er3Ni/HoCu2 as the second stage regenerator materials. Normally, the above systems are insulated by thermal radiation shields and mounted inside a vacuum chamber which is maintained at high vacuum. To evaluate the performance of these systems in the possible conditions of loss of vacuum with and without radiation shields, experimental studies have been performed. The heat-in-leak under such severe conditions has been estimated from the heat load characteristics of the respective stages. The experimental results are analyzed to obtain surface emissivities and effective thermal conductivities as a function of interspace pressure.

Effect of vacuum treatment on CsI photocathode performance in UV photon detectors

CsI can be used as a photocathode material in UV photon detectors. The detection efficiency of the detector strongly depends on the photoemission property of the photocathode. CsI is very hygroscopic in nature. This limits the photoelectron yield from the photocathode when exposed to humid air even for a short duration during photocathode mounting or transfer. We report here on the improvement of photoemission properties of both thick (300 nm) and thin (30 nm) UV-sensitive CsI film exposed to humid air by the process of vacuum treatment. (C) 2013 Optical Society of America

Dielectric and electrical conductivity properties of multi-stage spark plasma sintered HA-CaTiO3 composites and comparison with conventionally sintered materials

One of the different issues limiting the wider application of monolithic hydroxyapatite (HA) as an ideal bone replacement material is the lack of reasonably good electrical transport properties. The comprehensive electrical property characterization to evaluate the efficacy of processing parameters in achieving the desired combination of electroactive properties is considered as an important aspect in the development of HA-based bioactive material. In this perspective, the present work reports the temperature (RT-200 degrees C) and frequency (100 Hz-1 MHz) dependent dielectric properties and AC conductivity for a range of HA-CaTiO3 (HA-CT) composites, densified using both conventional pressureless sintering in air as well as spark plasma sintering in vacuum. Importantly, the AC conductivity of spark plasma sintered ceramics similar to upto 10(-5) (Omega cm)(-1)] are found to be considerably higher than the corresponding pressureless sintered ceramics similar to upto 10(-8) (Omega cm)(-1)]. Overall, the results indicate the processing route dependent functional properties of HA-CaTiO3 composites as well as related advantages of spark plasma sintering route. (C) 2013 Elsevier Ltd. All rights reserved.