Surface spin glass behavior in sol–gel derived La0.7Ca0.3MnO3 nanotubes

We report the fabrication of La0.7Ca0.3MnO3 nanotubes (LCMONTs) with a diameter of about 200 nm, by a modified sol-gel method utilizing nanochannel alumina templates. High resolution transmission electron microscopy confirmed that the obtained LCMONTs are made up of nanoparticles (8-12 nm), which are randomly aligned in the wall of the nanotubes. The strong irreversibility between zero field cooling (ZFC) and field cooling (FC) magnetization curves as well as a cusplike peak in the ZFC curve gives strong support for surface spin glass behavior.

Dielectric relaxation and electrical conductivity in Bi5NbO10 oxygen ion conductors prepared by a modified sol–gel process

Crystalline Bi5NbO10 nanoparticles have been achieved through a modified sol–gel process using a mixture of ethylenediamine and ethanolamine as a solvent. The Bi5NbO10 nanoparticles were characterized by X-ray diffraction (XRD), differential scanning calorimetry/thermogravimetry (DSC/TG), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM) and Raman spectroscopy. The results showed that well-dispersed 5–60 nm Bi5NbO10 nanoparticles were prepared through heat-treating the precursor at 650 °C and the high density pellets were obtained at temperatures lower than those commonly employed. The frequency and temperature dependence of the dielectric constant and the electrical conductivity of the Bi5NbO10 solid solutions were investigated in the 0.1 Hz to 1 MHz frequency range. Two distinct relaxation mechanisms were observed in the plots of dielectric loss and the imaginary part of impedance (Z″) versus frequency in the temperature range of 200–350 °C. The dielectric constant and the loss in the low frequency regime were electrode dependent. The ionic conductivity of Bi5NbO10 solid solutions at 700 °C is 2.86 Ω−1 m−1 which is in same order of magnitude for Y2O3-stabilized ZrO2 ceramics at same temperature. These results suggest that Bi5NbO10 is a promising material for an oxygen ion conductor.

Exfoliated graphite–ruthenium oxide composite electrodes for electrochemical supercapacitors

The performance of exfoliated graphite (EG)–ruthenium oxide (RuOx) composites as binderless electrodes is evaluated for electrochemical capacitors (ECs). A composite of EG–RuOx is prepared by a modified sol–gel process. The material is characterized using X-ray diffraction and microscopy. Electrochemical capacitors with the composite electrodes in the presence of aqueous sulfuric acid (H2SO4) electrolyte are evaluated using voltammetry, impedance and charge–discharge studies. Cyclic voltammetry reveals very stable current–voltage behaviour up to several thousands of cycles, as well as high specific capacitances, e.g., a few hundreds of farads per gram for the composite that contains 16.5 wt.% RuOx.

Effect of Substitution of Ca on Thermal Expansion of Cordierite (Mg2Al4Si5O18)

The effect of substitution of calcium on the anisotropic axial thermal expansion of cordierite was investigated by using a high-temperature X-ray diffraction technique. The compositions were prepared by the sol–gel route. In the Mg2-xCax-Al4Si5O18 system, single-phase cordierite can be prepared for x up to 0.5. Thermal expansion anisotropy (αa–αc) of cordierites reduces progressively by the substitution of increasing amounts of Ca for Mg.

Tailoring the Magnetic and Optical Characteristics of Nanocrystalline BiFeO3 by Ce Doping

The Ce-doped BiFeO3 (BFO) nanoparticles (NPs) were synthesized using a facile solgel route with varying Ce concentrations in the range of 15 mol%. Ferroelectric transition temperature was found to shift from 723 degrees C +/- 5 degrees C for pristine BFO NPs to 534 degrees C +/- 3 degrees C for 5 mol% Ce-doped BFO NPs. UVVis absorption spectra of BFO NPs showed a significant blue shift of similar to 100 nm on Ce doping. The Fourier transformed infrared (FTIR) spectrum centered similar to 550 cm(-1) becomes considerably broadened on Ce doping which is due to additional closely spaced vibrational peaks as revealed by the second derivative FTIR analysis. High-frequency EPR measurements indicated that clustering occurs at high dopant levels, and that Fe is present as Fe(3+)corroborating Mossbauer measurements. The values of saturation and remanent magnetization for 3% Ce-doped BFO NPs are 3.03 and 0.49 emu/g, respectively, which are quite significant at room temperature, making it more suitable for technological applications.