Experimental investigation of forming limit, void coalescence and crystallographic textures of aluminum alloy 8011 sheet annealed at various temperatures

In this work, a combined forming and fracture limit diagram, fractured void coalescence and texture analysis have been experimentally evaluated for the commercially available aluminum alloy Al 8011 sheet annealed at different temperatures viz. 200 degrees C, 250 degrees C, 300 degrees C and 350 degrees C. The sheets were examined at different annealing temperatures on microstructure, tensile properties, formability and void coalescence. The fractured surfaces of the formed samples were examined using scanning electron microscope (SEM) and these images were correlated with fracture behavior and formability of sheet metals. Formability of Al 8011 was studied and examined at various annealing temperatures using their bulk X-ray crystallographic textures and ODF plots. Forming limit diagrams, void coalescence parameters and crystallographic textures were correlated with normal anisotropy of the sheet metals annealed at different temperatures. (C) 2013 Politechnika Wroclawska. Published by Elsevier Urban & Partner Sp. z o.o. All rights reserved.

Kaiser effect observation in reinforced concrete structures and its use for damage assessment

Reinforced concrete (RC) beams of span 3 m were tested under incremental cyclic load at different loading rates and simultaneously during the fracture process in the RC beams acoustic emissions (AE) were recorded. An attempt has been made to study the Kaiser effect as a measure of damage in RC beams. It was observed that RC beams made with high strength concrete under incremental cyclic loading showed an obvious Kaiser effect before the failure load. The results may be useful to study the damage in concrete structures and provide a reference for the application of Kaiser effect in engineering practice. (C) 2014 Politechnika Wroclawska. Published by Elsevier Urban & Partner Sp. z.o.o. All rights reserved.