Synthesis and luminescence properties of Sm3+ doped CaTiO3 nanophosphor for application in white LED under NUV excitation

CaTiO3:Sm3+ (1-11 mol%) nanophosphors were successfully synthesized by a low temperature solution combustion method LCS]. The structural and morphological properties of the phosphors were studied by using Powder X-ray diffractometer (PXRD), Fourier transform infrared (FTIR), X-ray photo electron spectroscopy (XPS), scanning electron microscope (SEM) and transmission electron microscopy (TEM). TEM studies indicate that the size of the phosphor is similar to 20-35 nm. Photoluminescence (PL) properties of Sm3+ (1-11 mol%) doped CaTiO3 for NUV excitation (407 nm) was studied in order to investigate the possibility of its use in White light emitting diode (WLED) applications. The emission spectra consists of intra 4f transitions of Sm3+, such as (4)G(5/2) -> H-6(5/2) (561 nm), (4)G(5/2) -> H-6(7/2) (601-611 nm), (4)G(5/2) -> H-6(9/2) (648 nm) and (4)G(5/2) -> H-6(11/2) (703 nm) respectively. Further, the emission at 601-611 nm show strong orange-red emission and can be applied to the orange-red emission of phosphor for the application for near ultra violet (NUV) excitation. Thermoluminescence (TL) of the samples irradiated with gamma source in the dose range 100-500 Gy was recorded at a heating rate of 5 degrees C s(-1). Two well resolved glow peaks at 164 degrees C and 214 degrees C along with shouldered peak at 186 degrees C were recorded. TL intensity increases up to 300 Gy and thereafter, it decreases with further increase of dose. The kinetic parameters namely activation energy (E), frequency factor (s) and order of kinetics were estimated and results were discussed in detail. (C) 2014 Elsevier B.V. All rights reserved.

A Novel and Scalable LED Communication System

We describe our novel LED communication infrastructure and demonstrate its scalability across platforms. Our system achieves 50 kilo bits per second on very simple SoCs and scales to megabits bits per second rates on dual processor based mobile phone platforms.

Red-emitting LaOF:Eu3+ phosphors: Synthesis, structure and their Judd-Ofelt analysis for LED applications

In the present study, we have synthesized a series of La1-xEuxOF (0.01 <= x <= 0.09) phosphors by the conventional solid-state reaction route at relatively low temperature (500 degrees C) and shorter duration of 2 h. The compounds were crystallized in the rhombohedral structure with the space group R-3m (No. 166). Upon UV excitation (254 nm), the photoluminescence spectra exhibit characteristic luminescence D-5(0) -> F-7(J) (J= 1, 2, 3, and 4) intra-4f shell Eu3+ ion transitions. An intense red emission peak at 610 nm was observed due to electric dipole (D-5(0) -> F-7(2)) transition. Judd-Ofelt theory was employed to evaluate various radiative parameters such as radiative emission rates, lifetime, branching and asymmetry ratios. CIE color coordinates confirmed the red emission of the phosphors. The luminescent results reveal that LaOF:Eu3+ phosphor can be used as potential candidate for developing red component in white LED applications. (C) 2015 Elsevier Ltd. All rights reserved.