Remarkable Capacity Retention of Nanostructured Manganese Oxide upon Cycling as an Electrode Material for Supercapacitor

Electrochemical capacity retention of nearly X-ray amorphous nanostructured manganese oxide (nanoMnO2) synthesized by mixing directly KMnO4 with ethylene glycol under ambient conditions for supercapacitor studies is enhanced significantly. Although X-ray diffraction (XRD) pattern of nanoMnO2 shows poor crystallinity, it is found that by Mn K-edge X-ray absorption near edge structure (XANES) measurement that the nanoMnO2 obtained is locally arranged in a δ-MnO2-type layered structure composed of edge-shared network of MnO6 octahedra. Field emission scanning electron microscopy and XANES measurements show that nanoMnO2 contains nearly spherical shaped morphology with δ-MnO2 structure, and 1D nanorods of α-MnO2 type structure (powder XRD) in the annealed (600 °C) sample. Volumetric nitrogen adsorption−desorption isotherms, inductively coupled plasma analysis, and thermal analysis are carried out to obtain physicochemical properties such as surface area (230 m2 g−1), porosity of nanoMnO2 (secondary mesopores of diameter 14.5 nm), water content, composition, etc., which lead to the promising electrochemical properties as an electrode for supercapacitor. The nanoMnO2 shows a very high stability even after 1200 cycles with capacity retention of about 250 F g−1.

Excellent rectifying characteristics in Au/n-CdTe diodes upon exposure to rf nitrogen plasma

Nitrogen plasma exposure (NPE) effects on indium doped bulk n-CdTe are reported here. Excellent rectifying characteristics of Au/n-CdTe Schottky diodes, with an increase in the barrier height, and large reverse breakdown voltages are observed after the plasma exposure. Surface damage is found to be absent in the plasma exposed samples. The breakdown mechanism of the heavily doped Schottky diodes is found to shift from the Zener to avalanche after the nitrogen plasma exposure, pointing to a change in the doping close to the surface which was also verified by C-V measurements. The thermal stability of the plasma exposure process is seen up to a temperature of 350 degrees C, thereby enabling the high temperature processing of the samples for device fabrication. The characteristics of the NPE diodes are stable over a year implying excellent diode quality. A plausible model based on Fermi level pinning by acceptor-like states created by plasma exposure is proposed to explain the observations.

Effect of diethylstilbesterol and prolactin on the induction of follicle stimulating hormone receptors in immature and cycling rats

Induction of follicle stimulating hormone receptor in the granulosa cells of intact immature rat ovary by diethylstilbesterol, an estrogen, has been studied. A single injection of 4 mg of diethylstilbesterol produced 72 h later a 3-fold increase in follicle stimulating hormone receptor concentration as monitored by [125I]-oFSH binding to isolated cells. The newly induced receptors were kinetically indistinguishable from the preexisting ones, as determined by Lineweaver-Burk plot of the binding data. The induced receptors were functional as evidenced by increased ability of the granulosa cells to incorporate [3H]-leucine into cellular proteins. Neutralization of endogenous follicle stimulating hormone and luteinizing hormone by administering specific antisera had no effect on the ability of diethylstilbesterol to induce follicle stimulating hormone receptors, whereas blockade of endogenous prolactin secretion by ergobromocryptin administration significantly inhibited (∼ 30 %) the response to diethylstilbesterol; this inhibition could be completely relieved by ovine prolactin treatment. However, ovine prolactin at the dose tried did not by itself enhance follicle stimulating hormone receptor level. Administration of ergobromocryptin to adult cycling rats at noon of proestrus brought about as measured on diestrusII, (a) a reduction of both follicle stimulating hormone (∼ 30 %) and luteinizing hormone (∼ 45 %) receptor concentration in granulosa cells, (b) a drastic reduction in the ovarian tissue estradiol with no change in tissue progesterone and (c) reduction in the ability of isolated granulosa cells to convert testosterone to estradiol in response to follicle stimulating hormone. Ergobromocryptin treatment affected only prolactin and not follicle stimulating hormone or luteinizing hormone surges on the proestrus evening. Treatment of rats with ergobromocryptin at proestrus noon followed by an injection of ovine prolactin (1 mg) at 1700 h of the same day completely reversed the ergobromocryptin induced reduction in ovarian tissue estradiol as well as the aromatase activity of the granulosa cells on diestrus II, thus suggesting a role for proestrus prolactin surge in the follicular maturation process.

Formative time lags in nitrogen, oxygen and dry air In crossed electric and magnetic fields

Formative time lags in nitrogen, oxygen, and dry air are measured with and without a magnetic field over a range of gas pressures (0.05 ' p ' 20.2 torr 5 kPa to 2 MPa, electric field strengths (1.8xO14 EEs 60xlO V m l) and magnetic field strengths (85xl0-4 < B ' 16x10-2 Tesla). For experiments below the Paschen minimum, the electrodes are designed to ensure that breakdown occurs over longer gaps and for experiments above the Paschen minimum, a coaxial cylindrical system is employed. The experimental technique consists of applying pulse voltages to the gap at various constant values of E/p and B/p and measuring the time lags from which the formative time lags are separated. In the gases studed, formative time lags decrease on application of a magnetic field at a given pressure for conditions below the Paschen minimum. The voltages at which the formative time lags remain the same without and with magnetic fields are determined, and electron molecule collision frequencies (v/p) are determined using the Effective Reduced Electric Field [EREF] concept. With increasing ratio of E/p in crossed fields, v/p decreases in all the three gases. Measurements above the Paschen minimum yield formative time lags which increase on application of a magnetic field. Formative time lags in nitrogen in ExB fields are calculated assuming an average collision frequency of 8.5x109 sec-1 torr 1. It is concluded that the EREF concept can be applied to explain formative time lags in ExB fields.

Synthesis and Reactions of Binuclear Diolefin Rhodium(I) Compounds bridged by Nitrogen Heterocycles, Crystal Structure of Dichloro-Di-1,5-Cyclooctadiene(Mu-Pyrazine)-Dirhodium(I) [[Rh(1,5-C8h12)Cl]2(Mu-C4h4n2)]

Binuclear complexes of rhodium(I) of the type [(dien)(X)Rh(μ-N-N)Rh(X)(dien)] (dien = 1,5-cyclooctadiene or norbornadiene; N-N = pyrazine, 4,4′-bipyridine or Phenazine and X = Cl or Br) with bridging heterocycles have been isolated and their reactions with carbon monoxide, 2,2′-bipyridine and 1,10-phenanthroline investigated. The crystal structure of [(COD)(Cl)Rh(μ-pyrazine)Rh(Cl)(COD)] has been determined.

A combined XPS-UPS-EELS study of nitrogen adsorbed on clean and barium-promoted iron surfaces: The nature of the precursor to dissociation

For N2 on a clean Fe surface, the adsorbed precursor in a parallel orientation becomes predominant around 110 K, while at lower temperatures it coexists with a weakly adsorbed species. On a Ba-promoted Fe surface, however, N2 is present exclusively in the precursor state in the temperature range 80–150 K following moderate exposure. Besides exhibiting a low N-N stretching frequency of 1530 cm−1, the precursor shows a clear separation between the 5σ and 1π levels in the UPS; the precursor dissociates to give a nitridic species around 160 K.

Molecular analysis of inorganic nitrogen assimilation in yeasts

Assimilation of nitrate and various other inorganic nitrogen compounds by different yeasts was investigated. Nitrate, nitrite, hydroxylamine, hydrazine, ammonium sulphate, urea and L-asparagine were tested as sole sources of nitrogen for the growth of Candida albicans, C. pelliculosa, Debaryomyces hansenii, Saccharomyces cerevisiae, C. tropicalis, and C. utilis. Ammonium sulphate and L-asparagine supported the growth of all the yeasts tested except D. hansenii while hydroxylamine and hydrazine failed to support the growth of any. Nitrate and nitrite were assimilated only by C. utilis. Nitrate utilization by C. utilis was also accompanied by the enzymatic activities of NAD(P)H: nitrate oxidoreductase (EC 1.6.6.2) and NAD(P)H: nitrite oxidoreductase (EC 1.6.6.4), but not reduced methyl viologen-or FAD-nitrate oxidoreductases (EC 1.7.99.4). It is demonstrated here that nitrate and nitrite reductase activities are responsible for the ability of C. utilis to assimilate primary nitrogen.

Curing And Thermal Cycling Processes In Pvc Graphite Thick-Films

Abstract is not available.

Growth of ionization currents in nitrogen

Townsend's primary and secondary ionization coefficients α/p and γ were determined in nitrogen over a wide range of E/p (100-1000 V cm−1 Torr−1) and p (0·4 to 12 Torr at 0 °C) using the pressure variation technique. This technique, along with the Gosseries method of evaluation of ionization coefficients, seems to be more suitable at higher values of E/p, since the errors in these coefficients could be minimized by a suitable selection of p and d, thus eliminating the non-equilibrium ionization condition.

Growth of ionization currents in nitrogen

Townsend's primary and secondary ionization coefficients α/p and γ were determined in nitrogen over a wide range of E/p (100-1000 V cm−1 Torr−1) and p (0·4 to 12 Torr at 0 °C) using the pressure variation technique. This technique, along with the Gosseries method of evaluation of ionization coefficients, seems to be more suitable at higher values of E/p, since the errors in these coefficients could be minimized by a suitable selection of p and d, thus eliminating the non-equilibrium ionization condition.

Studies on Aspergillus niger glutamine synthetase: Regulation of enzyme levels by nitrogen sources and identification of active site residues

The specific activity of glutamine synthetase (L-glutamate: ammonia ligase, EC 6.3.1.2) in surface grown Aspergillus niger was increased 3-5 fold when grown on L-glutamate or potassium nitrate, compared to the activity obtained on ammonium chloride. The levels of glutamine synthetase was regulated by the availability of nitrogen source like NH4 + , and further, the enzyme is repressed by increasing concentrations of NH4 +. In contrast to other micro-organisms, the Aspergillus niger enzyme was neither specifically inactivated by NH4+ or L-glutamine nor regulated by covalent modification.Glutamine synthetase from Aspergillus niger was purified to homogenity. The native enzyme is octameric with a molecular weight of 385,000±25,000. The enzyme also catalyses Mn2+ or Mg2+-dependent synthetase and Mn2+-dependent transferase activity.Aspergillus niger glutamine synthetase was completely inactivated by two mol of phenylglyoxal and one mol of N-ethylmaleimide with second order rate constants of 3·8 M–1 min–1 and 760 M–1 min–1 respectively. Ligands like Mg. ATP, Mg. ADP, Mg. AMP, L-glutamate NH4+, Mn2+ protected the enzyme against inactivation. The pattern of inactivation and protection afforded by different ligands against N-ethylamaleimide and phenylglyoxal was remarkably similar. These results suggest that metal ATP complex acts as a substrate and interacts with an arginine ressidue at the active site. Further, the metal ion and the free nucleotide probably interact at other sites on the enzyme affecting the catalytic activity.

Ratio of Diffusion Coefficient to Mobility for Electrons in SF6-Air and Freon-Nitrogen Mixtures

The ratio of diffusion coefficient to mobility (D/¿) for electrons has been measured in SF6-air and freon-nitrogen mixtures for various concentrations of SF6 and freon in the mixtures over the range 140¿ E/p¿ 220 V.cm-1 - torr-1. In SF6-air mixtures, the values of D/¿ were always observed to lie intermediate between the values for the pure gases. However, in freon-nitrogen mixtures, with a small concentration (10 percent) of freon in the mixture, the values of D/¿ are found to lie above the boundaries determined by the pure gases. In this mixture, over the lower E/p range (140 to 190) the electrons appear to lose a large fraction of their energy by the excitation of the complex freon molecules, while at higher E/p values (200 to 240), the excitation and consequent deexcitation of nitrogen molecules and its metastables seem to cause an increased rate of ionization of freon molecules.

Ionization and breakdown in sf6-air and freon-nitrogen mixtures

The sparking potentials and swarm coefficients (ionization and attachment coefficients) have been measured in sulphurhexafluoride- air and freon-nitrogen mixtures over the range of 110 ¿ E/p ¿ 240 V cm-1 torr-l and gas pressures varying between 1 and 20 torr, at 20°C. Addition of strongly attaching salphur-hexafluoride and freon gases increased the sparking potentials and the rate of increase of the attachment coefficient with increasing percentage of the strongly attaching gases in the mixtures was much larger than the rate of change of the first ionization coefficient.

Effect of mechanical cycling on the stress-strain response of a martensitic Nitinol shape memory alloy

An experimental investigation into the ambient temperature, load-controlled tension�tension fatigue behavior of a martensitic Nitinol shape memory alloy (SMA) was conducted. Fatigue life for several stress levels spanning the critical stress for detwinning was determined and compared with that obtained on an alloy similar in composition but in the austenitic state at room temperature. Results show that the fatigue life of the pseudo-plastic alloy is superior to superelastic shape memory alloy. The stress�strain hysteretic response, monitored throughout the fatigue loading, reveals progressive strain accumulation with the cyclic loading. In addition, the area of hysteresis and recoverable and frictional energies were found to decrease with increasing number of fatigue cycles. Post-mortem characterization of the fatigued specimens through calorimetry and fractography was conducted in order to get further insight into the fatigue micromechanisms. These results are discussed in terms of reversible and irreversible microstructural changes that take place during cyclic loading. Aspects associated with self-heating of martensitic alloy undergoing high frequency stress cycling are discussed.