Direct precipitation of lead zirconate titanate by the hydrothermal method

Direct precipitation of fine powders of lead zirconate titanate (PZT) in the complete range of solid solution, is investigated under hydrothermal conditions, starting from lead oxide and titania/zirconia mixed gels. The perovskite phase is formed in the temperature range of 165 – 340°C. Sequence of the hydrothermal reactions is studied by identifying the intermediate phases. The initial formation of PbO: TiO2 solid solution is followed by the reaction of the same with the remaining mixed gels giving rise to X-ray amorphous PZT phase. Further, through crystallite growth, the X-ray crystalline PZT is formed. This method can be extended for the preparation of PLZT powder as well. The resulting powders are sinterable to high density ceramics.

BaSnO3 fine powders from hydrothermal preparations

Attempts to prepare BaSnO3 by the hydrothermal method starting from SnO2·xH2O gel and Ba (OH)2 solution in teflonlined autoclaves at 150–260°C invariably lead to the formation of a hydrated phase, BaSn(OH)6·3H2O. On heating in air or on releasing the pressure Image at ≈260°C, BaSN (OH)6·3H2O converts to BaSnO3 fine powder which involves the formation of an intermediate oxyhydroxide, BaSnO(OH)4. TEM studies show that particle size of the resulting BaSnO3 ranges from 0.2–0.6 μm. Solid solutions of Ba(Ti, Sn) O3 were prepared from (TiO2+SnO2)·xH2O mixed gel and Ba(OH)2 solutions. Single-phase perovskite Ba(Ti, Sn)O3 was obtained up to 35 atom % Sn. Above this composition, the hydrothermal products are mixtures of BaTiO3 (cubic) and BaSn(OH)6·3H2O which on heating at ≈260°C give rise to BaTiO3+BaSnO3. Annealing at 1000°C results in monophasic Ba(Ti, Sn)O3, in the complete range of Sn/Ti. Formation of the hydrated phase is attributed to the amphoteric nature of SnO2·xH2O gel which stabilises Sn(OH)62− anions under higher H2O-pressures and elevated temperatures. The sintering characteristics and dielectric properties of ceramics prepared from these fine powders are presented.

Optimal hydrothermal load flow: Formulation and a successive approximation solution for fixed head systems

This paper deals with the optimal load flow problem in a fixed-head hydrothermal electric power system. Equality constraints on the volume of water available for active power generation at the hydro plants as well as inequality constraints on the reactive power generation at the voltage controlled buses are imposed. Conditions for optimal load flow are derived and a successive approximation algorithm for solving the optimal generation schedule is developed. Computer implementation of the algorithm is discussed, and the results obtained from the computer solution of test systems are presented.

Hydrothermal synthesis of polycrystalline carbonates

Polycrystals of orthorhobic carbonates RCO3 (R = Sr, Ba and Pb) were synthesised for the first time using formic acid as mineraliser. The unit cell parameters of this synthetic pure carbonates are: BaCO3:a=5.309, B=8.889, C=6.401; srCO3:a=5.108, B=8.420, C=6.040; PbCO3: A=5.176, B=8.511, C=6.137.

Hydrothermal phase equilibria in Ln2O3-H2O-CO2 systems : I. The lighter lanthanides

Phase diagrams for Nd2O3-H2O-CO2 and Gd2O3-H2O-CO2 systems at 1500 atm are given along with the results of selected runs in La, Sm and Eu systems. The stable phases in systems of La and Nd, are Ln(OH)CO3-B, Ln2O2CO3-II and LnOOH, in addition to the Ln(OH)3 phase at extremely low partial pressures of CO2 in the system. The systems become more and more complex with decreasing ionic radi and the number of stable carbonate phases increases. Ln2(CO3)3 · 3H2O orthorhombic (tengerate-like phase) is stable from Sm to Gd in addition to the other phases. The Gd(OH)CO3-A (ancylite-like phase) is hydrothermally stable at XCO2 greater-or-equal, slanted 0.5 while its hexagonal polymorph, Gd(OH)CO3-B is stable at low partial pressures of CO2 in the system.

Ultrafine powders of SrTiO3 from the hydrothermal preparation and their catalytic activity in the photolysis of water

Ultrafine powders of SrTiO3 are prepared at 100–150°C by the hydrothermal method, starting from TiO2·xH2O gel and Sr(OH)2 and H2O-isopropanol mixed solvent as the medium, The X-ray diffractograms of the powder show line broadening. The minimum crystallite size obtained ranges from 5 to 20nm with 20% H2O-80% C3H7OH as the reaction medium, as estimated from X-ray half-peak widths and TEM studies. The electron diffraction results indicate high concentration of lattice defects in these crystallites. The optical spectra of the particle suspensions in water show that the absorption around the band gap is considerably broadened, together with the appearance of maxima in the far ultraviolet. Aqueous suspensions of SrTiO3 powders, as such, do not produce H2 or O2 on UV irradiation. After coating with rhodium, H2 and O2 are evolved on illumination. However, the turn over number of O2 is lower than the stoichiometrically expected values from the corresponding values of H2. No correlation of the photocatalytic activity with surface area is observed. The activity of Rh-SrTiO3 slowly deteriorates with extended period of irradiation.

Hydrothermal phase equilibria studies in Ln2O3---H2O systems and synthesis of cubic lanthanide oxides

Phase diagrams for the systems Ln2O3---H2O (Ln = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Lu and Y) studied at 5000 to 10,000 psi and temperature range of 200–900°C, show that Ln(OH)3 hexagonal and LnOOH monoclinic are the only stable phases from Nd to Ho. The cubic oxide phase (C---Ln2O3) is stable for systems of Er, Tm, Yb and Lu, with no evidence of its equilibrium in the systems of lighter lanthanides. Using strong acids, HNO3 and HCOOH, as mineralisers the cubic oxides could be stabilised from Eu down to Lu. Solid solution phases of CeO2---Y2O3 and Eu2O3---Y2O3 have also been synthesised with HNO3 as mineraliser, since these compounds have promising use as solid electrolyte and phosphor materials respectively.

Preparation of CaTiO3 fine powders by the hydrothermal method

Fine powders consisting of 0.1–0.5 μm size crystallites of CaTiO3 are prepared at 150–200°C by the hydrothermal method starting from hydrated titania gel and reactive calcium oxide suspended as an aqueous slurry in an autoclave. The resulting high-purity CaTiO3 is characterised by TEM, X-ray powder diffraction, chemical analyses and sintering characteristics. The hydrothermally prepared CaTiO3 powders are sinterable to high-density ceramics below 1400°C. The dc conductivity behaviour of the chemically reduced ceramics is presented.

Hydrothermal preparation of Ba(Ti,Zr)O3 fine powders

Fine powders consisting of aggregated submicron crystallites of Ba(Ti,Zr)O3 in the complete range of Ti/Zr ratios are prepared at 85–130°C by hydrothermal method, starting from TiO2 + ZrO2 · xH2O mixed gel and Ba(OH)2 solution. The products obtained below 110°C incorporate considerable amounts of H2O and OH− within the lattice. As-prepared BaTiO3 is cubic and converts to tetragonal phase after the heat treatment at 1200°C, accompanied by the loss of residual hydroxyl ions. TEM investgations of the growth features show a transformation of the gel to the crystallite. Ba2+ ions entering the gel produce chemical changes within the gel, followed by dehydration, resulting in a cubic perovskite phase irrespective of Ti/Zr. The sintering properties of these powders to fine-grained, high density ceramics and their dielectric properties are presented.

Hydrothermal synthesis of Ba(Ti, Sn)O3 fine powders and dielectric properties of the corresponding ceramics

Fine powders of submicron-sized crystallites of BaTiO3 were prepared at 85–130°C by the hydrothermal method, starting from TiO2.ξH2O gel and Ba(OH)2 solution. The products obtained below 110°C incorporated considerable amounts of H2O and OH− in the lattice. As-prepared BaTiO3 is cubic and converts to the tetragonal phase after heat treatment at 1200°C, accompanied by the loss of residual OH− ions. Hydrothermal reaction of SnO2.ξH2O gel with Ba(OH)2 at 150–260°C gives rise to the hydrated phase, BaSn(OH)6.3H2O, due to the amphoteric nature of SnO2.ξH2O which stabilises Sn(OH)62− anions in basic media. On heating in air or releasing the pressure in situ at 260°C, BaSn(OH)6.3H2O converts to BaSnO3 through an intermediate, BaSnO(OH)4. Solid solutions of Ba(Ti,Sn)O3 are directly formed from (TiO2 + SnO2)..ξH2O gel up to 35 mol% SnO2. At higher Sn contents, the hydrothermal products are mixtures of BaSn(OH)6.3H2O and BaTiO3, which on annealing at 1000°C result in monophasic Ba(Ti,Sn)O3. The sintering characteristics and the dielectric properties of the ceramics prepared out of these fine powders are presented. The dielectric properties of fine-grained Ba(Ti,Sn)O3 ceramics are explained on the basis of the prevailing diffuse phase transition behaviour.

Correlation Between The Stability Of Carbonates In Ternary Ln2o3-H2o-Co2 Hydrothermal Systems And Lanthanide Systematics

Phase diagrams for ternary Ln2O3-H2O-CO2 systems for the entire lanthanide series (except promethium) were studied at temperatures in the range 100–950 °C and pressures up to 3000 bar. The phase diagrams obtained for the heavier lanthanides are far more complex, with the appearance of a number of stable carbonate phases. New carbonates isolated from lanthanide systems (Ln ≡ Tm, Yb, Lu) include Ln6(OH)4(CO3)7, Ln4(OH)6-(CO3)3, Ln2O(OH)2CO3, Ln6O2(OH)8(CO3)3 and Ln12O7(OH)10(CO3)6. Stable carbonate phases common to all the lighter lanthanides are hexagonal LnOHCO3 and hexagonal Ln2O2CO3. Ln2(CO3)3• 3H2O is stable from samarium onwards and orthorhombic LnOHCO3 is stable from gadolinium onwards. On the basis of the appearance of stable carbonates, four different groups of lanthanides were established: lanthanum to neodymium, promethium to europium, terbium to erbium and thulium to lutetium. Gadolinium is the connecting element between groups II and III. This is in accordance with the tetrad classification for f transition elements.

Precipitation of rutile and anatase (Tio12) fine powders and their conversion to MTiO3 (M = Ba, Sr, Ca) by the hydrothermal method

Fine powders of TiO2 (rutile) with high degree of crystallinity are formed from aqueous titanium oxychloride solution under hydrothermal conditions at 160–230°C and 15–100 kg/cm2 for 1–2 hours. The anatase phase is produced from the same medium when sulfate ion impurity is present, with Image . Both these fine powders are converted to BaTiO3, SrTiO3 or CaTiO3 when suspended in Ba(OH)2 or Sr(OH)2 solution or in an aqueous slurry of carbonate-free CaO with Image , at 180–280°C and 12–65 kg/cm2 for 4–8 hours. The resulting fine powders contain monocrystallites of the perovskite phase with 0.1–1.5 μm particle size.

Sacrificial photolysis of water on TiO2 fine powders prepared by the hydrothermal method

The often discussed role of surface hydroxylation of TiO2 particles as an essential characterestics for their photocatalytic activity can be verified by preparing TiO2 powders by hydrothermal method since hydroxylated surface layers will be better retained on these particles formed in superheated water. Thus, fine powders of TiO2 (rutile) with high degree of crystallinity are formed from titanium oxychloride in the mixed solvent of water and 2-propanol at 160–230°C and 20–120 atm. The anatase phase is produced from the same medium when sulfate ion impurity is present, with Image . TiO2 powders are washed free of anions and 2-propanol by ultrafiltration and are Pt mounted by a photochemical method. Aqueous suspensions of both forms of TiO2 neither as such nor after Pt-loading, do not produce H2 on band gap illumination whereas, H2 is generated in presence of hole scavengers such as EDTA, TEOA, sulfite or hypophosphite. The effects of hole scavenger concentration, Pt : TiO2 ratio, particulate suspension density and the nature of hole scavengers on H2 production are presented. Platinised rutile powders are equally active as anatase in sacrificial systems.

Hydrothermal phase equilibria in Ln2O3-H2O-CO2 systems for Tm, Yb and Lu

Phase diagrams for Tm2O3-H2O-CO2. Yb2O3-H2O-CO2 and Lu2O3-H2O-CO2 systems at 650 and 1300 bars have been investigated in the temperature range of 100–800°C. The phase diagrams are far more complex than those for the lighter lanthanides. The stable phases are Ln(OH)3, Ln2(CO3)3.3H2O (tengerite phase), orthorhombic-LnOHCO3, hexagonal-Ln2O2CO3. LnOOH and cubic-Ln2O3. Ln(OH)3 is stable only at very low partial pressures of CO2. Additional phases stabilised are Ln2O(OH)2CO3and Ln6(OH)4(CO3)7 which are absent in lighter lanthanide systems. Other phases, isolated in the presence of minor alkali impurities, are Ln6O2(OH)8(CO3)3. Ln4(OH)6(CO3)3 and Ln12O7(OH)10,(CO3)6. The chemical equilibria prevailing in these hydrothermal systems may be best explained on the basis of the four-fold classification of lanthanides.