Texture dependent stress corrosion failure of commercial titanium sheets in bromine-methanol solution

The stress corrosion cracking (SCC) characteristics of agr-titanium sheets in a bromine-methanol solution have been studied in the annealed and cold-rolled conditions using longitudinal and transverse specimens. The times to failure for annealed longitudinal specimens were longer than those for similarly tested transverse specimens. The cold-rolled specimens developed resistance to SCC, but failed by cleavage when notched, unlike the intergranular separation in annealed titanium. The apparent activation energy was found to be texture dependent and was in the range 30 to 51 kJ mol–1 for annealed titanium, and 15kJ mol–1 for cold-rolled titanium. The dependence of SCC behaviour on the texture is related to the changes in the crack initiation times. These are caused by changes in the passivation and repassivation characteristics of the particular thickness plane. The thickness planes are identified with the help of X-ray pole figures obtained on annealed and cold-rolled material. On the basis of the activation energy and the electrochemical measurements, the mechanism of SCC in annealed titanium is identified to be the one involving stress-aided anodic dissolution. On the other hand, the results on the cold-rolled titanium are in support of the hydrogen embrittlement mechanism consisting of hydride precipitation. The cleavage planes identified from the texture data match with the reported habit planes for hydride formation.

Growth and defect characterization of L-arginine phosphate monohydrate

L-arginine phosphate monohydrate (LAP) is a relatively new organic nonlinear optical material. In this paper, the results of our recent investigations on the growth of this crystal are presented. The growth of the undesirable micro-organisms was prevented by protecting the solution surface by placing a thick layer of n-hexane over it. Colouration of the solution could be avoided by keeping the growth temperature low and by protecting it from light. The effect of pH value of the solution on the solubility and habit was analysed. The grown crystals were characterized by means of X-ray topography.

Defect characterization of KTP single crystals

Potassium titanyl phosphate (KTP) is a relatively new nonlinear optical material with excellent combination of physical properties. This paper presents the combined etching and X-ray topographic studies carried out on KTP crystals with a view to characterizing their defects. KTP crystals employed in this investigation were grown from flux. Optical microscopic study of habit faces revealed growth layers and growth hillocks on (100) and (011) faces respectively. Etching of (011) habit faces proved that growth hillocks corresponded to the emergence point of dislocation out crops on these faces. The suitability of the new etchant to reveal dislocation was confirmed by etching the matched pairs obtained by cleaving. The defects present in the crystal were also studied by X-ray topography. The defect configuration in these crystals is characteristic of crystals grown from solution. The dislocations arc predominantly linear with their origin either at the nucleation centre or inclusions. In general, grown crystals were found to have low dislocation density and often large volumes of crystals free from dislocation could be obtained.

Plate-shaped transformation products in zirconium-base alloys

Plate-shaped products resulting from martensitic, diffusional, and mixed mode transformations in zirconium-base alloys are compared. in the present study. These alloys are particularly suitable for the comparison in view of the fact that the lattice correspondence between the parent beta (bcc) and the product alpha (hcp) or gamma-hydride (fct) phases are remarkably similar for different types of transformations. Crystallographic features such as orientation relations, habit planes, and interface structures associated with these transformations have been compared:, with a view toward examining whether the transformation mechanisms have characteristic imprints on these experimental observables. Martensites exhibiting dislocated lath, internally twinned plate, and self-accommodating three-plate cluster morphologies have been encountered in Zr-2.5Nb alloy. Habit planes corresponding to all these morphologies have been found to be consistent with the predictions based on the invariant plane strain (IFS) criterion. Different morphologies have been found to reflect the manner in which the neighboring martensite variants are assembled. Lattice-invariant shears (LISs) for all these cases have been identified to be either {10 (1) over bar 1}(alpha) ((1) over bar 123)(alpha) slip or twinning on (10 (1) over bar 1)(alpha) planes. Widmanstatten alpha precipitates, forming in a step-quenching treatment, have been shown to have a lath morphology, the alpha/beta interface being decorated with a periodic array of (c + a) dislocations at a spacing of 8 to 10 nm. The line vectors of these dislocations are nearly parallel to the invariant lines. The alpha precipitates, forming in the retained beta phase on aging, exhibit an internally twinned structure with a zigzag habit plane. Average habit planes for the morphologies have been found to lie near the {103}(beta) - {113}(beta) poles, which are close to the specific variant of the {112}(beta) plane, which transforms into a prismatic plane of the type {1 (1) over bar 00}(alpha). The crystallography of the formation of the gamma-hydride phase (fct) from both the alpha and beta phases is seen to match the IFS predictions. While the beta-gamma transformation can be treated approximately as a simple shear on the basal plane involving a change in the stacking sequence, the alpha-gamma transformation call be conceptually broken into a alpha --> beta transformation following the Burgers correspondence and the simple beta-gamma shear process. The active eutectoid decomposition in the Zr-Cu system, beta --> alpha + beta', has been described in terms of cooperative growth of the alpha phase from the beta phase through the Burgers correspondence and of the partially ordered beta' (structurally similar to the equilibrium Zr2Cu phase) through an ordering process. Similarities and differences in crystallographic features of these transformations have been discussed. and the importance of the invariant line vector in deciding the geometry of the corresponding habit planes has been pointed out.

Woody plant seedling distribution under invasive Lantana camara thickets in a dry-forest plot in Mudumalai, southern India

Lantana camara, a shrub of Central and South American origin, has become invasive across dry forests worldwide. The effect of the thicket-forming habit of L. camara as a dispersal and recruitment barrier in a community of native woody seedlings was examined in a 50-ha permanent plot located in the seasonally dry forest of Mudumalai, southern India. Sixty 100-m(2) plots were enumerated for native woody seedlings between 10-100 cm in height. Of these, 30 plots had no L. camara thickets, while the other 30 had dense thickets. The frequency of occurrence and abundance of seedlings were modelled as a function of dispersal mode (mammal, bird or mechanical) and affinities to forest habitats (dry forest, moist forest or ubiquitous) as well as presence or absence of dense L. camara thickets. Furthermore, frequency of occurrence and abundance of individual species were also compared between thickets and no L. camara. At the community level, L. camara density, dispersal mode and forest habitat affinities of species determined both frequency of occurrence and abundance of seedlings, with the abundance of dry-forest mammal-dispersed species and ubiquitous mechanically dispersed species being significantly lower under L. camara thickets. Phyllanthus emblica and Kydia calycina were found to be significantly less abundant under L. camara, whereas most other species were not affected by the presence of thickets. It was inferred that, by affecting the establishment of native tree seedlings, L. camara thickets could eventually alter the community composition of such forests.

Worker piping triggers hissing for coordinated colony defence in the dwarf honeybee Apis florea

Defending a large social insect colony containing several thousands of workers requires the simultaneous action of many individuals. Ideally this action involves communication between the workers, enabling coordinated action and a fast response. The Asian dwarf honeybee, Apis florea, is a small honeybee with an open nesting habit and a comparatively small colony size, features that leave them particularly exposed to predators. We describe here a novel defence response of these bees in which the emission of an initial warning signal from one individual (“piping”) is followed 0.3 to 0.7 seconds later by a general response from a large number of bees (“hissing”). Piping is audible to the human ear, with a fundamental frequency of 384 ± 31Hz and lasting for 0.82 ± 0.35 seconds. Hissing is a broad band, noisy signal, clearly audible to the human observer and produced by slight but visible movements of the bees' wings. Hissing begins in individuals close to the piping bee, spreads rapidly to neighbours and results in an impressive coordinated crescendo occasionally involving the entire colony. Piping and hissing are accompanied by a marked decrease, or even cessation, of worker activities such as forager dancing and departures from the colony. We show that whereas hissing of the colony can be elicited without piping, the sequential and correlated piping and hissing response is specific to the presence of potential predators close to the colony. We suggest that the combined audio-visual effect of the hissing might deter small predators, while the cessation of flight activity could decrease the risk of predation by birds and insects which prey selectively on flying bees.

Crystallography of Hydride Formation in Zr-Nb Alloys

he crystallographic and morphological aspect associated with the formation of γ hydride phase (fct) from the β phase in β abilized Zr-20%Nb alloy has been reported. In this paper the βto γ transformation has been considered in the terms of the phenomenological theory of martensitic crystallography in order to predict the crystallographic features of the γ hydride in the β to γ transformation. The prediction made in the present analysis has been found to match very closely to the experimentally observed habit plane. The possibility of the α to γ transition through the formation of a transient β configuration has been examined.

Synthesis and characterization of nickel/barium hexa-aluminate composite coatings

Electrodeposition of nickel/barium hexa-aluminate (Ni/BHA) composite coatings has been carried out from a Watt's bath on mild steel substrate. BHA powders with plate habit were synthesized by solution combustion synthesis followed by heat treatment to ensure complete conversion to the hexa-aluminate phase. Heat treated material was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) combined with X-ray analysis. The dispersion behaviour and stability of BHA suspensions with cationic and anionic surfactants at room temperature were studied by dynamic light scattering under different pH. The influence of BHA concentration in the electrolytic bath, deposition temperature, pH, current density and duty cycle on particle incorporation in the coatings were studied and conditions for maximum particle incorporation were established. Coatings with a roughness of about 0 center dot 4 mu m were produced by using this technique. Effect of BHA content on microhardness was also investigated. A reasonably good thickness of the coatings was achieved in a given set of conditions.

Lithium D-Isoascorbate Monohydrate, a New Nonlinear Optical Material

Single crystals of lithium D-isoascorbate monohydrate (LDAM), (C6H7O6Li center dot H2O), are grown by a solution growth method. The crystal structure of LDAM is solved using single crystal X-ray diffraction. The space group is orthorhombic P2(1)2(1)2(1) with four formula units per unit cell and lattice parameters a = 7.7836(3) angstrom, b = 8.7456(3) angstrom, and c = 11.0368(4) angstrom. Solubility of the material in water is determined thermogravimetrically and found to have a positive temperature coefficient of solubility. Large optical quality single crystals are subsequently grown from aqueous solution by a slow cooling method. The crystal has a bulky prismatic habit and among the prominent faces the c face appears as the only principal morphological face. The crystal exhibits a (010) cleavage. Dielectric spectroscopy reveals a nearly Debye type Cole-Cole behavior with anisotropy in relaxation. Optical transmission range is found to be from 300 to 1400 nm. The principal refractive indices of this biaxial crystal, measured using Brewster's angle method, at wavelengths 405, 543, and 632.8 nm, show high dispersion. The crystal is negative biaxial with 2V(z) = 107.8 degrees (405 nm) and belongs to the Hobden class 3. Theoretically generated type 1 and type 2 second order phase matching curves match very well with the experimental results. The second-order nonlinear coefficient d(14) was determined to be 7 x 10(-13) m/V. For the optimum phase matching direction (type 2), the second-order effective nonlinear coefficient and the walk off angle are determined to be 0.84 times d(14) and 3.5 degrees respectively. The crystal possesses high multiple surface damage thresholds of 18 GW/cm(2) and 8 GW/cm(2) at laser wavelengths 1064 and 532 nm, respectively.

Studies on lithium L-ascorbate dihydrate: An interesting chiral nonlinear optical crystal

Lithium L-Ascorbate dihydrate (LLA) is a new metal organic nonlinear optical crystal belonging to the saccharide family. Single crystals of LLA were grown from aqueous solution. Solubility of the crystal has a positive temperature coefficient facilitating growth by slow cooling. Rietveld refinement was used to confirm the phase formation. The crystal has prismatic habit with (010), (001) and (10-1) prominent faces. Thermal analysis shows that the crystal is stable up to 102 degrees C. Transmission spectrum of the crystal extends from 302 nm to 1600 nm. Dielectric spectroscopic analysis revealed Cole Cole behaviour and prominent piezoelectric resonance peaks were observed in the range of 100-200 kHz. Second harmonic generation (SHG) conversion efficiency of up to 2.56 times that of a phase matched KDP crystal was achieved when the (010) plate of LLA single crystal was rotated about the +ve c axis, by 9.4 degrees in the clockwise direction. We also observed SHG conical sections which were attributed to noncollinear phase matching. The observation of the third conical section suggests very high birefringence and large nonlinear coefficients. A detailed study of surface laser damage showed that the crystal has high multiple damage thresholds of 9.7 GW cm(-2) and 42 GW cm(-2) at 1064 nm and 532 nm radiation respectively. (C) 2012 Elsevier B.V. All rights reserved.