Electro-Oxidation of Borohydride on Rhodium, Iridium, and Rhodium-Iridium Bimetallic Nanoparticles with Implications to Direct Borohydride Fuel Cells

Electrochemical oxidation of borohydride is studied on nanosized rhodium, iridium, and bimetallic rhodium-iridium catalysts supported onto Vulcan XC72R carbon. The catalysts are characterized by X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy in conjunction with cyclic voltammetry and polarization studies. The studies reveal that a 20 wt % bimetallic Rh-Ir catalyst supported onto carbon (Rh-Ir/C) is quite effective for the oxidation of borohydride. Direct borohydride fuel cell with Rh-Ir/C as the anode catalyst and Pt/C as the cathode catalyst exhibits a peak power density of 270 mW/cm(2) at a load current density of 290 mA/cm(2) as against 200 mW/cm(2) at 225 mA/cm(2) for Rh/C and 140 mW/cm(2) at 165 mA/cm(2) for Ir/C while operating at 80 degrees C. The synergistic catalytic activity for the bimetallic Rh-Ir nanoparticles toward borohydride oxidation is corroborated by density-functional theory calculations using electron-localization function. (C) 2010 The Electrochemical Society. [DOI:10.1149/1.3442372] All rights reserved.

Pt metal-CeO2 interaction: Direct observation of redox coupling between Pt-0/Pt2+/Pt4+ and Ce4+/Ce3+ states in Ce0.98Pt0.02O2-delta catalyst by a combined electrochemical and x-ray photoelectron spectroscopy study

Pt ions-CeO2 interaction in Ce1-xPtxO2-delta (x=0.02) has been studied for the first time by electrochemical method combined with x-ray diffraction and x-ray photoelectron spectroscopy. Working electrodes made of CeO2 and Ce0.98Pt0.02O2-delta mixed with 30% carbon are treated electrochemically between 0.0-1.2 V in potentiostatic (chronoamperometry) and potentiodynamic (cyclic voltametry) mode with reference to saturated calomel electrode. Reversible oxidation of Pt-0 to Pt2+ and Pt4+ state due to the applied positive potential is coupled to simultaneous reversible reduction of Ce4+ to Ce3+ state. CeO2 reduces to CeO2-y (y=0.35) after applying 1.2 V, which is not reversible; Ce0.98Pt0.02O2-delta reaches a steady state with Pt2+:Pt4+ in the ratio of 0.60:0.40 and Ce4+:Ce3+ in the ratio of 0.55:0.45 giving a composition Ce0.98Pt0.02O1.74 at 1.2 V, which is reversible. Composition of Pt ion substituted compound is reversible between Ce0.98Pt0.02O1.95 to Ce0.98Pt0.02O1.74 within the potential range of 0.0-1.2 V. Thus, Ce0.98Pt0.02O2-delta forms a stable electrode for oxidation of H2O to O-2 unlike CeO2. A linear relation between oxidation of Pt2+ to Pt4+ with simultaneous reduction in Ce4+ to Ce3+ is observed demonstrating Pt-CeO2 metal support interaction is due to reversible Pt-0/Pt2+/Pt4+ interaction with Ce4+/Ce3+ redox couple.

An EXAFS study of the cobalt-molybdenum/.gamma.-alumina hydrodesulfurization catalyst

While Mo in the Co-Mo/y-A1203 hydrodesulfurization catalyst is present as a sulfidic species similar to MoS2, Co shows two types of coordination, one with six sulfurs (but not a bulk sulfide) and the other with four oxygens. The significance of such species is discussed. In addition to an additive relation of the EXAFS function and the residual spectra, the ratio of amplitude terms of the catalyst and the model system has been employed in the analysis.

A kinetic study of the methanation of CO2 over Ni-Al2O3 catalyst

CO2 methanation has been studied over Ni-Al2O3 and the intrinsic kinetic data obtained are related by a powerlaw type rate expression, which established a good agreement between calculated and experimental values of conversion.

In Situ Phase Separation Following Dehydration in Bimetallic Sulfates: A Variable-Temperature X-Ray Diffraction Study

Phase separation resulting in a single-crystal-single-crystal transition accompanied by a polycrystalline phase following the dehydration of hydrated bimetallic sulfates [Na2Mn1.167(SO4)(2)S0.33O1.167 center dot 2H(2)O and K4Cd3-(SO4)(5)center dot 3H(2)O] has been investigated by in situ variable-temperature single-crystal X-ray diffraction. With two examples, we illustrate the possibility of generating structural frameworks following dehydration in bimetallic sulfates, which refer to the possible precursor phases at that temperature leading to the mineral formation. The room-temperature structure of Na2Mn1.167(SO4)(2)S0.33O1.167 center dot 2H(2)O is trigonal, space group R (3) over bar. On heating the crystal in situ on the diffractometer, the diffraction images display spherical spots and concentric rings suggesting phase separation, with the spherical spots getting indexed in a monoclinic space group, C2/c. The structure determination based on this data suggests the formation of Na2Mn(SO4)(2). However, the diffraction images from concentric rings could not be indexed. In the second example, the room-temperature structure is determined to be K4Cd3(SO4)(5)center dot 3H(2)O, crystallizing in a monoclinic space group, P2(1)/n. On heating the crystal in situ, the diffraction images collected also have both spherical spots and diffuse rings. The spherical spots could be indexed to a cubic crystal system, space group P2(1)3, and the structure is K4Cd3(SO4)(3). The possible mechanism for the phase transition in the dehydration regime resulting in this remarkable single-crystal to single-crystal transition with the appearance of a surrogate polycrystalline phase is proposed.

Ce1-xRuxO2-delta (x=0.05, 0.10): A New High Oxygen Storage Material and Pt, Pd-Free Three-Way Catalyst

Nanocrystalline Ce1-xRuxO2-delta (x = 0.05 and 0.10) of 8-10 nm sizes have been synthesized by hydrothermal method using melamine as complexing agent. Compounds have been characterized by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and energy-dispersive X-ray analysis (EDX) and their structures have been refined by the Rietveld method.The compounds crystallize in fluorite structure and the composition is Ce1-xRuxO2-x/2 where Ru is in +4 state and Ce is in mixed-valence (+3, +4) state. Substitution of Ru4+ ion in CeO2 activated the lattice oxygen. Ce1-xRuxO2-x/2 reversibly releases 0.22[O] and 0.42[O] for x = 0.05 and 0.10, respectively, which is higher than the maximumpossible OSC of 0.22 [O] observed for Ce0.50Zr0.50O2. Utilization of Higher OSC of Ce1-xRuxO2-delta (x = 0.05 and 0.10) is also reflected in terms of low-temperature CO oxidation with these catalysts, both in the presence and absence of feed oxygen. The Ru4+ ion acts as an active center for reducing molecules (CO, hydrocarbon ``HC'') and oxide ion vacancy acts as an active center for O-2 and NO, leading to low-temperature NO conversion to N-2. Thus due to Ru4+ ion, Ce1-xRuxO2-delta is not just a high oxygen storage material but also shows high activity toward CO, hydrocarbon ``HC'' oxidation, and NO reduction by CO at low temperature with high N-2 selectivity for three-way catalysis.

Effectiveness factor for zeroth-order catalytic reactions with volume change and nonuniform catalyst activity profiles

Analytical solutions are presented for the effectiveness factor of a zeroth-order reaction with volume change and nonuniform catalyst activity profile in slab, cylinder and spherical pellets. The possibility of shape normalization is considered for a variety of activity profiles and pellet shapes. When the catalyst activity at the external surface of the pellet is non-zero, shape normalization is obtained, which makes the asymptotic behavior of the effectiveness factor identical for small and large values of Thiele modulus, however, the normalization can lead to significant errors, particularly for the case of activity profiles decreasing towards the outer surface of the catalyst.

On the non-existence of hydrodynamic solution of surface plasmons at the bimetallic interface

It is shown that for an abrupt bimetallic interface a hydrodynamic solution for interface plasmons does not exist. It appears that this result is valid irrespective of the choice of of the additional boundary condition, thereby suggesting a careful look at the use of usual hydrodynamic equations for a bimetallic interface.

Kinetics of vapour phase oxidation of furfural on vanadium catalyst

Vapour phase oxidation of furfural over vanadium pentoxide catalyst was studied using an isothermal flow reactor in the temperature range of 220–280°C. Maleic anhydride and carbon dioxide are found to be formed from furfural by a parallel reaction scheme. The following rate equation based on the two-stage redox mechanism—the substance to be oxidized reduces the catalyst which in turn is reoxidized by oxygen from the feed—is found to explain the data satisfactorily.The reoxidation of the reduced catalyst was found to be the rate controlling step.

Mechanism of vapour phase oxidation of anthracene over cobalt molybdate catalyst

Vapour phase oxidation of anthracene over cobalt molybdate catalyst was investigated in an isothermal flow reactor in the temperature range of 280—340°C. Fifteen different models based on redox, Langmuir—Hinshelwood and Rideal mechanisms were tested in order to elucidate the mechanism of the above reaction. These models were compared on the basis of three criteria and were finally discriminated employing the non-intrinsic parameter method. Two-stage redox mechanism was found to explain the data satisfactorily.

Kinetics of vapour phase oxidation of furfural on vanadium catalyst

Vapour phase oxidation of furfural over vanadium pentoxide catalyst was studied using an isothermal flow reactor in the temperature range of 220–280°C. Maleic anhydride and carbon dioxide are found to be formed from furfural by a parallel reaction scheme. The following rate equation based on the two-stage redox mechanism—the substance to be oxidized reduces the catalyst which in turn is reoxidized by oxygen from the feed—is found to explain the data satisfactorily. The reoxidation of the reduced catalyst was found to be the rate controlling step.

Mechanism of vapour phase oxidation of anthracene over cobalt molybdate catalyst

Vapour phase oxidation of anthracene over cobalt molybdate catalyst was investigated in an isothermal flow reactor in the temperature range of 280—340°C. Fifteen different models based on redox, Langmuir—Hinshelwood and Rideal mechanisms were tested in order to elucidate the mechanism of the above reaction. These models were compared on the basis of three criteria and were finally discriminated employing the non-intrinsic parameter method. Two-stage redox mechanism was found to explain the data satisfactorily.

Catalyst effectiveness factor for redox model kinetic equation

A generalized isothermal effectiveness factor correlation has been proposed for catalytic reactions whose intrinsic kinetics are based on the redox model. In this correlation which is exact for asymptotic values of the Thiele parameter the effect of the parameters appearing in the model, the order of the reaction and particle geometry are incorporated in a modified form of Thiele parameter. The relationship takes the usual form: Image and predicts effectiveness factor with an error of less than 2% in a range of Thiele parameter that accommodates both the kinetic and diffusion control regimes.