On Coloration of Polyacrylonitrile: A Nuclear Magnetic Resonance Study

Coloration in polyacrylonitrile can be induced in three distinct ways: by heat treatment, by treatment with base, or during synthesis of the polymer itself using ionic initiators at relatively higher temperatures. The present investigation employing 'H and NMR spectroscopy has revealed some common features in colored polyacrylonitrile irrespective of ita mode of coloration. All colored polyacrylonitriles give an additional peak around S 2.7 in 'H NMR spectra and, except for heat-treated polyacrylonitrile, one extra group of peaks in the region 8 12-16 in 13C NMR spectra. The former peak has been attributed to methine and/or methylene protons in branched and/or cyclized structures, while the latter peak has been attributed to methylene carbon atoms in the branched structure. Colorless polyacrylonitriles have been found to be predominantly heterotactic, while colored polyacrylonitriles have been found to have appreciable isotactic contribution.

Optical, Electrochemical, and Structural Properties of Spray Coated Dihexyl Substituted Poly (3,4 propylene dioxythiophene) Film for Optoelectronics Devices

The dihexyl substituted poly (3,4-propylenedioxythiophene) (PProDOT-Hx(2)) thin films uniformly deposited by cost effective spray coating technique on transparent conducting oxide coated substrates. The electro-optical properties of PProDOT-Hx(2) films were studied by UV-Vis spectroscopy that shows the color contrast about 45% with coloration efficiency of approximate to 185cm(2)/C. The electrochemical properties of PProDOT-Hx(2) films were studied by cyclic voltammetry and AC impedance techniques. The cyclic voltammogram shows that redox reaction of films are diffusion controlled and ions transportation will be faster on the polymer film at higher scan rate. Impedance spectra indicate that polymer films are showing interface charge transfer process as well as capacitive behavior between the electrode and electrolyte. The XRD of the PProDOT-Hx(2) thin films revealed that the films are in amorphous nature, which accelerates the transportation of ions during redox process.