Synthesis of zinc oxide porous structures by anodization with water as an electrolyte

We report a simple, reliable and one-step method of synthesizing ZnO porous structures at room temperature by anodization of zinc (Zn) sheet with water as an electrolyte and graphite as a counter electrode. We observed that the de-ionized (DI) water used in the experiment is slightly acidic (pH=5.8), which is due to the dissolution of carbon dioxide from the atmosphere forming carbonic acid. Porous ZnO is characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectroscopy and photoluminescence (PL) studies. The current-transient measurement is carried out using a Gamry Instruments Reference 3000 and the thickness of the deposited films is measured using a Dektak surface profilometer. The PL, Raman and X-ray photoelectron spectroscopy are used to confirm the presence of ZnO phase. We have demonstrated that the hybrid structures of ZnO and poly (3,4-ethylenedioxythiophene):poly (styrene sulfonate) (PEDOT:PSS) exhibit good rectifying characteristics. The evaluated barrier height and the ideality factor are 0.45 eV and 3.6, respectively.

Anodization of sputtered metallic films: The microstructural connection

A simple microstructural rationale for successful anodization of metallic films into ordered oxide nanostructures has been identified. It applies to three of the most commonly studied systems, Zr, Ti and Al films and can be extended to other such oxides. A dense Zone T or II microstructure, in sputtered films, is the most critical ingredient. While T-substrate > 0.3T(melting) Ching is the simplest route, pressure and plasma heating can also be exploited. Such microstructures are also associated with a unique growth stress signature. (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Anodization of Aluminium using a fast two-step process

Ultra-fast two-step anodization method is developed for obtaining ordered nano-pores on aluminium (Al) foil. First anodization was carried out for 10 min, followed by 3 min of second anodization at high voltage (150 V) compared to previous reports of anodization times of 12 h (40-60 V). The pore dimensions on anodized alumina are 180 nm for pore diameter and 130 nm for inter-pore distance. It was evident that by increasing the anodization voltage to 150 V, the diameter of the pores formed was above 150 nm. The electrolyte and its temperature affect the shape and size of the pore formation. At lower anodization temperature, controlled pore formation was observed. The anodized samples were characterized using the field emission scanning electron microscope (FE-SEM) to determine the pore diameter and inter-pore distance. Using UV-Visible spectroscopy, the reflectance spectra of anodized samples were measured. The alumina (Al2O3) peaks were identified by x-ray diffraction (XRD) technique. The x-ray photo electron spectroscopy (XPS) analysis confirmed the Al 2p peak at 73.1 eV along with the oxygen O 1s at 530.9 eV and carbon traces C 1s at 283.6 eV.

Adherent Nanoporous Anatase TiO2 Membranes on Stainless Steel Substrates

Nanostructured TiO2 is one of the most commonly used materials in photocatalytic applications and photochemical solar cells. This article describes a method to synthesize nanoporous anatase TiO2 membranes directly on stainless steel (SS), an easily available substrate by anodization to form amorphous TiO2 and a subsequent heat treatment to convert it into anatase, the photoactive phase. To obtain adherent membranes with interfaces that are resistant to peeling, both anodization and heat treatment parameters need to be optimized to obtain a heterostructure that contains a Ti film between the TiO2 membrane and the substrate.

On Using Nanoporous Alumina Films as Tribological Coating

Anodization of aluminum alloys is a common surface treatment procedure employed for the protection against corrosion. A thin amorphous layer of alumina is formed on the surface of alloy, which seals the alloy surface from the surrounding. This alumina layer being harder than the base aluminum alloy can be useful as a tribological coating. But since this alumina layer is randomly formed with disordered voids and pores, predicting the mechanical properties is difficult. Specific anodizing conditions can be used to form highly ordered anodic nanoporous alumina films 1] on the aluminum alloy surface. These nanoporous alumina layer can be effectively used as a tribological coating, because of the highly ordered controllable geometry and the empty pores which can be used as reservoirs for lubricant.