Combustion synthesis and properties of fine-particle rare-earth-metal zirconates, Ln2Zr2O7

Fine-particle rare-earth-metal zirconates, Ln2Zr2O7, where Ln = La, Ce, Pr, Nd, Sm, Gd and Dy having the pyrochlore structure have been prepared using a novel combustion process. The process employs aqueous solutions of the corresponding rare-earth-metal nitrate, zirconium nitrate and carbohydrazide/urea in the required molar ratio. When the solution is rapidly heated to 350–500 °C it boils, foams and burns autocatalytically to yield voluminous oxides. The formation of single-phase Ln2Zr2O7 has been confirmed by powder X-ray diffraction, infrared and fluorescence spectroscopy. The solid combustion products are fine, having surface areas in the range 6–20 m2 g–1. The cold-pressed Pr2Zr2O7 compact when sintered at 1500 °C, 4 h in air, achieved 99% theoretical density.

Potentiometric determination of the gibbs energies of formation of SrZrO3 and BaZrO3

The Gibbs free energies of formation of strontium and barium zirconates have been determined in the temperature range 960 to 1210 K using electrochemical cells incorporating the respective alkaline-earth fluoride single crystals as solid electrolytes. Pure strontium and barium monoxides were used in the reference electrodes. During measurements on barium zirconate, the oxygen partial pressure in the gas phase over the electrodes was maintained at a low value of 18.7 Pa to minimize the solubility of barium peroxide in the monoxide phase. Strontium zirconate was found to undergo a phase transition from orthorhombic perovskite to) with space group Cmcm; D-2h(17) to tetragonal perovskite (t) having the space group 14/mcm; D-4h(18) at 1123 (+/- 10) K. Barium zirconate does not appear to undergo a phase transition in the temperature range of measurement. It has the cubic perovskite (c) structure. The standard free energies of formation of the zirconates from their component binary oxides AO (A = Sr, Ba) with rock salt (rs) and ZrO2 with monoclinic (m) structures can be expressed by the following relations:SrO (rs) + ZrO2 (m) --> SrZrO3 (o) Delta G degrees = -74,880 - 14.2T (+/-200) J mol(-1) SrO (rs) + ZrO2 (m) --> SrZrO3 (t) Delta G degrees = -73,645 - 15.3T (+/-200) J mol(-1) BaO (rs) + ZrO2 (m) --> BaZrO4 (c) Delta G degrees = -127,760 - 1.79T (+/-250) J mol(-1) The results of this study are in reasonable agreement with calorimetric measurements reported in the literature. Systematic trends in the stability of alkaline-earth zirconates having the stoichiometry AZrO(3) are discussed.