Pt metal-CeO2 interaction: Direct observation of redox coupling between Pt-0/Pt2+/Pt4+ and Ce4+/Ce3+ states in Ce0.98Pt0.02O2-delta catalyst by a combined electrochemical and x-ray photoelectron spectroscopy study

Pt ions-CeO2 interaction in Ce1-xPtxO2-delta (x=0.02) has been studied for the first time by electrochemical method combined with x-ray diffraction and x-ray photoelectron spectroscopy. Working electrodes made of CeO2 and Ce0.98Pt0.02O2-delta mixed with 30% carbon are treated electrochemically between 0.0-1.2 V in potentiostatic (chronoamperometry) and potentiodynamic (cyclic voltametry) mode with reference to saturated calomel electrode. Reversible oxidation of Pt-0 to Pt2+ and Pt4+ state due to the applied positive potential is coupled to simultaneous reversible reduction of Ce4+ to Ce3+ state. CeO2 reduces to CeO2-y (y=0.35) after applying 1.2 V, which is not reversible; Ce0.98Pt0.02O2-delta reaches a steady state with Pt2+:Pt4+ in the ratio of 0.60:0.40 and Ce4+:Ce3+ in the ratio of 0.55:0.45 giving a composition Ce0.98Pt0.02O1.74 at 1.2 V, which is reversible. Composition of Pt ion substituted compound is reversible between Ce0.98Pt0.02O1.95 to Ce0.98Pt0.02O1.74 within the potential range of 0.0-1.2 V. Thus, Ce0.98Pt0.02O2-delta forms a stable electrode for oxidation of H2O to O-2 unlike CeO2. A linear relation between oxidation of Pt2+ to Pt4+ with simultaneous reduction in Ce4+ to Ce3+ is observed demonstrating Pt-CeO2 metal support interaction is due to reversible Pt-0/Pt2+/Pt4+ interaction with Ce4+/Ce3+ redox couple.

X-ray and ultraviolet photoelectron spectroscopy studies of the interaction of carbon monoxide with oxygen adsorbed on silver covered with potassium, caesium or barium

X-ray and He(II) ultraviolet photoelectron spectroscopy studies of the interaction of CO with oxygen on potassium-, caesium- and barium-covered Ag surfaces have shown the formation of carbonate at 300 K. While on a caesium-covered surface only carbonate formation takes place, on the potassium- and barium-covered surfaces molecularly chemisorbed CO is also formed. The variation of the surface concentrations of carbon and oxygen with temperature has been examined and a reaction sequence for the interaction of CO with adsorbed oxygen on potassium-, caesium- and barium-covered Ag surfaces is suggested.

Ce CORE level X-ray photo electron spectroscopy of CeX2Si2 (X = Fe, Co, Ni and Cu)

Ce(3d) and (4d) core level XPS spectra of CeX = Fe, Co, Ni and Cu) suggest that the mean valence of Ce was as well as 4f hybridization strength decrease systematically from Fe to Cu. This observation is in agreement with the results of Bremstrahlung Isochromat Spectroscopy (BIS), but in disagreement with LIII-edge data reported earlier.

Study of strontium compounds and minerals by X-ray absorption spectroscopy. I. K-edge shifts

The chemical shifts in the X-ray K-absorption edge of strontium in various compounds and in six minerals are measured using a single crystal X-ray spectrometer. Besides valence, the shifts are found to be governed by ionic charges on the absorbing ions, which are calculated employing Pauling's method. For the minerals the plot of chemical shift against the theoretically calculated ionic charges is used to determine the charges on the strontium ions.

3d and 4d core level X-ray photoelectron spectroscopy of mixed-valence CePd3

3d and 4d core-level XPS spectra for CePd3, a mixed-valence system, have been measured. Each spectrum exhibits two sets of structures, each corresponding to one of the valence states of cerium. Thus the usefulness of XPS, which has so far not been used extensively to investigate the mixed-valence cerium systems, is pointed out.

Surface segregation and oxidation studies of Cu-Sn and Cu-Pd alloys by x-ray photoelectron and auger spectroscopy

X-ray photoelectron and Auger spectroscopic techniques have been employed to study surface segregation and oxidation of Cu-1 at%Sn, Cu-9at%Pd and Cu-25at%Pd alloys. Both Cu-Pd(9%) and Cu-Pd(25%) alloys show segregation of Cu when heated above 500 K. The Pd concentration was reduced by 50% at 750 K compared to the bulk composition; the enthalpy of segregation of Cu is around - 6kJ/mol. Sn segregation is seen from 470 to 650 K in the Cu-Sn(1%) alloy, and a saturation plateau of Sn concentration above 650 K is observed. Surface oxidation of Cu-Sn(1%) and Cu-Pd(9%) alloys at 500 K showed the formation of Cu2O on the surface with total suppression of Sn or Pd on the respective alloy surfaces. On vacuum annealing the oxidised Cu-Sn alloy surface at 550 K, a displacement reaction 2Cu2O+Sn→4Cu+SnO2 was observed. However, under similar annealing of the oxidised Cu-Pd(9%) alloy surface at 500 K, oxide oxygen was totally desorbed leaving the Cu-Pd alloy surface clean. In the case of the Cu-Pd(25%) alloy, only dissociatively chemisorbed oxygen was seen at 500 K which desorbed at the same temperature. Oxygen spill-over from copper to palladium is suggested as the mechanism of oxygen desorption from the oxidised Cu-Pd alloy surfaces.

Chlorination of silver dosed with potassium and barium in presence of oxygen: An X-ray photoelectron spectroscopy study

XPS studies show that the presence of chemisorbed chlorine stabilizes and also enhances molecular dioxygen species on Ag surfaces dosed with either K or Ba. The surface atomic oxygen is found to become depleted on chlorination. The variation in the nature of surface species with respect to temperature shows chlorine-induced diffusion of atomic oxygen into the subsurface region at 300 K. For coverages of potassium up to 8 × 1014 atoms/cm2, preferential chloridation of Ag occurs while at higher potassium coverages, KCl formation is distinctly observed on the surface. In the case of barium, two types of adsorbed chlorine species, Cl(α) and Cl(β), associated with Ag and Ba, respectively, are clearly seen even at low barium coverages. This is believed to be due to the higher valence occupation of barium compared to potassium. The Cl(α) species associated with Ag is found to occupy a preferred site on both K- and Ba-dosed surfaces, involving chemisorptive replacement of O(α) to the subsurface region.

Study of As2(Se,Te)3 glasses by X-ray absorption and photoelectron spectroscopy

Arsenic selenide-telluride glasses have been investigated by X-ray absorption and photoelectron spectroscopy. The core electron energy shifts and chemical shifts in K-absorption edge measurements associated with the glass-crystal transitions of pure As2Se3 and As2Te3 have been studied. The effect of composition on the core level energy and valence bands of As2(Se,Te)3 glasses, has been discussed. Mixed-composition glasses are found to be considerably ionic.

X-ray photoelectron spectroscopy of superconducting RuSr2Eu1.5Ce0.5Cu2O10 and nonsuperconducting RuSr2EuCeCu2O10

We report x-ray photoelectron spectroscopic investigation of RuSr2Eu1.5Ce0.5Cu2O10 with ferromagnetic T-C similar to 100 K and a superconducting transition temperature of similar to 30 K compared with RuSr2EuCeCu2O10, which is a ferromagnetic (T-C similar to 150 K) insulator. Our results show that the rare earths, Eu and Ce, are in 3+ and 4+ states, respectively. Comparing the Ru core level spectra from these compounds to those from two Ru reference oxides, we also show that Ru in these ruthenocuprates is always in 5+ state, suggesting that the doped holes in the superconducting compound arising from the substitution of Ce4+ by Eu3+ are primarily in the Cu-O plane, in close analogy to all other doped high-T-C cuprates. Analysis of Cu 2p spectra in terms of a configuration interaction model provides a quantitative description of the gross electronic structures of these ruthenocuprates.

Nature of Pb in superconducting cuprates containing lead: A Pb L3 x‐ray absorption near‐edge spectroscopy study

X‐ray absorption near‐edge spectroscopy studies show that Pb in superconducting Tl0.5Pb0.5CaSr2Cu2O7+δ is essentially in the 4+ state while it is in the 2+ state in Pb2Sr2Ca1−xLnxCu3O8+δ.

Electronic structure of high-Tc Ba0.6K0.4BiO3 by x-ray photoelectron spectroscopy

We have investigated the electronic structure of Ba1-xKxBiO3 (0x-ray photoelectron spectroscopy. The Bi(4f) core levels show a normal valency of +3 as in Bi2O3 and we find no evidence for the disproportionation of Bi4+ to Bi3+ and Bi5+. Instead, we find that BaBiO3 has mixed valent O2- and O1- ions. As the potassium doping is increased, the binding energy of the O2- ions in the O(1s) photoelectron spectra steadily decreases from 529.7 to 528.8 eV. The effect of lowering the O(1s) binding energy is to raise the O(2p) band towards EF and at the superconducting composition a finite density of O(2p) states is observed near EF. Similarly, the Ba(5p) binding energies decrease with potassium doping, indicating increased metallicity. The behavior of the O(1s), Ba(5p), and the valence band resembles that of all the cuprate superconductors and we conclude that in all these oxide superconductors, a hole in the (filled) O(2p) band is the carrier responsible for superconductivity, which predicts hole conduction in the Ba-K-Bi-O and Ba-Pb-Bi-O systems.

Transition metal oxide perovskites by photoelectron and x-ray absorption spectroscopy

X-ray and ultraviolet photoelectron spectroscopy as well as x-ray absorption spectroscopy have been employed to investigate transition metal oxide perovskites of the general formula ABOs (A=La or rare-earth ion, B=trivalent transition metalion). Systematics in the core levels and in the valence bands in the series of LaBOa compounds have been discussed. Lanthanum chemical shifts in the x-ray absorption spectra in this series show interesting trends. Photoelectron spectra of the solid solutions, LaNil_x Coxes, LaNix_x FexO8 and LaFel_x Coxes show that the rigid band model is applicable to these systems. It is shown that x-ray photoelectron spectroscopy can be employed to identify multiple oxidation states of transition metal ions in oxide perovskites.

Metal-insulator transitions in Cr-doped V2O3 by x-ray and ultraviolet photoelectron spectroscopy

X-ray and ultraviolet photoelectron spectroscopy have been employed to investigate the high temperature metal-insulator transitions in V2O3 and (V0.99Cr0.01)2O3. The high temperature transitions are associated with more gradual changes in the 3d bands compared to the low-temperature transitions