Phase Relations in the System La-Rh-O and Thermodynamic Properties of LaRhO3

Phase relations in the system La-Rh-O at 1223 Ii have been determined by examination of equilibrated samples by optical and scanning electron microscopy, powder X-ray diffraction (XRD), and energy-dispersive analysis of X-rays (EDAX). Only one ternary oxide, LaRhO3, with distorted orthorhombic perovskite structure (Pbnm, a = 0.5525, b = 0.5680, and c = 0.7901 nm) was identified. The alloys and intermetallics along the La-Rh binary are in equilibrium with La2O3. The thermodynamic properties of LaRhO3 were determined in the temperature range 890 to 1310 K, using a solid-state cell incorporating yttria-stabilized zirconia as the electrolyte. A new four-compartment design of the emf cell was used to enhance the accuracy of measurement. For the reaction 1/2La(2)O(3) + 1/2Rh(2)O(3) --> LaRhO3, Delta G degrees = - 70 780 + 4.89T (+/- 90) J.mol(-1) The compound decomposes on heating to a mixture of La2O3, Ph and O-2. The calculated decomposition temperatures are 1843 (+/- 5) K in pure O-2 and 1728 (+/- 5) K in air at a pressure of 1.01 x 10(5) Pa. The phase diagrams for the system La-Rh-O at different partial pressures of oxygen are calculated from the thermodynamic information.

Gibbs energy of formation of lead zirconate

The Gibbs energy of formation of zirconia-saturated lead zirconate was determined by emf measurements on the solid state cells and at 800 to 1400 K. The results obtained differ significantly from those reported in the literature based on vapor-pressure measurements, using Knudsen effusion and transportation techniques and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor-pressure studies, using mass-spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead zirconate which are in better agreement with those obtained in this study. Recent electrochemical measurements using CaO-ZrO2 and PbF2 solid electrolytes are in good agreement with the present study. The results obtained in this study are also consistent with the phase diagram which shows decomposition of the zirconate to tetragonal zirconia and a liquid phase rich in PbO at 1843 K.