Amide-based Room Temperature Molten Salt as Solvent cum Stabilizer for Metallic Nanochains

A simple and efficient method for spontaneous organization of long assemblies of gold nanoparticles is described. This is achieved in a molten solvent containing acetamide, urea and ammonium nitrate that acts as a solvent cum stabilizer. There is no external aggregating agent or stabilizing agent added to the system. Depending on the concentration of the metal salt in the ternary melt, either chain-like assemblies or individual nanoparticles could be obtained. The amine groups present in the components of the melt (acetamide and urea) help in the stabilization of nanoparticles. Ammonium ions present in the eutectic mixture are likely to assist in the organization of the particles. The method is simple, highly reproducible and does not require any templating agent for the formation of chain-like assemblies.

Template-Assisted Sol-Gel Synthesis of Nanocrystalline BaTiO3

Nanocrystalline perovskite barium titanate with an average particle size less than similar to 10 nm is produced using sol-gel route involving ligand-assisted templating. BaTiO3 is obtained by the controlled hydrolysis and condensation reaction of barium acetate (Ba(CH3COO)(2)) with titanium tetra chloride (TiCl4) in the reverse micelles of dodecylamine (DDA) which is used as the template. Our attempts to produce mesoporous BaTiO3 have resulted in the formation of nanocrystalline BaTiO3. The synthesis of nanostructured BaTiO3 is carried out using the ligand-assisted templating approach which proceeds through the sol-gel route. Dodecylamine is used as the template. The sol-gel process in general presents inherent advantages because the nanostructure of the desired materials can be controlled together with their porous structure. Ligand-assisted templating approach involves the formation of covalent bond between the inorganic analogue and the template. Ba(CH3COO)(2) and TiCl4 are used as barium-source and titanium-source respectively. The reaction between Ba(CH3COO)(2) and TiCl4 is found to take place deliberately on the pre-assembled species which acts as the template or occurring with in them which in turn will lead to the generation of the desired nanoscale structure (nanopores or nanoparticles).

Rapid growth of nanotubes and nanorods of wurtzite ZnO through microwave-irradiation of a metalorganic complex of zinc and a surfactant in solution

Large quantities of single-crystalline ZnO nanorods and nanotubes have been prepared by the microwave, irradiation of a metalorganic complex of zinc, in the presence of a surfactant. The method is simple, fast, and inexpensive (as it uses a domestic microwave oven), and yields pure nanostructures of the hexagonal wurtzite phase of ZnO in min, and requires no conventional templating. The ZnO nanotubes formed have a hollow core with inner diameter varying from 140-160 nm and a wall of thickness, 40-50 nm. The length of nanorods and nanotubes varies in the narrow range of 500-600 nm. These nanostructures have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). The ZnO nanorods and nanotubes are found by SAED to be single-crystalline. The growth process of ZnO nanorods and nanotubes has been investigated by varying the surfactant concentration and microwave irradiation time. Based on the various results obtained, a tentative and plausible mechanism for the formation of ZnO nanostructures is proposed.

Synthesis of metal oxide nanorods using carbon nanotubes as templates

Nanorods of several oxides, with diameters in the range of 10-200 nm and lengths upto a few microns, have been prepared by templating against carbon nanotubes. The oxides include V2O5, WO3, MoO3 and Sb2O5 as well as metallic MoO2, RuO2 and IrO2. The nanorods tend to be single-crystalline structures. Nanotube structures have also been obtained in MoO3 and RuO2.

High Rate Capability of a Dual-Porosity LiFePO4/C Composite

Mesoporous intercalation compounds consisting of two differentdistributions of pores represent a potentially attractive material for high-rate cathodes. A mesoporous LiFePO4/C composite with two sizes of pores is prepared for the first time via a solution-based polymer templating technique. The precursor of the LiFePO4/C composite is heated at different temperatures in the range from 600 to 800 degrees C to study the effect of crystallinity, porosity, and morphology on the electrochemical performance. The composite is found to attain reduction in the surface area, carbon content, and porosity upon increasing temperature. Nonetheless, the composite prepared at 700 degrees C with pore-size distributions of around 4 and 50 nm exhibits a high rate capability and stable capacity retention upon cycling.

Synthesis of mesoporous materials based on titanium(IV)oxide and titanium nitride

Nanoparticles of titania were obtained by the controlled hydrolysis of Ti(i-OC3H7)(4) in the reverse micelles of dodecylamine derived from dodecylamine-isopropanol-water solution (water/oil microemulsion). The mesolamellar phase based on titanium nitride (TiN) was obtained by first decomposing TiN atleast partially using the 1:1 solution of acid mixture (HF and HNO3 in the ratio of 9:1) in water and then templating onto the cationic surfactant namely, cetyltrimethylammaniumbromide (abbreviated as CTAB) at 80 degrees C. The synthesis of mesolamellar phase based on TiN involves the charge matched templating approach following the counter-ion mediated pathway. The samples thus obtained were characterized by small angle x-ray diffraction using Cuk(a) radiation, scanning electron microscopy and transmission electron microscopy, which indicated some satisfactory results. (C) 1999 Acta Metallurgica Inc.

Boron nitride nanotubes and nanowires

Simple methods of preparing boron nitride nanotubes and nanowires have been investigated. The methods involve heating boric acid with activated carbon, multi-walled carbon nanotubes, catalytic iron particles or a mixture of activated carbon and iron particles, in the presence of NH3. While with activated carbon, boron nitride nanowires constitute the primary product, high yields of clean boron nitride nanotubes are obtained with multi-walled carbon nanotubes. Aligned boron nitride nanotubes are produced when aligned multi-walled carbon nanotubes are employed as the starting material suggesting the templating role of the nanotubes. Boron nitride nanotubes with different structures have been obtained by reacting boric acid with NH3 in the presence of a mixture of activated carbon and Fe particles. (C) 2002 Elsevier Science B.V. All rights reserved.

Hydrothermal synthesis and structure of organically templated one-dimensional and three-dimensional iron fluorophosphate

Two new open-framework iron fluorophosphates, [C(4)N(2)H(12)](0.5) [FeF(HPO(4))(H(2)PO(4))] (I) and [C(4)N(2)H(12)][Fe(4)F(2)(H(2)O)(4)(PO(4))(4)]. 0.5H(2)O (II), were synthesized hydrothermally using piperazine as a templating agent. The structures were determined by single-crystal X-ray diffraction. Compound I crystallizes in the orthorhombic space group Pbca, a = 7.2126(2) Angstrom, b = 14.2071(4) Angstrom, c = 17.1338(2) Angstrom, Z = 8. The structure is composed of infinite anionic chains of [FeF(HPO(4))(H(2)PO(4))](n)(-) built by trans-fluorine sharing FeF(2)O(4) octahedra. These chains are similar to those found in tancoite-type minerals. Compound II crystallizes in the monoclinic space group P2(1)/n, a = 9.9045(3) Angstrom, b = 12.3011(3) Angstrom, c = 17.3220(4) Angstrom, beta = 103.7010(10)degrees, Z = 4. The structure of compound II has a three-dimensional (3D) architecture with an eight-membered channel along the b axis, in which protonoted piperazine molecules reside. The complex framework is built from two types of secondary building unit (SBU): one hexamer [Fe(3)F(2)(H(2)O)(2)(PO(4))(3)] (SBU6), and one dimer [FeO(4)(H(2)O)(2)PO(4)] (SBU2). The vertex sharing between these SBUs create the 3D structure.