Growth and electron effective mass measurements of strained Si and Si0.94Ge0.06 on relaxed Si0.62Ge0.38 buffers grown by rapid thermal chemical vapor deposition

Abstract: We report the growth and the electron cyclotron resonance measurements of n-type Si/Si0.62Ge0.38 and Si0.94Ge0.06/Si0.62Ge0.38 modulation-doped heterostructures grown by rapid thermal chemical vapor deposition. The strained Si and Si0.94Ge0.06 channels were grown on relaxed Si0.62Ge0.38 buffer layers, which consist of 0.6 mu m uniform Si0.62Ge0.38 layers and 0.5 mu m compositionally graded relaxed SiGe layers from 0 to 38% Ge. The buffer layers were annealed at 800 degrees C for 1 h to obtain complete relaxation. A 75 Angstrom Si(SiGe) channel with a 100 Angstrom spacer and a 300 Angstrom 2 X 10(19) cm(-3) n-type supply layer was grown on the top of the buffer layers. The cross-sectional transmission electron microscope reveals that the dense dislocation network is confined to the buffer layer, and relatively few dislocations terminate on the surface. The plan-view image indicates the threading dislocation density is about 4 X 10(6) cm(-2). The far-infrared measurements of electron cyclotron resonance were performed at 4 K with the magnetic field of 4-8 T. The effective masses determined from the slope of the center frequency of the absorption peak versus applied magnetic field plot are 0.203m(0) and 0.193m(0) for the two dimensional electron gases in the Si and Si0.94Ge0.06 channels, respectively. The Si effective mass is very close to that of a two dimensional electron gas in an Si MOSFET (0.198m(0)). The electron effective mass of Si0.94Ge0.06 is reported for the first time and is about 5% lower than that of pure Si.

Impression creep of zinc and the rate-controlling dislocation mechanism of plastic flow at high temperatures

The impression creep behaviour of zinc is studied in the range 300 to 500 K and the results are compared with the data from conventional creep tests. The steady-state impression velocity is found to exhibit the same stress and temperature dependence as in conventional tensile creep with the same power law stress exponent. Also studied is the effect of indenter size on the impression velocity. The thermal activation parameters for plastic flow at high temperatures derived from a number of testing techniques agree reasonably well. Grain boundary sliding is shown to be unimportant in controlling the rate of plastic flow at high temperatures. It is observed that the Cottrell-Stokes law is obeyed during high-temperature deformation of zinc. It is concluded that a mechanism such as forest intersection involving attractive trees controls the high-temperature flow rather than a diffusion mechanism.

Grain boundary sliding during diffusion and dislocation creep in a Mg-0.7 pct Al alloy

Early studies on grain boundary sliding (GBS) in Mg alloys have suggested frequently that the contribution of GBS to creep is high even under conditions corresponding to dislocation creep. The role of creep strain and grain size in influencing the experimental measurements has not been clearly identified. Grain boundary sliding measurements were conducted in detail over experimental conditions corresponding to diffusion creep as well as dislocation creep in a single-phase Mg-0.7 wt pet Al alloy. The results indicated clearly that the GBS contribution to creep was Very high during,, diffusion creep at low stresses (similar to 75 pct) and substantially reduced during dislocation creep at high stresses (similar to 15 pct). These measurements were consistent with the observation of significant intragranular slip band activity observed in most grains at high stresses and very little slip band activity at low stresses. The experimental measurements and analysis indicated also that the GBS contribution to creep was high during the initial stages of creep and decreased to a steady-state value at large strains.

Dislocation dynamics in alpha titanium Dynamique des dislocations dans le titane alphaVersetzungsdynamik in alpha-Titan

The activation area and activation enthalpy are determined as a function of stress and temperature for alpha titanium. The results indicated that plastic flow below about 700°K occurs by a single thermally activated mechanism. Activation area determined by differential-stress creep tests falls in the range 80−8b2 and does not systematically depend on the impurity content. The total activation enthalpy derived from the temperature and strain-rate dependence of flow stress is 1.15 eV. The experimental data support a lattice hardening mechanism as controlling the low-temperature deformation in alpha titanium.

The nature of dislocation motion in quasicrystals

Calculations in a hydrodynamic model of quasicrystal dynamics show that dislocation motion in these systems is impeded by a drag far greater than that in crystals.

Dislocation characterization in crystals of potash alum grown by seeded solution growth under conditions of low supersaturation

An analysis has been carried out of the genesis and character of growth dislocations present in all growth sectors of single crystals of potash alum. The crystals, grown from seeded solutions by the temperature lowering method under conditions of low supersaturation, presented the well-developed forms: {111} dominant, {100} and {110}. Growth dislocations formed predominately during refacetting of the edges and corners of the seed, rounded during preparation and insertion into the supersaturated solution. From here they become refracted into the {111} sectors which proved to be the most defective. Smaller numbers of dislocations form at the {111}, {100} and {110} seed interfaces and propagate in these sectors. In crystals of inferior quality, a number of inclusions were found predominantly in the fast growing {100} sectors which become the source of additional dislocations. Dislocations present in the original seed did not propagate across the interface into the developing crystal. Dislocations of all characters were observed. The principal Burgers vectors were found to be left angle bracket100right-pointing angle bracket, left angle bracket110right-pointing angle bracket and left angle bracket111right-pointing angle bracket.

Kinetic approach to dislocation bending in low-mobility films

A kinetic model has been developed for dislocation bending at the growth surface in compressively stressed low-mobility films such as III-V nitrides. It is based on a reduction in the number of atoms at the growth surface. Stress and nonstress sources of driving force for such a reduction are discussed. A comparison between the derived equations and experimentally measured stress evolution data yields good agreement between the predicted and observed angles through which dislocations bend.

Sintering of beta titanium: Role of dislocation pipe diffusion

Sintering of titanium in its high temperature beta phase was studied by isothermal dilatometry. The sintering shrinkage y did not follow the normal time exponent type of behaviour, instead being described by the equation y = Kt(m)/[1-(A+Bt)(2)], where m = 1.93 +/- 0.07, with an activation energy of 62-90 kJ mol(-1). A detailed analysis of these results, based on the 'anomalous' diffusion behaviour reported for beta titanium, is carried out. It is shown that the generation of a high density of dislocations during the alpha --> beta phase transformation, coupled with sluggish recovery at the sintering necks, enables sintering mass transport by pipe diffusion through dislocation cores from sources of matter within the particles to become dominant.

Dislocation mechanisms for plastic flow of nickel in the temperature range 4.2 – 1200 K

The temperature ranges of thermal and athermal deformation behaviour of nickel are identified by employing the temperature-dependence of flow-stress and strain-rate cycling data. The results are used to present a unified view of dislocation mechanisms of glide encompassing the two thermally activated and the intermediate athermal regimes of plastic flow.In the low-temperature thermally activated region (<250 K) the strain rate is found to be controlled by the repulsive intersection of glide and forest dislocations, in accordance with current ideas. The athermal stress in this region can be attributed mainly to the presence of strong attractive junctions which are overcome by means of Orowan bowing, a small contribution also coming from the elastic interactions between dislocations. The values of activation area and activation energy obtained in the high-temperature region (> 750 K) negate the operation of a diffusion-controlled mechanism. Instead, the data support a thermal activation model involving unzipping of the attractive junctions. The internal (long-range) stress contribution here results solely from the elastic interactions between dislocations. This view concerning the high-temperature plastic flow is further supported by the observation that the Cottrell–Stokes law is obeyed over large strains in the range 750–1200 K.

Synergistic effect of reactor chemistry and compressive stress on dislocation bending during GaN growth

The synergistic effect of compressive growth stresses and reactor chemistry, silane presence, on dislocation bending at the very early stages of GaN growth has been studied using in-situ stress measurements and cross-sectional transmission electron microscopy. A single 100 nm Si-doped GaN layer is found to be more effective than a 1 mu m linearly graded AlGaN buffer layer in reducing dislocation density and preventing the subsequent layer from transitioning to a tensile stress. 1 mu m crack-free GaN layers with a dislocation density of 7 x 10(8)/cm(2), with 0.13 nm surface roughness and no enhancement in n-type background are demonstrated over 2 inch substrates using this simple transition scheme. (C) 2013 AIP Publishing LLC.

Dislocation dynamical approach to force fluctuations in nanoindentation experiments

We develop an approach that combines the power of nonlinear dynamics with the evolution equations for the mobile and immobile dislocation densities and force to explain force fluctuations in nanoindentation experiments. The model includes nucleation, multiplication, and propagation thresholds for mobile dislocations, and other well known dislocation transformation mechanisms. The model predicts all the generic features of nanoindentation such as the Hertzian elastic branch followed by several force drops of decreasing magnitudes, and residual plasticity after unloading. The stress corresponding to the elastic force maximum is close to the yield stress of an ideal solid. The predicted values for all the quantities are close to those reported by experiments. Our model allows us to address the indentation-size effect including the ambiguity in defining the hardness in the force drop dominated regime. At large indentation depths, the hardness remains nearly constant with a marginal decreasing trend.

Microstructural characterization of ultrafine-grain interstitial-free steel by X-ray diffraction line profile analysis

This paper highlights the microstructural features of commercially available interstitial free (IF) steel specimens deformed by equal channel angular pressing (ECAP) up to four passes following the route A. The microstructure of the samples was studied by different techniques of X-ray diffraction peak profile analysis as a function of strain (epsilon). It was found that the crystallite size is reduced substantially already at epsilon=2.3 and it does not change significantly during further deformation. At the same time, the dislocation density increases gradually up to epsilon=4.6. The dislocation densities estimated from X-ray diffraction study are found to correlate very well with the experimentally obtained yield strength of the samples.

High temperature time-dependent low cycle fatigue behaviour of a type 316L(N) stainless steel

Total strain controlled low cycle fatigue tests on 316L(N) stainless steel have been conducted in air at various strain rates in the temperature range of 773-873 K to identify the operative time-dependent mechanisms and to understand their influence on the cyclic deformation and fracture behaviour of the alloy. The cyclic stress response at all the testing conditions was marked by an initial hardening followed by stress saturation. A negative strain rate stress response is observed under specific testing conditions which is attributed to dynamic strain ageing (DSA). Transmission electron microscopy studies reveal that there is an increase in the dislocation density and enhanced slip planarity in the DSA regime. Fatigue life is found to decrease with a decrease in strain rate. The degradation in fatigue resistance is attributed to the detrimental effects associated with DSA and oxidation. Quantitative measurement of secondary cracks indicate that both transgranular and intergranular cracking are accelerated predominantly under conditions conducive to DSA.