Synthesis and photoluminescence properties of a novel Sr2CeO4:Dy3+ nanophosphor with enhanced brightness by Li+ co-doping

A series of Dy3+ (0.5-9 mol%) and Li+ (0.5-3 mol%) co-doped strontium cerate (Sr2CeO4) nanopowders are synthesized by low temperature solution combustion synthesis. The effects of Li+ doping on the crystal structure, chemical composition, surface morphology and photoluminescence properties are investigated. The X-ray diffraction results confirm that all the samples calcined at 900 degrees C show the pure orthorhombic (Pbam) phase. Scanning electron microscopy analysis reveals that the particles adopt irregular morphology and the porous nature of the product. Room temperature photoluminescence results indicate that the phosphor can be effectively excited by near UV radiation (290 to 390 nm) which results in the blue (484 nm) and yellow (575 nm) emission. Furthermore, PL emission intensity and wavelength are highly dependent on the concentration of Li+ doping. The emission intensity is enhanced by similar to 3 fold with Li+ doping. White light is achieved by merely varying dopant concentration. The colour purity of the phosphor is confirmed by CIE co-ordinates (x = 0.298, y = 0.360). The study demonstrates a simple and efficient method for the synthesis of novel nanophosphors with enhanced white emission.

Kinetics of thermal decomposition of strontium zirconyl carbonate, Sr2Zr2O5CO3

The kinetics of decomposition of the carbonate Sr2Zr2O5CO3, are greatly influenced by the thermal effects during its formation. (α−t) curves are found to be sigmoidal and they could be analysed based on power law equations followed by first-order decay. The presence of carbon in the vacuum-prepared sample of carbonate has a strong deactivating effect. The carbonate is fairly crystalline and its decomposition leads to the formation of crystalline strontium zirconate.

Study of strontium compounds and minerals by X-ray absorption spectroscopy. I. K-edge shifts

The chemical shifts in the X-ray K-absorption edge of strontium in various compounds and in six minerals are measured using a single crystal X-ray spectrometer. Besides valence, the shifts are found to be governed by ionic charges on the absorbing ions, which are calculated employing Pauling's method. For the minerals the plot of chemical shift against the theoretically calculated ionic charges is used to determine the charges on the strontium ions.

Switching transients in ferroelectric dicalcium strontium propionate (DSP) and azoxybenzene

The switching transients in dicalcium strontium propionate and azoxybenzene were studied by the use of the Merz method. It was observed that the switching time depends linearly on the applied electric field. Under similar electric fields, the switching processes in DSP and azoxybenzene are slower than in triglycine sulphate (TGS) at 27°C.

Switching transients in ferroelectric dicalcium strontium propionate (DSP) and Azoxybenzene

The ferroelectric polarization switching was studied in DSP single crystal and Azoxybenzene liquid film using the method described by Merz (1954). The DSP single crystal samples were in the form of plates 0.5 mm - 1.0 mm thick. The Azoxybenzene liquid film samples had a thickness from 0.025 mm - 0.125 mm. Switching in DSP was observed in the temperature range +7°C to -30°C, while in Azoxybenzene it was observed from 30°C to 70°C.

The growth and characterization of strontium fluoro chloride crystals

Abstract is not available.

Strontium diffusion in feldspars—a laboratory study

Sr90 Radiotracer diffusion studies have been carried out on crystals of orthoclase and microcline using an ion implantation method. The activation energies are consistent with calculations based on mineral age data.

Studies on strontium titanate/barium zirconate superlattices

Artificial superlattices of SrTiO3 and BaZrO3 were grown epitaxially with different periodicities on SrRuO3 coated (00 1) SrTiO3 substrates by pulsed excimer laser ablation. Superlattices were structurally characterized by X-Ray theta-2 theta diffraction data. Electrical characterization was done in metal-insulation-metal configuration. Capacitance-voltage measurements showed limited amount of tunability. The DC field induced tunability has been observed to be sensitive to the periodicity of the superlattices, hence the effective strain present in the layers. Hysteretic behaviour in capacitance-voltage (C-V) and polarization versus electric field (P-E) results from the superlattices also indicate the sensitivity of the interfaces. Interfacial strain is supposed to be the most probable cause for such a behaviour which is also manifested in the variation of dielectric constant with individual layer thicknesses. (c) 2007 Elsevier Ltd. All rights reserved.

Infrared spectra of trichloroacetates of copper, calcium, strontium and barium

Infrared spectra of trichloroacetates of Cu, Ca, Sr and Ba were studied in order to investigate the effect of coordination on the vibration spectra of the ligand. The shifts of the antisymmetric and symmetric COO- stretching frequencies are explained on the basis of the type of co-ordination of the COO- group to the metal ion. From the spectra it is established that the coordination of the COO- group to metal is different for trichloroacetates and monochloroacetates.

Raman spectrum of strontium titanate

The Raman spectrum of strontium titanate has been recorded using λ 4358 of mercury as exciter. The observed spectrum consists of 7 Raman lines, one of which is of low frequency, as expected from the recent theory of Cochran. 6 of these Raman lines have been interpreted as the first order spectrum arising from a small deviation of the cubic strontium titanate from its idealized symmetry. It has been shown that one normal mode of SrTiO3 neglected by J.T. Last, will be really active in infrared absorption in the region of 440 cm-1 and that it has to be taken into account in the interpretation of the infrared spectra of titanates. The four vibrational modes of the unit cell of SrTiO3 correspond to frequencies of 90, 335, 441 and 620 cm-1 observed in Raman effect. The large width of the Raman lines and the additional lines at 256 cm-1 and 726 cm-1 have been attributed to a splitting of the longitudinal and transverse optical modes. With the observed frequencies it has been found possible to account for in a satisfactory manner the specific heat of SrTiO3 in the range 54·84° K to 1800° K.

ESR studies of X-irradiated strontium mixed calcium tartrate crystals

The electron spin resonance spectra of X-ray irradiated single crystals of strontium doped calcium tartrate tetrahydrate (CST) with molecular formula Ca0.88Sr0.12C4H4O6.4H(2)O grown in gels has been investigated. Only one species of free radical but with two magnetically unequivalent sites was observed at room temperature. The free radical was found to be the result of the splitting of a C-II bond adjacent to both the hydroxyl and carboxyl groups. The a factor was found to be slightly anisotropic. Couplings with two H nuclei, believed to be the proton of the OH group attached directly to the unsaturated asymmetric carbon atom and the proton attached directly to the: other asymmetric carbon atom of the molecule were observed. The principal g-values were found to be 2.0030, 2.0017, 2.0027. The principal elements of the nuclear coupling are 7.45, 6.59, 4.28 and 8.56, 7.22, 18.71 G, respectively. The radical was found to be very stable. (C) 2000 Elsevier Science Ltd. All rights reserved.

The vapour pressures of barium and strontium

The vapour pressures of barium and strontium have been measured by continuous monitoring of the weight loss of Knudsen cells in the temperature range 700�1200 K. The results for strontium agree with those reported in the literature, but the vapour pressure of barium has been found to be considerably lower than the generally accepted value. The experimentally determined pressures are in good agreement with theoretical values obtained using the Gibbs-Bogoliubov first-order variational method.

Thermodynamics Of Aluminum Strontium Alloys

The activity of strontium in liquid Al-Sr alloys (X(Sr) less-than-or-equal-to 0.17) at 1323 K has been determined using the Knudsen effusion-mass loss technique. At higher concentrations (X(Sr) greater-than-or-equal-to 0.28), the activity of strontium has been determined by the pseudoisopiestic technique. Activity of aluminium has been derived by Gibbs-Duhem integration. The concentration - concentration structure factor of Bhatia and Thornton at zero wave vector has been computed from the thermodynamic data. The behaviour of the mean square thermal fluctuation in composition and the thermodynamic mixing functions suggest association tendencies in the liquid state. The associated solution model with Al2Sr as the predominant complex can account for the properties of the liquid alloy. Thermodynamic data for the intermetallic compunds in the Al-Sr system have been derived using the phase diagram and the Gibbs' energy and enthalpy of mixing of liquid alloys. The data indicate the need for redetermination of the phase diagram near the strontium-rich corner.