Morphological transitions in polymer monolayers under compression

We present a systematic investigation of morphological transitions in poly vinylacetate Langmuir monolayers. On compression, the polymer monolayer is converted to a continuous membrane with a thickness of similar to 2-3 nm. Above a certain surface concentration the monolayer, on water, undergoes a morphological transition-buckling, leading to formation of striped patterns of period of lambda(b)similar to 160 nm, as determined from in situ grazing incidence small angle x-ray scattering measurements. The obtained value is much smaller than what has been typically observed for Langmuir monolayers on water or thin films on soft substrates. Using existing theories for buckling of fluidlike films on fluid substrates, we obtain very low values of bending rigidity and Young's modulus of the polymer monolayer compared to that observed earlier for lipid or polymeric monolayers. Since buckling in these monolayers occurs only above a certain surface concentration, we have looked at the possibility that the buckling in these films occurs due to changes in their mechanical properties under compression. Using the model of Huang and Suo of buckling of solidlike films on viscoelastic substrates, we find values of the mechanical properties, which are much closer to the bulk values but still significantly lower. Although the reduction could be along the lines of what has been observed earlier for ultrathin polymer film or surface layers of polymers, the possibility of micromechanical effects also determining the buckling in such polymer monolayers cannot be ruled out. We have provided possible explanation of the buckling of the poly vinylacetate monolayers in terms of the change in isothermal compression modulus with surface concentration.

Suspensions of polymer-grafted nanoparticles with added polymers-Structure and effective pair-interactions

We present the results of combined experimental and theoretical (molecular dynamics simulations and integral equation theory) studies of the structure and effective interactions of suspensions of polymer grafted nanoparticles (PGNPs) in the presence of linear polymers. Due to the absence of systematic experimental and theoretical studies of PGNPs, it is widely believed that the structure and effective interactions in such binary mixtures would be very similar to those of an analogous soft colloidal material-star polymers. In our study, polystyrene-grafted gold nanoparticles with functionality f = 70 were mixed with linear polystyrene (PS) of two different molecular weights for obtaining two PGNP: PS size ratios, xi = 0.14 and 2.76 (where, xi = M-g/M-m, M-g and M-m being the molecular weights of grafting and matrix polymers, respectively). The experimental structure factor of PGNPs could be modeled with an effective potential (Model-X), which has been found to be widely applicable for star polymers. Similarly, the structure factor of the blends with xi = 0.14 could be modeled reasonably well, while the structure of blends with xi = 2.76 could not be captured, especially for high density of added polymers. A model (Model-Y) for effective interactions between PGNPs in a melt of matrix polymers also failed to provide good agreement with the experimental data for samples with xi = 2.76 and high density of added polymers. We tentatively attribute this anomaly in modeling the structure factor of blends with xi = 2.76 to the questionable assumption of Model-X in describing the added polymers as star polymers with functionality 2, which gets manifested in both polymer-polymer and polymer-PGNP interactions especially at higher fractions of added polymers. The failure of Model-Y may be due to the neglect of possible many-body interactions among PGNPs mediated by matrix polymers when the fraction of added polymers is high. These observations point to the need for a new framework to understand not only the structural behavior of PGNPs but also possibly their dynamics and thermo-mechanical properties as well. (C) 2015 AIP Publishing LLC.

Anomalous Viscosity Reduction and Hydrodynamic Interactions of Polymeric Nanocolloids in Polymers

One of the central dogmas of fluid physics is the no-slip boundary condition, whose validity has come under scrutiny, especially in the fields of micro and nanofluidics. Although various studies show the violation of the no-slip condition its effect on flow of colloidal particles in viscous media has been rarely explored. Here we report unusually large reduction of effective viscosity experienced by polymeric nano colloids moving through a highly viscous and confined polymer, well above its glass transition temperature. The extent of reduction in effective interface viscosity increases with decreasing temperature and polymer film thickness. Concomitant with the reduction in effective viscosity we also observe apparent divergence of the wave vector dependent hydrodynamic interaction function of these colloids with an anomalous power law exponent of similar to 2 at the lowest temperatures and film thickness studied. Such strong hydrodynamic interactions are not expected for polymeric colloidal motion in polymer melts. We suggest hydrodynamics, especially slip present at the colloid-polymer interface which determines the observed reduction in interface viscosity and presence of strong hydrodynamic interactions.