The Influence of Processing Parameters on Characteristics of an Aluminum Alloy Spray Deposition

In the present investigation, two nozzle configurations are used for spray deposition, convergent nozzle (nozzle-A), and convergent nozzle with 2 mm parallel portion attached at its end (nozzle-C) without changing the exit area. First, the conditions for subambient aspiration pressure, i.e., pressure at the tip of the melt delivery tube, are established by varying the protrusion length of the melt delivery tube at different applied gas pressures for both of the nozzles. Using these conditions, spray deposits in a reproducible manner are successfully obtained for 7075 Al alloy. The effect of applied gas pressure, flight distance, and nozzle configuration on various characteristics of spray deposition, viz., yield, melt flow rate, and gas-to-metal ratio, is examined. The over-spray powder is also characterized with respect to powder size distribution, shape, and microstructure. Some of the results are explained with the help of numerical analysis presented in an earlier article.

Spray erosion studies on pressed soil blocks

Erosion resistance of pressed soil blocks used for wall construction is discussed. The spray erosion test using a standardized shower spray is discussed. Spray erosion behaviour of pressed soil blocks made out of five different soils is presented. Results of laboratory and field tests are compared. Effect of clay content of the soil and density of the pressed soil block on erosion are discussed. Also the effect of water-proof coatings on erosion of soil blocks is presented. Erosion resistance of soil blocks stabilized with organic (jaggery syrup and starch) or inorganic binders is also discussed.

Microstructure and Properties of the Spray-Formed and Extruded 7075 Al Alloy

In the present investigation, a very good combination of strength and ductility, 630MPa 0.2% proof stress and 14.8% elongation to fracture in tensile test, has been obtained for the 7075 Al alloy after optimizing the processing parameters for spray forming, hot extruding the spray deposit, and peak aging the samples taken from the extruded rod. The spray deposits contained some porosity but it was almost eliminated on hot extrusion. Electron probe microanalysis revealed that even though spray forming was carried out in an open atmosphere, it did not affect the oxygen content and its distribution in the material on spray forming, because the atomizing argon gas provided a protective cover to molten droplets and prevented their oxidation. The chemical composition of the spray-formed material was found to be almost the same as the raw material, and the major alloying elements were found to be uniformly distributed in the extruded rod.

Polycrystalline Lead Tin Chalcogenide Thin Film Grown by Spray Pyrolysis

PbSnS2 thin film has been prepared for the first time by spray pyrolysis technique on FTO substrate at 570K. The preliminary optical and structural characteristics of the film have been reported. The optical studies showed that the value of the fundamental absorption edge lies at 1.47eV and a low energy absorption band tail has been observed. The prepared film is p- type electrical conductivity, polycrystalline in nature and has an orthorhombic crystal structure. The value of an average grain size of the film is 350Å.

Precursor Dependent Microstructure Evolution and Nonstoichiometry in Nanostructured Cerium Oxide Coatings Using the Solution Precursor Plasma Spray Technique

A solution precursor plasma spray (SPPS) technique has been used for direct deposition of cerium oxide nanoparticles (CNPs) from various cerium salt solutions as precursors. Solution precursors were injected into the hot zone of a plasma plume to deposit CNP coatings. A numerical study of the droplet injection model has been employed for microstructure development during SPPS. The decomposition of each precursor to cerium oxide was analyzed by thermogravimetric-differential thermal analysis and validated by thermodynamic calculations. The presence of the cerium oxide phase in the coatings was confirmed by X-ray diffraction studies. Transmission electron microscopy studies confirmed nanocrystalline (grain size <14 nm) characteristic of the coatings. X-ray photoelectron spectroscopy studies indicated the presence of a high concentration of Ce3+ (up to 0.32) in the coating prepared by SPPS. The processing and microstructure evolution of cerium oxide coatings with high nonstoichiometry are reported.

Novel mechanism for high speed growth of transparent and conducting tin oxide thin films by spray pyrolysis

A novel mechanism is proposed for efficient manipulation of transport forces acting on the droplets during spray pyrolytic deposition of thin films. A ‘‘burst mode’’ technique of spraying is used to adjust the deposition conditions so as to transport the droplets under the new mechanism. Transparent, conducting thin films of undoped tin oxide prepared by this method showed significant improvement in growth rate. The films are found to be of fairly good quality with optical transmission of 82% and sheet resistance of 35 Ω/☒. The films are chemically homogeneous and grow preferentially along 〈200〉 direction.

Some features of spray breakup in effervescent atomizers

The near orifice spray breakup at low GLR (gas to liquid ratio by mass) values in an effervescent atomizer is studied experimentally using water as a simulant and air as atomizing gas. From the visualizations, the near orifice spray structures are classified into three modes: discrete bubble explosions, continuous bubble explosions and annular conical spray. The breakup of the spray is quantified in terms of the mean bubble bursting distance from the orifice. The parametric study indicates that the mean bubble bursting distance mainly depends on airflow rate, jet diameter and mixture velocity. It is also observed that the jet diameter has a dominant effect on the bubble bursting distance when compared to mixture velocity at a given airflow rate. The mean bubble bursting distance is shown to be governed by a nondimensional two-phase flow number consisting of all the aforementioned parameters. The location of bubble bursting is found to be highly unsteady spatially, which is influenced by flow dynamics inside the injector. It is proposed that this unsteadiness in jet breakup length is a consequence of varying degree of bubble expansion caused due to the intermittent occurrence of single phase and two-phase flow inside the orifice.

Ultrasonic spray pyrolysis of CZTS solar cell absorber layers and characterization studies

CZTS (Copper Zinc Tin Sulphide) is a wide band gap quartnery chalcopyrite which has a band gap of about 1.45 eV and an absorption coefficient of 10(4) cm(-1); thus making it an ideal material to be used as an absorber layer in solar cells. Ultrasonic Spray Pyrolysis is a deposition technique, where the solution is atomized ultrasonically, thereby giving a fine mist having a narrow size distribution which can be used for uniform coatings on substrates. An Ultrasonic Spray Pyrolysis equipment was developed and CZTS absorber layers were successfully grown with this technique on soda lime glass substrates using aqueous solutions. Substrate temperatures ranging from 523 K to 723 K were used to deposit the CZTS layers and these films were characterized using SEM, EDAX and XRD. It was observed that the film crystallized in the kesterite structure and the best crystallites were obtained at 613 K. It was observed that the grain size progressively increased with temperature. The optical band gap of the material was obtained as 1.54 eV.

Oriented ferroelectric thin films of PbTiO3, (Pb,La)TiO3, and Pb(Zr,Ti)O3 by nebulized spray pyrolysis

Nebulized spray pyrolysis provides a good low?temperature chemical route for preparing thin films of PbTiO3, (Pb0.9,La0.1)TiO3 and Pb(Zr0.52,Ti0.48)O3. The films are a? or c? axis oriented, with spherical grains of ?30 nm and give satisfactory P?E hysteresis loops. © 1995 American Institute of Physics.

Oriented films of LaNiO3 and other members of the Lan+1NinO3n+1 series, LaCuO3−δ and Pb(Zr0.52Ti0.48)O3, obtained by nebulized spray pyrolysis

The technique of nebulized spray pyrolysis has been explored to find out whether oriented films of certain important oxides can be produced on single-crystal substrates by this relatively gentle method. Starting with acetylacetonate precursors, oriented films of metallic LaNiO3 containing nearly spherical grains (30 nm) have been obtained. Films of near-stoichiometric La4Ni3O10 and La3Ni2O7 showing metallic conductivity have been obtained by this method. This is indeed gratifying since it is difficult to prepare monophasic and stoichiometric bulk samples of these materials. Films of La2NiO4 show the expected semiconducting behavior. In the La-Cu-O system, starting with acetylacetonates, we have obtained films mainly comprising semiconducting La2Cu2O5, which is generally difficult to prepare in bulk form. More interestingly, nebulized spray pyrolysis gives excellent stoichiometric films of Pb(Zr0.52Ti0.48)O-3 consisting of nearly spherical grains (30 nm) which show ferroelectric behavior. The present investigation demonstrates that nebulized spray pyrolysis provides a useful and desirable route to deposite oriented films of complex oxide materials on single-crystal substrates.

Phase evolution and densification of spray pyrolysed ZrO2-Al2O3 powders

Devitrification of spray pyrolysed, amorphous ZrO2-Al2O3 solid solution produces nanocrystalline microstructures (grain sizes 10-20 nm). In this study, spray pyrolysed amorphous ZrO2-40 mol% Al2O3 powder displayed good sinterability during decomposition, after spraying, of the nitrate precursors up to 1023K. Hot pressing of fully pyrolysed, pre-sintered (more than 70% dense) pellets at 923K and 750 MPa produced an amorphous pellet with less than 2% porosity. The results indicate the possibility of producing dense, amorphous pellets that can be heat treated further to produce nanocrystalline microstructures conducive for superplasticity.

Sub-micrometre spherical particles of TiO2, ZrO2, and PZT by nebulized spray pyrolysis of metal-organic precursors

Nebulized spray pyrolysis of metal-organic precursors in methanol solution has been employed to prepare powders of TiO2, ZrO2 and PbZr0.5Ti0.5O3 (PZT). This process ensures complete decomposition of the precursors at relatively low temperatures. The particles have been examined by scanning and transmission electron microscopy as well as X-ray diffraction. As prepared, the particles are hollow agglomerates of diameter 0.1-1.6 mu m, but after heating to higher temperatures the ultimate size of the particles comprising the agglomerates are considerably smaller (0.1 mu m or less in diameter) and crystalline.

Synthesis of metastable, wurzite-based zinc oxide-cobalt(II) oxide solid solutions by spray pyrolysis

Aqueous solutions of acetates and nitrates of zinc and cobalt have been spray decomposed to study the production of extended solid solutions in the ZnO-CoO system. Examination of the products of a variety of synthesis conditions indicates that up to 70% CoO may be retained in the solid solution in the wurzite phase, even though a comparison of the equilibrium solubility in the phase diagram might be expected to favor the formation of a rock-salt-based solid solution.

Microstructure and mechanical properties of spray-formed Al-Si-Pb alloys

Liquid phase co-spray forming (LPCSF) was employed to produce two Al-Si-Pb alloys. The preforms thus obtained were then subjected to hot extrusion at different extrusion ratios. Following extrusion, the materials were tensile tested at room temperature. The distribution of Pb particles and the microstructural characterization in as-formed preforms and in the extruded rods were studied on the basis of SEM observation. The influence of the Pb content on the mechanical properties was investigated. (C) 2002 Published by Elsevier Science B.V.

Preparation of a ZrO2–Al2O3 nanocomposite by high-pressure sintering of spray-pyrolyzed powders

ZrO2–Al2O3 powders were synthesized by spray pyrolysis. These powders were sintered at 1 GPa in the temperature range of 700–1100 °C. The microstructural evolution and densification are reported in this paper. The application of 1 Gpa pressure lowers the crystallization temperature from ∼850 to <700 °C. Similarly, the transformation temperature under 1 GPa pressure for γ → α–Al2O3 reduces from ∼1100 to 700–800 °C range, and that for t → m ZrO2 reduces from ∼1050 to 700–800 °C range. It was possible to obtain highly dense nanocrystalline ZrO2–Al2O3 composite at temperatures as low as 700 °C. The effect of high pressure on nucleation and transformation of phases is discussed.