Thermoelectric properties of indium filled and germanium doped Co4Sb12 skutterudites

In-filled and Ge-doped Co4Sb12 skutterudites materials were synthesized by an induction melting process which was followed by annealing at 650 degrees C for 7 days. A structural, compositional, and morphological study was carried out by X-ray diffraction (XRD), electron probe micro analysis (EPMA), and scanning electron microscopy (SEM). The formation of a single skutterudite phase (delta-CoSb3) was confirmed by XRD and the composition of all the samples was verified by EPMA. The homogeneity and morphology of the samples was observed by potential Seebeck microprobe (PSM) and SEM, respectively. The PSM result confirmed the inhomogeneity of the samples. The temperature dependence of the Seebeck coefficient, electrical conductivity, and thermal conductivity were measured in the temperature range of 300-650 K. The samples of In0.16Co4Sb12-xGex (x = 0.05, 0.1, and 0.2) show a negative Seebeck coefficient confirming an n-type conductivity and the In0.16Co4Sb11.7Ge0.3 sample shows a positive Seebeck coefficient confirming a p-type conductivity. There was a change in the Seebeck coefficient from an n-type to a p-type at the doping concentration of x = 0.3 due to the excess Ge which increases in hole carrier concentration. Electrical conductivity decreases with an increase in Ge doping concentrations and with increases in temperature due to the bipolar effect. Thermal conductivity increases with an increase in carrier concentration and decreases when the temperature is increased. The highest ZT = 0.58 was achieved by In0.16Co4 Sb11.95Ge0.05 at 673K and In-filled and Ge-doped Co4Sb12 was not effective in improving the figure of merit. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3677982]

Thermoelectric properties of Bi-added Co4Sb12 skutterudites

Void filling in (I) Bi-x-added Co4Sb12 or (II) Sb/Bi substitution of Co4Sb12-xBix has been investigated for structural and thermoelectric properties evaluation. X-ray powder data Rietveld refinements combined with electron probe microanalyses showed a polycrystalline and practically Bi-free CoSb3 skutterudite phase as the major constituent as well as a secondary Bi phase in the grain boundaries. For series I alloys, the electrical conductivity, Seebeck coefficient and thermal conductivity were measured as a function of temperature in the range from 450 to 750 K. The electrical conductivity of all the samples increased with increasing temperature, showing a semiconducting nature with smaller values of the Seebeck coefficient for higher Bi fractions. Conduction over the entire temperature range was found to arise from a single p-type carrier. Thermal conductivity showed a reduction with Bi added in all the samples, except for Bi0.75Co4Sb12, and the lowest lattice thermal conductivity was found for a Bi-added fraction of 0.5. The maximum zT value of 0.53 at 632 K is higher than that of Co4Sb12.

Thermoelectric properties of Fe(0.2)Co(3.8)Sbi(12-x)Te(x) skutterudites

Skutterudites Fe(0.)2Co(3.8)Sb(12),Te-x (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6) were synthesized by induction melting at 1273 K, followed by annealing at 923 K for 144 h. X-ray powder diffraction and electron microprobe analysis confirmed the presence of the skutterudite phase as the main phase. The temperature-dependent transport properties were measured for all the samples from 300 to 818 K. A positive Seebeck coefficient (holes are majority carriers) was obtained in Fe0.2Co3.8Sb 12 in the whole temperature range. Thermally excited carriers changed from n-type to p-type in Fe(0.)2Co(3.8)Sb(12),Te-x 19Te0.1 at 570 K, while in all the other samples, Fe(0.)2Co(3.8)Sb(12),Te-x (x = 0.2, 0.3, 0.4, 0.5, 0.6) exhibited negative Seebeck coefficients in the entire temperature range measured. Whereas for the alloys up to x = 0.2 (Fe(0.)2Co(3.8)Sb(12),Te-x ) the electrical resistivity decreased by charge compensation, it increased for x> 0.2 with an increase in Te content as a result of an increase in the electron concentration. The thermal conductivity decreased with Te substitution owing to carrier phonon scattering and point defect scattering. The maximum dimensionless thermoelectric figure of merit, ZT = 1.04 at 818 K, was obtained with an optimized Te content for Fe0.2Co3.8Sb1 1.5Te0.5 and a carrier concentration of,,J1/ =- 3.0 x 1020 CM-3 at room temperature. Thermal expansion (a = 8.8 x 10-6 K-1), as measured for Fe(0.)2Co(3.8)Sb(12),Te-x , compared well with that of undoped Co4Sb12. A further increase in the thermoelectric figure of merit up to ZT = 1.3 at 820 K was achieved for Fe(0.)2Co(3.8)Sb(12),Te-x , applying severe plastic deformation in terms of a high-pressure torsion process. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Nanostructuring of p- and n-type skutterudites reaching figures of merit of approximately 1.3 and 1.6, respectively

Thermoelectric (TE) conversion of waste heat into useful electricity demands optimized thermal and electrical transport in the leg material over a wide temperature range. In order to gain a reasonably high figure of merit (ZT) as well as high thermal electric conversion efficiency, various conditions of the starting material were studied: industrially produced skutterudite powders of p-type DDy(Fe1-xCox)(4)Sb-12 (DD: didymium) and n-type (Mm, Sm)(y)Co4Sb12 (Mm: mischmetal) were used. After a rather fast reaction-melting technique, the bulk was crushed and sieved with various strainers in order to obtain particles below the respective mesh sizes, followed by ball-milling under three different conditions. The dependence of the TE properties (after hot pressing) on the micro/nanosized particles, grains and crystallites was investigated. Optimized conditions resulted in an increase of ZT for bulk material to current record-high values: from ZT similar to 1.1 to ZT similar to 1.3 at 775 K for p-type and from ZT similar to 1.0 to ZT similar to 1.6 at 800 K for n-type, resulting in respective efficiencies (300-850 K) of eta > 13% and eta similar to 16%. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

In-doped multifilled n-type skutterudites with ZT=1.8

In this paper we maximize the thermoelectric (TE) figure of merit, ZT, of n-type skutterudites, (In,Sr,Ba,Yb)(y)Co4Sb12, via three different routes: (i) find the optimum fraction of In as fourth filler (ii) check the influence of powder particle, grain, and crystallite size on the TE properties and (iii) check thermal stability. Filled n-type (Sr, Ba, Yb)(y)Co4Sb12 was mixed in three different proportions with In0.4Co4Sb12, ball milled (regular or high-energy (HB) ball milling) and hot-pressed. Particle size analyses and SEM pictures of the broken surfaces of the hot pressed samples document that only HB produces uniform particles/grains with average crystallite sizes similar to 100 nm, proven by transmission electron microscopy. X-ray Rietveld refinements combined with EDX indicate that in all cases indium entered the icosahedral voids of the skutterudite. Temperature dependent physical properties of all three regularly ball-milled samples show that increasing In-content infers an increasing electrical resistivity, increasing Seebeck coefficient but a decreasing total thermal conductivity. Although ZT (823 K) is in the same range as for the sample without In, the ZT values in the whole temperature range are higher and consequently the TE-conversion efficiency, eta is at least 10% higher. Annealing the samples at 600 degrees C for three days shows minor changes in structure and thermoelectric properties, indicating TE stability. The HB sample, due to uniformly small particles, equally sized grains and crystallites, exhibits a high power factor (4.4 mW/m K-2 at 730 K) and a very low thermal conductivity leading to an outstanding high ZT = 1.8 at 823 K (eta(max) = 17.5%). (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Raman & Infrared Study of Bi Filled Co4Sb12

CoSb3 skutterudites are established thermoelectric materials in the 500-800K temperature range. Undoped and Bi filled CoSb3 samples were synthesized by induction melting-annealing process and phase confirmation done by X-Ray diffraction. The role of bismuth as a filler in CoSb3 was investigated by Raman and far infrared reflectance study. It was found that bismuth strengthens Sb vibrations, and can potentially scatter Sb related acoustic phonons effectively. As a result substantial reduction in thermal conductivity may be possible with proper control of Bi filling.