Fatigue crack growth under an eqivalent falstaff spectrum

Optical fractography was used to estimate growth of small cracks at notches under programmed FALSTAFF loading in an Al-Cu alloy. Crack sizes as low as 25 microns and growth rates over two orders of magnitude could be resolved using this technique. Randomized MiniFALSTAFF load sequence was modified into a programmed load equivalent with major loads either preceding or following marker loads. Crack growth rate under programmed FALSTAFF spectrum as estimated by optical fractography conformed to compliance based estimates on a SE(T) specimen. Long crack growth rates under programmed and randomized MiniFALSTAFF spectrum were essentially similar. Spectrum load fatigue crack growth was studied in central hole coupons under notch inelastic conditions. Scatter in growth rates for small notch cracks was found to be of the same magnitude as that of long cracks. Multiple fatigue cracks are observed at the notch root, and they appear to influence each other.

High temperature time-dependent low cycle fatigue behaviour of a type 316L(N) stainless steel

Total strain controlled low cycle fatigue tests on 316L(N) stainless steel have been conducted in air at various strain rates in the temperature range of 773-873 K to identify the operative time-dependent mechanisms and to understand their influence on the cyclic deformation and fracture behaviour of the alloy. The cyclic stress response at all the testing conditions was marked by an initial hardening followed by stress saturation. A negative strain rate stress response is observed under specific testing conditions which is attributed to dynamic strain ageing (DSA). Transmission electron microscopy studies reveal that there is an increase in the dislocation density and enhanced slip planarity in the DSA regime. Fatigue life is found to decrease with a decrease in strain rate. The degradation in fatigue resistance is attributed to the detrimental effects associated with DSA and oxidation. Quantitative measurement of secondary cracks indicate that both transgranular and intergranular cracking are accelerated predominantly under conditions conducive to DSA.

Some Considerations on the Occurrence of Intergranular Fracture during Fatigue Crack growth in Steels

The occurrence of a maximum in the percentage of intergranular fracture on the fracture surface during the transition from intermediate to low fatigue crack growth rates has been observed for a high strength steel. It is suggested that transgranular planar slip leading to slip localization is essential in promoting intergranular fracture when the cyclic plastic zone size becomes equal to the prior austenite grain size.

A rationalisation of fatigue thresholds in pearlitic steels using a theoretical model

From a detailed re-examination of results in the literature, the effects of microstructure sizes, namely interlamellar spacing, pearlitic colony size and the prior austentitic grain size on the thresholds for fatigue crack growth (ΔKth) and crack closure (Kcl, th) have been illustrated. It is shown that while interlamellar spacing explicitly controls yield strength, a similar effect on ΔKth cannot be expected. On the other hand, the pearlitic colony size is shown to strongly influence ΔKth and Kcl, th through the deflection and retardation of cracks at colony boundaries. Consequently, an increase in ΔKth and Kcl, th with colony size has been found. The development of a theoretical model to illustrate the effects of colony size, shear flow stress in the slip band and macroscopic yield strength on Kcl, th and ΔKth is presented. the model assumes colony boundaries as potential sites for slip band pile-up formation and subsequent crack deflection finally leading to zig-zag crack growth. Using the concepts of roughness induced crack closure, the magnitude of Kcl, th is quantified as a function of colony size. In deriving the model, the flow stress in the slip band has been considered to represent the work hardened state in pearlite. Comparison of the theoretically predicted trend with the experimental data demonstrates very good agreement. Further, the intrinsic or closure free component of the fatigue threshold, ΔKeff, th is found to be insensitive to colony size and interlamellar spacing. Using a criterion for intrinsic fatigue threshold which considers the attainment of a critical fracture stress over a characteristic distance corresponding to interlamellar spacing, ΔKth values at high R values can be estimated with reasonable accuracy. The magnitude of ΔKth as a function of colony size is then obtained by summing up the average value of experimentally obtained ΔKeff, th values and the predicted Kcl, th values as a function of colony size. Again, very good agreement of the theoretically predicted ΔKth values with those experimentally obtained has been demonstrated.

Effect of strain rate on the high-temperature low-cycle fatigue properties of a nimonic PE-16 superalloy

Strain-rate effects on the low-cycle fatigue (LCF) behavior of a NIMONIC PE-16 superalloy have been evaluated in the temperature range of 523 to 923 K. Total-strain-controlled fatigue tests were per-formed at a strain amplitude of +/-0.6 pct on samples possessing two different prior microstructures: microstructure A, in the solution-annealed condition (free of gamma' and carbides); and microstructure B, in a double-aged condition with gamma' of 18-nm diameter and M23C6 carbides. The cyclic stress response behavior of the alloy was found to depend on the prior microstructure, testing temperature, and strain rate. A softening regime was found to be associated with shearing of ordered gamma' that were either formed during testing or present in the prior microstructure. Various manifestations of dynamic strain aging (DSA) included negative strain rate-stress response, serrations on the stress-strain hysteresis loops, and increased work-hardening rate. The calculated activation energy matched well with that for self-diffusion of Al and Ti in the matrix. Fatigue life increased with an increase in strain rate from 3 x 10(-5) to 3 x 10(-3) s-1, but decreased with further increases in strain rate. At 723 and 823 K and low strain rates, DSA influenced the deformation and fracture behavior of the alloy. Dynamic strain aging increased the strain localization in planar slip bands, and impingement of these bands caused internal grain-boundary cracks and reduced fatigue life. However, at 923 K and low strain rates, fatigue crack initiation and propagation were accelerated by high-temperature oxidation, and the reduced fatigue life was attributed to oxidation-fatigue interaction. Fatigue life was maximum at the intermediate strain rates, where strain localization was lower. Strain localization as a function of strain rate and temperature was quantified by optical and scanning electron microscopy and correlated with fatigue life.

Fatigue crack growth studies on lug joints

Pin loaded lug joints fitted with different types of pins are analysed in the presence of cracks at pin-plate interface. An algorithm for finite element contact stress analysis of joints developed earlier to deal with varying partial contact/separation at the pin-plate interface using a marching solution is used in the present analysis. Stress Intensity Factors (SIF) at the crack tips are evaluated using Modified Crack Closure Integral (MCCI) method within the realm of Linear Elastic Fracture Mechanics (LEFM) assumptions. A comparison of fatigue crack growth lives between interference and push fit pin joints is carried out using these SIF's. Results from a finite element analysis on a push fit pin joint are used to fit experimental fatigue crack growth data.

Analysis of fatigue crack growth in reinforced concrete beams

Mechanical behavior of reinforced concrete members is influenced by the action of unknown crack bridging reactions of rebars. Under cyclic loading, due to progressive growth of cracks, this bridging action contributes to the overall strength, stiffness and hysteretic behavior of the member. In this work, fatigue behavior of reinforced concrete beams are studied using a crack propagation law, developed using dimensional analysis for plain concrete with the effect of reinforcement being simulated through constraint exerted on the crack opening. The parameters considered in the model are fracture toughness, crack length, loading ratio and structural size. A numerical procedure is followed to compute fatigue life of RC beams and the dissipated energy in the steel reinforcement due to the shake down phenomenon under cyclic loading. Through a sensitivity study, it is concluded that the structural size is the most sensitive parameter in the fatigue crack propagation phenomenon. Furthermore, the residual moment carrying capacity of an RC member is determined as a function of crack extension by including the bond-slip mechanism.

A comparative study of failure features in aerospace grade unidirectional and bidirectional woven CFRP composite laminates under four-point bend fatigue loads

Damage mechanisms in unidirectional (UD) and bi-directional (BD) woven carbon fiber reinforced polymer (CFRP) laminates subjected to four point flexure, both in static and fatigue loadings, were studied. The damage progression in composites was monitored by observing the slopes of the load vs. deflection data that represent the stiffness of the given specimen geometry over a number of cycles. It was observed that the unidirectional composites exhibit gradual loss in stiffness whereas the bidirectional woven composites show a relatively quicker loss during stage II of fatigue damage progression. Both, the static and the fatigue failures in unidirectional carbon fiber reinforced polymer composites originates due to generation of cracks on compression face while in bidirectional woven composites the damage ensues from both the compression and the tensile faces. These observations are supported by a detailed fractographic analysis.

Fatigue Laws Via Functional Equations

In routine industrial design, fatigue life estimation is largely based on S-N curves and ad hoc cycle counting algorithms used with Miner's rule for predicting life under complex loading. However, there are well known deficiencies of the conventional approach. Of the many cumulative damage rules that have been proposed, Manson's Double Linear Damage Rule (DLDR) has been the most successful. Here we follow up, through comparisons with experimental data from many sources, on a new approach to empirical fatigue life estimation (A Constructive Empirical Theory for Metal Fatigue Under Block Cyclic Loading', Proceedings of the Royal Society A, in press). The basic modeling approach is first described: it depends on enforcing mathematical consistency between predictions of simple empirical models that include indeterminate functional forms, and published fatigue data from handbooks. This consistency is enforced through setting up and (with luck) solving a functional equation with three independent variables and six unknown functions. The model, after eliminating or identifying various parameters, retains three fitted parameters; for the experimental data available, one of these may be set to zero. On comparison against data from several different sources, with two fitted parameters, we find that our model works about as well as the DLDR and much better than Miner's rule. We finally discuss some ways in which the model might be used, beyond the scope of the DLDR.

Impedance-fatigue correlated studies on SrBi2Ta2O9

Ceramic samples of SrBi2Ta2O9 (SBT) were prepared by the solid state reaction method with a view to study their electrical properties. Reasons as to why SBT shows better fatigue endurance than conventional perovskites like Pb(Zr, Ti)O-3 are looked into. Complex impedance spectroscopy (CIS) was used as a tool to do so. CIS data was acquired over the temperature range from room temperature to 500 degrees C over a wide range of frequencies. Electrical conductivity data indicates that the conductivity in SBT is essentially due to oxygen vacancies and the activation energy for conduction in the high temperature region was found to be 0.95 eV. CIS was used to separate out the bulk and the interfacial contributions to complex impedance.

Effects of tempered structure on the near threshold fatigue crack growth behavior of a coarse grained high strength steel

Near threshold fatigue crack growth behavior of a high strength steel under different temper levels was investigated. It is found that the observed variations in ΔKth could predominantly be attributed to roughness induced crack closure. The closure-free component of the threshold stress intensity range, ΔKeff,th showed a systematic variation with monotonic yield strength.

Short-lived triplets of aliphatic thioketenes

The photophysical behavior of the triplets of three aliphatic thioketenes, namely di-tert-butylthioketene (1), 2,6-di-tert-butylcyclohexylthioketene (2) and 2,2,6,6-tetramethylcyclohexylthioketene, has been studied in fluid solutions at room temperature by nanosecond laser flash photolysis. Upon 532 nm laser excitation into the S1 state, the thioketenes in concentrated benzene solutions produce very short-lived transient absorptions (τ < 5 ns; λmax ≈ 450 nm) attributable to their triplets. The photogeneration of the latter under S1 excitation has also been established by energy transfer to all-trans-1,6-diphenyl-1,3,5-hexatriene. The factors which render the triplet lifetimes short are shown to be intrinsic in origin (rather than self-quenching). Unlike thiocarbonyl compounds in general, the thioketenes posses low intersystem crossing yields (less than 0.1 in benzene). From the kinetics of the quenching of a series of sensitizer triplets by 1 and 2, the thioketene triplet energies are estimated to be 43 – 44 kcal mol−1.

Fatigue crack growth rates and fracture toughness in electroslag refined En 52 steel

En 52 steel has been electroslag refined and the resultant effects of refining on its mechanical properties have been assessed. It was found that refining caused a decrease in fatigue crack growth rates and increases in fatigue strength, fracture toughness, Charpy fracture energy and tensile ductility. Fatigue crack growth rates in region I and in region III were found to be considerably lower in the electroslag refined steel: they were unaffected in region II. The fracture toughness values for the electroslag refined steel are nearly twice those estimated for the unrefined steel. Measurements on heat-treated samples have shown that the electroslag refined steel has a better response to heat-treatment. The improvement in the mechanical properties is explained in terms of the removal of nonmetallic inclusions and a reduction in the sulphur content of the steel.

Effect of electroslag refining on the fracture toughness and fatigue crack propagation rates in heat treated AISI 4340 steel

The AISI 4340 steel has been electroslag refined and the improvement in mechanical properties has been assessed. Electroslag refining (ESR) has improved tensile ductility, plane strain fracture toughness, Charpy fracture energy, and has decreased fatigue crack growth rates. The KIC values for the ESR steel are nearly twice those estimated in the unrefined steel and higher than those obtained in the vacuum arc remelted steel. Fatigue crack growth rates in region I and in region III are found to be decreased considerably in the ESR steel, while they are unaffected in region II. Measurements on heat treated samples have shown that the ESR steel has a better response to heat treatment. Both the suggested heat treatments namely austenitizing at 1140–1470 K as well as the conventional heat treatment of austenitizing at 1140 K have been followed. The improvement in the mechanical properties of ESR steel has been explained on the basis of removal of nonmetallic inclusions and reduction in sulfur content in the steel.