Solvothermal Synthesis of InP Quantum Dots

We report an efficient and fast solvothermal route to prepare highly crystalline monodispersed InP quantum dots. This solvothermal route, not only ensures inert atmosphere, which is strictly required for the synthesis of phase pure InP quantum dots but also allows a reaction temperature as high as 430 degrees C, which is otherwise impossible to achieve using a typical solution chemistry; the higher reaction temperature makes the reaction more facile. This method also has a judicious control over the size of the quantum dots and thus in tuning the bandgap.

Temperature Dependent Photoluminescence Studies in Hg0.2Cd0.8Te Nanorods Synthesized by Solvothermal Method

Hg0.2Cd0.8Te nanorods were synthesized via solvothermal route using an air-stable Na2Te-O-3. The structural and morphological studies were done by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The diameters of the nanorods were found to be 20-50 nm. The growth of the nanorods were facilitated due to the use of CTAB as surfactant. The temperature dependent photoluminescence (PL) studies between 10-300 K show three prominent PL bands in 0.5-0.7 eV and are attributed to defect centers. The features like temperature independent peak energy and quite sensitive PL intensity which shows a thermal quenching behavior indicate that the defects are related to the compositional disorder.

Tailoring the Cu(In, Al)S-2 nanostructures for photonic applications

Solvent dependent and low temperature based Chalcopyrite CuIn1-xAlxS2 (CIAS) nano structures were synthesized by a simple one-pot solvothermal route. X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible spectroscopy and micro-Raman spectroscopy were used to characterize the nanostructures structurally and optically. CIAS hollow spheres were constructed from the nanoplates. Detailed formation mechanism of the hollow spheres was explained. Tentative optical phonon vibrational modes have been discussed. Steady state room temperature IR photodectection have been demonstrated with all the CIAS nanostructures under IR lamp illumination. Photo current was amplified by two orders and one order in case of nano needle like structures and hollow spheres respectively, which was explained based upon the trap assisted space charge. Growth and decay constants lasted for few milli seconds.

Ionothermal Synthesis of High-Voltage Alluaudite Na2+2xFe2-x(SO4)(3) Sodium Insertion Compound: Structural, Electronic, and Magnetic Insights

Exploring future cathode materials for sodium-ion batteries, alluaudite class of Na2Fe2II(SO4)(3) has been recently unveiled as a 3.8 V positive insertion candidate (Barpanda et al. Nat. Commun. 2014, 5, 4358). It forms an Fe-based polyanionic compound delivering the highest Fe-redox potential along with excellent rate kinetics and reversibility. However, like all known SO4-based insertion materials, its synthesis is cumbersome that warrants careful processing avoiding any aqueous exposure. Here, an alternate low temperature ionothermal synthesis has been described to produce the alluaudite Na2+2xFe2-xII(SO4)(3). It marks the first demonstration of solvothermal synthesis of alluaudite Na2+2xM2-xII(SO4)(3) (M = 3d metals) family of cathodes. Unlike classical solid-state route, this solvothermal route favors sustainable synthesis of homogeneous nanostructured alluaudite products at only 300 degrees C, the lowest temperature value until date. The current work reports the synthetic aspects of pristine and modified ionothermal synthesis of Na2+2xFe2-xII(SO4)(3) having tunable size (300 nm similar to 5 mu m) and morphology. It shows antiferromagnetic ordering below 12 K. A reversible capacity in excess of 80 mAh/g was obtained with good rate kinetics and cycling stability over 50 cycles. Using a synergistic approach combining experimental and ab initio DFT analysis, the structural, magnetic, electronic, and electrochemical properties and the structural limitation to extract full capacity have been described.

A simple single-source precursor route to the nanostructures of AIN, GaN and InN

In an effort to find a simple and common single-source precursor route for the group 13 metal nitride semiconductor nanostructures, the complexes formed by the trichlorides of Al, Ga and In with urea have been investigated. The complexes, characterized by X-ray crystallography and other techniques, yield the nitrides on thermal decomposition. Single crystalline nanowires of AlN, GaN and InN have been deposited on Si substrates covered with Au islands by using the complexes as precursors. The urea complexes yield single crystalline nanocrystals under solvothermal conditions. The successful synthesis of the nanowires and nanocrystals of these three important nitrides by a simple single-precursor route is noteworthy and the method may indeed be useful in practice.

Metal-Ion Metathesis in Metal-Organic Frameworks: A Synthetic Route to New Metal-Organic Frameworks

A porous metalorganic framework, Mn(H3O)(Mn4Cl)(3)(hmtt)(8)] (POST-65), was prepared by the reaction of 5,5',10,10',15,15'-hexamethyltruxene-2,7,12-tricarboxylic acid (H(3)hmtt) with MnCl2 under solvothermal conditions. POST-65(Mn) was subjected to post-synthetic modification with Fe, Co, Ni, and Cu according to an ion-exchange method that resulted in the formation of three isomorphous frameworks, POST-65(Co/Ni/Cu), as well as a new framework, POST-65(Fe). The ion-exchanged samples could not be prepared by regular solvothermal reactions. The complete exchange of the metal ions and retention of the framework structure were verified by inductively coupled plasmaatomic emission spectrometry (ICP-AES), powder X-ray diffraction (PXRD), and BrunauerEmmettTeller (BET) surface-area analysis. Single-crystal X-ray diffractions studies revealed a single-crystal-to-single-crystal (SCSC)-transformation nature of the ion-exchange process. Hydrogen-sorption and magnetization measurements showed metal-specific properties of POST-65.

Preparation of lamellar and hexagonal forms of mesoporous silica and zirconiaby the neutral amine route: lamellar-hexagonal transformation in the solid state

The chain length of the surfactant and the solvent composition are two of the factors that determine whether the lamellar or the hexagonal form of mesoporous SiO2 (or ZrO2) is formed by the neutral amine route; a lamellar-hexagonal transformation occurs on removal of the amine from the former.

Homogeneous precipitation from solution by urea hydrolysis: a novel chemical route to the a-hydroxides of nickel and cobalt

Homogeneous precipitation from solution by hydrolysis of urea at elevated temperatures (T=120 degrees C) yields novel ammonia-intercalated alpha-type hydroxide phases of the formula M(OH)(x)(NH3)(0.4)(H2O)(y)(NO3)(2-x) where x=2, y=0.68 for M=Ni and x=1.85, y=0 for M=Co. These triple-layered hexagonal phases (a=3.08+/-0.01 Angstrom, c=21.7+/-0.05 Angstrom) are more crystalline than similar phases obtained by chemical precipitation or electrosynthesis. This method can be adapted as a convenient chemical route to the bulk synthesis of alpha-hydroxides.

Synthesis of nanoparticles of the giant dielectric material, CaCu3Ti4O12 from a precursor route

A complex oxalate precursor, CaCu3(TiO)(4)(C2O4)(8)center dot 9H(2)O, (CCT-OX), was synthesized and the precipitate that obtained was confirmed to be monophasic by the wet chemical analyses, X-ray diffraction, FTIR absorption and TG/DTA analyses. The thermal decomposition of this oxalate precursor led to the formation of phase-pure calcium copper titanate, CaCu3Ti4O12, (CCTO) at a parts per thousand yen680A degrees C. The bright-field TEM micrographs revealed that the size of the as synthesized crystallites to be in the 30-80 nm range. The powders so obtained had excellent sinterability resulting in high density ceramics which exhibited giant dielectric constants upto 40000 (1 kHz) at 25A degrees C, accompanied by low dielectric losses.

A Radical Cyclization Route To +/-Andirolactone, A Spiro-Gamma-Butyrolactone

Synthesis of Andirolactone (Image ), starting from 4-methyl cyclohex-3-en-1-one (Image ), via the radical cyclisation of the bromoacetal (Image ), is described.

An elegant direct route for the preparation of pyridinium, ammonium and alkali metal hexafluorotitanates (IV)

Pyridinium hexafluorotitanate (IV) has been prepared by a one step procedure. Addition of titanium tetrachloride to pyridinium poly(hydrogen fluoride) yields nearly quantitative amounts of pyridinium hexafluorotitanate(IV). Making use of pyridinium hexafluorotitanate as precursor, ammonium and alkali metal (Na, K, Rb, and Cs) hexafluorotitanates have been prepared in good yields. These salts have been characterised by IR, N.M.R. (1H, 13C and 19F), X-ray powder diffraction data and chemical analysis.

Synthesis and Characterization of Carbon-Coated LiNi1/3Co1/3Mn1/3O2 in a Single Step by an Inverse Microemulsion Route

Layered LiNi1/3Co1/3Mn1/3O2, which is isostructural to LiCoO2, is considered as a potential cathode material. A layer of carbon coated on the particles improves the electrode performance, Which is attributed to an increase of the grain connectivity and also to protection of metal oxide from chemical reaction. The present work involves in situ synthesis of carbon-coated submicrometer-sized particles of LiNi1/3Co1/3Mn1/3O2 in an inverse microemulsion medium in the presence of glucose. The precursor obtained from the reaction is heated in air at 900 degrees C for 6 h to get crystalline LiNi1/3Co1/3Mn1/3O2. The carbon coating is found to impart porosity as well as higher surface area in relation to bare samples of the compound. The electrochemical characterization studies provide that carbon-coated LiNi1/3Co1/3Mn1/3O2 samples exhibit improved rate capability and cycling performance. The carbon coatings are shown to suppress the capacity fade, which is normally observed for the bare compound. Impedance spectroscopy data provide additional evidence for the beneficial effect of a carbon coating on LiNi1/3Co1/3Mn1/3O2 particles.

A Convenient Route for the Synthesis of Complex Metal Oxides Employing Solid-Solution Precursors

Synthesis of complex metal oxides by the thermal decomposition of solid-solution precursors (formed by isomorphous compounds of component metals) has been investigated since the method enables mixing of cations on an atomic scale and drastically reduces diffusion distances to a few angstroms. Several interesting oxides such as Ca2Fe03,5C, aCoz04,C a2C0205a, nd Ca,FeCo05 have been prepared by this technique starting from carbonate solid solutions of the type Ca,-,Fe,C03, Cal-,Co,C03, and Ca,-,,M,M'yC03 (M, M' = Mn, Fe, Co). The method has been extended to oxalate solid-solution precursors, and the possibility of making use of other kinds of precursor solid solutions is indicated.

High lithium storage in micrometre sized mesoporous spherical self-assembly of anatase titania nanospheres and carbon

Composite of anatase titania (TiO2) nanospheres and carbon grown and self-assembled into micron-sized mesoporous spheres via a solvothermal synthesis route are discussed here in the context of rechargeable lithium-ion battery. The morphology and carbon content and hence the electrochemical performance are observed to be significantly influenced by the synthesis parameters. Synthesis conditions resulting in a mesoporous arrangement of an optimized amount carbon and TiO2 exhibited the best lithium battery performance. The first discharge cycle capacity of carbon-titania mesoporous spheres (solvothermal reaction at 150 degrees C at 6 h, calcination at 500 degrees C under air, BET surface area 80 m(2)g(-1)) was 334 mAhg(-1) (approximately 1 Li) at current rate of 0.066 Ag-1. High storage capacity and good cyclability is attributed to the nanostructuring of TiO2 (mesoporosity) as well as due to formation of a percolation network of carbon around the TiO2 nanoparticles. The micron-sized mesoporous spheres of carbon-titania composite nanoparticles also show good rate cyclability in the range (0.066-6.67) Ag-1.