Zn incorporation and band gap shrinkage in p-type GaAs

Dimethylzine (DMZn) was used as a p-type dopant in GaAs grown by low pressure metalorganic vapor phase epitaxy using trimethylgallium and arsine (AsH3) as source materials, The hole carrier concentrations and zinc (Zn) incorporation efficiency are studied by using the Hall effect, electrochemical capacitance voltage profiler and photoluminescence (PL) spectroscopy, The influence of growth parameters such as DMZn mole fraction, growth temperature, and AsH, mole fraction on the Zn incorporation have been studied. The hole concentration increases with increasing DMZn and AsH3 mole fraction and decreases with increasing growth temperature. This can be explained by vacancy control model. The PL experiments were carried out as a function of hole concentration (10(17)-1.5 x 10(20) cm(-3)). The main peak shifted to lower energy and the full width at half maximum (FWHM) increases with increasing hole concentrations. We have obtained an empirical relation for FWHM of PL, Delta E(p)(eV) = 1.15 x 10(-8)p(1/3). We also obtained an empirical relation for the band gap shrinkage, Delta E-g in Zn doped GaAs as a function of hole concentration. The value of Delta E-g(eV) = -2.75 x 10(-8)p(1/3), indicates a significant band gap shrinkage at high doping levels, These relations are considered to provide a useful tool to determine the hole concentration in Zn doped GaAs by low temperature PL measurement. The hole concentration increases with increasing AsH3 mole fraction and the main peak is shifted to a lower energy side. This can be explained also by the vacancy control model. As the hole concentration is increased above 3.8 x 10(18) cm(-3), a shoulder peak separated from the main peak was observed in the PL spectra and disappears at higher concentrations. (C) 1997 American Institute of Physics.

Si incorporation and Burstein-Moss shift in n-type GaAs

Silane (SiH4) was used as an n-type dopant in GaAs grown by low pressure metalorganic vapor phase epitaxy using trimethylgallium (TMGa) and arsine (AsH3) as source materials. The electron carrier concentrations and silicon (Si) incorporation efficiency are studied by using Hall effect, electrochemical capacitance voltage profiler and low temperature photoluminescence (LTPL) spectroscopy. The influence of growth parameters, such as SiH4 mole fraction, growth temperature, TMGa and AsH3 mole fractions on the Si incorporation efficiency have been studied. The electron concentration increases with increasing SIH4 mole fraction, growth temperature, and decreases with increasing TMGa and AsH3 mole fractions. The decrease in electron concentration with increasing TMGa can be explained by vacancy control model. The PL experiments were carried out as a function of electron concentration (10(17) - 1.5 x 10(18) cm(-3)). The PL main peak shifts to higher energy and the full width at half maximum (FWHM) increases with increasing electron concentrations. We have obtained an empirical relation for FWHM of PL, Delta E(n) (eV) = 1.4 x 10(-8) n(1/3). We also obtained an empirical relation for the band gap shrinkage, Delta E-g in Si-doped GaAs as a function of electron concentration. The value of Delta E-g (eV) = -2.75 x 10(-8) n(1/3), indicates a significant band gap shrinkage at high doping levels. These relations are considered to provide a useful tool to determine the electron concentration in Si-doped GaAs by low temperature PL measurement. The electron concentration decreases with increasing TMGa and AsH3 mole fractions and the main peak shifts to the lower energy side. The peak shifts towards the lower energy side with increasing TMGa variation can also be explained by vacancy control model. (C) 1999 Elsevier Science S.A. All rights reserved.

Optimization of off-oriented Ge substrates for MOVPE-grown GaAs solar cells

GaAs/Ge heterostructures having abrupt interfaces were grown on 2degrees, 6degrees, and 9degrees off-cut Ge substrates and investigated by cross-sectional high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy, photoluminescence spectroscopy and electrochemical capacitance voltage (ECV) profiler. The GaAs films were grown on off-oriented Ge substrates with growth temperature in the range of 600-700degreesC, growth rate of 3-12 mum/hr and a V/III ratio of 29-88. The lattice indexing of HRTEM exhibits an excellent lattice line matching between GaAs and Ge substrate. The PL spectra from GaAs layer on 6degrees off-cut Ge substrate shows the higher excitonic peak compared with 2degrees and 9degrees off-cut Ge substrates. In addition, the luminescence intensity from the GaAs solar cell grown on 6degrees off-cut is higher than on 9degrees off-cut Ge substrates and signifies the potential use of 6degrees off-cut Ge substrate in the GaAs solar cells industry. The ECV profiling shows an abrupt film/substrate interface as well as between various layers of the solar cell structures.

Temperature dependent magnetic ordering and electrical transport behavior of nano zinc ferrite from 20 to 800 K

The nano ZnFe2O4 compound was prepared by eco-friendly hydrothermal method. The characterization of the sample for its structure, morphology and composition were done by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), dynamic light scattering, Fourier transform infrared spectroscopy, zeta surface profiler and UV-Visible spectroscopy studies. The PXRD measurement reveals that the compound shows spinel cubic phase belong Fd (3) over barm (227) space group. Morphology of the compound from SEM and surface profile shows nearly spherical agglomerated particles with well defined grains and grain boundaries. The material shows the semiconducting behavior with E-g of 2.3 eV at room temperature (RT). The variation in the magnetic ordering was observed for wide range of temperature. The compound behaves like a soft magnetic material with ferrimagnetic at various temperatures except at RT. Both magnetic and EPR studies supports the superparamagnetic behavior of the the sample. The DC conductivity, dielectric and AC conductivity behavior of the 1000 degrees C pellets sintered for 2 h shows good frequency dependent transport properties. The present study facilitate in selecting the suitable materials for the nanoelectronics and spintronic applications. (C) 2013 Elsevier B.V. All rights reserved.