Synthesis, characterization and photocatalytic activity of MxCe1-xVO4 (M = Li, Ca and Fe)

Non-stoichiometric substituted cerium vanadates, MxCe1-xVO4 (M = Li, Ca and Fe), were synthesized by solid-state reactions. The crystal structure was analyzed by powder X-ray diffraction and it exhibits a tetragonal zircon Structure, crystallizing in the space group I4(1)/amd with a = 7.3733(4) and c = 6.4909(4) angstrom and Z = 4. Particle sizes were in the range of 600-800 nm, as observed by scanning electron microscopy. The thermal analysis of the compounds showed phase stability up to 1100 degrees C. The UV diffuse reflectance spectra indicated that the compounds have band gaps in the range of 2.6-2.9 eV. The photocatalytic activity of these Compounds was investigated for the first time for the degradation of different dyes, and organics, the oxidation of cyclohexane and the hydroxylation of benzene. The degradation of dyes was modeled using the Langmuir-Hinshelwood kinetics, while the oxidation of cyclohexane and hydroxylation of benzene were modeled using a free radical mechanism and a series reaction mechanism, respectively.

Novel features of rapidly quenched melts of Bi2(Ca,Sr) 3Cu2O8+δ

By roller quenching and water quenching melts of Bi2(Ca, Sr)3Cu2O8+δ, glasses have been obtained. These glasses exhibit two glass transitions as well as two crystallization transitions. Microwave absorption studies show the glass to be weakly superconducting at 77 K, probably due to the presence of ultramicrocrystallites. The glass on crystallization at 870 K gives the crystalline n=1 member of the homologous series Bi2(Ca, Sr)n+1CunO 2n+4 and the n=2 member on annealing at 1100 K. The glass route provides a unique means of obtaining the n=2 member of the series. On prolonged annealing of the glass at 1120 K, the n=3 member seems to be formed.

Trends in the stability of ternary oxides: Systems M-Pb-O (M = Ca, Sr, Ba)

Recent experimental investigations of phase equilibria and thermodynamic properties of the systems M-Pb-O, where M = Ca, Sr or Ba, indicate a regular increase in thermodynamic stability of ternary oxides, MPbO3 and M2PbO4, with increasing basicity of the oxide of the alkaline-earth metal. Number of stable interoxide compounds at 1100 K in the systems M-Pb-O (M = Mg, Ca, Sr, Ba) increases in unit increments from Mg to Ba. In this paper, experimentally determined standard Gibbs energies of formation of M2PbO4 (M = Ca, Sr, Ba) and MPbO3 (M = Sr, Ba) from their component binary monoxides and oxygen gas are combined with an estimated value for CaPbO3 to delineate systematic trends in thermodynamic stability of the ternary oxides. The trends are interpreted using concepts of tolerance factor and acid-base interactions. All the ternary oxides in these systems contain lead in the tetravalent state. The small Pb4+ ions polarize the surrounding oxygen ions and cause the formation of oxyanions which are acidic in character. Hence, the higher oxidation state of lead is stabilized in the presence of basic oxides of alkaline-earth group. A schematic subsolidus temperature-composition phase diagram is presented for the system BaO-PbO-O-2 to illustrate the change in oxidation states in binary and ternary oxides with temperature.

Energetics of rare earth manganese perovskites A1-xA ' xMnO3 (A = La, Nd, Y and A ' = Sr, La) systems

High temperature reaction calorimetry using molten lead berate as solvent has been used to study the thermochemistry of NdMnO3, YMnO3, La1-xSrxMnO3 (with 0 < x < 0.5), and Ln(0.5)Ca(0.5)MnO(3) (with Ln = La, Nd, Y), The enthalpies of formation of these multicomponent oxides from their binary constituents have been calculated from the measured enthalpy of drop solution, The energetic stability of the perovskite depends on the size of the A cation, The enthalpy of formation of YMnO3 (smallest A cation) is more endothermic than those of NdMnO3 and LaMnO3. The energetics of the perovskite also depends on the oxidation state of the B site's ions. In the La1-xSrxMnO3 system, the energetic stability of the structure increases with the Mn4+/Mn3+ ratio, The new values of the enthalpies of oxidations, with reliable standard entropies, were used to plot the phase stability diagram of the lanthanum-manganese-oxygen system in the temperature range 300-1100 K, The LaMnO3/MnO phase boundary evaluated in this study agrees with the one published by Atsumi et nl. calculated from thermogravimetric and conductivity measurements.

Phase conversions in calcium manganites with changing Ca/Mn ratios and their influence on the electrical transport properties

The phase-interconversions between the spinel-, brownmillerite-, defect rocksalt and perovskite-type structures have been investigated by way of (i) introducing deficiency in A-sites in CaxMn2-xO3 (0.05 <= x <= 1) i.e., by varying Ca/Mn ratio from 0.025 to 1 and (ii) nonstoichiometric CaMnO3-delta (CMO) with 0.02 <= delta <= 1. The temperature dependence of resistivity (rho-T) have been investigated on nonstoichiometric CaMnO3-delta (undoped) as well as the CMO substituted with donor impurities such as La3+, Y3+, Bi3+ or acceptor such as Na1+ ion at the Ca-site. The rho-T characteristics of nonstoichiometric CaMnO3-delta is strongly influenced by oxygen deficiency, which controls the concentration of Mn3+ ions and, in turn, affects the resistivity, rho. The results indicated that the substitution of aliovalent impurities at Ca-site in CaMnO3 has similar effects as of CaMnO3-delta ( undoped) annealed in atmospheres of varying partial pressures whereby electron or hole concentration can be altered, yet the doped samples can be processed in air or atmospheres of higher P-O2. The charge transport mechanisms of nonstoichiometric CaMnO3-delta as against the donor or acceptor doped CaMnO3 (sintered in air, P-O2 similar to 0.2 atm) have been predicted. The rho (T) curves of both donor doped CaMnO3 as well as non-stoichiometric CaMnO3-delta, is predictable by the small polaron hopping (SPH) model, which changes to the variable range hopping (VRH) at low temperatures whereas the acceptor doped CaMnO3 exhibited an activated semiconducting hopping ( ASH) throughout the measured range of temperature (10-500 K).

Structure of nonactin-calcium perchlorate, C40H64O12.Ca(ClO4)2, and a comparative study of metal-nonactin complexes

M r= 975.9, orthorhombic, Pnna, a = 20.262 (3), b= 15.717 (2), c= 15.038 (1)A, V= 4788.97 A 3, z = 4, D x = 1.35 Mg m -3, Cu Kct radiation, 2 = 1.5418 A, /t = 2.79 mm -1, F(000) -= 2072, T = 293 K, R = 0.08, 3335 observed reflections. The molecular structure and the crystal packing are similar to those observed in the nonactin complexes of sodium thiocyanate and potassium thiocyanate. The eight metal-O distances are nearly the same in the potassium complex whereas the four distances involving carbonyl O atoms are shorter than the remaining four involving the tetrahydrofuran-ring O atoms in the Na and the Ca complexes. This observation can be explained in terms of the small ionic radii of Na + and Ca 2+, and leads to a plausible structural rationale for the stronger affinity of nonactin for K + than for the other two metal ions.

TlCaBa2Cu2O7: The 1122 (90 K) superconductor in the new Tl(Ca,Ba)n+1CunO2n+3 seriesstar, open

The 1122 (n=2) member of the Tl(Ca,Ba)n+1CunO2n+3 series containing a single Tl-O layer is shown to be associated with a Tc of 90 K. This value of Tc is significantly lower than that of the 2122 phase (Tcnot, vert, similar110 K) with two Tl-O layers.

Precipitation of rutile and anatase (Tio12) fine powders and their conversion to MTiO3 (M = Ba, Sr, Ca) by the hydrothermal method

Fine powders of TiO2 (rutile) with high degree of crystallinity are formed from aqueous titanium oxychloride solution under hydrothermal conditions at 160–230°C and 15–100 kg/cm2 for 1–2 hours. The anatase phase is produced from the same medium when sulfate ion impurity is present, with Image . Both these fine powders are converted to BaTiO3, SrTiO3 or CaTiO3 when suspended in Ba(OH)2 or Sr(OH)2 solution or in an aqueous slurry of carbonate-free CaO with Image , at 180–280°C and 12–65 kg/cm2 for 4–8 hours. The resulting fine powders contain monocrystallites of the perovskite phase with 0.1–1.5 μm particle size.

Degenerate rhombohedral and orthorhombic states in Ca-substituted Na0.5Bi0.5TiO3

Neutron powder diffraction and temperature dependent dielectric studies were carried out on Ca-substituted Na0.5Bi0.5TiO3, i.e., (Na0.5Bi0.5)(1-x)CaxTiO3. Stabilization of an orthorhombic phase even at a low Ca concentration (0.05 < x < 0.10) suggests that Na0.5Bi0.5TiO3 (NBT) is susceptible to orthorhombic distortion. The orthorhombic and rhombohedral phases coexist for x=0.10, suggesting these phases to be nearly degenerate. The orthorhombic distortion favoring tendency of Ca assists in promoting the inherent instability with regard to this structure in pure NBT, which was reported recently.

Spatial patterning of the distribution of Ca-2+ in Dictyostelium discoideum

We have shown previously that the Ca2+-specific fluorescent dyes chlortetracycline (CTC) and indo-1/AM can be used to distinguish between prestalk and prespore cells in Dictyostelium discoideum at a very early stage. In the present study, pre- and post-aggregative amoebae of Dictyostelium discoideum were labelled with CTC or indo-1 and their fluorescence monitored after being drawn into a fine glass capillary. The cells rapidly form two zones of Ca2+-CTC or Ca2+-indo-1 fluorescence. Anterior (air side) cells display a high level of fluorescence; the level drops in the middle portion of the capillary and rises again to a lesser extent in the posteriormost cells (oil side). When bounded by air on both sides, the cells display high fluorescence at both ends. When oil is present at both ends of the capillary, there is little fluorescence except for small regions at the ends. These outcomes are evident within a couple of minutes of the start of the experiment and the fluorescence pattern intensifies over the course of time. By using the indicator neutral red, as well as with CTC and indo-1, we show that a band displaying strong fluorescence moves away from the anterior end before stabilizing at the anterior-posterior boundary. We discuss our findings in relation to the role of Ca2+ in cell-type differentiation in Dictyostelium discoideum.

Rotational isomerism about the Ca-CO bond in proline derivatives. 1H and 13C NMR studies of benzyloxycarbonyl-Pro-N-methylamide and pivaloyl-Pro-N-methylamide

The 270 MHz 1H n.m.r. spectrum of benzyloxycarbonyl-Pro-N-methylamide in CDCl3 is exchange broadened at 293° K. Spectral lines due to two species are frozen out at 253° K and a dynamically averaged spectrum is obtained at 323° K. A selective broadening of the Cβ and Cγ resonances in the 13C n.m.r. spectrum is observed at 253° K, with a splitting of the Cβ and Cγ resonances into a pair of lines of unequal intensity. A similar broadening of Cβ and Cγ peaks is also detected in pivaloyl-Pro-N-methylamide where cis-trans interconversion about the imide bond is precluded by the bulky t-butyl group. The rate process is thus attributed to rotation about the Cα-CO bond (ψ) and a barrier (ΔG#) of 14kcal mol-1 is estimated. 13C n.m.r. data for pivaloyl-Pro-N-methylamide in a number of solvents is presented and the differences in the Cβ and Cγ chemical shifts are interpreted in terms of rotational isomerism about the Cα-CO bond.

Phase diagram of the system Ca-Ti-O at 1200 K

Phase relations in the system Ca-Ti-O have been established by equilibration of several samples at 1200 K for prolonged periods and identification of phases in quenched samples by optical and scanning electron microscopy, XRD and EDS. Samples representing 20 compositions in the ternary system were analyzed. There was negligible solid solubility of Ca in the phases along the binary Ti-O, and of Ti in CaO. Four ternary oxides were identified: CaTiO3, Ca4Ti3O10 and Ca3Ti2O7 containing tetravalent titanium, and CaTi2O4 containing trivalent titanium. Tie-lines link calcium titanite (CaTi2O4) with the three calcium titanates (CaTiO3, Ca4Ti3O10 and Ca3Ti2O7), CaO, oxygen excess TiO1+delta and stoichiometric TiO. Tie-lines connect CaTiO3 with TiO2-x, Magneli phases TinO2n-1 (28 >= n >= 4), Ti3O5, Ti2O3 and TiO1+delta. CaO was found to coexist with TiO, and Ti-O solid solutions alpha and beta. The phase diagram is useful for understanding the mechanisms and kinetics of direct calciothermic reduction of TiO2 to metal and electrochemical reduction of TiO2 using graphite anode and molten CaCl2 electrolyte.

Study of (Ba3MMWO9)-M-II-W-IV (M-II = Ca, Zn; M-IV = Ti, Zr) perovskite oxides: Competition between 3C and 6H perovskite structures

We describe an investigation of (Ba3MMWO9)-M-II-W-IV oxides for M-II = Ca, Zn, and other divalent metals and M-IV = Ti, Zr. In general, a 1:2-ordered 6H (hexagonal, P6(3)/mmc) perovskite structure is stabilized at high temperatures (1300 degrees C) for all of the (Ba3MTiWO9)-Ti-II oxides investigated. An intermediate phase possessing a partially ordered 1:1 double perovskite (3C) structure with the cation distribution, Ba-2(Zn2/3Ti1/3)(W2/3Ti1/3)O-6, is obtained at 1200 degrees C for Ba3ZnTiWO9. Sr substitution for Ba in the latter stabilizes the cubic 3C structure instead of the 6H structure. A metastable Ba3CaZrWO9 that adopts the 3C (cubic, Fm (3) over barm) structure has also been synthesized by a low-temperature metathesis route. Besides yielding several new perovskite oxides that may be useful as dielectric ceramics, the present investigation provides new insights into the complex interplay of crystal chemistry (tolerance factor) and chemical bonding (anion polarization and d(0)-induced distortion of metal-oxygen octahedra) in the stabilization of 6H versus 3C perovskite structures for the (Ba3MMWO9)-M-II-W-IV series.

Study of (Ba3MMWO9)-M-II-W-IV (M-II = Ca, Zn; M-IV = Ti, Zr) perovskite oxides: Competition between 3C and 6H perovskite structures

We describe an investigation of (Ba3MMWO9)-M-II-W-IV oxides for M-II = Ca, Zn, and other divalent metals and M-IV = Ti, Zr. In general, a 1:2-ordered 6H (hexagonal, P6(3)/mmc) perovskite structure is stabilized at high temperatures (1300 degrees C) for all of the (Ba3MTiWO9)-Ti-II oxides investigated. An intermediate phase possessing a partially ordered 1:1 double perovskite (3C) structure with the cation distribution, Ba-2(Zn2/3Ti1/3)(W2/3Ti1/3)O-6, is obtained at 1200 degrees C for Ba3ZnTiWO9. Sr substitution for Ba in the latter stabilizes the cubic 3C structure instead of the 6H structure. A metastable Ba3CaZrWO9 that adopts the 3C (cubic, Fm (3) over barm) structure has also been synthesized by a low-temperature metathesis route. Besides yielding several new perovskite oxides that may be useful as dielectric ceramics, the present investigation provides new insights into the complex interplay of crystal chemistry (tolerance factor) and chemical bonding (anion polarization and d(0)-induced distortion of metal-oxygen octahedra) in the stabilization of 6H versus 3C perovskite structures for the (Ba3MMWO9)-M-II-W-IV series.

Infra-red spectra of crystalline chloroacetates of Cu, Ca, Sr, Ba and Pb

The infra-red spectra of Cu, Ca, Sr, Ba and Pb chloroacetates were studied in order to investigate the effect of co-ordination on the vibration spectra of the ligand. The shifts of the symmetric and antisymmetric COO− vibrational frequencies indicate a bridged structure as the most probable one for the complexes investigated. No linear relationship between the shifts of the COO− stretching frequencies and E/r (where E is the electron excitation energy and r the ionic radius) was observed. No systematic mass effect on these COO− frequencies also could be established.