A two Roll Mill as a Rheomer for Pastes

Previous work involving the squeeze-film flow of a model paste substance, a mixture of clay particles and mineral oil commonly known as ‘Plasticine’, has suggested that it behaves as a simple Herschel-Bulkley fluid which exhibits little strain history. However, tensile measurements, which are naturally limited to small strains by the onset of necking, indicate that this material shows strain hardening. A two roll-mill is employed here to investigate the influence of larger extensional strains. The data are analysed using an available first order engineering plasticity solution. The results confirm that this material exhibits both extensional strain and strain rate hardening. This observed strain hardening effect, which is not observed in the squeeze-film experiments, is attributed, in part, to the more homogeneous deformation fields induced during rolling and tensile extension.

Three-dimensional plotted hydroxyapatite scaffolds with predefined architecture: comparison of stabilization by alginate cross-linking versus sintering

Scaffolds for bone tissue engineering are essentially characterized by porous three-dimensional structures with interconnected pores to facilitate the exchange of nutrients and removal of waste products from cells, thereby promoting cell proliferation in such engineered scaffolds. Although hydroxyapatite is widely being considered for bone tissue engineering applications due to its occurrence in the natural extracellular matrix of this tissue, limited reports are available on additive manufacturing of hydroxyapatite-based materials. In this perspective, hydroxyapatite-based three-dimensional porous scaffolds with two different binders (maltodextrin and sodium alginate) were fabricated using the extrusion method of three-dimensional plotting and the results were compared in reference to the structural properties of scaffolds processed via chemical stabilization and sintering routes, respectively. With the optimal processing conditions regarding to pH and viscosity of binder-loaded hydroxyapatite pastes, scaffolds with parallelepiped porous architecture having up to 74% porosity were fabricated. Interestingly, sintering of the as-plotted hydroxyapatite-sodium alginate (cross-linked with CaCl2 solution) scaffolds led to the formation of chlorapatite (Ca9.54P5.98O23.8Cl1.60(OH)(2.74)). Both the sintered scaffolds displayed progressive deformation and delayed fracture under compressive loading, with hydroxyapatite-alginate scaffolds exhibiting a higher compressive strength (9.5 +/- 0.5MPa) than hydroxyapatite-maltodextrin scaffolds (7.0 +/- 0.6MPa). The difference in properties is explained in terms of the phase assemblage and microstructure.