Low temperature fabrication and impedance spectroscopy of PMN-PT ceramics

Single phase perovskite 0.9Pb(Mg1/3Nb2/3)O-3-0.1(PbTiO3) ceramics were prepared using the columbite precursor method after optimizing the synthesis conditions. X-ray diffraction (XRD) studies were carried out to verify the phase formation at each processing step. Scanning electron microscopy (SEM) was employed to observe the microstructure of the sintered ceramics. Impedance and modulus spectroscopic data were used to gain an insight into the electrical properties of the samples and with a view to observing the relaxations in them. (C) 1999 Elsevier Science Ltd.

The study of dielectric, pyroelectric and piezoelectric properties on hot pressed PZT-PMN systems

Hot uniaxial pressing technique has been adopted for the densification of PZT-PMN system with an aim to yield dense ceramics and to lower the sintering temperature and time for achieving better and reproducible electronic properties. The ceramics having >97% theoretical density and micron size grains are investigated for their dielectric, pyroelectric and piezoelectric properties. The effect of Li and Mn addition has also been studied. Copyright 2012 Author(s). This article is distributed under a Creative Commons Attribution 3.0 Unported License. http://dx.doi.org/10.1063/1.4769889]

Investigation of biferroic properties in La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3â0.3PbTiO3 epitaxial bilayered heterostructures

Epitaxial bilayered thin films consisting of La0.6Sr0.4MnO3 (LSMO) and 0.7Pb(Mg1/3Nb2/3)O3â0.3PbTiO3 (PMN-PT) layers of relatively different thicknesses were fabricated on LaNiO3 coated LaAlO3 (100) single crystal substrates by pulsed laser ablation technique. The crystallinity, ferroelectric, ferromagnetic, and magnetodielectric properties have been studied for all the bilayered heterostructures. Their microstructural analysis suggested possible StranskiâKrastanov type of growth mechanism in the present case. Ferroelectric and ferromagnetic characteristics of these bilayered heterostructures over a wide range of temperatures confirmed their biferroic nature. The magnetization and ferroelectric polarization of the bilayered heterostructures were enhanced with increasing PMN-PT layer thickness owing to the effect of lattice strain. In addition, evolution of the ferroelectric and ferromagnetic properties of these heterostructures with changing thicknesses of the PMN-PT and LSMO layers indicated possible influence of several interfacial effects such as space charge, depolarization field, domain wall pinning, and spin disorder on the observed properties. Dielectric properties of these heterostructures studied over a wide range of temperatures under different magnetic field strengths suggested a possible role of elastic strain mediated magnetoelectric coupling behind the observed magnetodielectric effect in addition to the influence of rearrangement of the interfacial charge carriers under an applied magnetic field.

Interfacial coupling and its size dependence in PbTiO3 and PbMg1/3Nb2/3O3 multilayers

Multilayers of Pb(Mg1/3Nb2/3)O-3 (PMN)-PbTiO3 (PT) were deposited through pulsed laser ablation deposition with different periodicities (d=10, 20, 30, 40, 50, 60, and 70 nm) for a constant total thickness of the film. The presence of superlattice reflections in the x-ray diffraction pattern clearly showed the superlattice behavior of the fabricated structures over a periodicity range of 20-50 nm. Polarization hysteresis and the capacitance-voltage characteristics of these films show clear size dependent ferroelectric and antiferroelectric (AFE) characteristics. Presence of long-range coupling and strain in multilayers with lower periodicity (similar to 10 nm) exhibited a clear ferroelectric behavior similar to a solid solution of PMN and PT. Multilayers with higher periodicities (20-50 nm) exhibited antiferroelectric behavior, which could be understood from the energy arguments. On further increase of periodicity, they again exhibit ferroelectric behavior. The polarization studies were carried out beyond the Curie temperature T-c of PMN to understand the interlayer interaction. The interaction is changed to a ferroelectric-paraelectric interlayer and tends to lose its antiferroelectric behavior. The behavior of remnant polarization P-r and dP(r)/dT with temperature clearly proves that the AFE coupling of these superlattices is due to the extrinsic interfacial coupling and not an intrinsic interaction as in a homogeneous conventional AFE material. The evidence of an averaged behavior at a periodicity of similar to 10 nm, and the behavior of individual materials at larger periodicities were further confirmed through dielectric phase transition studies. The presence of AFE interfacial coupling was insignificant over the dielectric phase transition of the multilayers.

Synthesis and structural characterization of perovskite 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) nanotubes

We report the synthesis and structural characterization of 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) (PMN-PT) nanotubes prepared by a novel sal-gel template method. X-ray diffraction (XRD) and selected-area electron diffraction (SAED) investigations demonstrated that the postannealed (650 degrees C for 1 h) PMN-PT nanotubes were polycrystalline with perovskite crystal structure. The field emission scanning electron microscope (FE-SEM) shows that as prepared PMN-PT nanotubes were hollow with diameter to be about 200 nm. High resolution transmission electron microscope (HRTEM) analysis confirmed that the obtained PMN-PT nanotubes made up of nanoparticles (10-20 nm) which were randomly aligned in the nanotubes. Energy-dispersive X-ray spectroscopy (EDX) analysis confirmed the stoichiometric 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3). The possible formation mechanism of PMN-PT nanotubes was proposed at the end. (C) 2011 Elsevier B.V. All rights reserved.

Study of relaxor behavior of 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) thin films

Relaxor properties of polycrystalline 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) (PMN-PT) thin films were studied in terms of the diffuse nature of phase transition along with the frequency dispersion of temperature (T-m) at which the dielectric constant exhibits maximum value. Existence of remnant polarization (P-r) above the phase transition temperature, which is a characteristic property of typical relaxor ferroelectric has also been observed in the present case. The films exhibited a gradual decrease of remnant polarization with increase of temperature. Among the different models of relaxor ferroelectric, Vogel-Fulcher model has been found to be suitable to describe the frequency dispersion of T-m in this case. Freezing of dipole moment with decrease of temperature was thought to be the origin of the temperature dependence of dielectric dispersion.

Engineered Biferroic 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3/La0.6Sr0.4MnO3 Epitaxial Superlattices

Symmetric and asymmetric superlattices (SLs) composed of ferromagnetic La0.6Sr0.4MnO3 (LSMO) and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3 – 0.3PbTiO3 (PMN-PT) with different periodicities have been fabricated on LaNiO3 (LNO) coated LaAlO3 (100) (LAO) substrates by pulsed laser ablation deposition. Structural, ferromagnetic and ferroelectric properties have been studied for all the SLs. All the heterostructures exhibited good ferromagnetic response over a wide range of temperatures (10K – 300K), whereas only the asymmetric SLs exhibited reasonably good ferroelectric behaviour. Ferromagnetic and ferroelectric hysteresis loops observed in the asymmetric SLs confirmed their biferroic nature. Studies were conducted towards understanding the influence of LSMO layers on the electrical responses of the heterostructures. Absence of ferroelectricity in the symmetric SL structures has been attributed to their high leakage characteristics. Strong influence of an applied magnetic field of 1.2T was observed on the ferroelectric properties of the asymmetric SLs. The effect of magnetic field on the ferroelectric properties of the SLs indicated possibility of strong interfacial effect.

Field Induced Dielectric Properties of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 Thin Films

DC electric field induced dielectric properties of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) thin films were studied as a function of frequency at different temperatures. It was observed that the dielectric constant (ε) and dissipation factor (tanδ) were decreased in presence of bias field. The temperature of dielectric maxima was found to increase with increasing bias level. The low temperature (PMN and its family is believed to be the origin of relaxor behavior, disappearance of relaxor nature in PMN-PT (70/30) films could be attributed to manifestation of long-range order at higher bias voltage. This was observed in the temperature dependence of dielectric constant i.e. the films neither exhibited any frequency dispersion in the temperature of dielectric maximum (Tm) nor showed any diffused phase transition. The relaxor property of PMN-PT thin films was studied in terms of diffused phase transition together with frequency dispersion of the temperature of dielectric maximum (Tm). Vogel-Fulcher relation was used to analyze the frequency dependence of temperature of dielectric maximum.

Impact of Template Layers on Dielectric and Electrical Properties of Pulsed-Laser Ablated Pb(Mg1/3 Nb2/3)O3 - PbTiO3 Thin Films

A study was done on pulsed laser deposited relaxor ferroelectric thin films of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) deposited on platinized silicon substrates with template layers to observe the influence of the template layers on physical and electrical properties. Initial results, showed that perovskite phase (80% by volume) was obtained through proper selection of the processing conditions on Pt/Ti/SiO2/Si substrates. The films were grown at 300°C and then annealed in a rapid thermal annealing furnace in the temperature range of 750-850°C to induce crystallization. Comparison of the films annealed at different temperatures revealed a change in crystallinity, perovskite phase formation and grain size. These results were further used to improve the quality of the perovskite PMN-PT phase by inserting thin layers of TiO2 on the Pt substrate. These resulted in an increase in perovskite phase in the films even at lower annealing temperatures. Dielectric studies on the PMN-PT films show very high values of dielectric constant (1300) at room temperature, which further improved with the insertion of the template seed layer. The relaxor properties of the PMN-PT were correlated with Vogel-Fulcher theory to determine the actual nature of the relaxation process.

Radiation resistance of PFN and PNM-PT relaxor ferroelectrics

The relaxor ferroelectric compositions Pb(Fe1/2Nb1/2)O-3 (PEN) and [Pb(Mg1/3Nb2/3)O-3](0.8)-[PbTiO3](0.2) (PMN-PT) are studied for their radiation response to the high energy heavy ions (50 MeV Li3+, fluence 1 X 10(13)-1 X 10(14) ions/cm(2)) in terms of their structural, dielectric and piezoelectric properties. There was no change in the crystallinity of both the compositions after irradiation as seen from the XRD. The PEN composition did not show much change in the dielectric constant but the value of T-m decreased by 8degreesC. The PMN-PT composition showed an increase in the dielectric constant with increase in the irradiation fluence from 1 x 10(13) to 1 X 10(14) ions/cm(2) with no change in the value of T-m. The piezoelectric coefficient decreased in both the samples after irradiation. Among the compositions studied, PEN is observed to be more radiation resistant to changes in structural and dielectric properties than PM-PT. (C) 2003 Elsevier Ltd. All rights reserved.

Role of La0.5Sr0.5COO3 template layers on dielectric and electrical properties of pulsed-laser ablated Pb(Nb2/3Mg1/3)O-3-PbTiO3 thin films

Relaxor ferroelectric thin films of 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) (PMN-PT) deposited on platinized silicon substrates with and without template layers were studied. Perovskite phase (80% by volume) was obtained through proper selection of the processing conditions on bare Pt/Ti/SiO2/Si substrates. The films were initially grown at 300 degreesC using pulsed-laser ablation and subsequently annealed in a rapid thermal annealing furnace in the temperature range of 750-850 degreesC to induce crystallization. Comparison of microstructure of the films annealed at different temperatures showed change in perovskite phase formation and grain size etc. Results from compositional analysis of the films revealed that the films initially possessed high content of lead percentage, which subsequently decreased after annealing at temperature 750-850 degreesC. Films with highest perovskite content were found to form at 820-840 degreesC on Pt substrates where the Pb content was near stoichiometric. Further improvement in the formation of perovskite PMN-PT phase was obtained by using buffer layers of La0.5Sr0.5CoO3 (LSCO) on the Pt substrate. This resulted 100% perovskite phase formation in the films deposited at 650 degreesC. Dielectric studies on the PMN-PT films with LSCO template layers showed high values of relative dielectric constant (3800) with a loss factor (tan delta) of 0.035 at a frequency of 1 kHz at room temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Perovskite phase transformation in 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) nanoparticles derived by sol-gel

Fabrication of 0.65Pb(Mg1/3Nb2./3)O-3-0.35PbTiO(3) (PMN-PT) nanoparticles with an average size of about 40 nm and their phase transformation behavior from pyrochlore to perovskite phase is investigated. A novel sol-gel method was used for the synthesis of air-stable and precipitate-free diol-based sol of PMN-PT which was dried and partially calcined at 450 degrees C for 1 h to decompose organics and bring down the free energy barrier for perovskite crystallization and then finally annealed in the temperature range 600 to 700 degrees C. Annealed at around 700 degrees C for 1 h, PMN-PT gel powder exhibited nanocrystalline morphology with perovskite phase as confirmed by the transmission electron microscopy and X-ray diffraction techniques. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3677974]

Compositionally modulated Pb(Mg1/3Nb2/3)O-3-PbTiO3 relaxor thin films deposited by pulsed excimer laser ablation technique

Thin films of (1-x)Pb(Mg1/3Nb2/3)O-3 - xPbTiO(3) (x = 0.1 to 0.3)(PMN-PT) were deposited on the platinum coated silicon substrate by pulsed excimer laser ablation technique. A template layer of LaSr0.5Co0.5O3 (LSCO) was deposited on platinum substrate prior to the deposition of PMN-PT thin films. The composition and the structure of the films were modulated via proper variation of the deposition parameter such as substrate temperature, laser fluence and thickness of the template layers. We observed the impact of the thickness of LSCO template layer on the orientation of the films. A room temperature dielectric constant varying from 2000 to 4500 was noted for different composition of the films. The dielectric properties of the films were studied over the frequency range of 100 Hz - 100 kHz over a wide range of temperatures. The films exhibited the relaxor- type behavior that was characterized by the frequency dispersion of the temperature of dielectric constant maxima (T-m) and also diffuse phase transition. C1 Indian Inst Sci, Mat Res Ctr, Bangalore, Karnataka 560012 India.

Compositionally and structurally modulated Pb(Mg1/3Nb2/3)O3-PbTiO3 relaxor thin films for microactuator application

Thin films of (1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3(x = 0.1 to 0.3) (PMN-PT) were successfully grown on the platinum coated silicon substrate by pulsed excimer laser ablation technique. A thin template layer of LaSr0.5Co0.5O3 (LSCO) was deposited on platinum substrate prior to the deposition of PMN-PT thin films. The composition and the structure of the films were modulated via proper variation of the deposition parameter such as substrate temperature, laser fluence and thickness of the template layers. We observed the impact of the thickness of LSCO template layer on the orientation of the films. The crystallographic structure and compositional variation were confirmed with x-ray diffraction and energy diffraction x-ray (EDX) analysis. A room temperature dielectric constant varying from 2000 to 4500 was noted for different composition of the films. The dielectric properties of the films were studied over the frequency range of 100 Hz - 100 kHz over a wide range of temperatures. The films exhibited the relaxor-type behavior that was characterized by the frequency dispersion of the temperature of dielectric constant maxima (Tm) and also diffuse phase transition. This relaxor nature in PMN-PT thin films was attributed to freezing of the dipole moment, which takes place below a certain temperature. This phenomenon was found to be very similar to spin glass system, where spins are observed to freeze after certain temperature.