Laser damage studies in nonlinear optical crystal sodium p-nitrophenolate dihydrate

We report the surface laser damage threshold in sodium p-nitrophenolate dihydrate, a nonlinear optical crystal. The experiment is performed with a pulsed Nd:YAG laser in TEM00 mode. The single shot damage thresholds are 11.16 +/- 0.28GWcm(-2) and 1.25 +/- 0.02GWcm(-2) for 1064 nm and 532 nm laser wavelengths respectively. A close correlation between the laser damage threshold and mechanical hardness is observed. A possible mechanism of laser damage is discussed.

Physical characterization of the organic nonlinear optical crystal � 3-methoxy 4-hydroxy benzaldehyde

We highlight our recent experimental work on an efficient molecular nonlinear optical crystal, 3-methoxy 4-hydroxy benzaldehyde (MHBA). Optical quality single crystals of MHBA were grown from mixtures of solvents and from melt. The overall absorption and transparency window were improved by growing them in a mixture of chloroform and acetone. The grown crystals were characterized for their optical transmission, mechanical hardness and laser damage. We have observed a strong correlation between mechanical properties and laser induced damage.

Crystal growth and defects characterization of zinc tris (thiourea) sulfate: a novel metalorganic nonlinear optical crystal

Single crystals of the metalorganic nonlinear optical material zinc tris (thiourea) sulfate (ZTS) were grown from aqueous solution. The morphology of the crystals was indexed. The grown crystals were characterized by recording the powder X-ray diffraction pattern and by identifying the diffracting planes. Spectrophotometric studies on ZTS reveal that it has good transparency for the Nd: YAG laser fundamental wavelength. Differential thermal analysis of ZTS indicates that the material does not sublime before melting but decomposes immediately after melting. The defect content of the crystals was estimated using etching and X-ray topography. The mechanical hardness anisotropy was evaluated in the (100) plane, which indicates the presence of soft directions.

Laser damage threshold studies on urea L-malic acid: A nonlinear optical crystal

A detailed study of surface laser damage performed on a nonlinear optical crystal, urea L-malic acid, using 7 ns laser pulses at 10 Hz repetition rate from a Q-switched Nd:YAG laser at wavelengths of 532 and 1064 nm is reported. The single shot and multiple shot surface laser damage threshold values are determined to be 26.64±0.19 and 20.60±0.36 GW cm−2 at 1064 nm and 18.44±0.31 and 7.52±0.22 GW cm−2 at 532 nm laser radiation, respectively. The laser damage anisotropy is consistent with the Vickers mechanical hardness measurement performed along three crystallographic directions. The Knoop polar plot also reflects the damage morphology. Our investigation reveals a direct correlation between the laser damage profile and hardness anisotropy. Thermal breakdown of the crystal is identified as the possible mechanism of laser induced surface damage.

Studies on lithium L-ascorbate dihydrate: An interesting chiral nonlinear optical crystal

Lithium L-Ascorbate dihydrate (LLA) is a new metal organic nonlinear optical crystal belonging to the saccharide family. Single crystals of LLA were grown from aqueous solution. Solubility of the crystal has a positive temperature coefficient facilitating growth by slow cooling. Rietveld refinement was used to confirm the phase formation. The crystal has prismatic habit with (010), (001) and (10-1) prominent faces. Thermal analysis shows that the crystal is stable up to 102 degrees C. Transmission spectrum of the crystal extends from 302 nm to 1600 nm. Dielectric spectroscopic analysis revealed Cole Cole behaviour and prominent piezoelectric resonance peaks were observed in the range of 100-200 kHz. Second harmonic generation (SHG) conversion efficiency of up to 2.56 times that of a phase matched KDP crystal was achieved when the (010) plate of LLA single crystal was rotated about the +ve c axis, by 9.4 degrees in the clockwise direction. We also observed SHG conical sections which were attributed to noncollinear phase matching. The observation of the third conical section suggests very high birefringence and large nonlinear coefficients. A detailed study of surface laser damage showed that the crystal has high multiple damage thresholds of 9.7 GW cm(-2) and 42 GW cm(-2) at 1064 nm and 532 nm radiation respectively. (C) 2012 Elsevier B.V. All rights reserved.

Analysis of Nonlinear Optical Properties of Photonic Crystal Beam-splitters

The paper analyses electromagnetic wave propagation through nonlinear photonic crystal beam-splitters. Different lattice configurations of Y-junction beam-splitters are simulated and propagation properties are investigated with introducing nonlinearity with varying the rod size in crystal lattice. It is seen that nonlinear photonic crystal shows a considerable band-gap even at low refractive contrast. The division of power in both arms of beam-splitters can be controlled by varying the nonlinearity.

Growth and characterization of single crystal cored fibers of organic nonlinear optical materials

The recent development of several organic materials with large nonlinear susceptibilities, high damage threshold and low melting points encouraged researchers to employ these materials in fiber form to efficiently couple diode laser pumps and obtain enhanced second harmonic generation (SHG). In this paper we report the growth of single crystal cored fibers of 4-nitro-4'-methylbenzylidene aniline, ethoxy methoxy chalcone and (-)2-((alpha) -methylbenzylamino)-5- nitropyridine by inverted Bridgman-Stockbarger technique. The fibers were grown in glass capillaries with varying internal diameters and lengths and were characterized using x-ray and polarizing microscope techniques. The propagation loss at 632.8 nm and 1300 nm were measured and SHG was studied using 1064 nm pump.

Hydrogen-Bond-Directed Nonlinear-Optical Organic Materials - Evidence For The Control Of 2nd-Harmonic Generation Activities From The X-Ray Crystal-Structures Of The Complexes Of L-Tartaric Acid With M-Anisidine and P-Toluidine

Several substituted anilines were converted to binary salts with L-tartaric acid. Second harmonic generation (SHG) activities of these salts were determined. The crystal packing in two structures, (i) m-anisidinium-L-tartrate monohydrate (i) and (ii) p-toluidinium-L-tartrate (2), studied using X-ray diffraction demonstrates that extensive hydrogen bonding steers the components into a framework which has a direct bearing on the SHG activity

Optical and dielectric studies of gel grown alpha-hopeite single crystal

Single crystals of a-hopeite exhibiting high transparency were grown by single diffusion gel growth technique. Single crystal X-ray diffraction analysis reveals that the crystal belongs to orthorhombic system. The values of several structural and physical parameters have been determined for the grown crystal. The optical absorption study reveals the transparency of the crystal and is noticed in the entire visible region and the cut-off wavelength was found to be 230 nm. The optical band gap found to be at 3.25 eV. The dependence of extinction co-efficient (k) and the refractive index (n) on the wavelength was also shown. The dielectric constant and dielectric loss of the crystal was studied as a function of frequency and temperature. Transport properties of the grown crystal have been studied from the Cole-Cole plot. (C) 2010 Elsevier GmbH. All rights reserved.

Crystal growth and nonlinear optical properties of sodium D-isoascorbate monohydrate

Optical quality single crystals of sodium D-isoascorbate monohydrate were grown by a slow cooling technique. The crystal possesses a bulky prismatic morphology. Thermal analyses indicate that the crystals are stable up to 125 degrees C. The optical transmission window ranges from 307 nm to 1450 nm. The principal refractive indices have been measured employing Brewster's angle method. The crystallographic and the principal dielectric axes coincide with each other such that a lies along Z, b along X and c along Y. The optic axis is oriented 58 degrees (at 532 nm) to the crystallographic a axis in the XZ plane and the crystal is negative biaxial. Type 1 and type 2 phase matching curves are generated and experimentally verified. No polarization dependence of the light absorption was observed confirming the validity of Kleinman's symmetry conjecture, leading to a single nonvanishing nonlinear tensor component. According to Hobden's classification the crystal belongs to class 3. The crystal also exhibits second order noncollinear conic sections. The single shot and multiple shot surface laser damage thresholds are determined to be 32.7 GW cm(-2) and 6.5 GW cm(-2) respectively for 1064 nm radiation.

Studies in Nonlinear Optical Materials: Structure of 3-Menthyl 2-[Bis(dimethylarnino)methylene]-3-oxobutyrate Hemihydrate

C 19Ha4N203.~xH 2 O, Mr= 347.5, monoclinic, C2, a = 15.473 (3), b = 6.963 (2), c = 20.708 (4) ]1, //=108.2(2) ° , V=2119(2)A 3, Z=4, Ox= 1.089 Mg m -3, ,~(Cu Ktx) = 1.5418 ]1, p = 0.523 mm -~, F(000) = 760.0, T= 293 K, R = 0.068 for 1967 unique reflections. The C=C bond length is 1-447 (6)]1, significantly longer than in ethylene, 1.336 (2)]1. The crystal structure is stabilized by O-H...O hydrogen bonding. Explanation for the observed low second-harmonic-generation efficiency (0.5 times that of urea) is provided.

Studies in Nonlinear Optical Materials: Structure of Methyl 2-(4-Ethyl-5-methyl- 2-thioxo-2,3-dihydro-l,3-thiazol- 3-yl) propionate

CIoH15NO282, Mr=245"0, orthorhombic, P21212 ~, a = 6.639 (2), b = 8.205 (2), c = 22.528(6)A, V= I227.2(6)A 3, z=4, Dm= 1.315, Dx= 1.326gem -3, MoKa, 2=0.7107A, 12= 3.63 cm -1, F(000) = 520, T= 293 K, R = 0.037 for 1115 significant reflections. The second-harmonicgeneration (SHG) efficiency of this compound is only 1/10th of the urea standard. The observed low second-order nonlinear response may be attributed to the unfavourable packing of the molecules in the crystal lattice.

Optical Properties of Nanocrystalline Potassium Lithium Niobate in the Glass System (100-x) TeO2-x(1.5K(2)O-Li2O-2.5Nb(2)O(5))

Optically clear glasses of various compositions in the system (100-x) TeO2-x(1.5K(2)O-Li2O-2.5Nb(2)O(5)) (2 <= x <= 12, in molar ratio) were prepared by the melt-quenching technique. The glassy nature of the as-quenched samples was established via differential scanning calorimetry (DSC). The amorphous and the crystalline nature of the as-quenched and heat-treated samples were confirmed by the X-ray powder diffraction and transmission electron microscopic (TEM) studies. Transparent glasses comprising potassium lithium niobate (K3Li2Nb5O15) microcrystallites on the surface and nanocrystallites within the glass were obtained by controlled heat-treatment of the as-quenched glasses just above the glass transition temperature (T-g). The optical transmission spectra of these glasses and glass-crystal composites of various compositions were recorded in the 200-2500 nm wavelength range. Various optical parameters such as optical band gap, Urbach energy, refractive index were determined. Second order optical non-linearity was established in the heat-treated samples by employing the Maker-Fringe method.

Observation of kink shear bands in an aluminium single crystal fracture specimen

The near-tip deformation field in a high-constraint three-point bend specimen of pure aluminium single crystal is studied using in situ electron back-scattered diffraction and optical metallography. The orientation considered has the notch lying on the (0 1 0) plane and the notch front along direction. Results clearly show the occurrence of a kink shear sector boundary at 90° to the notch line on the specimen free surface as predicted by the analytical model of Rice [J.R. Rice, Mech. Mater. 6 (1987) 317].

Growth and physical properties of a new chiral open-framework crystal for NLO applications: Cesium hydrogen l-malate monohydrate

Cesium hydrogen l-malate monohydrate, CsH(C4H4O5)·H2O, is a new chiral open-framework semi-organic crystalline material with a second-harmonic generation efficiency one order of magnitude greater than KDP. Single crystals of this new material have been grown by the conventional slow cooling technique from aqueous solution. Grown crystals display both platy and prismatic morphologies depending on the imposed supersaturation. Hardness values measured using Vickers hardness indenter show considerable anisotropy. The resistivity behavior at room temperature and above, places the crystal between an ionic conductor and a dielectric. The single-crystal SHG efficiency estimated through Maker fringes experiment gives deff which is 4.24 times that of KDP. Single and multiple shot experiments performed on the grown crystals for the fundamental and second harmonic of pulsed Nd:YAG laser (1064 and 532 nm) show that it exhibits a high laser damage threshold which is a favorable property for nonlinear optical applications.