Structural transitions in (La,Ln)2CuO4 and La2(Cu,Ni)O4 systems

Solid solutions of the formula La2−xLnxCuO4 (Ln = Pr, Nd) possess the orthorhombic structure of La2CuO4 for small values of x and transform to the tetragonal Nd2CuO4 structure at a critical value of x. At the critical composition, there is an abrupt change in specific volume as well as the Image ratio. The material exhibits temperature-independent electrical resistivity below the critical value x and semiconducting behaviour above it. The specific volume and Image ratio smoothly decrease with increase in x in the La2Cu1−xNixO4 system, although the solid solution possess the tetragonal K2NiF4 structure when x>0.1. Compositions with x>0.1 exhibit a gradual semiconductor metal transition similar to that of La2NiO4, the transition temperature decreasing with increasing

Energetics of rare earth manganese perovskites A1-xA ' xMnO3 (A = La, Nd, Y and A ' = Sr, La) systems

High temperature reaction calorimetry using molten lead berate as solvent has been used to study the thermochemistry of NdMnO3, YMnO3, La1-xSrxMnO3 (with 0 < x < 0.5), and Ln(0.5)Ca(0.5)MnO(3) (with Ln = La, Nd, Y), The enthalpies of formation of these multicomponent oxides from their binary constituents have been calculated from the measured enthalpy of drop solution, The energetic stability of the perovskite depends on the size of the A cation, The enthalpy of formation of YMnO3 (smallest A cation) is more endothermic than those of NdMnO3 and LaMnO3. The energetics of the perovskite also depends on the oxidation state of the B site's ions. In the La1-xSrxMnO3 system, the energetic stability of the structure increases with the Mn4+/Mn3+ ratio, The new values of the enthalpies of oxidations, with reliable standard entropies, were used to plot the phase stability diagram of the lanthanum-manganese-oxygen system in the temperature range 300-1100 K, The LaMnO3/MnO phase boundary evaluated in this study agrees with the one published by Atsumi et nl. calculated from thermogravimetric and conductivity measurements.

Structure and magnetotransport properties of the layered manganites REl.2Srl.8Mn,07(R E = La, Pr, Nd)

We have examined the magnetotransport properties and the structure, by Rietveld refinement of powder X-ray data, of the phases RE(1.2)Sr(1.8)Mn(2)O(7) (RE = La, Pr, Nd). We find that on cooling, La1.2Sr1.8Mn2O7 undergoes a transition to a nearly perfect ferromagnet with 90% magnetization at 1.45 T, as reported by earlier workers, but the Pr and Nd phases show only a small magnetization that grows gradually as the temperature is decreased. There seems to be significant correlation between electrical transport and the Jahn-Teller elongation of the apical Mn-O bonds in these systems. The elongation of the apical Mn-O bonds forces the nine-coordinate rock-salt site to be occupied preferentially by the smaller rare-earth-metal cations. This preferential occupation is reliably obtained from the X-ray refinement. All three title phases show a magnetoresistance ratio of about 4(corresponding to a magnetoresistance, [R(0)-R(H)]/R(0), of about 75%) at a field of 7 T and temperatures around 100 K.

Influence of non-stoichiometric defects on nonlinear absorption and refraction in Nd:Zn co-doped lithium niobate

Nonlinear absorption and refraction phenomena in stoichiometric lithium niobate (SLN) pure and co-doped with Zn and Nd, and congruent lithium niobate (CLN) were investigated using Z-scan technique. Femtosecond laser pulses from Ti:Sapphire laser (800 nm, 110 fs pulse width and 1 kHz repetition rate) were utilized for the experiment. The process responsible for nonlinear behavior of the samples was identified to be three photon absorption (3PA). This is in agreement with the band gap energies of the samples obtained from the linear absorption cut off and the slope of the plot of Ln(1 − TOA) vs. Ln(I0) using Sutherland’s theory (s = 2.1, for 3PA). The nonlinear refractive index (n2) of Zn doped samples was found to be lower than that of pure samples. Our experiments show that there exists a correlation between the nonlinear properties and the stoichiometry of the samples. The values of n2 fall into the same range as those obtained for the materials of similar band gap.

Infrared spectra of 1.3-dithiole-2-thione and its selenium analogues ând frequency assignment and molecular force constants

Infrared spectra of 1,3-dithiole-2-thione (DTT) and its four selenium analogues have been studied in the region 4000 to 20 cm�1. Assignment of all the fundamental frequencies was made by noting the band shifts on progressive selenation. Normal coordinate analysis procedures have been applied for both in-plane and out-of-plane vibrations to help the assignments. The Urey�Bradley force function supplemented with valence force constants for the out-of-plane vibrations was employed for coordinate calculations. A correlation of the infrared assignments of DTT with its different selenium analogues is accomplished. Further, the infrared assignments are compared with those of trithiocarbonate ion and its selenium analogues and other structurally related heterocyclic molecules.

Anderson transitions in Ln1-xSrxCoO3 (Ln=Pr or Nd)

Electrical conductivity measurements show that Ln1-xSrxCoO3, (Ln = Pr or Nd) undergoes a non-metal-metal transition when x-0 3. The d.c. conductivity of compositions with 0<x<0.l obeys the T-1/4law up to 400 K and the a.c. conductivity data follow the \omega law with \delta in the range 0.6-0.8. Surprisingly, however, \delta seems to increase with increasing temperature. Thermopower measurements show clear evidence for a change in the mechanism of conduction (around 350 K) from variable range hopping to transport at Ec. All these transport properties suggest that Co4+ ions in Ln1-xSrxCoO3 (0<x<0.1), considered as moving in a lattice of Co3+, form a degenerate gas and that the states at the Fermi energy are Anderson localized.

Dielectric properties of some MM′O4 and MTiM′O6 (M=Cr, Fe, Ga; M′=Nb, Ta, Sb) rutile-type oxides

We describe an investigation of the structure and dielectric properties of MM'O-4 and MTiM'O-6 rutile-type oxides for M = Cr, Fe, Ga and M' = Nb. Ta and Sb. All the oxides adopt a disordered rutile structure (P4(2)/mnm) at ambient temperature. A partial ordered trirutile-type structure is confirmed for FeTaO4 from the low temperature (17 K) neutron diffraction studies While both the MM'O-4 oxides (CrTaO4 and FeTaO4) investigated show a normal dielectric property MTiM'O-6 oxides for M = Fe, Cr and M' = Nb/Ta/Sb display a distinct relaxor/relaxor-like response. Significantly the corresponding gallium analogs, GaTiNbO6 and GaTiTaO6, do not show a relaxor response at T<500K (C) 2010 Elsevier Inc All rights reserved

New family of thallium cuprate superconductors not containing calcium or barium: TlSrn+1−xLnxCunO2n+3+δ (Ln=La, Pr, or Nd)

The first two members of the new TlSrn+1−xLnxCunO2n+3+δ (Ln=La, Pr, or Nd) series of superconducting cuprates possessing 1021 and 1122 type structures are described. The n=1 (1021) members with Tcs around 40 K have electrons or holes as the majority charge carriers depending on x. The n=2 (1122) cuprate (Ln=Pr or Nd) shows a Tc in the 80–90 K range.

Evidence for two distinct orthorhombic structures associated with different Tc regimes in LnBa2Cu3O7 − δ (Ln = Nd, Eu, Gd and Dy): A study of the dependence of superconductivity on oxygen stoichiometry

Superconductivity in LnBa2Cu3O7 − δ with Ln = Nd, Eu, Gdand Dy has been investigated as a function of δ, closely following the accompanying changes in crystal structure. Orthorhombic GdBa2Cu3O7 − δ and DyBa2Cu3O7 − δ show a Tc of ≈ 90 K up to δ = 0.2 and a lower Tc plateau (40–50 K) in the δ range 02 to 0.4, similar to that found in YBa2Cu3O7 − δ. The orthorhombic structure II in the lower Tc regions is different from the structure I in the 90 K Tc (low δ) region. The unit cell parameters of the orthorhombic I structure in the high Tc region bear the relationship of a a ≠ b not, vert, similar c/3. This relationship is not seen in the low Tc plateau. The low Tc plateau region does not distinctly manifest itself in NdBa2Cu3O7 − δ just as in LaBa2Cu3O7 − δ.

Radical Annulation Strategy to Chiral Pupukeanones: Total Synthesis of (+)-10-ex&l(- Naphthyl)pupukean-9-onea nd (+)-lO-exo-l(- Naphthyl)-5-epipupukean-9-ones1

Intramolecular alkylation reaction of the bromoenone 12, obtained from S-carvone in three steps, furnished the bicyclo[2.2.2]octenone 13. Contrary to the anticipated radical annulation reaction, the bicyclic bromides 14 and 15, obtained from the enone 13, generated exclusively the cyclopropane product 18 via a 3-exo-trig radical cyclization on reaction with nBu3SnH and AIBN, even in the presence of a large excess of a radicophile. On the other hand, bromoenone 24, synthesized from R-carvone via S-naphthylcarvone 21, underwent radical annulation reaction in the presence of radicophiles to furnish the isotwistanes 25-28 in a regio- and stereospecific manner. Hydrogenation of the olefin 34, obtained from the diketone 27 via a regiospecific Wittig reaction, furnished the naphthyl-5-epipupukean-9-one 33, whereas stereoselective hydrogenation of the enone 36, prepared from the keto ester 25 via a Grignard reaction and dehydration sequence, generated the naphthylpupukeanone 32.

Synthesis of Novel Oxide Pyrochlores, A2BB?O7 (A = La, Nd; BB? = Pb, Sn, Bi), by Alkali Melt Route

Oxide pyrochlores of the formula A2BB? O7 (A = La, Nd; BB? = Pb, Sn, Bi) have been synthesized by a low-temperature ambient-pressure route employing KOH melts. All the compositions, including La2Bi2O7 and its strontium-substituted derivatives, La2-xSrxBi2O7-?, are deeply colored insulators, confirming that a metallic ground state is not achieved for Pb(IV) and Bi(IV/V) oxides with the pyrochlore structure.

Superconducting YBa2Cu3O7-delta thick films on Ba2RETaO6 (RE=Pr, Nd, Eu, and Dy) substrates

Thick films of YBa2Cu3O7-delta fabricated on polycrystalline Ba2RETaO6 (where RE= Pr, Nd, Eu, and Dy) substrates by dip-coating and partial melting techniques are textured and c-axis oriented, showing predominantly (00l) orientation. All the thick films show a superconducting zero resistance transition of 90 K. SEM studies clearly indicate platelike and needlelike grain growth over a wide area of the thick films. The values of the critical current density for these thick films are similar to 10(4) A/cm(2) at 77 K as determined by the nonresonant R.F. absorption method. Various processing conditions that affect the critical current density of thick films are also discussed.

Grain size effects on charge-ordering, phase segregation and related properties of rare-earth manganates, Nd(0.5)A(0.5)MnO(3) (A = Ca or Sr)

Grain size has marked effects on charge-ordering and other properties of Nd(0.5)A(0.5)MnO(3) (A=Ca or Sr). Thus, the anti-ferromagnetic (AFM) transition in Nd0.5Ca0.5MnO3 is observed distinctly only in samples sintered at 1273 K or higher. The sample with a small grain size (sintered at 1173 K) shows evidence for greater ferromagnetic (FM) interaction at low temperatures, probably due to phase segregation. The FM transition as well as the charge-ordering transition in Nd0.5Sr0.5MnO3 becomes sharper in samples sintered at 1273 K or higher. The sample sintered at 1173 K does not show the AFM-CO transition around 150 K and is FM down to low temperatures; the apparent T-c-T-co gap decreases with the increase in the grain size. The samples sintered at lower temperatures (<1673 K) show evidence for greater segregation of the AFM and FM domains. (C) 2002 Elsevier Science Ltd. All rights reserved.

Phase diagram for the system Nd-Mn-O and thermodynamic properties of NdMnO3 and NdMn2O5

Studies on the phase relations in the system Nd-Mn-O at 1223 K showed two stable ternary compounds, NdMnO3 and NdMn2O5. An isothermal section of the ternary phase diagram for the system Nd-Mn-O was constructed based on phase analysis of samples quenched after equilibration using XRPD and EDS. An advanced version of the solid-state cell incorporating a buffer electrode was used to determine the Gibbs energies of decomposition of NdMnO3 and NdMn2O5 in the temperature range from 925 to 1400 K. Pure oxygen gas at 0.1 MPa was used as the reference electrode, and yttria-stabilized zirconia as the solid electrolyte. The buffer electrode was designed to prevent polarization of the three-phase electrode and ensure accurate data. The measured oxygen potential corresponding to the reaction,2 Nd2O3 + 4 MnO + O-2 --> 4 NdMnO3 can be represented by the equation,Amu(o2) / J.mol(-1) (+/-580) = -523 960 + 170.96 (T/K)Similarly, for the formation of NdMn2O5 according to the reaction,3 NdMnO3 + Mn3O4 + O-2 --> 3 NdMn2O5 Amu(o2) / J.mol(-1) (+/-660) = - 269 390 + 181.74 (T/K) (C) 2002 Elsevier Science Ltd. All rights reserved.

An infrared spectroscopic study of the low-spin to intermediate-spin state (1A1–3T1) transition in rare earth cobaltates, LnCoO3 (Ln=La, Pr and Nd)

Low-spin (LS) to intermediate-spin (IS) state transitions in crystals of LnCoO3 (Ln=La, Pr and Nd) have been investigated by variable temperature infrared spectroscopy. The spectra reveal the occurrence of the transition around 120, 220 and 275 K, respectively, in LaCoO3,PrCoO3 and NdCoO3, at which temperatures the intensities of the stretching and the bending modes associated with the LS state decrease, accompanied by an increase in the intensities of the bands due to IS state. The characteristic frequencies of both the spin states decrease with increase in temperature, showing anomalies around the transition.