A novel fiber-coated strong base-type anion exchanger with superfast kinetics. Removal and recovery of silver thiosulfate from aqueous solutions

A commercial acrylic fiber with 92% (w/w) acrylonitrile content was partially hydrolyzed converting a fraction of the nitrile (-CN) groups to carboxylic acid (-COOH) groups, to coat the fiber with polyethylenimine (PEI) resin, which was then crosslinked with glutaraldehyde and further quaternized with ethyl chloroacetate to produce a novel strong-base anionic exchanger in the form of fiber. Designated as PAN(QPEI.XG)(Cl-), the fibrous sorbent was compared with a commercial bead-form resin Amberlite IRA-458(Cl-) in respect of sorption capacity, selectivity, and kinetics for removal of silver thiosulfate complexes from aqueous solutions. Though the saturation level of [Ag(S2O3)(2)](3-) on PAN(QPEI.XG)(Cl-) is considerably less than that on IRA-458(Cl-), the gel-coated fibrous sorbent exhibits, as compared to the bead-form sorbent, a significantly higher sorption selectivity for the silver thiosulfate complex in the presence of excess of other anions Such as S2O32-, SO42-, and Cl-, and a remarkably faster rate of both sorption and stripping. The initial uptake of the sorbate by the fibrous sorbent is nearly instantaneous, reaching up to similar to 80% of the saturation capacity within 10 s, as compared to only similar to 12% on the bead-form sorbent. The high initial rate of uptake fits a shell-core kinetic model for sorption on fiber of cylindrical geometry. With 4M HCl, the stripping of the sorbed silver complex from the fibrous sorbent is clean and nearly instantaneous, while, in contrast, a much slower rate of stripping on the bead-form sorbent leads to its fouling due to a slow decomposition of the silver thiosulfate complex in the acidic medium.

Oxidation of substituted benzylic hydrocarbons and naphthalenes by peroxydisulphate in the presence of metal ions

Oxidations of various substituted benzylic hydrocarbons with peroxydisulphate in the presence of metal ion catalysts like iron, nickel, copper, cobalt, silver and cerium were examined. Among the metal ions copper (II) catalysed reaction gives products in excellent yield, whereas oxidation of naphthalene and substituted naphthalenes gives low to moderate yield of the products with peroxydisulphate- copper (II).

Delamination of Surfactant-Intercalated Brucite-Like Hydroxy Salts of Cobalt and Copper and Solvothermal Decomposition of the Resultant Colloidal Dispersions

Surfactant anion intercalated hydroxy salts of copper and cobalt of the formula M(OH)(2-x)(surf)(x)center dot mH(2)O [M = Cu, Co; surf = dodecyl sulfate. dodecyl benzene sulfonate. and x = 0.5 for Cu and 0.67 for Co] delaminate readily in 1-butanol to give translucent colloidal dispersions that are stable for months. The extent of delamination and the colloidal dispersion observed in these solids is higher than what had been observed for layered double hydroxides. The dispersions yield the corresponding nanoparticulate oxides on solvothermal decomposition. While the copper hydroxy salt forms similar to 300 nm dendrimer-like CuO nanostructures comprising nanorods of similar to 10 nm diameter, the cobalt analogue forms similar to 20 nm superparamagnetic particles of Co3O4.

Structure-thermal behaviour studies on the salicylato complex of cobalt

The salicylato complex of cobalt was synthesized and its structure established to be [Co(sal)2] · 4 H2O, where, sal =, from elemental analysis, IR spectroscopy, magnetic susceptibility, cryoscopy and conductivity. The X-ray diffractogram of the complex has been given. Thermal decomposition has been studied in air by thermogravimetry (TG), differential thermal analysis and differential scanning calorimetry. TG shows three main steps of decomposition. The intermediates formed at various stages were collected and analysed. From the TG results and chemical analysis of the intermediates, a mechanism has been proposed for the thermal decomposition of the complex, leading to the oxide formation in the final stage.

Thermal decomposition of rare-earth trioxalatocobaltates

The thermal decomposition of rare-earth trioxalatocobaltates LnCo(C2O4)3 · x H2O, where Ln = La, Pr, Nd, has been studied in flowing atmospheres of air/oxygen, argon/ nitrogen, carbon dioxide and a vacuum. The compounds decompose through three major steps, viz. dehydration, decomposition of the oxalate to an intermediate carbonate, which further decomposes to yield rare-earth cobaltite as the final product. The formation of the final product is influenced by the surrounding gas atmosphere. Studies on the thermal decomposition of photodecomposed lanthanum trioxalatocobaltate and a mechanical mixture of lanthanum oxalate and cobalt oxalate in 1 : 2 molar ratio reveal that the decomposition behaviour of the two samples is different. The drawbacks of the decomposition scheme proposed earlier have been pointed out, and logical schemes based on results obtained by TG, DTA, DTG, supplemented by various physico-chemical techniques such as gas and chemical analyses, IR and mass spectroscopy, surface area and magnetic susceptibility measurements and X-ray powder diffraction methods, have been proposed for the decomposition in air of rare-earth trioxalatocobaltates as well as for the photoreduced lanthanum salt and a mechanical mixture of lanthanum and cobalt oxalates.

Thermal decomposition of hydrazinium monoperchlorate in the molten state

The thermal decomposition of hydrazinium monoperchlorate (HP-1) in the molten state has been investigated using differential thermal analysis, thermogravimetric analysis, a constant volume manometric technique and mass-spectrometry. The stoichiometry of the reaction can be represented by the equation: 20 N2H5C1O4 13 NH4C1O4 + 3.5 Cl2 + 2 O2 + 13 N2 + 0.5 N2O + 0.5 H2 + + 23.5 H2O The data seem to indicate that the mechanism, which involves an associated complex, remains unchanged from 140 to 190°. Consequently, impurities capable of forming associated complexes with the hydrazinium or the perchlorate ion desensitize the thermal decomposition of HP-1, the extent of desensitization being determined by the size, the charge and the concentration of the impurity.

Thermodynamics of Cobalt (II, III) Oxide (Co3O4): Evidence of Phase Transition

The Gibbs' energy change for the reaction, 3CoO (r.s.)+1/2O2(g)→Co3O4(sp), has been measured between 730 and 1250 K using a solid state galvanic cell: Pt, CuO+Cu2O|(CaO)ZrO2|CoO+Co3O4,Pt. The emf of this cell varies nonlinearly with temperature between 1075 and 1150 K, indicating a second or higher order phase transition in Co3O4around 1120 (±20) K, associated with an entropy change of ∼43 Jmol-1K-1. The phase transition is accompanied by an anomalous increase in lattice parameter and electrical conductivity. The cubic spinel structure is retained during the transition, which is caused by the change in CO+3 ions from low spin to high spin state. The octahedral site preference energy of CO+3 ion in the high spin state has been evaluated as -24.8 kJ mol-1. This is more positive than the value for CO+2 ion (-32.9 kJ mol-1). The cation distribution therefore changes from normal to inverse side during the phase transition. The transformation is unique, coupling spin unpairing in CO+3 ion with cation rearrangement on the spinel lattice, DTA in pure oxygen revealed a small peak corresponding to the transition, which could be differentiated from the large peak due to decomposition. TGA showed that the stoichiometry of oxide is not significantly altered during the transition. The Gibbs' energy of formation of Co3O4 from CoO and O2 below and above phase transition can be represented by the equations:ΔG0=-205,685+170.79T(±200) J mol-1(730-1080 K) and ΔG0=-157,235+127.53T(±200) J mol-1(1150-1250 K).

Synthesis of graphene oxide-intercalated alpha-hydroxides by metathesis and their decomposition to graphene/metal oxide composites

Graphene oxide-intercalated alpha-metal hydroxides were prepared using layers from the delaminated colloidal dispersions of cetyltrimethylammonium-intercalated graphene oxide and dodecylsulfate-intercalated alpha-hydroxide of nickel/cobalt as precursors. The reaction of the two dispersions leads to de-intercalation of the interlayer ions from both the layered solids and the intercalation of the negatively charged graphene oxide sheets between the positively charged layers of the alpha-hydroxide. Thermal decomposition of the intercalated solids yields graphene/nanocrystalline metal oxide composites. Electron microscopy analysis of the composites indicates that the nanoparticles are intercalated between graphene layers. (C) 2010 Elsevier Ltd. All rights reserved.

On the existence of hydrotalcite-like phases in the absence of trivalent cations

alpha-Hydroxides of nickel(II) and cobalt(II) are hydrotalcite-like phases, possessing a layered double hydroxide (LDH) structure even though there are no trivalent cations in the lattice. While the LDHs acquire a positive charge on the hydroxide layers by the incorporation of trivalent cations, we suggest that the alpha-hydroxides acquire a positive charge by partial protonation of the hydroxyl ions according to the equation M(OH)(2)+xH(+) --> [M(OH)(2-x)(H2O)(x)](x+). As in the LDHs, charge balance is restored by the incorporation of anions in the interlayer region. (C) 1997 Academic Press.

Oxidation and decomposition of NH3 over combustion synthesized Al2O3 and CeO2 supported Pt, Pd and Ag catalysts

The catalytic oxidation and decomposition of NH3 have been carried out over combustion synthesized Al2O3 and CeO2 supported Pt, Pd and Ag catalysts using temperature programmed reaction (TPR) technique in a packed bed tubular reactor. Metals are ionically dispersed over CeO2 and fine metal particles are found on Al2O3. NH3 oxidation occurs over 1% Pt/Al2O3, 1% Pd/Al2O3 and 1% Ag/Al2O3 at 175, 270 and 350 C respectively producing N-2, NO, N2O and H2O, whereas 1% Pt/CeO2, 1% Pd/CeO2 and 1% Ag/CeO2 give N-2 along with NO, N2O and H2O at 200, 225 and 250degreesC respectively. N-2 predominates over other nitrogen-containing products during the reaction on all catalysts. At less O-2 concentration, N-2 and H2O are the only products obtained during NH3 Oxidation. NH3 decomposition over all the catalysts occurs above 450degreesC.

Self-assembled molecular films of tetraamino metal (Co, Cu, Fe) phthalocyanines on gold and silver. Electrochemical and spectroscopic characterization

The formation of molecular films of 2,9,16,23-tetraamino metal phthalocyanines [TAM(II)Pc; M (II) = Co, Cu, and TAM(III)Pc; M = Fe] by spontaneous adsorption on gold and silver surfaces is described. The properties of these films have been investigated by cyclic voltammetry, impedance, and FT-Raman spectroscopy. The charge associated with Co(II) and Co(I) redox couple in voltammetric data leads to a coverage of (0.35+/-0.05) x 10(-10) mol cm(-2), suggesting that the tetraamino cobalt phthalocyanine is adsorbed as a monolayer with an almost complete coverage. The blocking behavior of the films toward oxygen and Fe(CN)(6)(3-/4-) redox couple have been followed by cyclic voltammetry and impedance measurements. This leads to an estimate of the coverage of about 85 % in the case of copper and the iron analogs. FT-Raman studies show characteristic bands around 236 cm(-1) revealing the interaction between the metal substrate and the nitrogen of the -NH2 group on the phthalocyanine molecules.

Cobalt-doped ZnO nanowires on quartz: Synthesis by simple chemical method and characterization

The synthesis of cobalt-doped ZnO nanowires is achieved using a simple, metal salt decomposition growth technique. A sequence of drop casting on a quartz substrate held at 100 degrees C and annealing results in the growth of nanowires of average (modal) length similar to 200 nm and diameter of 15 +/- 4 nm and consequently an aspect ratio of similar to 13. A variation in the synthesis process, where the solution of mixed salts is deposited on the substrate at 25 degrees C, yields a grainy film structure which constitutes a useful comparator case. X-ray diffraction shows a preferred 0001] growth direction for the nanowires while a small unit cell volume contraction for Co-doped samples and data from Raman spectroscopy indicate incorporation of the Co dopant into the lattice; neither technique shows explicit evidence of cobalt oxides. Also the nanowire samples display excellent optical transmission across the entire visible range, as well as strong photoluminescence (exciton emission) in the near UV, centered at 3.25 eV. (C) 2012 Elsevier B.V. All rights reserved.

Carbonization of solvent and capping agent based enhancement in the stabilization of cobalt nanoparticles and their magnetic study

We describe a hybrid synthetic protocol, the solvated metal atom dispersion (SMAD) method, for the synthesis and stabilization of monodisperse amorphous cobalt nanoparticles. By employing an optimized ratio of a weakly coordinating solvent and a capping agent monodisperse colloidal cobalt nanoparticles (2 +/- 0.5 nm) have been prepared by the SMAD method. However, the as-prepared samples were found to be oxidatively unstable which was elucidated by their magnetic studies. Oxidative stability in our case was achieved via a pyrolysis process that led to the decomposition of the organic solvent and the capping agent resulting in the formation of carbon encapsulated cobalt nanoparticles which was confirmed by Raman spectroscopy. Controlled annealing at different temperatures led to the phase transformation of metallic cobalt from the hcp to fcc phase. The magnetic behaviour varies with the phase and the particle size; especially, the coercivity of nanoparticles exhibited strong dependence on the phase transformation of cobalt. The high saturation magnetization close to that of the bulk value was achieved in the case of the annealed samples. In addition to detailed structural and morphological characterization, the results of thermal and magnetic studies are also presented.

Size Control and Magnetic Property Trends in Cobalt Ferrite Nanoparticles Synthesized Using an Aqueous Chemical Route

Cobalt ferrite (CoFe2O4) is an engineering material which is used for applications such as magnetic cores, magnetic switches, hyperthermia based tumor treatment, and as contrast agents for magnetic resonance imaging. Utility of ferrites nanoparticles hinges on its size, dispersibility in solutions, and synthetic control over its coercivity. In this work, we establish correlations between room temperature co-precipitation conditions, and these crucial materials parameters. Furthermore, post-synthesis annealing conditions are correlated with morphology, changes in crystal structure and magnetic properties. We disclose the synthesis and process conditions helpful in obtaining easily sinterable CoFe2O4 nanoparticles with coercive magnetic flux density (H-c) in the range 5.5-31.9 kA/m and M-s in the range 47.9-84.9 A.m(2)Kg(-1). At a grain size of similar to 54 +/- 2 nm (corresponding to 1073 K sintering temperature), multi-domain behavior sets in, which is indicated by a decrease in H-c. In addition, we observe an increase in lattice constant with respect to grain size, which is the inverse of what is expected of in ferrites. Our results suggest that oxygen deficiency plays a crucial role in explaining this inverse trend. We expect the method disclosed here to be a viable and scalable alternative to thermal decomposition based CoFe2O4 synthesis. The magnetic trends reported will aid in the optimization of functional CoFe2O4 nanoparticles