Photocatalytic and Thermal Degradation of Poly(methyl methacrylate), Poly(butyl acrylate), and Their Copolymers

The photocatalytic and thermal degradations of poly(methyl methacrylate), poly(butyl acrylate), and their copolymers of different compositions were studied. The photocatalytic degradation was investigated in o-dichlorobenzene in the presence of two different catalysts, namely, Degussa P-25 and combustion synthesized nanotitania (CSN-TiO2). The samples were analyzed by using gel permeation chromatography (GPC) to obtain the molecular weight distributions (MWDs) as a function of reaction time. Experimental data indicated that the photodegradation of these polymers occurs by both random and chain end scission. A continuous distribution kinetic model was used to determine the degradation rate coefficients by fitting the experimental data with the model. Both the random and specific rate coefficients of the copolymers decreased with increasing percentage of butyl acrylate (BA). Thermal degradation of the copolymers was investigated by thermo-gravimetry. The normalized weight loss profiles for the copolymers showed that the thermal stability of the copolymers increased with mole percentage of BA in the copolymer (PMMABA). The Czawa method was used to determine the activation energies at different conversions. At low acrylate content in the copolymer, the activation energy depends on conversion, indicating multiple degradation mechanisms. At high acrylate content in the copolymer, the activation energy is independent of conversion, indicating degradation by a one-step mechanism.

Cavitation erosion characteristics of poly(methyl methacrylate) in a rotating disk device

Experimental results pertaining to the initiation, dynamics and mechanism of cavitation erosion on poly(methyl methacrylate) specimens tested in a rotating disk device are described in detail. Erosion normally starts at the location nearest to the center of rotation (CR). As the exposure time to cavitation increases, additional erosion areas or sites appear away from the CR and secondary erosion (induced by eroded pits) spreads upstream and merges with the main pit. The microcracks increase in density towards the end of the incubation period and transform into macrocracks in most cases. A study of light optical photographs and scanning electron micrographs of the eroded area shows that material particles are removed from the network of cracks because of crack joining and pits indicate particle debris. Optical degradation (loss of transmittance) is observed to be greater on the back of the specimen than on the front.

Application of various viscosity theories to the viscosity data of methyl methacrylate-acrylonitrile random copolymersstar

Values of Ko, Flory constant related to unperturbed dimensions, are evaluated for methyl methacrylate-acrylonitrile random copolymers using Flory-Fox, Kurata-Stockmayer and Inagaki-Ptitsyn methods and compared with the Ko values obtained by Stockmayer-Fixman method. Ko values are seen to be less in solvents which have large a (Mark-Houwink exponent) values. A correlation between Ko and a is developed to arrive at a more reliable estimate of Ko for this copolymer system.

Photooxidative and pyrolytic degradation of methyl methacrylate-alkyl acrylate copolymers

Different compositions of poly(methyl methacrylate-co-methyl acrylate) (PMMAMA), poly(methyl methacrylate-co-ethyl acrylate) (PMMAEA) and poly(methyl methacrylate-co-butyl acrylate) (PMMABA) copolymers were synthesized and characterized. The photocatalytic oxidative degradation of all these copolymers were studied in presence of two different catalysts namely Degussa P-25 and combustion synthesized titania using azobis-iso-butyronitrile and benzoyl peroxide as oxidizers. Gel permeation hromatography (GPC) was used to determine the molecular weight distribution of the samples as a function of time. The GPC chromatogram indicated that the photocatalytic oxidative degradation of all these copolymers proceeds by both random and chain end scission.Continuous distribution kinetics was used to develop a model for photocatalytic oxidative degradation considering both random and specific end scission. The degradation rate coefficients were determined by fitting the experimental data with the model. The degradation rate coefficients of the copolymers decreased with increase in the percentage of alkyl acrylate in the copolymer. This indicates that the photocatalytic oxidative stability of the copolymers increased with increasing percentage of alkyl acrylate. From the degradation rate coefficients, it was observed that the photocatalytic oxidative stability follows the order PMMABA > PMMAEA > PMMAMA. The thermal degradation of the copolymers was studied by using thermogravimetric analysis (TGA). The normalized weight loss and differential fractional weight loss profiles indicated that the thermal stability of the copolymer increases with an increase in the percentage of alkyl acrylate and the thermal stability of poly(methyl methacrylate-co-alkyl acrylate)s follows the order PMMAMA > PMMAEA > PMMABA. The observed contrast in the order of photostability and thermal stability of the copolymers was attributed to different mechanisms involved for the scission of polymer chain and formation of different products in both the processes.

Dilute Solution Properties of Methyl Methacrylate/Acrylonitrile Random Copolymers, 2a)

The Stockmayer-Fixman relation was used to evaluate the short range and long range interaction parameters for methyl methacrylate/acrylonitrile copolymers of 0,566 and 0,657 mole fraction of monomeric units of acrylonitrile in the solvents acetonitrile, 2-butanone, dimethyl formamide, and y-butyrolactone, at different temperatures (30, 45, and 60 “C). The values of KO were found to be lower than those of the parent homopolymers, and their values depend on both solvent and temperature. Even negative Ko-values were obtained, in cases in which the Mark Houwink exponent a is nearly unity. The values of the polymer-solvent interaction parameter, x, , are high and close to 0,5, indicating that these solvents are not good. The values of the excess interaction parameter, xAB, are negative and are not affected by temperature. The large extension of these copolymer chains, as exhibited by a and a;-values, can be understood in terms of unusual short range interactions only. Similar results were obtained for some cellulose derivatives.

Dilute solution properties of methyl methacrylate�acrylonitrile copolymer (MA1)

This paper deals with studies on the dilute solution properties of methyl methacrylate�acrylonitrile copolymer of 0.289 mole fraction (mf) of acrylonitrile composition. Mark�Houwink parameters for this copolymer have been evaluated in acetonitrile (MeCN), 2-butanone (MEK), dimethylformamide (DMF) and γ-butyrolactone (γ-BL). The solvent power is found to be in the order of MEK < MeCN < DMF < γ-BL at 30°C. Herein, probably for the first time, the steric factor for the copolymer is found to be lower than that for the parent homopolymers and the excess interaction parameter, �AB is found to be negative. This probably suggests that the units are compatible to each other.

Temperature influence on the excess interaction parameter of styrene-methyl methacrylate copolymer

Intrinsic viscosity data for polystyrene, poly(methyl methacrylate) and styrene-methyl methacrylate copolymer of azeotropic composition have been used to evaluate the excess interaction parameters at different temperatures in γ-butyrolactone and dimethylformamide. It is found that these values are positive and show a negligible increase with increase in temperature, indicating therefore that the hetero-contact interactions are not influenced by temperature, contrary to the results obtained by Dondos and Benoit for the same copolymer system in p-xylene and iso-amyl acetate.

Ultrasonic degradation of poly(methyl methacrylate-co-alkyl acrylate) copolymers

The copolymers, poly(methyl methacrylate-co-methyl acrylate) (PMMAMA), poly(methyl methacrylate-co-ethyl acrylate) (PMMAEA) and poly(methyl methacrylate-co-butyl acrylate) (PMMABA), of different compositions were synthesized and characterized. The effect of alkyl acrylate content, alkyl group substituents and solvents on the ultrasonic degradation of these copolymers was studied. A model based on continuous distribution kinetics was used to study the kinetics of degradation. The rate coefficients were obtained by fitting the experimental data with the model. The linear dependence of the rate coefficients on the logarithm of the vapor pressure of the solvent indicated that vapor pressure is the crucial parameter that controls the degradation process. The rate of degradation increases with an increase in the alkyl acrylate content. At any particular copolymer composition, the rate of degradation follows the order: PMMAMA > PMMAEA > PMMABA. It was observed that the degradation rate coefficient varies linearly with the mole percentage of the alkyl acrylate in the copolymer.

Hydrocarbon oxidation and three-way catalytic activity on a single step directly coated cordierite monolith: High catalytic activity of Ce0.98Pd0.02O2−δ

Catalytic activity of cordierite honeycomb by a completely new coating method for the oxidation of major hydrocarbons in exhaust gas is reported here. The new coating process consists of (a) dipping and growing γ-Al2O3 on cordierite by combustion of monolith dipped in the aqueous solution of Al(NO3)3 and oxalyldihydrazide (ODH) (or glycine) at 600 °C and active catalyst phase Ce0.98Pd0.02O2−δ on γ-Al2O3-coated cordierite again by combustion of monolith dipped in the aqueous solution of ceric ammonium nitrate, ODH and 1.2 × 10−3 M PdCl2 solution at 500 °C. Weight of active catalyst can be varied from 0.02 wt% to 2 wt% which is sufficient but can be loaded even up to 12 wt% by repeating dip dry combustion. Adhesion of catalyst to cordierite surface is via oxide growth, which is very strong. ‘HC’ oxidation over the monolith catalyst is carried out with a mixture having the composition, 470 ppm of both propene and propane and 870 ppm of both ethylene and acetylene with the varying amount of O2. Three-way catalytic test is done by putting hydrocarbon mixture along with CO (10 000 ppm), NO (2000 ppm) and O2 (15 000 ppm). Below 350 °C full conversion is achieved. In this method, handling of nano-material powder is avoided.

Photocatalytic degradation of methyl methacrylate copolymers

The photolytic and photocatalytic degradation of the copolymers poly(methyl methacrylate-co-butyl methacrylate) (MMA–BMA), poly(methyl methacrylate-co-ethyl acrylate) (MMA–EA) and poly(methyl methacrylate-co-methacrylic acid) (MMA–MAA) have been carried out in solution in the presence of solution combustion synthesized TiO2 (CS TiO2) and commercial Degussa P-25 TiO2 (DP 25). The degradation rates of the copolymers were compared with the respective homopolymers. The copolymers and the homopolymers degraded randomly along the chain. The degradation rate was determined using continuous distribution kinetics. For all the polymers, CS TiO2 exhibited superior photo-activity compared to the uncatalysed and DP 25 systems, owing to its high surface hydroxyl content and high specific surface area. The time evolution of the hydroxyl and hydroperoxide stretching vibration in the Fourier transform-infrared (FT-IR) spectra of the copolymers indicated that the degradation rate follows the order MMA–MAA > MMA–EA > MMA–BMA. The same order is observed for the rate coefficients of photocatalytic degradation. The photodegradation rate coefficients were compared with the activation energy of pyrolytic degradation. In degradation by pyrolysis, it was observed that MMA–BMA was the least stable followed by MMA–EA and MMA–MAA. The observed contrast in the order of thermal stability compared to the photo-stability of these copolymers was attributed to the two different mechanisms governing the scission of the polymer and the evolution of the products.

Enzymatic Degradation of Poly(soybean oil-g-methyl methacrylate)

This study discusses grafting of methyl methacrylate units from thepolymeric soybean oil peroxide to produce poly(soybean oil-graft-methyl methacrylate) (PSO-g-PMMA). The degradation of this copolymer in solution was evaluated in the presence of different lipases, viz Candida rugosa (CR), Lipolase 100T (LP), Novozym 435 (N435) and Porcine pancreas (PP), at different temperatures The copolymer degraded by specific chain end scission and the mass fraction of the specific product evolved was determined The degradation was modeled using continuous distribution kinetics to determine the rate coefficients ofmenzymatic chain end scission and deactivation of the enzyme The enzymes, CR. LP and N435 exhibited maximum activity for the degradation of PSO-g-PMMA at 60 degrees C, while PP was most active at 50 degrees C. The thermal degradability of the copolymer, assessed by thermo-gravimetry, indicated that the activation energy of degradation of the copolymer was 154 kJ mol(-1), which was lesser than that of the PMMA homopolymer.

Adsorption of anionic dyes on chitosan grafted poly(alkyl methacrylate)s

Chitosan grafted poly(alkyl methacrylate)s (namely chitosan grafted poly(methyl methacrylate) (ChgPMMA), chitosan grafted poly(ethyl methacrylate)(ChgPEMA), chitosan grafted poly(butyl methacrylate) (ChgPBMA) and chitosan grafted poly(hexyl methacrylate) (ChgPHMA)) were synthesized and characterized by using FT-IR and C-13 NMR techniques. The adsorption batch experiments on these grafted copolymers were conducted by using an anionic sulfonated dye. Orange-G. A pseudo-second-order kinetic model was used to determine the kinetics of adsorption. The effect of grafting, effect of process variables and the effect of different sulfonated anionic dyes (Orange-C, Congo Red, Remazol Brill Blue R and Methyl Blue) on the adsorption kinetics was determined. The Langmuir and Freundlich models were used to fit the adsorption isotherms and from the values of correlation coefficients (R-2), it was observed that the experimental data fits very well to the Langmuir model. The values of the maximum adsorption capacity of the adsorbents follow the order: ChgPMMA > ChgPEMA > ChgPBMA > ChgPHMA > chitosan. (C) 2010 Elsevier B.V. All rights reserved.

Main chain and segmental dynamics of semi interpenetrating based on polyisoprene and poly(methyl methacrylate)

Main chain and segmental dynamics of polyisoprene (PI) and poly(methyl methacrylate)(PMMA) chains in semi IPNs were systematically studied over a wide range of temperatures (above and below T-g of both polymers) as a function of composition, crosslink density, and molecular weight. The immiscible polymers retained most of its characteristic molecular motion; however, the semi IPN synthesis resulted in dramatic changes in the motional behavior of both polymers due to the molecular level interpenetration between two polymer chains. ESR spin probe method was found to be sensitive to the concentration changes of PMMA in semi IPNs. Low temperature spectra showed the characteristics of rigid limit spectra, and in the range of 293-373 K.complex spectra were obtained with the slow component mostly arisingout of the PMMA rich regions and fast component from the PI phase. We found that the rigid PMMA chains closely interpenetrated into thehighly mobile PI network imparts motional restriction in nearby PI chains, and the highly mobile PI chains induce some degree of flexibility in highly rigid PMMA chains. Molecular level interchain mixing was found to be more efficient at a PMMA concentration of 35 wt.%. Moreover, the strong interphase formed in the above mentionedsemi IPN contributed to the large slow component in the ESR spectra at higher temperature. The shape of the spectra along with the data obtained from the simulations of spectra was correlated to the morphology of the semi IPNs. The correlation time measurement detected the motional region associated with the glass transition of PI and PMMA, and these regions were found to follow the same pattern of shifts in a-relaxation of PI and PMMA observed in DMA analysis. Activation energies associated with the T-g regions were also calculated. T-50G was found to correlate with the T-g of PMMA, and the volume of polymer segments undergoing glass transitional motion was calculated to be 1.7 nm(3).C-13 T-1 rho measurements of PMMA carbons indicate that the molecular level interactions were strong in semi IPN irrespective of the immiscible nature of polymers. The motional characteristics of H atoms attached to carbon atoms in both polymers were analyzed using 2D WISE NMR. Main relaxations of both components shifted inward, and both SEM and TEM analysis showed the development of a nanometer sized morphology in the case of highly crosslinked semi IPN. (C) 2010 Elsevier Ltd. All rights reserved.

Ultrasonic degradation of poly (styrene-co-alkyl methacrylate) copolymers

The ultrasonic degradation of poly (styrene-co-methyl methacrylate) (SMMA), poly (styrene-co-ethyl methacrylate) (SEMA) and poly (styrene-co-butyl methacrylate) (SBMA) copolymers of different compositions was studied. The copolymers were synthesized and NMR spectroscopy was used to determine the composition, and the glass transition temperatures were determined by DSC. The reactivity ratios were determined by the Kelen-Tudos method and it indicated that the copolymers were random. The effect of solvent, temperature and copolymer composition on the ultrasonic degradation rate of these copolymers was investigated. A model based on continuous distribution kinetics was employed to study the degradation kinetics. The degradation rate coefficients of the copolymers decreased with an increase in the styrene content in the copolymer. At any particular copolymer composition the rate of degradation follows the order: SBMA >SEMA > SMMA. Thermogravimetric analysis (TGA) of the copolymers was carried in order to assess their thermal stability. The same order of degradation was observed for the thermal degradation of the copolymers as that observed for ultrasonic degradation. (C) 2010 Elsevier B.V. All rights reserved.