Switching transients in ferroelectric dicalcium strontium propionate (DSP) and Azoxybenzene

The ferroelectric polarization switching was studied in DSP single crystal and Azoxybenzene liquid film using the method described by Merz (1954). The DSP single crystal samples were in the form of plates 0.5 mm - 1.0 mm thick. The Azoxybenzene liquid film samples had a thickness from 0.025 mm - 0.125 mm. Switching in DSP was observed in the temperature range +7°C to -30°C, while in Azoxybenzene it was observed from 30°C to 70°C.

Polarization enhancement in compositionally graded vanadium doped bismuth titanate thin films

Compositionally up and downgraded Bi4-x/3Ti3-xVxO12 (x=0.0, 0.012,0.03, 0.06) thin films were grown on Pt coated silicon substrates by pulsed laser deposition technique. Downgraded fabrication showed improved ferroelectric polarization in comparison to upgraded fabrication. Films deposited at 650 and 700 degrees C showed very large remnant polarization (2P(r)) value of 82 mu C cm(-2), which is comparatively large among all bismuth based thin films reported so far. A mechanism based on vanadium enrich seeded layer formation in the downgraded structure is proposed for the improvement. Moreover, frequency independent behavior (100Hz-5kHz) of the graded films ensures its potential application for various microelectronic devices. (c) 2010 American Institute of Physics. [doi :10.1063/1.3431543].

Investigation of biferroic properties in La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3â0.3PbTiO3 epitaxial bilayered heterostructures

Epitaxial bilayered thin films consisting of La0.6Sr0.4MnO3 (LSMO) and 0.7Pb(Mg1/3Nb2/3)O3â0.3PbTiO3 (PMN-PT) layers of relatively different thicknesses were fabricated on LaNiO3 coated LaAlO3 (100) single crystal substrates by pulsed laser ablation technique. The crystallinity, ferroelectric, ferromagnetic, and magnetodielectric properties have been studied for all the bilayered heterostructures. Their microstructural analysis suggested possible StranskiâKrastanov type of growth mechanism in the present case. Ferroelectric and ferromagnetic characteristics of these bilayered heterostructures over a wide range of temperatures confirmed their biferroic nature. The magnetization and ferroelectric polarization of the bilayered heterostructures were enhanced with increasing PMN-PT layer thickness owing to the effect of lattice strain. In addition, evolution of the ferroelectric and ferromagnetic properties of these heterostructures with changing thicknesses of the PMN-PT and LSMO layers indicated possible influence of several interfacial effects such as space charge, depolarization field, domain wall pinning, and spin disorder on the observed properties. Dielectric properties of these heterostructures studied over a wide range of temperatures under different magnetic field strengths suggested a possible role of elastic strain mediated magnetoelectric coupling behind the observed magnetodielectric effect in addition to the influence of rearrangement of the interfacial charge carriers under an applied magnetic field.

Dielectric properties of (110) oriented PbZrO3 and La-modified PbZrO3 thin films grown by sol-gel process on Pt(111)/Ti/SiO2/Si substrate

Highly (110) preferred orientated antiferroelectric PbZrO3 (PZ) and La-modified PZ thin films have been fabricated on Pt/Ti/SiO2/Si substrates using sol-gel process. Dielectric properties, electric field induced ferroelectric polarization, and the temperature dependence of the dielectric response have been explored as a function of composition. The Tc has been observed to decrease by ∼ 17 °C per 1 mol % of La doping. Double hysteresis loops were seen with zero remnant polarization and with coercive fields in between 176 and 193 kV/cm at 80 °C for antiferroelectric to ferroelectric phase transformation. These slim loops have been explained by the high orientation of the films along the polar direction of the antiparallel dipoles of a tetragonal primitive cell and by the strong electrostatic interaction between La ions and oxygen ions in an ABO3 perovskite unit cell. High quality films exhibited very low loss factor less than 0.015 at room temperature and pure PZ; 1 and 2 mol % La doped PZs have shown the room temperature dielectric constant of 135, 219, and 142 at the frequency of 10 kHz. The passive layer effects in these films have been explained by Curie constants and Curie temperatures. The ac conductivity and the corresponding Arrhenius plots have been shown and explained in terms of doping effect and electrode resistance.

Metastable monoclinic and orthorhombic phases and electric field induced irreversible phase transformation at room temperature in the lead-free classical ferroelectric BaTiO3

For decades it has been a well-known fact that among the few ferroelectric compounds in the perovskite family, namely, BaTiO3, KNbO3, PbTiO3, and Na1/2Bi1/2TiO3, the dielectric and piezoelectric properties of BaTiO3 are considerably higher than the others in polycrystalline form at room temperature. Further, similar to ferroelectric alloys exhibiting morphotropic phase boundary, single crystals of BaTiO3 exhibit anomalously large piezoelectric response when poled away from the direction of spontaneous polarization at room temperature. These anomalous features in BaTiO3 remained unexplained so far from the structural standpoint. In this work, we have used high-resolution synchrotron x-ray powder diffraction, atomic resolution aberration-corrected transmission electron microscopy, in conjunction with a powder poling technique, to reveal that at 300 K (i) the equilibrium state of BaTiO3 is characterized by coexistence of metastable monoclinic Pm and orthorhombic (Amm2) phases along with the tetragonal phase, and (ii) strong electric field switches the polarization direction from the 001] direction towards the 101] direction. These results suggest that BaTiO3 at room temperature is within an instability regime, and that this instability is the fundamental factor responsible for the anomalous dielectric and piezoelectric properties of BaTiO3 as compared to the other homologous ferroelectric perovskite compounds at room temperature. Pure BaTiO3 at room temperature is therefore more akin to lead-based ferroelectric alloys close to the morphotropic phase boundary where polarization rotation and field induced ferroelectric-ferroelectric phase transformations play a fundamental role in influencing the dielectric and piezoelectric behavior.

Polarization switching in radiation damaged ferroelectric crystals

The polarization switching processes in radiation damaged ferroelectrics were studied by the Merz method. In irradiated triglycine sulphate and sodium nitrite, the switching time depends exponentially on the applied electric field. Irradiation increases the importance of nucleation and sideways motion of the domain walls in polarization switching.

Polarization reversal studies in ferroelectric taap

Telluric Acid Ammonium Phosphate (Te(OH)62(NH4)H2PO4(NH4)2HPO4) reffered to as TAAP is a recently discovered class m ferroelectric.1 It undergoes FE-PE transition at 48°C. Switching studies in this crystal has been carried out in the temperature range -14°C to 39°C by applying fields up to 4 kV/cm. Measurements were carried out on (101) plates cut from the crystals grown from solution. X-ray irradiation was carried out at room temperature by means of an x-ray tube operating at 25 kV and 15 mA with copper target. Air drying silver paste was used as electrodes. Samples were checked for hysteresis loop using a modified Sawyer-Tower circuit. The Ps value obtained from the loop is 2.1 μC/cm2 which is comparable to the earlier reported value. It was however noticed that the loop was slightly shifted to right with respect to the origin indicating the presence of a small internal bias which was 100 V/cm in the virgin crystal. This bias could not be removed even after repeated crystallization. On irradiation the internal biasing field increased which was indicated by a further shift of the hysteresis loop. The bias seems to saturate at about 750 V/cm for which the crystal had to be irradiated for about 3 hours.

Polarization switching studies in ferroelectric glycine phosphite single crystals

Glycine Phosphite [NH3CH2COOH3PO3], abbreviated as GPI, undergoes a para-ferroelectric phase transition from the monoclinic symmetry P2(1)/a to P2(1) at 224.7 K. We report here a systematic study of the polarization switching process in this crystal. Growth of these crystals from aqueous solution has been undertaken employing both solvent evaporation and slow cooling methods. Hysteresis loop measurements along the polar b-axis yielded a spontaneous polarization value of 0.5 muC/cm(2) and a coercive field of 2.5 kV/cm. Conventional Merz technique was employed for polarization switching studies, wherein bipolar square pulses were applied to the sample to induce domain reversal. The transient switching pulse that flows through the sample on application of the field was recorded. The maximum switching time required for domain switching was measured both as a function of electric field and temperature. The experimentally observed switching curves were fitted with the model based on the Pulvari-Kuebler theory of nucleation and growth of domains. From the experimental data, the values of mobility and activation field were obtained. It was observed that switching process in this crystal is predominantly governed by the forward growth of domain walls in the high field region. However, switching process in GPI crystal was found to be slower than that found in other glycine based ferroelectric crystals.

Ferroelectric interaction and polarization studies in BaTiO3/SrTiO3 superlattice

Ferroelectric superlattice structures consisting of alternating layers of BaTiO3 and SrTiO3 with variable interlayer thickness were grown on Pt (111)/TiO2/SiO2/Si (100) substrates by pulsed laser deposition. The presence of superlattice reflections in the x-ray diffraction pattern clearly showed the superlattice behavior of the fabricated structures over a range of 6.4–20 nm individual layer thicknesses. Depth profile conducted by secondary ion mass spectrometry analysis showed a periodic concentration of Ba and Sr throughout the film. Polarization hysteresis and the capacitance-voltage characteristics of these films show clear size dependent ferroelectric characteristics. The spontaneous (Ps) and remnant (Pr) polarizations increase gradually with decreasing periodicity, reach a maximum at a finite thickness and then decrease. The competition between the size effect and long-range ferroelectric interaction is suggested as a possible reason for this phenomenon. The temperature dependence of Ps and Pr shows a single ferroelectric phase transition, and the Curie temperature is estimated to be about 316 K. The curve shows that the ferroelectric superlattice tends to form an artificial material, responding as a single structure with an averaged behavior of both the parent systems.

Anomalous polarization in the antiferroelectric-ferroelectric phase coexistence state in PbZrO3-Bi(Mg1/2Ti1/2)O-3

The ferroelectric system (1-x)PbZrO3-(x)Bi(Mg1/2Ti1/2)O-3 has been investigated as a function of composition, temperature, and electric field by x-ray powder diffraction, dielectric, and ferroelectric measurements. Within the solubility limit (x similar to 0.25), the system evolves from an orthorhombic-antiferroelectric to rhombohedral-ferroelectric state through a phase coexistence region. The highest polarization was found not for the composition exhibiting a pure ferroelectric state, but for a composition x = 0.15 exhibiting ferroelectric + antiferroelectric phase coexistence close to the rhombohedral phase boundary. Electric poling of the equilibrium two-phase state led to irreversible enhancement in the rhombohedral phase fraction suggesting that the enhanced polarization is related to the enhanced polarizability of the lattice due to first order criticality as in ferroelectric-ferroelectric morphotropic phase boundary systems. (C) 2013 AIP Publishing LLC.

Enhancement of nonvolatile polarization and pyroelectric sensitivity in lithium tantalate (LT)/poly(vinylidene fluoride) (PVDF) nanocomposite

We report the ferroelectric and pyroelectric properties of the composite films of lithium tantalate (LT) nanoparticle in poly(vinylidene fluoride) PVDF matrix at different volume fractions of LT (f(LT) = 0.047, 0.09 and 0.17). For an applied electric field of 150 kV cm(-1) the nonvolatile polarization of the composite was observed to increase from 0.014 mu C cm(-2) at f(LT) = 0 to 2.06 mu C cm(-2) at f(LT) = 0.17. For f(LT) = 0.17, the composite films exhibit a saturated ferroelectric hysteresis loop with a remanent polarization (2P(r) = 4.13 mu C cm(-2)). Compared with pure poled PVDF the composite films also showed a factor of about five enhancement in the pyroelectric coefficient at f(LT) = 0.17. When used in energy detection mode the pyroelectric voltage sensitivity of the composite films was found to increase from 3.93 to 18.5 VJ(-1) with an increase in f(LT) from 0.0 to 0.17.

Influence of lanthanum doping on the dielectric, ferroelectric and relaxor behaviour of barium bismuth titanate ceramics

Barium lanthanum bismuth titanate (Ba1−(3/2)xLaxBi4Ti4O15, x = 0–0.4) ceramics were fabricated using the powders synthesized via the solid-state reaction route. X-ray powder diffraction analysis confirmed the above compositions to be monophasic and belonged to the m = 4 member of the Aurivillius family of oxides. The effect of the partial presence of La3+ on Ba2+ sites on the microstructure, dielectric and relaxor behaviour of BaBi4Ti4O15 (BBT) ceramics was investigated. For the compositions pertaining to x ≤ 0.1, the dielectric constant at both room temperature and in the vicinity of the temperature of the dielectric maximum (Tm) of the parent phase (BBT) increased significantly with an increase in x while Tm remained almost constant. Tm shifted towards lower temperatures accompanied by a decrease in the magnitude of the dielectric maximum (εm) with an increase in the lanthanum content (0.1 < x ≤ 0.4). The dielectric relaxation was modelled using the Vogel–Fulcher relation and a decrease in the activation energy for frequency dispersion with increasing x was observed. The frequency dispersion of Tm was found to decrease with an increase in lanthanum doping, and for compositions corresponding to x ≥ 0.3, Tm was frequency independent. Well-developed P(polarization)–E(electric field) hysteresis loops were observed at 150 °C for all the samples and the remanent polarization (2Pr) was improved from 6.3 µC cm−2 for pure BBT to 13.4 µC cm−2 for Ba0.7La0.2Bi4Ti4O15 ceramics. Dc conductivities and associated activation energies were evaluated using impedance spectroscopy.

Study of switching characteristics and thermal noise in ferroelectric crystals both in the pure and radiation damaged state

The phase transition in gamma-irradiated triglycine sulphate (TGS) has been investigated by using a method based on the measurement of thermal noise. The results of a study of the polarization switching characteristics of gamma irradiated TGS and sodium nitrite (NaNO2) have also been presented. The effect of irradiation on the phase transition and the switching processes has been discussed.

Bi4Ti3O12-5BiFeO(3) Aurivillius intergrowth: Structural and ferroelectric properties

Aurivillus intergrowth Bi4Ti3O12-5BiFeO(3) was demonstrated to be ferroelectric that evoked the possibility of achieving high temperature magnetoelectric property in this family of compounds. X-ray diffraction studies confirmed its structure to be orthorhombic [Fmm2; a=5.5061(11) A degrees, b=5.4857(7) A degrees, c=65.742(12) A degrees]. However, transmission electron microscopy established the random incidence of intergrowth at nanoscale corresponding to n=6 and n=7 members of the Aurivillius family. Diffuse ferroelectric orthorhombic to paraelectric tetragonal phase transition around 857 K was confirmed by dielectric and high temperature x-ray diffraction studies. Polarization versus electric field hysteresis loops associated with 2P(r) of 5.2 mu C/cm(2) and coercive field of 42 kV/cm were obtained at 300 K.

Dielectric, Ferroelectric and Relaxor Behavior of BaLaxBi4-xTi4O15 Ceramics

Monophasic BaLaxBi4-xTi4O15 (x = 0, 0.2, 0.4, 0.6 and 0.8) ceramics, fabricated from the powders synthesized via the solid-state reaction route exhibited relaxor behavior. Dielectric properties of the well sintered ceramics were measured in a wide frequency range (1 kHz-1 MHz) at different temperatures (300-750 K). The temperature of dielectri maximum (T-m) was found to decrease significantly from 696 K for an undoped sample (x = 0) to 395 K for the sample corresponding to the composition x = 0.8 accompanied by a decrease in the magnitude ofdielectric maximum (epsilon(m)). The temperature variation of the dielectric constant on the high temperature slope of the peak (T > T-m) was analyzed by using the Lorentz-ype quadratic law and the diffuseness of the peak was found to increase with increasing x. Vogel-Fulcher modelling of dielectric relaxation showed a decrease in freezing temperature (T-VF) (from 678 to 340 K) and an increase in the activation energy (5 to 24 meV) for the frequency dispersion with increase in x (La-3 divided by content). Strength of frequency dispersion of the phase transition increased with lanthanum content. Polarization (P)-electric field (E) hysteresis loops recorded at 373 showed a transition from a nearly squarish to slim loop hysteresis behavior with increasing lanthanum content.