Sensitivity characteristics of Ag doped BaTiO3-CuO mixed oxide as Carbon-dioxide S ensor

Ag doped BaTiO3-CuO mixed oxide thin films are evaluated for their carbon-dioxide sensing characteristics. The metal oxide films of different thicknesses are deposited on oxidized p type Si < 100 > substrate by RF Sputtering. Sensing characteristics for different CO2 concentration, (300 ppm - 1000 ppm) are obtained for different operating temperatures, (100 degrees C - 400 degrees C). Optimum temperature for maximum sensitivity is found to be 250 degrees C. The effect of annealing on sensing properties is also evaluated. The unannealed films give better sensitivity than that of annealed films. Response time and recovery time are also calculated.

Photocatalytic Activity of Combustion Synthesized ZrO(2) and ZrO(2)-TiO(2) Mixed Oxides

Tetragonal ZrO(2), synthesized by solution combustion technique, was found to be photocatalytically active for the degradation of anionic dyes. The compound was characterized by FT-Raman spectroscopy, X-ray photoelectron spectroscopy, FT-infrared spectroscopy, UV-vis spectroscopy, BET surface area analysis, and zero point charge pH measurement. A high concentration of surface hydroxyl groups was observed over the catalyst, as confirmed by XPS and FUR. The photocatalytic degradation of orange G, amido black, remazol brilliant blue R, and alizarin cyanine green (ACG) was carried out with this material. The effect of pH, inorganic. salts, and H(2)O(2) on the activity of the catalyst was also studied, and it was found that the catalyst maintained its activity at a wide range of pH and in the presence of inorganic salts. Having established that ZrO(2) was photocatalytically active, mixed oxide catalysts of TiO(2)-ZrO(2) were also tested for the photocatalytic degradation of ACG, and the 50% ZrO(2)-TiO(2) mixed oxides showed activity that was comparable to the activity of TiO(2).

Ce0.67Cr0.33O2.11: A New Low-Temperature O-2 Evolution Material and H-2 Generation Catalyst by Thermochemical Splitting of Water

Ce0.67Cr0.33O2.11 was synthesized by hydrothermal method using diethylenetriamine as complexing agent (Chem. Mater. 2008, 20, 7268). Ce0.67Cr0.33O2.11 being the only compound likes UO2+delta to have excess oxygen, it releases a large proportion of its lattice oxygen (0.167 M [O]/mole of compound) at relatively low temperature (465 degrees C) directly and it has been utilized for generation of H-2 by thermo-splitting of water. An almost stoichiometric amount of H-2 (0.152 M/Mole of compound) is generated at much lower temperature (65 degrees C). There is an almost comparable amount of oxygen release and hydrogen generation over this material at very low temperature comparedto other CeO2-MOx (Mn, Fe, Cu, and Ni) mixed-oxide solid solutions (O-2 evolution >= 1300 degrees C and H-2 generation at 1000 degrees C). The reversible nature of oxygen release and intake of this material is attributed to its fluorite Structure and coupling between the Ce4+/Ce3+ and Cr4+/6+/Cr3+ redox couples. Compound shows reversible oxygen release and intake by H2O absorption and subsequent hydrogen release to gain parent structure and hence this material can be utilized for generation of H-2 at very low temperature by thermo-chemical splitting of water.

A novel sheet 4f-3d mixed-metal pyridine dicarboxylate: synthesis, structure, photophysical properties and its transformation to a perovskite oxide

The synthesis, characterization and photophysical properties of a 4f-3d mixed metal compound, Gd(H2O)(3)Co[C5N1H3-(COO)(2)](3), are described; the structure is unique, consisting of sheets with large pores ( ca. 7 angstrom diameter) in the sheets and transforms to a perovskite oxide at moderate temperatures.

Fe-57 Mössbauer and Mo K-EXAFS Investigations of MoxFe3-xO4, an Interesting Mixed-Valent Oxide System

Ferrites of the formula MoxFe3-xO4, prepared by a soft-chemistry route, show mixed valence states of both iron and molybdenum cations. Mössbauer studies show that Fe2+ and Fe3+ ions are present on both the A and B sites, giving Fe an average oxidation state between 2+ and 3+. Molybdenum is present in the 3+ and the 4+ states on the B sites. The presence of Mo in the 3+ state has been established by determining the Mo3+-O distance (2.2 Å), for the first time, by Mo K-EXAFS. The mixed valence of Fe on both the A and B sites and of Mo on the B sites is responsible for the fast electron transfer between the cations. All the Mössbauer parameters including the line width show a marked change at a composition (x ? 0.3) above which the concentration of Fe2+A increases rapidly.

Electron spin resonance studies of d5 ions (Fe3+ and Mn2+) in lead oxide-lead halide glasses

Electron spin resonance (ESR) of d5 ions (Fe3+ and Mn2+) has been investigated in PbO---PbF2 and PbO---PbCl2 glasses in wide ranges of composition. ESR spectra of d5 ions in these glasses exhibit significant differences which we have attributed to at least three important causes: (i) The ionic potentials of Fe3+ and Mn2+ are different. Hence Fe3+ ions tend to acquire their own environment while Mn2+ ions take up substitutional (Pb2+ ion) positions. (ii) The sizes and nephelauxetic behaviours of O2- and F- ions are similar. Thus even when there is a mixed anionic coordination, the environment of Mn2+ ions is highly symmetrical in oxyfluoride glasses. The Mn2+ spectra in oxychloride glasses are considerably different. (iii) Increase in halide ion concentration increases the ionicity of lead-ligand bonding and favours a more symmetrical environment around dopant ions in halide-rich glasses. The features in ESR spectra have been interpreted in the light of known behaviour of d5 ions in glasses and also in the context of known structural features of PbO---PbX2 glasses. Dopant ions appear to cluster at high concentrations although isolated low-symmetry sites are still observed. Effects of crystallization and annealing upon ESR spectra have also been investigated.

Solid-state chemistry of high-temperature oxide superconductors:The experimental situation

High-temperature superconductivity in oxides of the type(La, Ln)2?xBax(Sr)xCuO4, Y(Ln)Ba2Cu3O7??, La3?xBa3+xCu6O14, and related systems is discussed with emphasis on aspects related to experimental solid-state chemistry. All of these oxides possess perovskite-related structures. Oxygen-excess and La-deficient La2CuO4 also exhibit superconductivity in the 20�40 K just as La2?xBax(Srx)CuO4; these oxides are orthorhombic in the superconductivity phase. The crucial role of oxygen stoichiometry in the superconductivity ofYBa2Cu3O7?? (Tc = 95 ± 5K) is examined; this oxide remains orthorhombic up to ? ? 0.6 and becomes tetragonal and nonsuperconducting beyond this value of ?. Oxygen stoichiometry in this and related oxides has to be understood in terms of structure and disorder. The structure of La3?xBa3+xCu6O14 is related to that of YBa2Cu3O7, the orthorhombic structure manifesting itself when the population of O1 oxygens (along the Cusingle bondOsingle bondCu chains) is preponderant compared to that of O5 oxygens (along thea-axis); nearly equal populations of O1 and O5 sites give rise to the tetragonal structure. A transition from a high-Tc (95 K) superconductivity regime to a low-Tc (not, vert, similar60 K) regime occurs in YBa2Cu3O7?? accompanying a change in ?. There is no evidence for Cu3+ in these nominally mixed valent copper oxides. Instead, holes are present on oxygens giving rise to O? or O2?2 species, the concentration of these species increasing with the lowering of temperature. Certain interesting aspects of the superconducting oxides such as domain or twin boundaries, Raman spectra, microwave absorption, and anomalous high-temperature resistivity drops are presented along with the important material parameters. Preparative aspects of the superconducting oxides are briefly discussed. Phase transitions seem to occur atTc as well as at not, vert, similar240 K in YBa2Cu3O7.

Photoluminescence study of mixed doped Ge-Se-In-Bi glasses

Photoluminescence studies, carried out using the Fourier Transform method rather than the conventional monochromator-dispersion method,are reported on glassy samples of indium-bismuth mixed doped Ge (10) Se(90-x-y) In (x) Bi (y) system (x,y = 5,10). The amorphous Bi2Se3 is found to be n-type like the crystalline counterpart. The possible contributions from microscopic cluster-level phase separation of Bi2Se3 and from the defects to the change in conductivity from p- to n- typein this system is discussed. The similar situation in related systems is also pointed out.

Platinum Ion-Doped TiO2: High Catalytic Activity of Pt2+ with Oxide Ion Vacancy in Ti1-x4+Ptx2+O2-x Compared to Pt4+ without Oxide Ion Vacancy in Ti1-x4+Ptx4+O2

Ti0.97Pt0.032+O1.97 and Ti0.97Pt0.034+O2 have been synthesized by a solution combustion method using alanine and glycine as the fuels, respectively. Both crystallize in anatase TiO2 structure with 15 nm average crystallite size. X-ray photoelectron spectroscopy (XPS) confirmed Pt ions are in the 2+ state in Ti0.97Pt0.03O1.97 (alanine) and 4+ state in Ti0.97Pt0.03O2 (glycine). The rate of CO oxidation occurring over Ti0.97Pt0.032+O1.97 (0.76 mu mol.g(-1).s(-1)) is similar to 10, times more than that over Ti0.97Pt0.034+O2 at 60 degrees C (0.08 mu mol.g(-1).s(-1)). A large shift in 100% hydrocarbons conversion to lower temperature was observed for Pt2+ ion-substituted TiO2 relative 10 that for Pt4+ ion-substituted TiO2. After reoxidation of the reduced compound by H-2 as well as CO, Pt ions are stabilized in mixed valences, 2+ and 4+ states. The role of oxide ion vacancy has been demonstrated by CO oxidation and H-2 + O-2 recombination reactions in the presence and absence of O-2. We analyze the activated lattice oxygens upon substitution of Pt2+ and Pt4+ ions in TiO2, using first-principles density functional theory (DFT) calculations with supercells of Ti31Pt1O63, Ti30Pt2O62, and Ti29Pt3O61 for Pt2+ ion substitution and Ti31Pt1O64, Ti30Pt2O62, and Ti29Pt3O61 for Pt4+ ion substitution in TiO2. We find that the local structure of Pt2+ ion has a distorted square planar geometry and that of Pt4+ ion has an octahedral geometry similar to that of Ti4+ ion in pure TiO2. The change in coordination of Pt2+ ion gives rise to weakly bonded oxygens, and these oxygens are involved in high rates of catalytic reaction. Thus, the high catalytic activity results from synergistic roles of Pt2+ ion and oxide ion vacancy and weakly bonded lattice oxygen.

Epitaxial Co metal thin film grown by pulsed laser deposition using oxide target

We report here the growth of epitaxial Co metal thin film on c-plane sapphire by pulsed laser deposition (RD) using Co:ZnO target utilizing the composition inhomogeneity of the corresponding plasma. Two distinct plasma composition regions have been observed using heavily alloyed Co0.6Zn0.4O target. The central and intense region of the plasma grows Co:ZnO film; the extreme tail grows only Co metal with no trace of either ZnO or Co oxide In between the two extremes, mixed phases (Co +Co-oxides +Co:ZnO) were observed. The Co metal thin film grown in this way shows room temperature ferromagnetism with large in plane magnetization similar to 1288 emu cm(-3) and a coerciviLy of similar to 230 Oe with applied field parallel to the film-substrate interface. Carrier density of the film is similar to 10(22) cm(-3). The film is epiLaxial single phase Co metal which is confirmed by both X-ray diffraction and transmission electron microscopy characierizaLions. Planar Hall Effect (PHE) and Magneto Optic Kerr Effect (MOKE) measurements confirm that the film possesses similar attributes of Co metal. The result shows that the epiLaxial Co metal thin film can be grown from its oxides in the PLD. (C) 2014 Elsevier B.V. All rights reserved.

Highly efficient WO3-ZnO mixed oxides for photocatalysis

Monoclinic nanocuboid WO3 enhanced the photocatalyst efficiency of quasi nanobelt zinc oxide for dye degradation in the presence of visible light radiation. Combustion synthesized ZnO resulted in a belt-like morphology through in situ cluster formation of near spherical particles but homogenously disperses and strongly adheres to nanocuboid WO3 during physical mixing. Cationic methylene blue (MB) and anionic orange G (OG) undergo degradation through a charge transfer mechanism in the presence of WO3-ZnO (1 : 9 weight percentage ratio) mixture. The photocatalytic reaction was enhanced due to the reduction in the recombination of photogenerated electron-holes. The high degree of 90% degradation of both dyes is due to the activity of the mixed oxides, which is much higher than that obtained either with WO3 or ZnO individually.

Highly efficient WO3-ZnO mixed oxides for photocatalysis

Monoclinic nanocuboid WO3 enhanced the photocatalyst efficiency of quasi nanobelt zinc oxide for dye degradation in the presence of visible light radiation. Combustion synthesized ZnO resulted in a belt-like morphology through in situ cluster formation of near spherical particles but homogenously disperses and strongly adheres to nanocuboid WO3 during physical mixing. Cationic methylene blue (MB) and anionic orange G (OG) undergo degradation through a charge transfer mechanism in the presence of WO3-ZnO (1 : 9 weight percentage ratio) mixture. The photocatalytic reaction was enhanced due to the reduction in the recombination of photogenerated electron-holes. The high degree of 90% degradation of both dyes is due to the activity of the mixed oxides, which is much higher than that obtained either with WO3 or ZnO individually.

A unique strategy towards high dielectric constant and low loss with multiwall carbon nanotubes anchored onto graphene oxide sheets

Multiwall carbon nanotubes (MWNTs) were anchored onto graphene oxide sheets (GOs) via diazonium and C-C coupling reactions and characterized by spectroscopic and electron microscopic techniques. The thus synthesized MWNT-GO hybrid was then melt mixed with 50/50 polyamide6-maleic anhydride-modified acrylonitrile-butadiene-styrene (PA6-mABS) blend to design materials with high dielectric constant (30) and low dielectric loss. The phase morphology was studied by SEM and it was observed that the MWNT-GO hybrid was selectively localized in the PA6 phase of the blend. The 30 scales with the concentration of MWNT-GO in the blends, which interestingly showed a very low dielectric loss (< 0.2) making them potential candidate for capacitors. In addition, the dynamic storage modulus scales with the fraction of MWNT-GO in the blends, demonstrating their reinforcing capability as well.

Porous membranes designed from bi-phasic polymeric blends containing silver decorated reduced graphene oxide synthesized via a facile one-pot approach

In this work, porous membranes were designed by selectively etching the PEO phase, by water, from a melt-mixed PE/PEO blend. The pure water flux and the resistance across the membrane were systematically evaluated by employing an indigenously developed cross flow membrane setup. Both the phase morphology and the cross sectional morphology of the membranes was assessed by scanning electron microscopy and an attempt was made to correlate the observed morphology with the membrane performance. In order to design antibacterial membranes for water purification, partially reduced graphene oxide (rGO), silver nanoparticles (Ag) and silver nanoparticles decorated with rGO (rGO-Ag) were synthesized and incorporated directly into the blends during melt mixing. The loss of viability of bacterial cells was determined by the colony counting method using E. coli as a model bacterium. SEM images display that the direct contact with the rGO-Ag nanoparticles disrupts the cell membrane. In addition, the rGO-Ag nanoparticles exhibited a synergistic effect with respect to bacterial cell viability in comparison to both rGO and Ag nanoparticles. The possible mechanism associated with the antibacterial activity in the membranes was discussed. This study opens new avenues in designing antibacterial membranes for water purification.

Unimpeded permeation of water through biocidal graphene oxide sheets anchored on to 3D porous polyolefinic membranes

3D porous membranes were developed by etching one of the phases (here PEO, polyethylene oxide) from melt-mixed PE/PEO binary blends. Herein, we have systematically discussed the development of these membranes using X-ray micro-computed tomography. The 3D tomograms of the extruded strands and hot-pressed samples revealed a clear picture as to how the morphology develops and coarsens over a function of time during post-processing operations like compression molding. The coarsening of PE/PEO blends was traced using X-ray micro-computed tomography and scanning electron microscopy (SEM) of annealed blends at different times. It is now understood from X-ray micro-computed tomography that by the addition of a compatibilizer (here lightly maleated PE), a stable morphology can be visualized in 3D. In order to anchor biocidal graphene oxide sheets onto these 3D porous membranes, the PE membranes were chemically modified with acid/ethylene diamine treatment to anchor the GO sheets which were further confirmed by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and surface Raman mapping. The transport properties through the membrane clearly reveal unimpeded permeation of water which suggests that anchoring GO on to the membranes does not clog the pores. Antibacterial studies through the direct contact of bacteria with GO anchored PE membranes resulted in 99% of bacterial inactivation. The possible bacterial inactivation through physical disruption of the bacterial cell wall and/or reactive oxygen species (ROS) is discussed herein. Thus this study opens new avenues in designing polyolefin based antibacterial 3D porous membranes for water purification.