An investigation of structural, magnetic and dielectric properties of R2NiMnO6 (R = rare earth, Y)

We have investigated the structure, magnetic and dielectric properties of the double perovskite oxides, R2NiMnO6 (R = Pr, Nd, Sm, Gd, Tb, Dy, Ho and Y). We could refine powder X-ray diffraction patterns of all the phases on the basis of monoclinic (P2(1)/n) double perovskite structure where Ni and Mn atoms are ordered at 2c and 2d sites, respectively. All the phases are ferromagnetic insulators exhibiting relatively low dielectric loss and dielectric constants in the range 15-25. The ferromagnetic ordering temperature of the R2NiMnO6 series seems to correlate better with the radius of R3+ atoms than with the average Ni-O-Mn angle (phi) in the double perovskite structure. These results are consistent with all samples having Mn4+ and Ni2+ With minimal antisite disorder.

Energetics of rare earth manganese perovskites A1-xA ' xMnO3 (A = La, Nd, Y and A ' = Sr, La) systems

High temperature reaction calorimetry using molten lead berate as solvent has been used to study the thermochemistry of NdMnO3, YMnO3, La1-xSrxMnO3 (with 0 < x < 0.5), and Ln(0.5)Ca(0.5)MnO(3) (with Ln = La, Nd, Y), The enthalpies of formation of these multicomponent oxides from their binary constituents have been calculated from the measured enthalpy of drop solution, The energetic stability of the perovskite depends on the size of the A cation, The enthalpy of formation of YMnO3 (smallest A cation) is more endothermic than those of NdMnO3 and LaMnO3. The energetics of the perovskite also depends on the oxidation state of the B site's ions. In the La1-xSrxMnO3 system, the energetic stability of the structure increases with the Mn4+/Mn3+ ratio, The new values of the enthalpies of oxidations, with reliable standard entropies, were used to plot the phase stability diagram of the lanthanum-manganese-oxygen system in the temperature range 300-1100 K, The LaMnO3/MnO phase boundary evaluated in this study agrees with the one published by Atsumi et nl. calculated from thermogravimetric and conductivity measurements.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

High-temperature superconductivity in the 100 K region in perovskite-related oxides of the Ln-Ba-Cu-O (Ln=Y or La) system

Oxides of the Y-Ba-Cu-O system are found to show onset of superconductivity in the 100–120 K region.