Use of Composition-Graded Bi-Electrolyte Cells for Thermodynamic Studies on Lanthanum Aluminates

Innovative bi-electrolyte solid-state cells incorporating single crystal CaF2 and composition-graded solid electrolyte (LaF3) y (CaF2) 1-y (y = 0 to 0.32) were used for measurement of the standard Gibbs energy of formation of hexagonal La0.885Al11.782O19 and cubic LaAlO3 from component binary oxides La2O3 and alpha-Al2O3 in the temperature range from 875 to 1175 K. The cells were designed based on experimentally verified relevant phase relations in the systems La2O3-Al2O3LaF3 and CaF2-LaF3. The results can be summarized as: 5.891 alpha-Al2O3 + 0.4425 La2O3 (A-rare earth)-> La0.885Al11.782O19 (hex), Delta G(f(ox))(degrees)(+/- 2005)/Jmol(-1) = -80982 + 7.313(T/K); 1/2 La2O3 (A-rare earth) + 1/2 a-Al2O3 -> LaAlO3 (cubic), Delta G(f(ox))(degrees)(+/- 2100)/Jmol(-1) = -59810 + 4.51(T/K). Electron probe microanalysis was used to ascertain the non-stoichiometric range of the hexaaluminate phase. The results are critically analyzed in the light of earlier electrochemical measurements. Several imperfections in the electrochemical cells used by former investigators are identified. Data obtained in the study for LaAlO3 are consistent with calorimetric enthalpy of formation and entropy derived from heat capacity data. Estimated are the standard entropy and the standard enthalpy of formation from elements of hexagonal La0.885Al11.782O19 and rhombohedral LaAlO3 at 298.15 K. c 2014 The Electrochemical Society. All rights reserved.

Influence of lanthanum doping on the dielectric, ferroelectric and relaxor behaviour of barium bismuth titanate ceramics

Barium lanthanum bismuth titanate (Ba1−(3/2)xLaxBi4Ti4O15, x = 0–0.4) ceramics were fabricated using the powders synthesized via the solid-state reaction route. X-ray powder diffraction analysis confirmed the above compositions to be monophasic and belonged to the m = 4 member of the Aurivillius family of oxides. The effect of the partial presence of La3+ on Ba2+ sites on the microstructure, dielectric and relaxor behaviour of BaBi4Ti4O15 (BBT) ceramics was investigated. For the compositions pertaining to x ≤ 0.1, the dielectric constant at both room temperature and in the vicinity of the temperature of the dielectric maximum (Tm) of the parent phase (BBT) increased significantly with an increase in x while Tm remained almost constant. Tm shifted towards lower temperatures accompanied by a decrease in the magnitude of the dielectric maximum (εm) with an increase in the lanthanum content (0.1 < x ≤ 0.4). The dielectric relaxation was modelled using the Vogel–Fulcher relation and a decrease in the activation energy for frequency dispersion with increasing x was observed. The frequency dispersion of Tm was found to decrease with an increase in lanthanum doping, and for compositions corresponding to x ≥ 0.3, Tm was frequency independent. Well-developed P(polarization)–E(electric field) hysteresis loops were observed at 150 °C for all the samples and the remanent polarization (2Pr) was improved from 6.3 µC cm−2 for pure BBT to 13.4 µC cm−2 for Ba0.7La0.2Bi4Ti4O15 ceramics. Dc conductivities and associated activation energies were evaluated using impedance spectroscopy.

Crystal and molecular structure of a dimethyl sulphoxide complex with lanthanum nitrate, La(NO3)3.4(CH3)2SO

Abstract is not available.

Lanthanum, praseodymium and neodymium chloroacetates

The monochloroacetates of lanthanum, praseodymium and neodymium of the composition M(ClCH2COO)3·2H2O have been prepared and characterised. The compounds behave as non-electrolytes in dimethylformamide. The infrared spectra are consistent with bidentate coordination of the carboxylate group and show the presence of two types of water molecules, coordinated, and free. With six oxygen atoms from the three acetato groups and one from the water bonded to the metal, a coordination number of seven has been assigned to the rare earths in these compounds. On pyrolysis, the chloroacetates lose water at ~130 °C and yield the oxychlorides at ~500 °C. The X-ray powder patterns of the chloroacetates have been indexed for the monoclinic system, with four molecules per unit cell.

Photocytotoxic Lanthanum(III) and Gadolinium(III) Complexes of Phenanthroline Bases Showing Light-Induced DNA Cleavage Activity

Lanthanide complexes of formulation [La(B)(2)(NO3)(3)] (1-3) and [Gd(B)(2)(NO3)(3)] (4-6), where B is a N,N-donor phenanthroline base, namely, 1,10-phenanthroline (phen in 1, 4),dipyrido[3,2-d2',3'-f]quinoxaline (dpq in 2,5) and dipyrido[3,2-a2',3'-c]phenazine (dppz in 3, 6), have been prepared, characterized from physicochemical data, and their photoinduced DNA and protein cleavage activity studied The photocytotoxicity of the dppz complexes 3 and 6 has been studied using HeLa cancer cells. The complexes exhibitligand centered bands in the UV region The dppz complexes show thelowest energy band at 380 nm in N,N-dimethylformamide (DMF) The La(III)complexes are diamagnetic. The Gd(III) complexes (4-6) have magneticmoments that correspond to seven unpaired electrons The complexes are1(.)1 electrolytic in aqueous DMF The dpq and dppz complexes in DMFshow ligand-based reductions. The complexes display moderate binding propensity to calf thymus DNA giving binding constant values in the range of 5.7 x 10(4)-5.8 x 10(5) M-1 with a relative order. 3, 6 (dppz)> 2, 5 (dpq) > 1, 4 (phen) The binding data suggest DNA surface and/or groove binding nature of the complexes. The complexes do not show any hydrolytic cleavage of plasmid supercoiled pUC19 DNA. The dpq and dppz complexes efficiently cleave SC DNA to its nicked circular form onexposure to UV-A light of 365 nm at nanomolar complex concentration. Mechanistic studies reveal the involvement of singlet oxygen (O-1(2)) and hydroxyl radical (HO center dot) as the cleavage active species.The complexes show binding propensity to bovine serum albumin (BSA)protein giving K-BSA values of similar to 10(5) M-1. The dppz complexes 3 and 6 show BSA protein cleavage activity in UV-A light of 365 nm The dppz complexes 3 and 6 exhibit significant photocytotoxicity in HeLa cells giving respective IC50 values of 341 nM and 573 nM in UV-A light of 365 nm for an exposure time of 15 min (IC50 > 100 mu M in dark for both the complexes) Control experiments show significant dark and phototoxicity of the dppz base alone (IC50 = 413 nM in light with 4 h incubation in dark and 116 mu M in dark with 24 h incubation). A significant decrease in the dark toxicity of the dppz base is observedon binding to the lanthanide ions while retaining similar phototoxicity.

Raman spectrum of lanthanum ethyl sulphate nonahydrate

Raman spectrum of a single crystal of lanthanum ethyl sulphate has been recorded for the first time using the λ 2537 radiation Forty-one lines have been identified out of which eight belong to the lattice oscillations, seven to the internal vibrations of the water molecule and the remaining twenty-six to the internal vibrations of the ethyl sulphate group. The Raman spectrum of ethyl sulphate (liquid) has also been recorded using the λ 4358 excitation and is compared with the spectrum of lanthanum ethyl sulphate. Thirty Raman lines could be identified in the spectrum of ethyl sulphate, of which fourteen are recorded for the first time. Probable assignments of the observed frequencies are also given. The sulphate group is found to have O-SO3 structure in lanthanum ethyl sulphate, while it has a co-ordination {Mathematical expression} in ethyl sulphate.

Crystal And Molecular Structure Of A Dimethyl Sulphoxide Complex With Lanthanum Nitrate, La(No3)34.(Ch3)2so

The crystal structure of the complex La(NO3)3.4(CH3)2SO has been solved by the heavy-atom method. The complex crystallizes in the monoclinic space group C2/e with four formula units in a unit cell of dimensions a= 14.94, b= 11.04, c= 15.54 A and fl= 109 ° 10'. The parameters have been refined by threedimensional least-squares procedures with anisotropic thermal parameters for all atoms except hydrogen. The final R index for 1257 observed reflexions is 0.094. The La 3 + ion is coordinated by ten oxygen atoms with La-O distances varying from 2.47 to 2.71 A. The geometry of the coordination polyhedron is described.

Rare-earth chromium citrates as precursors for rare-earth chromites: lanthanum biscitrato chromium(III) dihydrate, La[Cr(C6H5O7)2]·2H

The thermal decomposition of lanthanum biscitrato chromium(III) dihydrate has been studied in static air and dynamic argon atmospheres. The complex decomposes in four steps: dehydration, decomposition of the citrate to an intermediate oxycarbonate, formation of LaCrO4(V) from oxycarbonate, and finally decomposition of LaCrO4(V) to LaCrO3. Formation of LaCrCrO4(V) requires the presence of oxygen The decomposition behaviour of a mechanical mixture of lanthanum citrate hydrate and chromium citrate hydrate was compared with that of the citrato complex. Both the starting material and the intermediates were characterized by X-ray diffraction, IR electronic and ESR spectroscopy, surface area and magnetic susceptibility measurements, as well as by chemical analysis. A scheme is proposed for the decomposition of lanthanum biscitrato chromium(III) dihydrate in air. LaCrO3 can be obtained at temperatures as low as 875 K by isothermal decomposition of the complex.

Elusive superconductivity in polycrystalline samples of layered lanthanum nickelates

La2-xNiO4, La2-xSrxNiO4 and related layered nickelates have been investigated for possible presence of superconductivity. While there is clear onset of diamagnetism around 20 K in many of these nickelates, we do not, however, find any anomaly in the electrical resistivity, magnetoresistance or thermopower around 20 K. High energy spectroscopic studies show Ni to be in the 2+ oxidation state accompanied by a substantial proportion of oxygen holes.

Low-temperature polymer precursor-based synthesis of nanocrystalline particles of lanthanum calcium manganese oxide (La0.67Ca0.33MnO3) with enhanced ferromagnetic transition temperature

We report a simple modified polymeric precursor route for the synthesis of highly crystalline and homogenous nanoparticles of lanthanum calcium manganese oxide (LCMO). The LCMO phase formation was studied by thermal analysis, x-ray powder diffraction, and infrared spectroscopy at different stages of heating. These nanocrystallites (average particle size of 30 nm) possess ferromagnetic-paramagnetic transition temperature (T-c) of 300 K, nearly 50 K higher than that of a single crystal. The Rietveld analysis of the powder x-ray diffraction data of the nanopowders reveals significant lattice contraction and reduction in unit cell anisotropy-these structural changes are correlated to the enhancement in T-c.

Thermal expansion of doped lanthanum gallates

Thermal expansion of several compositions of Sr and Mg-doped LaGaO3 including an A-site deficient composition (La0.9Sr0.1)(0.98)(Ga0.8Mg0.2)O-2.821 were measured in the temperature range from 298 to 1273 K. The effect of doping on thermal expansion was studied by varying the composition at one site of the perovskite structure (either A or B), while keeping the composition at the other site invariant. Thermal expansion varied nonlinearly with temperature and exhibited an inflexion between 550 and 620 K, probably related to the change in crystal structure from orthorhombic to rhombohedral. The dependence of average thermal expansion coefficient (alpha (av)) on the dopant concentration on either A or B site of the perovskite structure was found to be linear, when the composition at the other site was kept constant. Mg doping on the B-site had a greater effect on the average thermal expansion coefficient than Sr doping on the A-site. Cation deficiency at the A-site decreases thermal expansion when compositions at both sites are held constant.

A new perovskite series based on lanthanum chromite [LaCr1−xMxO3−δ]

A new series of substituted perovskites of the type LaCr1−xMxO3−δ, where M=Cu or Mg have been synthesised by the citrate gel process and characterized by means of powder X-ray diffraction, infrared spectroscopy, selected area diffraction and also by electron paramagnetic resonance spectroscopy. The general powder morphology was also observed using scanning electron microscopy. 40 mole percent substitution of Cr3+ by Cu2+ or Mg2+ have shown to result in single phase perovskite structure. Beyond x=0.5, a new phase has been identified in a narrow compositional range. Effect of Cu and Mg substitution on the sinterability of pure LaCrO3 has also been studied. It is possible to get near theoretically dense materials at a temperature as low as 1200°C in air by copper substitution.