Structure and magnetotransport properties of the layered manganites REl.2Srl.8Mn,07(R E = La, Pr, Nd)

We have examined the magnetotransport properties and the structure, by Rietveld refinement of powder X-ray data, of the phases RE(1.2)Sr(1.8)Mn(2)O(7) (RE = La, Pr, Nd). We find that on cooling, La1.2Sr1.8Mn2O7 undergoes a transition to a nearly perfect ferromagnet with 90% magnetization at 1.45 T, as reported by earlier workers, but the Pr and Nd phases show only a small magnetization that grows gradually as the temperature is decreased. There seems to be significant correlation between electrical transport and the Jahn-Teller elongation of the apical Mn-O bonds in these systems. The elongation of the apical Mn-O bonds forces the nine-coordinate rock-salt site to be occupied preferentially by the smaller rare-earth-metal cations. This preferential occupation is reliably obtained from the X-ray refinement. All three title phases show a magnetoresistance ratio of about 4(corresponding to a magnetoresistance, [R(0)-R(H)]/R(0), of about 75%) at a field of 7 T and temperatures around 100 K.

Magnetization and magnetoresistive response of LiMn2O4 near the charge ordering transition

We report magnetization and magnetoresistance studies of the geometrically frustrated spinel compound LiMn2O4 near its charge ordering temperature. The effect of a 7 T magnetic field is to very slightly shift the transition in the resistivity to lower temperatures resulting in large negative magnetoresistance with significant hysteresis. This hysteresis is not reflected in the magnetization. These observations are compared with what is found in the colossal magnetoresistance and charge ordering perovskite manganese oxides. The manner in which geometric frustration influences the coupling of charge and spin degrees of freedom is examined.

Mo3O5(OH)(2)(AsO4)2: A new solid with a structure related to beta VOPO4

Mo3O5(OH)(2)(AsO4)(2) was prepared at 100 degrees C from an aqueous solution of MoO3 containing arsenic and nitric acids. It crystallises in the monoclinic system, a = 13.024(1)Angstrom, b = 7.2974 (2) Angstrom, c = 13.281(1) Angstrom, beta = 121.124(8)degrees, Z = 4, space group C2/c. The structure was determined by Rietveld refinement from X-ray powder diffraction data. The three-dimensional structure is built up from MoO6 and MoO5OH octahedra and AsO4 tetrahedra sharing corners. The octahedra share two opposite vertices forming zigzag chains that run parallel to [10(1) over bar]. Each AsO4 tetrahedron is connected to four octahedra, two of which belong to the same chain, thus linking three chains. The resulting covalent framework is similar to that of beta VOPO4 in which one tetrahedral P site for every three is empty. The two protons are likely to be bonded to two (out of four) unshared oxygen atoms surrounding this empty site. All the Mo atoms are strongly off-centred in the octahedra; and the off-centring is disordered. The disorder is discussed in terms of Mo shifts perturbed by a disordered hydrogen bonding scheme.