Inter molecular azide-diisocyanate coupling: new insights for energetic solid propellants

Hydroxyl terminated azide binders can undergo a spurious reaction with diisocyanates to form tetrazoline-5-one via an inter molecular 1,3-dipolar cycloaddition reaction apart from urethane/allophanate groups which has been overlooked. This has serious implications on solid propellants. The computed activation barrier using density functional theory (DFT) for urethane formation reaction is 28.4 kJ mol(-1) and that for tetrazoline-5-one formation reaction is 108.0 kJ mol(-1). DFT studies reveal that the rate limiting step of the reaction is 1,3-dipolar cycloaddition between azide and isocyanate. A dual cure was observed in the temperature ranges 42-77 degrees C and 78-146 degrees C by differential scanning calorimetry (DSC) and rheological studies, confirming multiple reactions. Tetrazoline-5-one formation was confirmed by Fourier transform infrared spectroscopy (FTIR) and solid state nuclear magnetic resonance spectroscopy (NMR).

Site-Specific Functionalization of Hyperbranched Polymers Using ``Click'' Chemistry

Different strategies for functionalization of the core region and periphery of core-shell type hyperbranched polymers (HBP) using the ``click'' reaction have been explored. For achieving periphera functionalization, an AB(2) + A-R-1 + A-R-2 type copolymerization approach was used, where A-R-1 is heptaethylene glycol monomethyl ether (HPEG-M) and A-R-2 is tetraethylene glycol monopropargyl ether (TEG-P). A very small mole fraction of the propargyl containing monomer, TEG-P, was used to ensure that the water-solubility of the hyperbranched polymer is minimally affected. Similarly, to incorporate propargyl groups in the core region, a new propargyl group bearing B-2-typ monomer was designed and utilized in an AB(2) + A(2) + B-2 + A-R-1 type copolymerization, such that the total mole fraction of B-2 + A(2) is small and their mole-ratio is 1: 1. Further, using a combination of both the above approaches, namely AB(2) + A(2) + B-2 + A-R-1 + A-R-2, hyperbranched structures that incorporate propargyl groups both at theperiphery and within the core were synthesized. Since the AB(2) monomer carries a hexamethylene spacer (C-6) and the periphery is PEGylated all the derivatized polymers form core-shell type structures in aqueous solutions. Attempts were made to ascertain and probe the location of the propargyl groups in these HBP's, by ``clicking'' azidomethylpyrene, onto them. However, the fluorescence spectra of aqueous solutions of the pyrene derivatized polymers were unable to discriminate between the various locations, possibly because the relatively hydrophobic pyrene units insert themselves into the core region to minimize exposure to water.

Chemical toughening of epoxies. I. Structural modification of epoxy resins by reaction with hydroxy-terminated poly (butadiene-co-acrylonitrile)

In an attempt to toughen the epoxy resin matrix for fiber-reinforced composite applications, a chemical modification procedure of a commercially available bisphenol-A-based epoxy resin using reactive liquid rubber HTBN [hydroxy-terminated poly(butadiene-co-acrylonitrile)] and TDI (tolylene diisocyanate) is described. The progress of the reaction and the structural changes during modification process are studied using IR spectroscopy, viscosity data, and chemical analysis (epoxy value determination). The studies support the proposition that TDI acts as a coupling agent between the epoxy and HTBN, forming a urethane linkage with the former and an oxazolidone ring with the latter. The chemical reactions that possibly take place during the modification are discussed.

Chemical toughening of epoxies. I. Structural modification of epoxy resins by reaction with hydroxy-terminated poly(butadiene-co-acrylonitrile)

In an attempt to toughen the epoxy resin matrix for fiber-reinforced composite applications, a chemical modification procedure of a commercially available bisphenol-A-based epoxy resin using reactive liquid rubber HTBN [hydroxy-terminated poly(butadiene-co-acrylonitrile)] and TDI (tolylene diisocyanate) is described. The progress of the reaction and the structural changes during modification process are studied using IR spectroscopy, viscosity data, and chemical analysis (epoxy value determination). The studies support the proposition that TDI acts as a coupling agent between the epoxy and HTBN, forming a urethane linkage with the former and an oxazolidone ring with the latter. The chemical reactions that possibly take place during the modification are discussed.

Synthesis and characterization of carbon-covered alumina (CCA) supported TiO2 nanocatalysts with enhanced visible light photodegradation of Rhodamine B

The anatase phase of titania (TiO2) nano-photocatalysts was prepared using a modified sol gel process and thereafter embedded on carbon-covered alumina supports. The carbon-covered alumina (CCA) supports were prepared via the adsorption of toluene 2,4-diisocyanate (TDI) on the surface of the alumina. TDI was used as the carbon source for the first time for the carbon-covered alumina support system. The adsorption of TDI on alumina is irreversible; hence, the resulting organic moiety can undergo pyrolysis at high temperatures resulting in the formation of a carbon coating on the surface of the alumina. The TiO2 catalysts were impregnated on the CCA supports. X-ray diffraction analysis indicated that the carbon deposited on the alumina was not crystalline and also showed the successful impregnation of TiO2 on the CCA supports. In the Raman spectra, it could be deduced that the carbon was rather a conjugated olefinic or polycyclic hydrocarbons which can be considered as molecular units of a graphitic plane. The Raman analysis of the catalysed CCAs showed the presence of both the anatase titania and D and G band associated with the carbon of the CCAs. The scanning electron microscope micrographs indicated that the alumina was coated by a carbon layer and the energy dispersive X-ray spectra showed the presence of Al, O and C in the CCA samples, with the addition of Ti for the catalyst impregnated supports. The Brunauer Emmet and Teller surface area analysis showed that the incorporating of carbon on the alumina surface resulted in an increase in surface area, while the impregnation with TiO2 resulted in a further increase in surface area. However, a decrease in the pore volume and diameter was observed. The photocatalytic activity of the nanocatalysts was studied for the degradation of Rhodamine B dye. The CCA-TiO2 nanocatalysts were found to be more photocatalytically active under both visible and UV light irradiation compared to the free TIO2 nanocatalysts.

Modification of crosslinked chitosan membrane using NaY zeolite for pervaporation separation of water-isopropanol mixtures

The blocked diisocyanate crosslinked chitosan membrane was modified by incorporating different mass% of NaY zeolite. The physico-chemical properties of resulting composite membranes were studied using Fourier transform infrared spectroscopy (FTIR), wide-angle X-ray diffraction (WAXD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The mechanical properties of the membranes were studied using universal testing machine (UTM). After measuring the equilibrium swelling, membranes were subjected to pervaporation for separation of water-isopropanol mixtures. Both flux and selectivity were increased with increasing NaY zeolite content in the membranes. The membrane containing 40 mass% of NaY zeolite exhibited the highest separation selectivity of 11,241 with a flux of 11.37 x 10(-2) kg/m(2) h for 10 mass% of water in the feed. The total flux and flux of water are almost overlapping each other, suggesting that these membranes could be effectively used to break the azeotropic point of water-isopropanol mixture. From the temperature dependent diffusion and permeation values, the Arrhenius activation parameters were estimated. All the composite membranes exhibited lower activation energy compared to crosslinked membrane, indicating that the permeants require less energy during the process because of molecular sieving action attributed to the presence of sodalite and super cages in the framework of Nay zeolite. The Henry's mode of sorption dominates the process, giving an endothermic contribution. (C) 2014 The Institution of Chemical Engineers. Published by Elsevier B.V. All rights reserved.