Reversible and irreversible switching processes in pure and lanthanum modified lead zirconate thin films

The mechanism of field induced phase switching in antiferroelectric lead zirconate and La-modified lead zirconate thin films has been analysed in terms of reversible and irreversible switching process under weak fields as a function of donor concentration. Extension of Rayleigh law of ferromagnetic materials to the present antiferroelectric and modified antiferroelectric compositions have clearly showed that origin of small signal dielectric permittivity is due to reversible domain wall motion. Rayleigh's constant, a measure of irreversible switching process, exhibited a slight increase with lower La3+ concentrations and followed by a gradual fall for higher concentration. This clearly illustrates that donor addition to antiferroelectric thin films controls the domain switching even under weak fields. (C) 2002 Elsevier Science B.V. All rights reserved.

Synthesis, structural and ferromagnetic properties of La1-xKxMnO3 (0.0 <= x <= 0.25) phases by solution combustion method

We describe the solution combustion synthesis and characterization of La1-xKxMnO3 (0.0 <= x <= 0.25) perovskite phases, which is a low temperature initiated, rapid route to prepare metal oxides. As-synthesized compounds are amorphous in nature; crystallinity was observed on heating at 800 degrees C for 5 min. Structural parameters were determined by the Rietveld refinement method using powder XRD data. Parent LaMnO3 compound crystallizes in the orthorhombic structure (space group Pbnm, No. 62). Potassium substituted compounds were crystallized with rhombohedral symmetry (space group R-3c, No. 167). The ratio of the Mn3+/Mn4+ was determined by the iodometric titration. The Fourier transform infrared spectrum (FTIR) shows two absorption bands for Mn-O stretching vibration (v, mode), Mn-O-Mn deformation vibration (v(b) mode) around 600 cm(-1) and 400 cm(-1) for the compositions, x = 0.0, 0.05 and 0-10. Four-probe electrical resistivity measurements reveal a composition controlled metal to insulator transition (TM-1), the maximum TM-1 was observed for the composition La0.85K0.15MnO3 at 287 K. Room temperature vibrating sample magnetometer data indicate that for the composition up to x = 0-10, the compounds are paramagnetic whereas composition with x = 0.15, 0.20 and 0.25 show magnetic moments of 27, 29 and 30 emu/g, respectively.

Charge Ordering Induced Ferromagnetic Insulator: K2Cr8O16

Usually metallicity accompanies ferromagnetism. K2Cr8O16 is one of the less common examples of magnetic materials, exhibiting ferromagnetism in the insulating state. Analyzing the electronic and magnetic properties within first principles electronic structure calculations, we find that the doped electrons due to K induce a charge-ordered and insulating ground state and interestingly also introduce a ferromagnetic coupling between the Cr ions. The primary considerations driving the charge ordering are found to be electrostatic ones with the charge being localized on two Cr atoms that minimize the electrostatic energy. The structural distortion that accompanies the ordering gives rise to a rare example of a charge-order driven ferromagnetic insulator.

Low-temperature polymer precursor-based synthesis of nanocrystalline particles of lanthanum calcium manganese oxide (La0.67Ca0.33MnO3) with enhanced ferromagnetic transition temperature

We report a simple modified polymeric precursor route for the synthesis of highly crystalline and homogenous nanoparticles of lanthanum calcium manganese oxide (LCMO). The LCMO phase formation was studied by thermal analysis, x-ray powder diffraction, and infrared spectroscopy at different stages of heating. These nanocrystallites (average particle size of 30 nm) possess ferromagnetic-paramagnetic transition temperature (T-c) of 300 K, nearly 50 K higher than that of a single crystal. The Rietveld analysis of the powder x-ray diffraction data of the nanopowders reveals significant lattice contraction and reduction in unit cell anisotropy-these structural changes are correlated to the enhancement in T-c.

Rapid synthesis of room temperature ferromagnetic Ag-doped LaMnO3 perovskite phases by the solution combustion method

We report the rapid solution combustion synthesis and characterization of Ag-substituted LaMnO3 phases at relatively low temperature using oxalyl dihydrazide, as fuel. Structural parameters were refined by the Rietveld method using powder X-ray diffraction data. While the parent LaMnO3 crystallizes in the orthorhombic structure, the Ag-substituted compounds crystallize in the rhombohedral symmetry. On increasing Ag-content, unit cell volume and Mn-O-Mn bond angle decreases. The Fourier transform infra red spectrum shows two absorption bands corresponding to Mn-O stretching vibration (v(s) mode) and Mn-O-Mn deformation vibration (v(b) mode) around 600 cm(-1) and 400 cm(-1) for the compositions x = 0.0, 0.05 and 0.10, respectively. Electrical resistivity measurements reveal that composition-controlled metal to insulator transition, with the maximum metal to insulator being 280 K for the composition La0.75Ag0.25MnO3. Increase in magnetic moment was observed with increase in Ag-content. The maximum magnetic moment of 35 emu/g was observed for the composition La0.80Ag0.20MnO3. (C) 2010 Elsevier Ltd. All rights reserved.

Ferromagnetic La0.6Pb0.4MnO3 thin films with giant magnetoresistance at 300 K

Highly textured, as-deposited La0.6Pb0.4MnO3 thin films have been grown on LaAlO3 by pulsed laser deposition. The films are ferromagnetic metals below 300 K. Giant negative magnetoresistance of over 40% is observed at 300 K at 6 T.

A ferromagnetic resonance study of La1-xCaxMnO3

Ferromagnetic resonance spectra of La1-xCaxMnO3 powders (0.1 less than or equal to x 0.9) have been investigated over a range of temperatures. The spectra could be fitted to a sum of two Lorentzians for all the compositions. The intense line with a nearly constant g shows a linear decrease in linewidth with increase in temperature, while the weaker line with a variable g shows a maximum in linewidth in the T-c region. The latter is also associated with a g(eff) which depends on the composition. Copyright (C) 1996 Elsevier Science Ltd

A new class of magnetic materials: Sr2FeMoO6 and related compounds

Ordered double perovskite oxides of the general formula A2BB′O6 have been known for several decades to have interesting electronic and magnetic properties. However, a recent report of a spectacular negative magnetoresistance effect in a specific member of this family, namely Sr2FeMoO6, has brought this class of compounds under intense scrutiny. It is now believed that the origin of the magnetism in this class of compounds is based on a novel kinetically-driven mechanism. This new mechanism is also likely to be responsible for the unusually high temperature ferromagnetism in several other systems, such as dilute magnetic semiconductors, as well as in various half-metallic ferromagnetic systems, such as Heussler alloys.

Low temperature synthesis of ferromagnetic (LaK)MnO3 from KCl, KBr and KI fluxes

Potassium doped lanthanum manganites have been synthesized from KCl, KBr and KI fluxes at 900, 850 and 750 °C respectively. While all the flux-grown oxides are ferromagnetic metals (Tc=290–330 K), the oxides grown from KCl and KBr fluxes crystallize in the rhombohedral structure and that synthesized from KI flux adopts the cubic structure. The enhancement in Tc correlates with the increasing tendency of the flux to get oxidized and decreasing melting points of the flux. Nearly stoichiometric (LaK)MnO3 with 33 % of Mn4+ concentration could be prepared at temperature as low as 750 °C. Composition of all the phases have been obtained from the chemical analysis of the elements present.

Domain-wall creep driven by spin torque in nanoscale ferromagnetic cylinders

We have explored the mechanism of spin-torque-driven domain-wall (DW) depinning in cylindrical nanowires of nickel using noise in electrical resistance. We find that the spectral slope of noise is a sensitive probe to the DW kinetics that reveals a creeplike behavior of the DWs at the depinning threshold, and diffusive DW motion at higher spin-torque drive. Different regimes of DW kinetics were characterized by universal kinetic exponents.

Experimental evidence of Ga-vacancy induced room temperature ferromagnetic behavior in GaN films

We have grown Ga deficient GaN epitaxial films on (0001) sapphire substrate by plasma-assisted molecular beam epitaxy and report the experimental evidence of room temperature ferromagnetic behavior. The observed yellow emission peak in room temperature photoluminescence spectra and the peak positioning at 300 cm(-1) in Raman spectra confirms the existence of Ga vacancies. The x-ray photoelectron spectroscopic measurements further confirmed the formation of Ga vacancies; since the N/Ga is found to be >1. The ferromagnetism is believed to originate from the polarization of the unpaired 2p electrons of N surrounding the Ga vacancy. (C) 2011 American Institute of Physics. [doi:10.1063/1.3654151]

Ferromagnetic transition and specific heat of Pr(0.6)Sr(0.4)MnO(3)

The critical properties of orthorhombic Pr(0.6)Sr(0.4)MnO(3) single crystals were investigated by a series of static magnetization measurements along the three different crystallographic axes as well as by specific heat measurements. A careful range-of-fitting-analysis of the magnetization and susceptibility data obtained from the modified Arrott plots shows that Pr(0.6)Sr(0.4)MnO(3) has a very narrow critical regime. Nevertheless, the system belongs to the three-dimensional (3D) Heisenberg universality class with short-range exchange. The critical exponents obey Widom scaling and are in excellent agreement with the single scaling equation of state M(H,epsilon) = vertical bar epsilon vertical bar(beta) f(+/-)(H/vertical bar epsilon vertical bar((beta+gamma)); with f(+) for T > T(c) and f(-) for T < T(c). A detailed analysis of the specific heat that account for all relevant contributions allows us to extract and analyze the contribution related to the magnetic phase transition. The specific heat indicates the presence of a linear electronic term at low temperatures and a prominent contribution from crystal field excitations of Pr. A comparison with data from literature for PrMnO(3) shows that a Pr-Mn magnetic exchange is responsible for a sizable shift in the lowest lying excitation.

Dielectric relaxation and anti-ferromagnetic coupling of BiEu03 and BiGd03

BiEuO3 (BE) and BiGdO3 (BG) are synthesized by the solid-state reaction technique. Rietveld refinement of the X-ray diffraction data shows that the samples are crystallized in cubic phase at room temperature having Fm3m symmetry with the lattice parameters of 5.4925(2) and 5.4712(2) A for BE and BG, respectively. Raman spectra of the samples are investigated to obtain the phonon modes of the samples. The dielectric properties of the samples are investigated in the frequency range from 42 Hz to 1.1 MHz and in the temperature range from 303 K to 673 K. An analysis of the real and imaginary parts of impedance is performed assuming a distribution of relaxation times as confirmed by the Cole-Cole plots. The frequency-dependent maxima in the loss tangent are found to obey an Arrhenius law with activation energy similar to 1 eV for both the samples. The frequency-dependent electrical data are also analyzed in the framework of conductivity formalism. Magnetization of the samples are measured under the field cooled (EC) and zero field cooled (ZFC) modes in the temperature range from 5 K to 300 K applying a magnetic Field of 500 Oe. The FC and ZFC susceptibilities show that BE is a Van Vleck paramagnetic material with antiferromagnetic coupling at low temperature whereas BG is an anti-ferromagnetic system. The results are substantiated by the M-11 loops of the materials taken at 5 K in the ZFC mode. (C) 2014 Elsevier B.V. All rights reserved

Hot deformation behavior of Ni-Fe-Ga-based ferromagnetic shape memory alloy - A study using processing map

Ni-Fe-Ga-based alloys form a new class of ferromagnetic shape memory alloys (FSMAs) that show considerable formability because of the presence of a disordered fcc gamma-phase. The current study explores the deformation processing of this alloy using an off-stoichiometric Ni55Fe59Ga26 alloy that contains the ductile gamma-phase. The hot deformation behavior of this alloy has been characterized on the basis of its flow stress variation obtained by isothermal constant true strain rate compression tests in the 1123-1323 K temperature range and strain rate range of 10(-3)-10 s(-1) and using a combination of constitutive modeling and processing map. The dynamic recrystallization (DRX) regime for thermomechanical processing has been identified for this Heusler alloy on the basis of the processing maps and the deformed microstructures. This alloy also shows evidence of dynamic strain-aging (DSA) effect which has not been reported so far for any Heusler FSMAs. Similar effect is also noticed in a Ni-Mn-Ga-based Heusler alloy which is devoid of any gamma-phase. (C) 2014 Elsevier Ltd. All rights reserved.