Thermoelectric Properties of Co4Sb12 Skutterudite Materials with Partial In Filling and Excess In Additions

The properties of Co4Sb12 with various In additions were studied. X-ray diffraction revealed the presence of the pure δ-phase of In0.16Co4Sb12, whereas impurity phases (γ-CoSb2 and InSb) appeared for x = 0.25, 0.40, 0.80, and 1.20. The homogeneity and morphology of the samples were observed by Seebeck microprobe and scanning electron microscopy, respectively. All the quenched ingots from which the studied samples were cut were inhomogeneous in the axial direction. The temperature dependence of the Seebeck coefficient (S), electrical conductivity (σ), and thermal conductivity (κ) was measured from room temperature up to 673 K. The Seebeck coefficient of all In-added Co4Sb12 materials was negative. When the filler concentration increases, the Seebeck coefficient decreases. The samples with In additions above the filling limit (x = 0.22) show an even lower Seebeck coefficient due to the formation of secondary phases: InSb and CoSb2. The temperature variation of the electrical conductivity is semiconductor-like. The thermal conductivity of all the samples decreases with temperature. The central region of the In0.4Co4Sb12 ingot shows the lowest thermal conductivity, probably due to the combined effect of (a) rattling due to maximum filling and (b) the presence of a small amount of fine-dispersed secondary phases at the grain boundaries. Thus, regardless of the non-single-phase morphology, a promising ZT (S 2 σT/κ) value of 0.96 at 673 K has been obtained with an In addition above the filling limit.

Temperature influence on the excess interaction parameter of styrene-methyl methacrylate copolymer

Intrinsic viscosity data for polystyrene, poly(methyl methacrylate) and styrene-methyl methacrylate copolymer of azeotropic composition have been used to evaluate the excess interaction parameters at different temperatures in γ-butyrolactone and dimethylformamide. It is found that these values are positive and show a negligible increase with increase in temperature, indicating therefore that the hetero-contact interactions are not influenced by temperature, contrary to the results obtained by Dondos and Benoit for the same copolymer system in p-xylene and iso-amyl acetate.

Oxygen excess in layered lanthanide nickelates

Density measurements on large single-crystal specimens of La2NiO4+δ and Pr2NiO4+δ show that oxygen nonstoichiometry arises from the presence of excess lattice oxygen. X-ray photoelectron spectra as well as X-ray absorption edge studies provide no evidence for the existence of Ni3+ in these oxygen-excess nickelates under the conditions of the measurements. Transmission electron microscopy has revealed a novel type of exsolution process of the stoichiometric phase out of nonstoichiometric La2NiO4 during heating in CO2 at 870 K for 3 h. An interpretation of the results in terms of the existence of peroxide species within the conducting layers is proposed.

Metal-Insulator Transitions in Anion-Excess LaMnO3+? Controlled by the Mn4+ Content

LaMnO3+? samples with Mn4+ content up to 50% have been prepared by different methods. The structure of LaMnO3+? changes from orthorhombic to cubic (via rhombohedral) with increase in the Mn4+ content. LaMnO3+? samples containing greater than 20% Mn4+ are ferromagnetic and show resistivity maxima at a temperature Tt which is close to the ferromagnetic Curie temperature. The resistivity maximum is due to the occurrence of a metal-insulator transition. In samples heated to the same temperature, the value of Tt increases with % Mn4+. For a given sample, Tt increases with the temperature of heat treatment due to the increase in particle size. The onset of ferromagnetism in LaMnO3+? accompanied by an insulator-metal transition is similar to that found in La1-xCaxMnO3 and La1-xSrxCoO3.

Quantification of enantiomeric excess by H-1-detected heteronuclear refocusing and homonuclear multiple quantum NMR experiments

The omega(1)-heterodecoupled-C-13-filtered proton detected NMR experiments are reported for the accurate quantification of enantiomeric excess in chiral molecules embedded in chiral liquid crystal. The differential values of both H-1-H-1 and C-13-H-1 dipolar couplings in the direct dimension and only H-1-H-1 dipolar couplings in the indirect dimension enable unraveling of overlapped enantiomeric peaks. The creation of unequal C-13-bound proton signal for each enantiomer in the INEPT block and non-uniform excitation of coherences in homonuclear multiple quantum experiments do not yield accurate quantification of enantiomeric excess. In circumventing these difficulties, a coupling dependent intensity correction factor has been invoked. (C) 2010 Elsevier B.V. All rights reserved.

Application of selective F-1 decoupled H-1 NMR for enantiomer resolution and accurate measurement of enantiomeric excess at low chiral substrate/auxiliary concentration

The higher substrate and chiral auxiliary concentration is a pre-requisite to obtain efficient separation of H-1 NMR signals of enantiomers. The higher concentration of chiral lanthanide shift reagents provides broadened spectral lines resulting in a severe loss of resolution between the enantiomer resonances. In order to circumvent such difficulties, herein we present the application and the usefulness of a selective F-1 decoupled correlation (COSY) experiment which yields proton decoupled proton spectra in the indirect dimension. The potentiality of the experiment is demonstrated on several chiral compounds possessing different functional groups, employing either a lanthanide shift reagent or a solvating reagent as chiral auxiliaries. (C) 2011 Elsevier B.V. All rights reserved.

The effect of mischmetal addition on the structure and mechanical properties of a cast Al-7Si-0.3Mg alloy containing excess iron (up to 0.6 Pct)

The effect of Fe content (0.2 to 0.6 pct) on the microstructure and mechanical properties of a cast Al-7Si-0.3Mg (LM 25/356) alloy has been investigated. Further, 1 pct mischmetal (MM) additions (a mixture of rare-earth (RE) elements) were made to these alloys, and their mechanical properties at room and at elevated temperatures (up to 200 degreesC) were evaluated. A structure-property correlation on this alloy was attempted using optical microstructure analysis, fractographs, X-ray diffraction, energy-dispersive analysis of X-rays (EDX), and quantitative metallography by image analysis. An increase in Fe content increased the volume percentage of Fe-bearing intermetallic compounds (beta and pi phases), contributing to the lower yield strength (YS), ultimate tensile strength (UTS), percentage elongation, and higher hardness. An addition of 1 pct MM to the alloys containing 0.2 and 0.6 pct Fe was found to refine the microstructure; modify the eutectic silicon and La, Ce, and Nd present in the MM; form different intermetallic compounds with Al, Si, Fe, and Mg; and improve the mechanical properties of the alloys both at room and elevated temperatures.

Excess dissipation in dense emulsions

A new model for the structure, elastic properties and dynamics of foams and concentrated emulsions is presented, based on the idea of local regions lacking shear-rigidity in one or more directions which vary randomly through the medium. It is shown to lead naturally to slow (t(-1/2)) stress-relaxation, implying a piece of the dynamic modulus scaling with frequency omega as omega(1/2). Striking experimental confirmation of this prediction using a novel experimental technique is reported, and challenges for the theoretician are offered. This work was done in collaboration with Andrea Liu, Tom Mason, Hu Gang, and David Weitz [1].

Preferential oxidation of CO on Ni/CeO2 catalysts in the presence of excess H-2 and CO2

Preferential oxidation of CO (CO-PROX) was carried out over Ni supported on CeO2 prepared by the co-precipitation method. The influence of metal loadings (2.5, 5 and 10 wt.% Ni) and the reaction conditions such as reaction temperature and feed composition on CO oxidation and oxidation selectivity were evaluated by using dry reformate gas. No other reactions like CO or CO2 methanation, coking, reverse water gas shift (RWGS) reaction is observed in the temperature range of 100-200 A degrees C on these catalysts. Hydrogen oxidation dominates over CO oxidation above the temperature of 200 A degrees C. An increase in oxygen leads to an increase in CO conversion but a simultaneous decrease in the O-2 selectivity. It has been noticed that 5 and 10 % Ni/CeO2 show better catalytic activity towards CO-PROX reaction. These catalysts were characterized by S-BET, XRD, TEM, XPS and H-2-TPR.

Chiral discrimination and the measurement of enantiomeric excess from a severely overcrowded NMR spectrum

NMR spectroscopic chiral visualization, unambiguous assignment of peaks pertaining to R and S enantiomers and the subsequent measurement of enantiomeric composition demands a highly resolved spectrum. The method fails when the spectrum is severely overcrowded or highly complex, thereby hampering the determination of enantiomeric excess. In order to circumvent such problems we propose the utility of pure shift spectrum obtained by resolving the chemical shift and coupling information in two orthogonal dimensions. The skew projected spectrum yields singlet's at the respective chemical shift positions, permitting the unravelling of the superimposed spectral transitions for each enantiomer and measurement of enantiomeric composition. (C) 2012 Elsevier B. V. All rights reserved.