Phase relations in the system Ta-Rh-O and thermodynamic properties of TaRhO4

Phase relations in the system Ta-Rh-O were determined by analysis of quenched samples corresponding to thirteen compositions inside the ternary triangle after equilibration at 1273 K. All the Ta-Rh alloys were found to be in equilibrium with Ta2O5. Only one ternary oxide TaRhO4 was detected. Based on phase relations in the ternary system, a solid-state electrochemical cell, incorporating calcia-stabilized zirconia as the electrolyte, was designed to measure the standard Gibbs energy of formation (Delta G degrees, J mol(-1)) of TaRhO4 in the temperature range from 900 to 1300 K. For the reaction, 1/2 beta-Ta2O5 + 1/2 Rh2O3(ortho) -> TaRhO4 Delta G degrees = -42993 + 5.676T (+/- 85) The calculated decomposition temperatures of TaRhO4 are 1644 +/- 5K in pure O-2 and 1543 +/- 5K in air at a total pressure p(o) = 0.1 MPa. Thermodynamic properties of TaRhO4 at 298.15K have been evaluated from the results. The limited experimental thermodynamic data for Rh-rich alloys available in the literature are in fair accord with Miedema's model. The Gibbs energies of formation of the different phases in the binary system Ta-Rh were estimated based on these inputs, consistent with the binary phase diagram. Based on the thermodynamic information on the stability of various phases, an oxygen potential diagram for the system Ta-Rh-O at 1273K was constructed. Also presented are temperature-composition diagrams for the ternary system at constant oxygen partial pressures (po(2)/p(o) = 0.212 and 10(-6)) calculated form the basic data.

A reconsideration of phase relations in the Ti-Al-Mo and Ti-Al systems

A microstructural and X-ray investigation of Ti-AI-Mo alloys Ti-31 Al-15 Mo, Ti-31 Al-13 Mo, Ti-31Al-9Mo and Ti-35Al-9Mo (containing the Ti3Al, TiAl and β phases) indicates that the existing phase diagram of the ternary system for this composition range published by Ge Dhzhi-Min and Pylaeva is in error above 1473 K. An analysis of phase relations reveals that the error has arisen from their use of the Ti-AI diagram due to Bumps, Kessler and Hansen as a basis for generating the ternary. It is shown that a phase diagram of the ternary, consistent with the experimental results, can be generated using a version of the Ti-AI system due to Margolin. Simple geometric arguments are used to build up a new semi-quantitative description of the Ti-AI-Mo system which can be used as a basis for a detailed investigation of phase equilibria in this system.

Inventory Management Performance in Indian Machine Tool SMEs: What factors do influence them

These instructions give on basic guidelines for preparing papers for the IEEM 2008 Proceedings. Inventory Management (IM) plays a decisive role in the enhancement of efficiency for manufacturing enterprise competitiveness. Therefore, major manufacturing industries are following inventory management practices as a strategy to improve efficiency and achieve competitiveness. However, the spread of inventory management culture among Small and Medium Enterprises (SMEs) is limited due to lack of initiation, expertise and financial limitations in developed countries, leave alone developing countries.With this backdrop, this paper makes an attempt to ascertain the factors which influence the IM performance of SMEs in the machine tools industry of Bangalore, India. This issue is probed based on primary data gathered from 91 SMEs. The paper brings out that two sets of factors namely organizational support and external pressure have a positive impact on the inventory performance of SMEs.

Activity–Composition Relations in the Nickel Oxide–Magnesium Oxide System at 1300 K by the Solid-State Galvanic Cell Technique

The activity of NiO in NiO-MgO rock salt solid solution has been measured at 1300 K by employing a solid-state galvanic cell: Pt,Ni+ NiO||(CaO)ZrO2||Ni + (Nix,Mgl-x)O, Pt. A high-density tube of Zr02-15 mol% CaO has been used as the solid electrolyte for the emf measurements. The activities of the component oxides in the rock salt solid solution exhibit negative deviation from ideality at the temperature of investigation. The solid solution obeys regular solution behavior at 1300 K. The value of the regular solution parameter is found to be -12000 ((l000) J mol-1. The composition dependence of ΔGEx obtained in this study agrees reasonably well with the calorimetric data reported in the literature for NiO-MgO solid solution.

Phase relations in the system BiO1.5–SrO–CuO at 1123 K

Phase relations in the system Bi-Sr-Cu-O at 1123 K have been investigated using optical microscopy, electron-probe microanalysis (EPMA) and powder X-ray diffraction (XRD) of equilibrated samples. Differential thermal analysis (DTA) was used to confirm liquid formation for compositions rich in BiO1.5. Compositions along the three pseudo-binary sections and inside the pseudo-ternary triangle have been examined. The attainment of equilibrium was facilitated by the use of freshly prepared SrO as the starting material. The loss of Bi2O3 from the sample was minimized by double encapsulation. A complete phase diagram at 1123 K is presented. It differs significantly from versions of the phase diagram published recently.

Phase Relations in the System CaO-Fe2O3-Y2O3 at 1273 K and Compatibility Between Y1-xCaxFeO3-0.5x and Stabilized Zirconia

Phase relations in the system CaO-Fe2O3-Y2O3 in air (P-O2/P-o = 0.21) were explored by equilibrating samples representing eleven compositions in the ternary at 1273 K, followed by quenching to room temperature and phase identification using XRD. Limited mutual solubility was observed between YFeO3 and Ca2Fe2O5. No quaternary oxide was identified. An isothermal section of the phase diagram at 1273 K was constructed from the results. Five three-phase regions and four extended two-phase regions were observed. The extended two-phase regions arise from the limited solid solutions based on the ternary oxides YFeO3 and Ca2Fe2O5. Activities of CaO, Fe2O3 and Y2O3 in the three-phase fields were computed using recently measured thermodynamic data on the ternary oxides. The experimental phase diagram is consistent with thermodynamic data. The computed activities of CaO indicate that compositions of CaO-doped YFeO3 exhibiting good electrical conductivity are not compatible with zirconia-based electrolytes; CaO will react with ZrO2 to form CaZrO3.

Phase Relations in the System Cu-Gd-O and Gibbs Energy of Formation of CuGd204

The phase relations in the system Cu-Gd-O have been determined at 1273 K by X-ray diffrac- tion, optical microscopy, and electron microprobe analysis of samples equilibrated in quartz ampules and in pure oxygen. Only one ternary compound, CuGd2O4, was found to be stable. The Gibbs free energy of formation of this compound has been measured using the solid-state cell Pt, Cu2O + CuGd2O4 + Gd2O3 // (Y2O3) ZrO2 // CuO + Cu2O, Pt in the temperature range of 900 to 1350 K. For the formation of CuGd2O4 from its binary component oxides, CuO (s) + Gd2O3 (s) → CuGd2O4 (s) ΔG° = 8230 - 11.2T (±50) J mol-1 Since the formation is endothermic, CuGd2O4 becomes thermodynamically unstable with respect to CuO and Gd2O3 below 735 K. When the oxygen partial pressure over CuGd2O4 is lowered, it decomposes according to the reaction 4CuGd2O4 (s) → 4Gd2O3 (s) + 2Cu2O (s) + O2 (g) for which the equilibrium oxygen potential is given by Δμo 2 = −227,970 + 143.2T (±500) J mol−1 An oxygen potential diagram for the system Cu-Gd-O at 1273 K is presented.

Phase relations in the systems Cu–O–R2O3(R = Tm, Lu) and Gibbs energies of formation of Cu2R2O5 compounds

The phase relations in the systems Cu–O–R2O3(R = Tm, Lu) have been determined at 1273 K by X-ray diffraction, optical microscopy and electron probe microanalysis of samples equilibrated in evacuated quartz ampules and in pure oxygen. Only ternary compounds of the type Cu2R2O5 were found to be stable. The standard Gibbs energies of formation of the compounds have been measured using solid-state galvanic cells of the type, Pt|Cu2O + Cu2R2O5+ R2O3‖(Y2O3)ZrO2‖CuO + Cu2O‖Pt in the temperature range 950–1325 K. The standard Gibbs energy changes associated with the formation of Cu2R2O5 compounds from their binary component oxides are: 2CuO(s)+ Tm2O3(s)→Cu2Tm2O5(s), ΔG°=(10400 – 14.0 T/K)± 100 J mol–1, 2CuO(s)+ Lu2O3(s)→Cu2Lu2O5(s), ΔG°=(10210 – 14.4 T/K)± 100 J mol–1 Since the formation is endothermic, the compounds become thermodynamically unstable with respect to component oxides at low temperatures, Cu2Tm2O5 below 743 K and Cu2Lu2O5 below 709 K. When the chemical potential of oxygen over the Cu2R2O5 compounds is lowered, they decompose according to the reaction, 2Cu2R2O5(s)→2R2O3(s)+ 2Cu2O(s)+ O2(g) The equilibrium oxygen potential corresponding to this reaction is obtained from the emf. Oxygen potential diagrams for the Cu–O–R2O3 systems at 1273 K are presented.

Phase-relations in the system CAO-SIO2-ZRO2 AT 1573-K

Zirconia-based solid electrolytes with zircon (ZrSiO4) as the auxiliary electrode have been suggested of sensing silicon concentrations in iron and steel melts. A knowledge of phase relations in the ternary system MO-SiO2-ZrO2 (M = Ca, Mg) is useful for selecting an appropriate auxiliary electrode. In this investigation, an isothermal section for the phase diagram of the system CaO-SiO2ZrO2 at 1573 K has been established by equilibrating mixtures of component oxides in air, followed by quenching and phase identification by optical miroscopy, energy disperse analysis of X-rays (EDAX) and X-ray diffraction analysis (XRD). The equilibrium phase relations have also been confirmed by computation using the available thermodynamic data on condensed phases in the system. The results indicate that zircon is not in thermodynamic equilibrium with calcia-stabilized zirconia or calcium zirconate. The silica containing phase in equilibrium with stabilized zirconia is Ca3ZrSi2O9. Calcium zirconate can coexist with Ca3ZrSi2O9 and Ca2SiO4.

Phase relations in the system Cu─Ho─O and stability of Cu2Ho2O5

The phase relations in the system Cu-Ho-O have been determined at 1300 K using X-ray diffraction, optical microscopy, and electron microprobe analysis of samples equilibrated in evacuated quartz ampules and in pure oxygen. Only one ternary compound, Cu2Ho2O5, was found to be stable. The Gibbs free energy of formation of this compound has been measured using the solid-state cell Pt,Cu2O + Cu2Ho2O5 + Ho2O3/(Y2O3)ZrO2/CuO + Cu2O,Pt in the temperature range of 973 to 1350 K. For the formation of Cu2Ho2O5 from its binary component oxides, 2CuO(s) + Ho2O3(S) --> Cu2Ho2O5(s) DELTAG-degrees = 11190 - 13.8T(+/- 120) J-mol-1 Since the formation is endothermic, CU2Ho2O5 becomes thermodynamically unstable with respect to CuO and Ho2O3 below 810 K. When the oxygen partial pressure over Cu2Ho2O5 is lowered, it decomposes according to the reaction 2Cu2Ho2O5(s) --> 2Ho2O3(s) + 2Cu2O(S) + O2(g) for which the equilibrium oxygen potential is given by DELTAmu(O2) = - 238510 + 160.2T(+/- 450) J.mol-1 The decomposition temperature at an oxygen partial pressure of 1.52 x 10(4) Pa was measured using a combined DTA-TGA apparatus. Based on these results, an oxygen potential diagram for the system Cu-Ho-O at 1300 K is presented.

Phase Relations in the System La-Rh-O and Thermodynamic Properties of LaRhO3

Phase relations in the system La-Rh-O at 1223 Ii have been determined by examination of equilibrated samples by optical and scanning electron microscopy, powder X-ray diffraction (XRD), and energy-dispersive analysis of X-rays (EDAX). Only one ternary oxide, LaRhO3, with distorted orthorhombic perovskite structure (Pbnm, a = 0.5525, b = 0.5680, and c = 0.7901 nm) was identified. The alloys and intermetallics along the La-Rh binary are in equilibrium with La2O3. The thermodynamic properties of LaRhO3 were determined in the temperature range 890 to 1310 K, using a solid-state cell incorporating yttria-stabilized zirconia as the electrolyte. A new four-compartment design of the emf cell was used to enhance the accuracy of measurement. For the reaction 1/2La(2)O(3) + 1/2Rh(2)O(3) --> LaRhO3, Delta G degrees = - 70 780 + 4.89T (+/- 90) J.mol(-1) The compound decomposes on heating to a mixture of La2O3, Ph and O-2. The calculated decomposition temperatures are 1843 (+/- 5) K in pure O-2 and 1728 (+/- 5) K in air at a pressure of 1.01 x 10(5) Pa. The phase diagrams for the system La-Rh-O at different partial pressures of oxygen are calculated from the thermodynamic information.