System Dy-Fe-O: thermodynamic properties of ternary oxides using Calvet calorimetry and solid-state electrochemical cell

The enthalpy increments and the standard molar Gibbs energies of formation-of DyFeO3(s) and Dy3Fe5O12(s) have been measured using a Calvet micro-calorimeter and a solid oxide galvanic cell, respectively. A co-operative phase transition, related to anti-ferromagnetic to paramagnetic transformation, is apparent. from the heat capacity data for DyFeO3 at similar to 648 K. A similar type of phase transition has been observed for Dy3Fe5O12 at similar to 560 K which is related to ferrimagnetic to paramagnetic transformation. Enthalpy increment data for DyFeO3(s) and Dy3Fe5O12(s), except in the vicinity of the second-order transition, can be represented by the following polynomial expressions:{H(0)m(T) - H(0)m(298.15 K)) (Jmol(-1)) (+/-1.1%) = -52754 + 142.9 x (T (K)) + 2.48 x 10(-3) x (T (K))(2) + 2.951 x 10(6) x (T (K))(-1); (298.15 less than or equal to T (K) less than or equal to 1000) for DyFeO3(s), and {H(0)m(T) - H(0)m(298.15 K)} (Jmol(-1)) (+/-1.2%) = -191048 + 545.0 x (T - (K)) + 2.0 x 10(-5) x (T (K))(2) + 8.513 x 10(6) x (T (K))(-1); (208.15 less than or equal to T (K) less than or equal to 1000)for Dy3Fe5O12(s). The reversible emfs of the solid-state electrochemical cells: (-)Pt/{DyFeO3(s) + Dy2O3(s) + Fe(s)}/YDT/CSZ//{Fe(s) + Fe0.95O(s)}/Pt(+) and (-)Pt/{Fe(s) + Fe0.95O(s)}//CSZ//{DyFeO3(s) + Dy3Fe5O12(s) + Fe3O4(s)}/Pt(+), were measured in the temperature range from 1021 to 1250 K and 1035 to 1250 K, respectively. The standard Gibbs energies of formation of solid DyFeO3 and Dy3Fe5O12 calculated by the least squares regression analysis of the data obtained in the present study, and data for Fe0.95O and Dy2O3 from the literature, are given by Delta(f)G(0)m(DyFeO3,s)(kJmol(-1))(+/-3.2)= -1339.9 + 0.2473 x (T(K)); (1021 less than or equal to T (K) less than or equal to 1548)and D(f)G(0)m(Dy3Fe5O12,s) (kJmol(-1)) (+/-3.5) = -4850.4 + 0.9846 x (T (K)); (1035 less than or equal to T (K) less than or equal to 1250) The uncertainty estimates for Delta(f)G(0)m include the standard deviation in the emf and uncertainty in the data taken from the literature. Based on the thermodynamic information, oxygen potential diagram and chemical potential diagrams for the system Dy-Fe-O were developed at 1250 K. (C) 2002 Editions scientifiques et medicales Elsevier SAS. All rights reserved.

Determination of the Gibbs energy of diamond using a solid state cell

he chemical potential of carbon in diamond, relative to its value in graphite, has been directly determined using a solid state electrochemical cell incorporating single crystal CaF2 as the solid electrolyte. The cell can be represented as Pt, C(graphite) + CaC2 + CaF2double vertical barCaF2double vertical barCaF2 + CaC2 + C(diamond), Pt The reversible emf of this cell is directly related by the Nernst equation to the Gibbs free energy change for the conversion of diamond to graphite. The difference in the chemical potential of carbon in the two crystal structures varies linearly with temperature in the range 940 to 1260 K ?C(diamond) ? ?C(graphite) = 1100 + 4.64T (±50) J mol?1 On the average, the values given by the equation are 320 J mol?1 less positive than the currently accepted ones based on calorimetric studies. The difference is primarily in the enthalpy term.

Supercapacitor studies on globular polypyrrole microstructures developed by a facile electrochemical route

Micrometre-scale polypyrrole (PPy) structures are synthesised for electrochemical supercapacitor applications by a facile electrochemical route. Globular polypyrrole microstructures of size < 5 μm are grown on stainless steel (SS-304) substrate by electro-polymerisation of pyrrole on oxygen microbubble templates electrochemically generated and stabilised in the presence of surfactant/supporting electrolyte/ dopant b-naphthalene sulfonic acid (b-NSA). Microstructures obtained with scan range of 0??1.6 V (against Ag/AgCl) are uniformly distributed over the surface with high coverage density of 5 x 105 to 8 x 10 cm-2. Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy revealed that the formed microstructures are of Β-NSA doped PPy. Scanning electron microscopy showed the uniform spread and good coverage of microstructures over the substrate. Supercapacitor properties of PPy films are investigated by cyclic voltammetry, electrochemical impedance spectroscopy and galvanostatic charge/discharge methods with 1.0 M KCl as electrolyte in a three-electrode electrochemical cell. Specific capacitance of 583 Fg-1 is obtained, which is greater than the values (350-400 Fg-1 highest) usually reported for this material. Electrochemical impedance spectroscopy proves the superc

Supercapacitor studies on globular polypyrrole microstructures developed by a facile electrochemical route

Micrometre-scale polypyrrole (PPy) structures are synthesised for electrochemical supercapacitor applications by a facile electrochemical route. Globular polypyrrole microstructures of size <5 mu m are grown on stainless steel (SS-304) substrate by electro-polymerisation of pyrrole on oxygen microbubble templates electrochemically generated and stabilised in the presence of surfactant/supporting electrolyte/dopant beta-naphthalene sulfonic acid (beta-NSA). Microstructures obtained with scan range of 0-1.6 V (against Ag/AgCl) are uniformly distributed over the surface with high coverage density of 5 x 10(5) to 8 x 10 cm(-2). Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy revealed that the formed microstructures are of beta-NSA doped PPy. Scanning electron microscopy showed the uniform spread and good coverage of microstructures over the substrate. Supercapacitor properties of PPy films are investigated by cyclic voltammetry, electrochemical impedance spectroscopy and galvanostatic charge/discharge methods with 1.0 M KCl as electrolyte in a three-electrode electrochemical cell. Specific capacitance of 583 Fg(-1) is obtained, which is greater than the values (350-400 Fg(-1) highest) usually reported for this material. Electrochemical impedance spectroscopy proves the supercapacitance behaviour and explains the special inductive component of impedance observed in the high-frequency regime because of the globular structures of PPy deposited

Electrochemical determination of thermodynamic properties of DyRhO3 and phase relations in the system Dy-Rh-O

Thermodynamic properties of Dysprosium rhodite (DyRhO3) are measured in the temperature range from 900 to 1,300 K using a solid-state electrochemical cell incorporating yttria-stabilized zirconia as the electrolyte. The standard Gibbs free energy of formation of DyRhO3 with O-type perovskite structure from its components binary oxides, Dysprosia with C-rare earth structure and beta-Rh2O3 with orthorhombic structure, can be represented by the equation: Delta G(f(OX))(O) (+/- 182)/J mol(-1) = -52710+3.821(T/K). By using the thermodynamic data for DyRhO3 from experiment and auxiliary data for other phases from the literature, the phase relations in the system Dy-Rh-O are computed. Thermodynamic data for intermetallic phases in the binary system Dy-Rh, required for constructing the chemical potential diagrams, are evaluated using calorimetric data available in the literature for three intermetallics and Miedema's model, consistent with the phase diagram. The results are presented in the form of Gibbs triangle, oxygen potential-composition diagram, and three-dimensional chemical potential diagram at 1,273 K. Temperature-composition diagrams at constant oxygen partial pressures are also developed. The decomposition temperature of DyRhO3 is 1,732 (+/- 2.5) K in pure oxygen and 1,624 (+/- 2.5) K and in air at standard pressure.

Phase relations in the system Ta-Rh-O and thermodynamic properties of TaRhO4

Phase relations in the system Ta-Rh-O were determined by analysis of quenched samples corresponding to thirteen compositions inside the ternary triangle after equilibration at 1273 K. All the Ta-Rh alloys were found to be in equilibrium with Ta2O5. Only one ternary oxide TaRhO4 was detected. Based on phase relations in the ternary system, a solid-state electrochemical cell, incorporating calcia-stabilized zirconia as the electrolyte, was designed to measure the standard Gibbs energy of formation (Delta G degrees, J mol(-1)) of TaRhO4 in the temperature range from 900 to 1300 K. For the reaction, 1/2 beta-Ta2O5 + 1/2 Rh2O3(ortho) -> TaRhO4 Delta G degrees = -42993 + 5.676T (+/- 85) The calculated decomposition temperatures of TaRhO4 are 1644 +/- 5K in pure O-2 and 1543 +/- 5K in air at a total pressure p(o) = 0.1 MPa. Thermodynamic properties of TaRhO4 at 298.15K have been evaluated from the results. The limited experimental thermodynamic data for Rh-rich alloys available in the literature are in fair accord with Miedema's model. The Gibbs energies of formation of the different phases in the binary system Ta-Rh were estimated based on these inputs, consistent with the binary phase diagram. Based on the thermodynamic information on the stability of various phases, an oxygen potential diagram for the system Ta-Rh-O at 1273K was constructed. Also presented are temperature-composition diagrams for the ternary system at constant oxygen partial pressures (po(2)/p(o) = 0.212 and 10(-6)) calculated form the basic data.

An update on the thermodynamics of Ta2O5

Using a solid-state electrochemical cell incorporating yttria-doped thoria (YDT) as the electrolyte and a mixture of (Mn + MnO) as the reference electrode, standard Gibbs free energy of formation of beta-Ta2O5 has been determined as a function of temperature in the range (1000 to 1300) K. The solid-state electrochemical cell used can be represented as (-)Pt,Ta +Ta2O5//(Y2O3)ThO2//Mn + MnO, Pt(+) Combining the reversible e.m.f. of the cell with recent data on the free energy of formation of MnO, standard Gibbs free energy of formation of Ta2O5 from Ta metal and diatomic oxygen gas (O-2) in the temperature range (1000 to 1300) K is obtained: Delta fG degrees +/- 0.35/(kJ.mol(-1)) = -2004.376 + 0.40445(T/K). Because of the significant solid solubility of oxygen in tantalum, a small correction for the activity of Ta in the metal phase in equilibrium with Ta2O5 is applied. An analysis of the results obtained in this study and other free energy data reported in the literature by the "third law" method suggests the need for refining data for Ta2O5 reported in thermodynamic compilations. Used in the analysis is a revised value for standard entropy of Ta2O5 based on more recent low-temperature heat capacity measurements. An improved set of thermodynamic properties of ditantalum pentoxide (Ta2O5) are presented in the temperature range (298.15 to 2200) K. (C) 2008 Elsevier Ltd. All rights reserved.

Gibbs Energy of Formation of MnO: Measurement and Assessment

Based on the measurements of Alcock and Zador, Grundy et al. estimated an uncertainty of the order of +/- 5 kJ mol(-1) for the standard Gibbs energy of formation of MnO in a recent assessment. Since the evaluation of thermodynamic data for the higher oxides Mn3O4, Mn2O3, and MnO2 depends on values for MnO, a redetermination of its Gibbs energy of formation was undertaken in the temperature range from 875 to 1300 K using a solid-state electrochemical cell incorporating yttria-doped thoria (YDT) as the solid electrolyte and Fe + Fe1-delta O as the reference electrode. The cell can be presented as Pt, Mn + MnO/YDT/Fe + Fe1+delta O, Pt Since the metals Fe and Mn undergo phase transitions in the temperature range of measurement, the reversible emf of the cell is represented by the three linear segments. Combining the emf with the oxygen potential for the reference electrode, the standard Gibbs energy of formation of MnO from alpha-Mn and gaseous diatomic oxygen in the temperature range from 875 to 980 K is obtained as: Delta G(f)(o)/Jmol(-1)(+/- 250) = -385624 + 73.071T From 980 to 1300 K the Gibbs energy of formation of MnO from beta-Mn and oxygen gas is given by: Delta G(f)(o)/Jmol(-1)(+/- 250) = -387850 + 75.36T The new data are in excellent agreement with the earlier measurements of Alcock and Zador. Grundy et al. incorrectly analyzed the data of Alcock and Zador showing relatively large difference (+/- 5 kJ mol(-1)) in Gibbs energies of MnO from their two cells with Fe + Fe1-delta O and Ni + NiO as reference electrodes. Thermodynamic data for MnO is reassessed in the light of the new measurements. A table of refined thermodynamic data for MnO from 298.15 to 2000 K is presented.

Thermodynamic properties of RhO2

A solid-state electrochemical cell, with yttria-stabilized zirconia as the electrolyte and pure O-2 gas at 0.1 MPa as the reference electrode, has been used to measure the oxygen chemical potential corresponding to the equilibrium between beta-Rh2O3 and RhO2 in the temperature range from 850 to 1050K. Using standard Gibbs energy of formation of beta-Rh2O3 available in the literature and the measured oxygen potential, the standard Gibbs free energy of formation of RhO2 is derived as a function of temperature: Delta G(f)degrees(RhO2)(+/- 71)/J mol(-1) = 238,418 + 179.89T Using an estimated value of Delta C-p degrees; for the formation reaction of RhO2 from its elements, the standard enthalpy of formation, standard entropy and isobaric heat capacity of RhO2 at 298.15 K are evaluated: Delta H-f degrees (298.15 K)(+/- 164)/kJ mol(-1) = -244.94, S degrees (298.15 K)(+/- 3.00)/J mol(-1) K-1 = 45.11 and C-p degrees(298.15 K)(+/- 2.6)1mol(-1) K-1 =64.28. (C) 2010 Elsevier B.V. All rights reserved.

Gibbs energy of formation of orthorhombic CaZrO3

The Gibbs free energy of formation of the orthorhombic form of CaZrO3(o) from monoclinic ZrO2(m) and periclase CaO(p) has been determined as a function of temperature in the range 950-1225 K, using an electrochemical cell incorporating single-crystal CaF2 as the solid electrolyte. The results are corrected for the small solid solubility of CaO in ZrO2. For the reaction, ZrO2(m) + CaO(p) --> CaZrO3(o), DELTAG(phi) = -31590 -13.9T(+/- 180) J mol-1. The ''second-law'' enthalpy of formation of CaZrO3 obtained from the results of this study at a mean temperature of 1090 K is in excellent agreement with the high-temperature solution calorimetric measurements of Muromachi and Navrotsky at 1068 K (J. Solid State Chem., 72 (1988) 244), and the average value of the bomb and acid solution calorimetric studies of Lvova and Feodosev (Zh. Fiz. Khim., 38 (1964) 28), Korneev et al. (Izv. Akad. Nauk SSSR, Neorg. Mater., 7 (1971) 886) and Brown and Bennington (Thermochim. Acta, 106 (1986) 183). The standard entropy of CaZrO3(o) at 298.15 K from the free energy data is 96.4 (+/- 3.5) J K-1 mol-1. The results of this study are discussed in comparison with high-temperture e.m.f. measurements reported in the literature on cubic zirconia solid solutions.

Design of solid electrolytes for use with dissimilar gas electrodes

The design of a solid electrolyte that permits the use of dissimilar gas electrodes in an electrochemical cell is presented. It consists of a functionally gradient material with spatial variation in composition. The activity of the conducting ion is fixed at each electrode using different gas species. The system chosen for demonstrating the concept consists of a solid solution between K2CO3 and K2SO4. The composition of the solid solution varies from pure K2CO3 in contact with a CO2 + O2 gas mixture at one electrode to pure K2SO4 exposed to a mixture of SO3 + SO2 + O2 at the other. Two types of composition profiles are studied, one with monotonic variation in composition and the other with extrema. The e.m.f. of the cells is studied as a function of temperature and composition of the gas mixture at each electrode. The results indicate that the e.m.f. is determined primarily by the difference in the chemical potential of potassium at the two electrodes. The diffusion potential caused by ionic concentration gradients in the electrolyte appears to be negligible when the corresponding ionic transport numbers are insignificant. Studies on the response characteristics of the cell based on the gradient electrolyte indicate that the nature of the variation in composition of the electrolyte has only a minor effect on the time evolution of e.m.f. The gradient solid electrolytes have potential application in multielement galvanic sensors at high temperatures.

Systematic trends in structural and thermodynamic properties of ternary oxides in the systems Ln-Pd-O (Ln = lanthanide element)

Isothermal sections of the phase diagrams for the systems Ln-Pd-O (Ln = lanthanide element) at 1223 K indicate the presence of two inter-oxide compounds Ln(4)PdO(7) and Ln(2)Pd(2)O(5) for Ln = La, Pr, Nd, Sm, three compounds Ln(4)PdO(7), Ln(2)PdO(4) and Ln(2)Pd(2)O(5) for Ln = Eu, Gd and only one compound of Ln(2)Pd(2)O(5) for Ln = Tb to Ho. The lattice parameters of the compounds Ln(4)PdO(7), Ln(2)PdO(4) and Ln(2)Pd(2)O(5) show systematic nonlinear variation with atomic number. The unit cell volumes decrease with increasing atomic number. The standard Gibbs energies, enthalpies and entropies of formation of the ternary oxides from their component binary oxides (Ln(2)O(3) and PdO) have been measured recently using an advanced version of the solid-state electrochemical cell. The Gibbs energies and enthalpies of formation become less negative with increasing atomic number of Ln. For all the three compounds, the variation in Gibbs energy and enthalpy of formation with atomic number is markedly non-linear. The decrease in stability with atomic number is most pronounced for Ln(2)Pd(2)O(5), followed by Ln(4)PdO(7) and Ln(2)PdO(4). This is probably related to the repulsion between Pd2+ ions on the opposite phases Of O-8 cubes in Ln(2)Pd(2)O(5), and the presence of Ln-filled O-8 cubes that share three faces with each other in Ln4PdO7. The values for entropy of formation of all the ternary oxides from their component binary oxides are relatively small. Although the entropies of formation show some scatter, the average value for Ln = La, Pr, Nd is more negative than the average value for the other lanthanide elements. From this difference, an average value for the structure transformation entropy of Ln(2)O(3) from C-type to A-type is estimated as 0.87 J.mol(-1).K-1. The standard Gibbs energies of formation of these ternary oxides from elements at 1223 K are presented as a function of lanthanide atomic number. By invoking the Neumann-Kopp rule for heat capacity, thermodynamic properties of the inter-oxide compounds at 298.15 K are estimated. (C) 2002 Elsevier Science Ltd. All rights reserved.

A Sensor for Sulfur Gas Based on Silver β-Alumina

EMF measurements were made with an electrochemical cell of the type ~t/&(s)/&+-beta alumina/Ag~S(s)S. 2(g). S(s or 1)/R at temperatures between 95 and 241°C. Sflver $- alumina was prepared with the ion exchange technique. The patial pressure of diatomic gas obtained from cell voltages agreed with the literature data.

Gibbs energy of formation of CaCu3Ti4O12 and phase relations in the system CaO-CUO/CU2O-TiO2

he standard Gibbs energy of formation of CaCu3Ti4O12 (CCTO) from CaTiO3, CuO and TiO2 has been determined as a function of temperature from 925 to 1350 K using a solid-state electrochemical cell with yttria-stabilized zirconia as the solid electrolyte. Combining this result with information in the literature on CaTiO3, the standard Gibbs energy of formation of CCTO from its component binary oxides, CaO, CuO and TiO2, has been obtained: View the MathML source (CaCu3Ti4O12)/J mol−1 (±600) = −125231 + 6.57 (T/K). The oxygen chemical potential corresponding to the reduction of CCTO to CaTiO3, TiO2 and Cu2O has been calculated from the electrochemical measurements as a function of temperature and compared on an Ellingham diagram with those for the reduction of CuO to Cu2O and Cu2O to Cu. The oxygen partial pressures corresponding to the reduction reactions at any chosen temperature can be read using the nomograms provided on either side of the diagram. The effect of the oxygen partial pressure on phase relations in the pseudo-ternary system CaO–CuO/Cu2O–TiO2 at 1273 K has been evaluated. The phase diagrams allow identification of secondary phases that may form during the synthesis of the CCTO under equilibrium conditions. The secondary phases may have a significant effect on the extrinsic component of the colossal dielectric response of CCTO.