Durability of rammed earth walls exposed for 20 years to natural weathering

This paper presents a study on the durability of different types of stabilised and unstabilised rammed earth walls. These rammed earth walls were constructed and exposed for 20 years to natural weathering, in a wet continental climate. None of these walls have shown complete collapse to date. A method to measure the rammed earth walls erosion by stereo-photogrammetry has been developed. The result shows that the mean erosion depth of the studied walls is about 2 mm (0.5% wall thickness) in the case of rammed earth wall stabilised with 5% by dry weight of hydraulic lime and about 6.4 mm (1.6% wall thickness) in the case of unstabilised rammed earth walls. The stabilisation enables to not use any plaster to protect the walls. In the case of the unstabilised rammed earth walls, an extrapolated lifetime longer than 60 years can be assessed. This shows a potential for the use of unstabilised rammed earth in the similar climatic conditions with this study. The method of stereo-photogrammetry used to measure the erosion of rammed earth walls on site may also help to calibrate and develop more pertinent laboratory test to assess the durability of rammed earth wall.

Lipids of some thermophilic fungi

Total lipid content in the thermophilic fungi—Thermoascus aurantiacus, Humicola lanuginosa, Malbranchea pulchella var.sulfurea, andAbsidia ramosa—varied from 5.3 to 19.1% of mycelial dry weight. The neutral and polar lipid fractions accounted for 56.4 to 80.2% and 19.8 to 43.6%, respectively. All the fungi contained monoglycerides, diglycerides, triglycerides, free fatty acids, and sterols in variable amounts. Sterol ester was detected only inA. ramosa. Phosphatide composition was: phosphatidyl choline (15.9–47%), phosphatidyl ethanolamine (23.4–67%), phosphatidyl serine (9.3–17.6%), and phosphatidyl inositol (1.9–11.9%). Diphosphatidyl glycerol occurred in considerable quantity only inH. lanuginosa andM. pulchella var.sulfurea. Phosphatidic acid, detected as a minor component only inM. pulchella var.sulfurea andA. ramosa, does not appear to be a characteristic phosphatide of thermophilic fungi as suggested earlier. The 16∶0, 16∶1, 18∶0, 18∶1, and 18∶2 acids were the main fatty acid components. In addition,A. ramosa contained 18∶3 acid. Total lipids contained an average of 0.93 double bonds per mole of fatty acids, and neutral lipids tend to be more unsaturated than phospholipids.

Biotransformation of cholesterol to diosgenin by freely suspended and immobilised cells of Dioscorea bulbifera L.

The cell suspension cultures, established from the friable callus which was risen from the nodal segments of Dioscorea bulbifera L. in Murashige-Skoog (MS) medium supplemented with indole-3-butryic acid (20 mg L- 1), was examined for cell growth in MS medium fed with cholesterol (50 mg L- 1 and 100 mg L- 1) after 8, 10, 12, 14, 16, and 18 days of culture. The growth index of the cell suspension culture on the 8th day was 1.2 and gradually inclined to 1.9 on the 16th day and remained the same at the 18th day. There is no marked difference in the cell growth of cholesterol-treated and control cell suspension culture. The maximum accumulation of diosgenin was noticed on the 14th day in control and cholesterol-treated cell suspension culture and immobilised cell cultures. The highest concentration of diosgenin, 2.94% and 2.14% dry weight, was obtained in immobilised cell culture and cell suspension culture treated with 100 mg L- 1 cholesterol, respectively.

Expression of hyoscyamine 6 beta-hydroxylase in the root pericycle cells and accumulation of its product scopolamine in leaf and stem tissues of Datura metel L.

Hyoscyamine 60-hydroxylase (H6H: EC 1.14.11.11), a key enzyme at the terminal step of tropane alkaloid biosynthesis, converts hyoscyamine to scopolamine. The accumulation of scopolamine in different organs, in particular the aerial parts for storage, is subject to the expression of hyoscyamine 6-phydroxylase as well as its transport from the site of synthesis. To understand the molecular basis of this regulation, we have analyzed, in parallel, the relative levels of hyoscyamine and scopolamine, and the accumulation of H6H (both protein and transcript) in leaves, stems and roots of D. metel. The root, stem and leaf tissues all contain about 0.51-0.65 mg g(-1) dry weight of scopolamine. Hyoscyamine content was extremely low in leaf and stem tissues and was about 0.28 mg g(-1) dry weight in the root tissue. H6H protein and its transcript were found only in roots but not in the aerial parts viz. stems and leaves. The immunolocalization studies performed on leaf, stem, root as well as hairy root tissues showed that H6H was present only in the pericycle cells of young lateral and hairy roots. These studies suggest that the conversion of hyoscyamine to scopolamine takes place in the root pericycle cells, and the alkaloid biosynthesized in the roots gets translocated to the aerial parts in D. metel. (C) 2009 Elsevier Ireland Ltd. All rights reserved.

Collapse Behavior of an Artificially Cemented Clayey Silt

The present study examines the role of interparticle cementation in the collapse behavior of two partly saturated (S-r = 4 to 12%) and very highly porous (initial void ratio = 1.5 to 2) laboratory-desiccated clayey silt specimens containing varying amounts (5 and 15% by dry weight of the respective specimens) of the cementitious iron oxides hematite and goethite, which are generally encountered in tropical residual soils. Kaolinite is the representative clay mineral of the soil matrix used for this research. Interparticle cementation by the crystalline iron oxides was generated in the laboratory by repeated (six times) wetting and drying of the iron-hydroxide-admixed clayey silt specimens under ambient conditions of temperature and humidity. Results showed that, for a given laboratory-desiccated clayey silt specimen (i.e., a specimen containing 5 or 15% of iron oxide on a dry weight basis), the amount of collapse (represented by Delta epsilon, the change in vertical strain upon wetting under constant pressure) increases with an increase in the experimental loading under which the specimen is inundated. The laboratory results also show that the desiccated specimen with a higher iron oxide content (containing 15% iron oxide by dry weight of the desiccated specimen) in spite of a lower dry unit weight (gamma(d) = 8.8 kN/m(3)) undergoes a lesser amount of collapse on soaking under a constant external stress (50 or 100 kPa) than the desiccated specimen with a lower iron oxide content (i.e., containing 5% iron oxide by dry weight of the desiccated specimen, gamma(d) = 10.4 KN/m(3)). Based on the X-ray diffraction results and the stress-strain relationships obtained from isotropically consolidated undrained triaxial tests, it is suggested that the laboratory-desiccated specimens are characterized by a metastable bonding provided by capillary suction and the crystalline iron oxides. On soaking under load owing to the loss of the metastable bonding, collapse of the laboratory-desiccated specimens occurs. Also, in the case of the laboratory-desiccated specimen with a higher iron oxide content, the presence of a stronger interparticle cementation (due to a greater abundance of crystalline iron oxides) and a higher initial moisture content are considered responsible for the specimen exhibiting a lower amount of collapse in comparison to that exhibited by the desiccated specimen with a lesser iron oxide content.

Photo and Thermal Degradation of a Cationic Superabsorbent Polymer

A cationic superabsorbent polymer (SAP) was synthesized by carrying out the polymerization of 2-(methacryloyloxy)ethyl] trimethyl ammonium chloride) with N,N'-methylenebisacrylamide as the cross-linking agent. The SAP was subjected to degradation in dry and the equilibrium swollen state by thermo gravimetric analysis and exposure to ultraviolet radiation, respectively. The photodegradation was monitored by measuring changes in the swelling capacity and the dry weight of the SAP. The thermal degradation of the SAP occurred in three stages after the initial removal of moisture and the activation energies of the decomposition were determined.

Mercury exposure Aasessment in fish and humans from Sundarban Mangrove Wetland of India

Present study had documented total mercury levels in six commonly consumed fish species, and performed across-sectional study on local residents to gauge their intake of fish (via dietary survey) and mercury exposure (via hair biomarker analyses). Mean total mercury content in edible composites of locally-caught fishes (topse, hilsa, mackerel, topse, sardinella, khoira) was low and ranged from 0.01 to 0.11 mu g g(-1) mercury, dry weight. In a cross-sectional study of 58 area residents, the mercury content in hair ranged from 0.25 to 1.23 mu g g(-1), with a mean of 0.65 +/- 0.23 mu g g(-1), Flair mercury level was not influenced by gender, age, or occupation. Mean number of meals consumed per week was 3.1 +/- 1.1, and all participants consumed at least one fish meal per week. When related to fish consumption, a significant positive association was found between number of fish meals consumed per week and hair mercury levels.