Formation of a single, rotated-Brass (1 1 0)< 5 5 6 > texture by hot cross-rolling of an Al-Zn-Mg-Cu-Zr alloy

The present work describes the evolution of a strong, single-component rotated-Brass ((1 1 0) < 5 5 6 >) texture in an Al-Zn-Mg-Cu-Zr alloy by an uneven hot cross-rolling with frequent interpass annealing. This texture development is unique because hot rolling of aluminum alloys results in orientation distribution along the ``beta-fibre''. It has been demonstrated that the deformation by cross-rolling of a partially recrystallized grain structure having rotated-Cube and Goss orientations, and the recrystallization resistance of near-Brass-oriented elongated grains play a critical role in development of this texture. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Process and properties of electroless Ni-Cu-P-ZrO2 nanocomposite coatings

Electroless Ni-Cu-P-ZRO(2) composite coating was successfully obtained on low carbon steel matrix by electroless plating technique. Coatings with different compositions were obtained by varying copper as ternary metal and nano sized zirconium oxide particles so as to obtain elevated corrosion resistant Ni-P coating. Microstructure, crystal structure and composition of deposits were analyzed by SEM, EDX and XRD techniques. The corrosion behavior of the deposits was studied by anodic polarization, Tafel plots and electrochemical impedance spectroscopy (EIS) in 3.5% sodium chloride solution. The ZRO(2) incorporated Ni-P coating showed higher corrosion resistance than plain Ni-P. The introduction of copper metal into Ni-P-ZRO(2) enhanced the protection ability against corrosion. The influence of copper metal and nanoparticles on microhardness of coatings was evaluated. (C) 2011 Elsevier Ltd. All rights reserved.

High-temperature superconductivity in bismuth-copper oxides of the type BimMnCupOx (M=Mg, Ca, Sr, Ba, Bi)

Several oxides of the Bi m M n Cu p O x family (m=2, 3;n=2, 3, 4;p=1, 2, 3 and M=alkaline earth or Bi), possessing structures similar to the Aurivillius family of oxides, show highT c superconductivity.

Magnesium/Copper Nanocomposite through Digestive Ripening

Composing nanocomposites: Co-digestive ripening of as-prepared Mg and Cu colloids prepared by the solvated metal atom dispersion method results in a highly monodisperse colloid of Mg/Cu nanocomposite with an average particle size of 3.0 +/- 0.5 nm. Annealing of these samples at 300 degrees C gives the Cu/MgO nanocomposite.

Chelating and bridging diphosphinoamine (PPh2)(2)N(Pr-i) complexes of copper(I)

The ligand bis(diphenylphosphino) isopropylamine (dppipa) has been shown to be a versatile ligand sporting different coordination modes and geometries dictated by copper(I). Most of the molecular structures were confirmed by X-ray crystallography. It is found in a chelating mode, in a monomeric complex when the ligand to copper ratio is 2:1. A tetrameric complex is formed when low ratios of ligand to metal (1: 2) were used. But with increasing ratios of ligand to metal (1: 1 and 2: 1), a trimer or a dimer was obtained depending on the crystallization conditions. Variable temperature P-31{H-1} NMR spectra of these complexes in solution showed that the Cu-P bond was labile and the highly strained 4-membered structure chelate found in the solid state readily converted to a bridged structures. On the other hand, complexes with the ligand in a bridging mode in the solid state did not form chelated structures in solution. The effect of adding tetra-alkylammonium salts to solutions of various complexes of dppipa were probed by P-31{H-1} NMR and revealed the effect of counter ions on the stability of complexes in solution. (C) 2008 Elsevier B.V. All rights reserved.

Antihyperlipidemic potential of Cedrus deodara extracts in monosodium glutamate induced obesity in neonatal rats

Objective: To study the antihyperlipidemic effect of Cedrus deodara (C. deodara) against monosodium glutamate (MSG) induced obesity in neonatal rats. Materials and Methods: The studies were carried out on newborn neonatal rats and were injected intraperitoneally with 2 mg/g of MSG on the 2(nd) and 4(th) postnatal days and 4 mg/g on 6(th), 8(th) and 10(th) postnatal days. Ethanolic extract (EE) and acetone extract (AE) of C. deodara was administered in a dose of 100 and 200 mg/kg, p.o./day at the age of 65 days. On day 60 of treatment, body weight, locomotor activity, body temperature, and various biochemical parameters like serum glucose, total cholesterol, triglyceride, and organs weights were recorded. Results: There was a significant reduction in body weight, organs and increased body temperature, locomotor activity after treatment with extracts. C. deodara decreased serum glucose, total cholesterol and triglyceride, low density lipoprotein (LDL) and very low density lipoprotein (VLDL) levels and increased high density lipoprotein (HDL) significantly has compared to MSG-control rats. Conclusion: C. deodara extracts exhibited antihyperlipidemic effect and it possesses anti-obesity properties in MSG induced obese rats.

Effects of different modes of hot cross-rolling in 7010 aluminum alloy: part I. evolution of microstructure and texture

The current study describes the evolution of microstructure and texture in an Al-Zn-Mg-Cu-Zr-based 7010 aluminum alloy during different modes of hot cross-rolling. Processing of materials involves three different types of cross-rolling. The development of texture in the one-step cross-rolled specimen can be described by a typical beta-fiber having the maximum intensity near Copper (Cu) component. However, for the multi-step cross-rolled specimens, the as-rolled texture is mainly characterized by a strong rotated-Brass (Bs) component and a very weak rotated-cube component. Subsequent heat treatment leads to sharpening of the major texture component (i.e., rotated-Bs). Furthermore, the main texture components in all the specimens appear to be significantly rotated in a complex manner away from their ideal positions because of non-symmetric deformations in the two rolling directions. Detailed microstructural study indicates that dynamic recovery is the dominant restoration mechanism operating during the hot rolling. During subsequent heat treatment, static recovery dominates, while a combination of particle-stimulated nucleation (PSN) and strain-induced grain boundary migration (SIBM) causes partial recrystallization of the grain structure. The aforementioned restoration mechanisms play an important role in the development of texture components. The textural development in the current study could be attributed to the combined effects of (a) cross-rolling and inter-pass annealing that reduce the intensity of Cu component after each successive pass, (b) recrystallization resistance of Bs-oriented grains, (c) stability of Bs texture under cross-rolling, and (d) Zener pinning by Al3Zr dispersoids.

Tribological characteristics of A356 Al alloy-SiC(P) composite discs

The dry sliding wear and friction behaviour of A356 Al alloy and its composites containing 10 and 20 vol.% SiC(P) have been studied using pin-on-disc set up. In these tests, A356 Al alloy and its composites are used as disc whereas brake pad was used in the form of pins. Wear tests were carried out at a load of 192 N and the sliding speed was varied from 1 to 5 m/s. Tests were done for a sliding distance of 15 km. The effects of sliding velocity on the wear rate, coefficient of friction and nature of tribolayers formed on discs have been studied. Wear rates of composites as calculated by weight loss method, found to be negative at sliding speed of more than 2 m/s. Worn surfaces of pins and discs have been analyzed using scanning electron microscope. SEM and EDAX analysis of worn surfaces of composite discs showed formation of tribolayers, consisting of mixture of oxides of Al, Si, Cu, Ca, Ba, Mg, and Fe. In these layers, copper and barium content found to be increase with sliding speed in the case of composites. (C) 2011 Elsevier B.V. All rights reserved.

Interaction of Co, Mn, Mg and AI with d(GCGTACGC): a spectroscopic study

Spectroscopic study on the interactions of trace elements Co, Mn, Mg and Al with d(GCGTACGC) indicated the following: Al and Mg did not alter T-m values. Mn enhanced T-m at lower concentration and decreased it at higher concentrations. Interestingly Co at higher concentration elevated the T-m. These studies also showed lower concentrations of Mn displaced EtBr, whereas Al could displace it at higher ionic strength. Mg and Co displaced EtBr fluorescence at moderate concentrations. The binding constant values and CD spectra clearly indicated strong binding of these elements to DNA.

The effect of ball milling on the melting behavior of Sn-Cu-Ag eutectic alloy

Sn-Ag-Cu (SAC) solder alloys are the best Pb free alternative for electronic industry. Since their introduction, efforts are made to improve their efficacies by tuning the processing and composition to achieve lower melting point and better wettability. Nanostructured alloys with large boundary content are known to depress the melting points of metals and alloys. In this article we explore this possibility by processing prealloyed SAC alloys close to SAC305 composition (Sn-3wt%Ag-0.5wt%Cu) by mechanical milling which results in the formation of nanostructured alloys. Pulverisette ball mill (P7) and Vibratory ball mills are used to carry out the milling of the powders at room temperature and at lower temperatures (-104 A degrees C), respectively. We report a relatively smaller depression of melting point ranging up to 5 A degrees C with respect to original alloys. The minimum grain sizes achieved and the depression of melting point are similar for both room temperature and low-temperature processed samples. An attempt has been made to rationalize the observations in terms of the basic processes occurring during the milling.

Structure of the Monosodium Salt of D-Glucose 6-Hydrogenphosphate

Na+.C6HI209 P-, Mr=282.1, monoclinic, e2~, a=5-762(1), b=7.163(2), c=12.313(1)A, fl= 99.97 (1) °, U= 500.5 A 3, Z= 2, D m = 1.86, D x = 1.87 Mg m -s, Cu Ka, 2 = 1.5418 A, /a = 3-3 mm -1, F(000) = 292, T= 300 K, final R for 922 observed reflections is 0-042. The phosphate ester bond, P-O(6), is 1.575 (5)A, slightly shorter than the P~O bond in monopotassium phosphoenolpyruvate [1.612 (6) A] [Hosur & Viswamitra (1981). Acta Cryst. B37, 839-843]. The pyranose sugar ring takes a 4C 1 chair conformation. The conformation about the exocyclic C(5)-C(6) bond is gauche-trans. The endocyclic C-O bonds in the glucose ring are nearly equal with C(5)-O(5) = 1.435 (8) and C(1)-O(5) = 1.436 (9) A. The sodium ion has seven near neighbours within a distance of 2.9 A. The crystal structure is stabilized by hydrogen bonds between the O atoms of symmetryrelated molecules.

L-Arginyl-L-Glutamic Acid Dihydrate, C11h21n5o5.2h2o

M r = 339.35, monoclinic, P2 t, a = 11.028 (2), b=9.583 (2), c= 16.010 (2) A, fl= 96.57 (1) °, U= 1680.85 A 3, Z = 4, D m = 1.37, D x= 1.34 Mg m -3, Cu Ka, 2 = 1.54184 A, p = 0.85 mm -1, F(000)=728, T=300K, R=0.085 for 2845 diffractometer- measured reflections IF o > 3cr(Fo)]. The two molecules in the asymmetric unit have similar conformations except for a static disorder at the C ~ and C ~ positions in one of the glutamic-acid side chains. An interesting feature of the crystal structure is a pair of hydrogen bonds between the guanidinium and ycarboxylate groups of neighbouring molecules. This is the first such specific interaction observed between side chains of arginine and glutamic acid.

Metal chelates in vinyl polymerization: Bulk polymerization of acrylonitrile initiated by Cu(II)-imine complexes

This article deals with the kinetics and mechanism of acrylonitrile (AN) polymerization initiated by Cu(II)-4-anilino 3-pentene 2-one[Cu(II)ANIPO], Cu(II)-4-p-toluedeno 3-pentene 2-one [Cu(II)TPO], and Cu(II)-4-p-nitroanilino 3-pentene 2-one [Cu(II)NAPO] in bulk at 60°C. The polymerization is free radical in nature. The exponent of initiator(I) is 0.5. The initiation step is a complex formation between the chelate and monomer and subsequent decomposition of the intermediate complex giving rise to free radical and Cu(I). This is substantiated by ultraviolet (UV) and electron spin resonance (ESR) studies. The activation energies and kinetic and chain transfer constants have also been evaluated.