Preparation of lamellar and hexagonal forms of mesoporous silica and zirconiaby the neutral amine route: lamellar-hexagonal transformation in the solid state

The chain length of the surfactant and the solvent composition are two of the factors that determine whether the lamellar or the hexagonal form of mesoporous SiO2 (or ZrO2) is formed by the neutral amine route; a lamellar-hexagonal transformation occurs on removal of the amine from the former.

Homogeneous precipitation from solution by urea hydrolysis: a novel chemical route to the a-hydroxides of nickel and cobalt

Homogeneous precipitation from solution by hydrolysis of urea at elevated temperatures (T=120 degrees C) yields novel ammonia-intercalated alpha-type hydroxide phases of the formula M(OH)(x)(NH3)(0.4)(H2O)(y)(NO3)(2-x) where x=2, y=0.68 for M=Ni and x=1.85, y=0 for M=Co. These triple-layered hexagonal phases (a=3.08+/-0.01 Angstrom, c=21.7+/-0.05 Angstrom) are more crystalline than similar phases obtained by chemical precipitation or electrosynthesis. This method can be adapted as a convenient chemical route to the bulk synthesis of alpha-hydroxides.

Synthesis of nanoparticles of the giant dielectric material, CaCu3Ti4O12 from a precursor route

A complex oxalate precursor, CaCu3(TiO)(4)(C2O4)(8)center dot 9H(2)O, (CCT-OX), was synthesized and the precipitate that obtained was confirmed to be monophasic by the wet chemical analyses, X-ray diffraction, FTIR absorption and TG/DTA analyses. The thermal decomposition of this oxalate precursor led to the formation of phase-pure calcium copper titanate, CaCu3Ti4O12, (CCTO) at a parts per thousand yen680A degrees C. The bright-field TEM micrographs revealed that the size of the as synthesized crystallites to be in the 30-80 nm range. The powders so obtained had excellent sinterability resulting in high density ceramics which exhibited giant dielectric constants upto 40000 (1 kHz) at 25A degrees C, accompanied by low dielectric losses.

Highly Monodisperse Colloidal Magnesium Nanoparticles by Room Temperature Digestive Ripening

Nanoclusters of 25 nm sized Mg-THF have been prepared by the solvated metal atom dispersion method. Room-temperature digestive ripening of these nanoclusters in the presence of hexadecylamine (HDA) resulted in highly monodisperse colloidal Mg-HDA nanoparticles of 2.8 ± 0.2 nm. An insight into the room-temperature digestive ripening process was obtained by studying the disintegration of clusters for various Mg:HDA ratios. The Mg colloids are quite stable with respect to precipitation of particles under Ar atmosphere. Using this procedure, pure Mg(0) nanopowders were obtained in gram scale quantities. The Mg powder precipitated from the colloid was fully hydrided at 33 bar and 118 °C. Initial desorption of H2 from samples of MgH2 was achieved at a remarkably low temperature, 115 °C compared to >350 °C in bulk Mg, demonstrating the importance of the size on the desorption temperatures.

A Radical Cyclization Route To +/-Andirolactone, A Spiro-Gamma-Butyrolactone

Synthesis of Andirolactone (Image ), starting from 4-methyl cyclohex-3-en-1-one (Image ), via the radical cyclisation of the bromoacetal (Image ), is described.

An elegant direct route for the preparation of pyridinium, ammonium and alkali metal hexafluorotitanates (IV)

Pyridinium hexafluorotitanate (IV) has been prepared by a one step procedure. Addition of titanium tetrachloride to pyridinium poly(hydrogen fluoride) yields nearly quantitative amounts of pyridinium hexafluorotitanate(IV). Making use of pyridinium hexafluorotitanate as precursor, ammonium and alkali metal (Na, K, Rb, and Cs) hexafluorotitanates have been prepared in good yields. These salts have been characterised by IR, N.M.R. (1H, 13C and 19F), X-ray powder diffraction data and chemical analysis.

Synthesis and Characterization of Carbon-Coated LiNi1/3Co1/3Mn1/3O2 in a Single Step by an Inverse Microemulsion Route

Layered LiNi1/3Co1/3Mn1/3O2, which is isostructural to LiCoO2, is considered as a potential cathode material. A layer of carbon coated on the particles improves the electrode performance, Which is attributed to an increase of the grain connectivity and also to protection of metal oxide from chemical reaction. The present work involves in situ synthesis of carbon-coated submicrometer-sized particles of LiNi1/3Co1/3Mn1/3O2 in an inverse microemulsion medium in the presence of glucose. The precursor obtained from the reaction is heated in air at 900 degrees C for 6 h to get crystalline LiNi1/3Co1/3Mn1/3O2. The carbon coating is found to impart porosity as well as higher surface area in relation to bare samples of the compound. The electrochemical characterization studies provide that carbon-coated LiNi1/3Co1/3Mn1/3O2 samples exhibit improved rate capability and cycling performance. The carbon coatings are shown to suppress the capacity fade, which is normally observed for the bare compound. Impedance spectroscopy data provide additional evidence for the beneficial effect of a carbon coating on LiNi1/3Co1/3Mn1/3O2 particles.

A Convenient Route for the Synthesis of Complex Metal Oxides Employing Solid-Solution Precursors

Synthesis of complex metal oxides by the thermal decomposition of solid-solution precursors (formed by isomorphous compounds of component metals) has been investigated since the method enables mixing of cations on an atomic scale and drastically reduces diffusion distances to a few angstroms. Several interesting oxides such as Ca2Fe03,5C, aCoz04,C a2C0205a, nd Ca,FeCo05 have been prepared by this technique starting from carbonate solid solutions of the type Ca,-,Fe,C03, Cal-,Co,C03, and Ca,-,,M,M'yC03 (M, M' = Mn, Fe, Co). The method has been extended to oxalate solid-solution precursors, and the possibility of making use of other kinds of precursor solid solutions is indicated.

Delamination of Surfactant-Intercalated Brucite-Like Hydroxy Salts of Cobalt and Copper and Solvothermal Decomposition of the Resultant Colloidal Dispersions

Surfactant anion intercalated hydroxy salts of copper and cobalt of the formula M(OH)(2-x)(surf)(x)center dot mH(2)O [M = Cu, Co; surf = dodecyl sulfate. dodecyl benzene sulfonate. and x = 0.5 for Cu and 0.67 for Co] delaminate readily in 1-butanol to give translucent colloidal dispersions that are stable for months. The extent of delamination and the colloidal dispersion observed in these solids is higher than what had been observed for layered double hydroxides. The dispersions yield the corresponding nanoparticulate oxides on solvothermal decomposition. While the copper hydroxy salt forms similar to 300 nm dendrimer-like CuO nanostructures comprising nanorods of similar to 10 nm diameter, the cobalt analogue forms similar to 20 nm superparamagnetic particles of Co3O4.

Dielectric anomaly in Li-doped zinc oxide thin films grown by sol-gel route

Sol-gel route was employed to grow polycrystalline thin films of Li-doped ZnO thin films (Zn1-xLixO, x=0.15). Polycrystalline films were obtained at a growth temperature of 400-500 degrees C. Ferroelectricity in Zn0.85Li0.15O was verified by examining the temperature variation of the real and imaginary parts of dielectric constant, and from the C-V measurements. The phase transition temperature was found to be 330 K. The room-temperature dielectric constant and dissipation factor were 15.5 and 0.09 respectively, at a frequency of 100 kHz. The films exhibited well-defined hysteresis loop, and the values of spontaneous polarization (P-s) and coercive field were 0.15 mu C/cm(2) and 20 kV/cm, respectively, confirming the presence of ferroelectricity.

Link route pricing for enhanced QoS

Pricing is an effective tool to control congestion and achieve quality of service (QoS) provisioning for multiple differentiated levels of service. In this paper, we consider the problem of pricing for congestion control in the case of a network of nodes under multiple service classes. Our work draws upon [1] and [2] in various ways. We use the Tirupati pricing scheme in conjunction with the stochastic approximation based adaptive pricing methodology for queue control (proposed in [1]) for minimizing network congestion. However, unlike the methodology of [1] where pricing for entire routes is directly considered, we consider prices for individual link-service grade tuples. Further, we adapt the methodology proposed in [21 for a single-node scenario to the case of a network of nodes, for evaluating performance in terms of price, revenue rate and disutility. We obtain considerable performance improvements using our approach over that in [1]. In particular, our approach exhibits a throughput improvement in the range of 54 to 80 percent in all cases studied (over all routes) while exhibiting a lower packet delay in the range of 26 to 38 percent over the scheme in [1].

Structure and optical properties of Cd-substituted ZnO (Zn1-xCdxO) nanostructures synthesized by the high-pressure solution route

We report the synthesis of Cd-substituted ZnO nanostructures (Zn1-xCdxO with x up to approximate to 0.09) by the high-pressure solution growth method. The synthesized nanostructures comprise nanocrystals that are both particles (similar to 10-15 nm) and rods which grow along the [002] direction as established by transmission electron microscope (TEM) and x-ray diffraction (XRD) analysis. Rietveld analysis of the XRD data shows a monotonic increase of the unit cell volume with the increase of Cd concentration. The optical absorption, as well as the photoluminescence (PL), shows a red shift on Cd substitution. The line width of the PL spectrum is related to the strain inhomogeneity and it peaks in the region where the CdO phase separates from the Zn1-xCdxO nanostructures. The time-resolved photoemission showed a long-lived (similar to 10 ns) component. We propose that the PL behaviour of the Zn1-xCdxO is dominated by strain in the sample with the red shift of the PL linked to the expansion of the unit cell volume on Cd substitution.

A simple single-source precursor route to the nanostructures of AIN, GaN and InN

In an effort to find a simple and common single-source precursor route for the group 13 metal nitride semiconductor nanostructures, the complexes formed by the trichlorides of Al, Ga and In with urea have been investigated. The complexes, characterized by X-ray crystallography and other techniques, yield the nitrides on thermal decomposition. Single crystalline nanowires of AlN, GaN and InN have been deposited on Si substrates covered with Au islands by using the complexes as precursors. The urea complexes yield single crystalline nanocrystals under solvothermal conditions. The successful synthesis of the nanowires and nanocrystals of these three important nitrides by a simple single-precursor route is noteworthy and the method may indeed be useful in practice.

Structure and optical properties of Cd-substituted ZnO (Zn1-xCdxO) nanostructures synthesized by the high-pressure solution route

We report the synthesis of Cd-substituted ZnO nanostructures (Zn1-xCdxO with x up to approximate to 0.09) by the high-pressure solution growth method. The synthesized nanostructures comprise nanocrystals that are both particles (similar to 10-15 nm) and rods which grow along the [002] direction as established by transmission electron microscope (TEM) and x-ray diffraction (XRD) analysis. Rietveld analysis of the XRD data shows a monotonic increase of the unit cell volume with the increase of Cd concentration. The optical absorption, as well as the photoluminescence (PL), shows a red shift on Cd substitution. The line width of the PL spectrum is related to the strain inhomogeneity and it peaks in the region where the CdO phase separates from the Zn1-xCdxO nanostructures. The time-resolved photoemission showed a long-lived (similar to 10 ns) component. We propose that the PL behaviour of the Zn1-xCdxO is dominated by strain in the sample with the red shift of the PL linked to the expansion of the unit cell volume on Cd substitution.