Micro-Raman imaging of Te precipitates in CdZnTe (Zn similar to 4%) crystals

Micro-Raman imaging of the distribution of Te precipitates in CdZnTe crystals in different phases is reported. For the normal phase of Te precipitates, the Raman modes appear centered around 121(A1), 141(E)/TO(CdTe) cm−1 and a weak mode around 92(E) cm−1 in CdZnTe indicating the presence of trigonal lattice of Te. Under high pressure phase, the volume of Te precipitates collapses, giving more bond energy resulting in the blueshift of the corresponding Raman bands. Also, the spatial distribution of the area ratio of 121 to 141 cm−1 Raman modes is used to quantify Te precipitates. Further, near-infrared microscopy images support these results.

Quality assessment of CdZnTe (Zn similar to 4 %) crystals

We have studied the as grown and annealed CdZnTe (Zn similar to 4 %) crystals for the assessment of their crystalline quality. As grown crystals suffer from tellurium precipitates and cadmium vacancies, which are inherent, due to retrograde solid solubility curve in the phase diagram. This is reflected in the Fourier transform infrared (FTIR) spectra over the 400 - 4500 cm(-1) range by a strong absorption around 2661 cm(-1) which corresponds to the band gap of tellurium confirming their presence, where-as a monotonic decrease in the transmission with the decrease in wave number indicates the presence of cadmium vacancies. Obviously the presence of Cd vacancies lead to the formation of tellurium precipitates confirming their presence. Annealed samples under cadmium + zinc ambient at 650 degrees C for 6 hours show an improvement in the transmission over the same range. This can be attributed to thermo-migration of tellurium precipitates and hence bonding with Cd or Zn to form CdZnTe. This is further supported by the reduced full width at half maximum in the X-ray diffraction rocking curve of these CdZnTe crystals. Cadmium annealing although can passivate Cd vacancy related defects and reduce the Te precipitates, as is observed in our low temperature Photoluminescence (PL) spectra, alone may not be sufficient possibly due to the loss of Zn. Vacuum annealing at 650 degrees C for 6 hours further deteriorated the material quality as is reflected in the low temperature PL spectra by the introduction of a new defect band around 0.85 eV and reduced IR transmission.

Coexistence of para and ferromagnetic phases of Fe3+ in undoped CdZnTe (Zn similar to 4%) crystals

The signatures of the coexistence of para and ferromagnetic phases for the Fe3+ charge state of iron have been identified in the low temperature electron spin resonance (ESR) spectra in undoped CdZnTe (Zn similar to 4%) crystals and independently verified by superconducting quantum interference device (SQUID) and AC susceptibility measurements. In the paramagnetic phase the inverse of AC susceptibility follows the Curie-Weiss law. In the ferromagnetic phase the thermal evolution of magnetization follows the well-known Bloch T-3/2 law. This is further supported by the appearance of hysteresis in the SQUID measurements at 2 K below T-c which is expected to lie in between 2 and 2.5 K. (C) 2010 Elsevier Ltd. All rights reserved.