Preparation of the layered double hydroxide (LDH) LiAl2(OH)(7)center dot 2H(2)O, by gel to crystallite conversion and a hydrothermal method, and its conversion to lithium aluminates

A layered double hydroxide (LDH) with chemical composition LiAl2(OH)(7) . 2H(2)O was prepared via a wet chemical route of gel to crystallite (G-C) conversion at 80 degrees C involving the reaction of hydrated alumina gel, Al2O3.yH(2)O (80 < y < 120) with LiOH (Li2O/Al2O3 greater than or equal to 0.5) in presence of hydrophilic solvents such as ethanol under refluxing conditions. The hydrothermal synthesis was carried out using the same reactants by heating to less than or equal to 140 degrees C in a Teflon-lined autoclave under autogenerated pressure (less than or equal to 20 MPa). Transmission electron microscopy showed needle-shaped aggregates of size 0.04-0.1 mu m for the gel to crystallite conversion product, whereas the hydrothermal products consisted of individual lamellar crystallites of size 0.2-0.5 mu m with hexagonal morphology. The LDH prepared through the gel to crystallite conversion could be converted into LiAl(OH)(4) . H2O or LiAl(OH)(3)NO3 . H2O by imbibition of LiOH or LiNO3, respectively, under hydrothermal conditions. Thermal decomposition of LDH above 1400 degrees C gave rise to LiAl5O8 accompanied by the evaporation of Li2O. LiAl(OH)(4) . H2O and LiAl(OH)(3)NO3 . H2O decomposed in the temperature range 400-1000 degrees C to alpha- or beta-LiAlO2. The compositional dependence of the product, the intermediate phases formed during the heat treatment and the possible reactions involved are described in detail.

Rare-earth carboxylates, Ln(2)(III)(mu(3)-OH)(C4H4O5)(2)(C4H2O4)]center dot 2H(2)O Ln = Ce, Pr and Nd]: synthesis, structure and properties

A new series of inorganic-organic hybrid framework compounds, Ln(2)(mu(3)-OH)(C4H4O5)(2)(C4H2O4)]center dot 2H(2)O, (Ln = Ce, Pr and Nd), have been prepared employing a hydrothermal method. Malic acid and fumaric acid form part of the structure. The malate units connect the lanthanide centers forming Ln-O-Ln two-dimensional layers, which are cross-linked by the fumarate units forming the three-dimensional structure. Extra framework water molecules form a dimer and occupy the channels. The water molecules can be reversibly adsorbed. The dehydrated structure did not show any differences in framework structure/ connectivity. The presence of lattice water provides a pathway for proton conductivity. Optical studies suggest an up-conversion behavior involving more than one photon for a neodymium compound.

Synthesis of layered MoOPO4 center dot 2H(2)O and investigation of its intercalation chemistry

We describe in this paper the synthesis and characterization of a new layered phosphate, MoOPO4 . 2H(2)O (I), and its intercalation chemistry. The phosphate I, crystallizing in a tetragonal structure (a = 6.375(7), c = 7.80(1) Angstrom, and Z = 2) similar to that of VOPO4 . 2H(2)O, has been synthesized by the reduction of MoO2(HPO4). H2O (II) using ethylene glycol in an CH3CN medium at similar to 60 degrees C. Interestingly, I could be readily oxidized back to II using Br-2 in CH3CN at room temperature. Considering the close structural relationship existing between I and II, it is likely that the reduction and oxidation of the phosphates proceed by a topotactic mechanism. I is a novel layered host intercalating a variety of organic bases such as n-alkylamines, pyridine, and aniline, mainly through an acid-base interaction. Unlike VOPO4 . 2H(2)O, I does not exhibit reductive intercalation reactivity.

High microwave susceptibility of NaH2PO4 center dot 2H(2)O: Rapid synthesis of crystalline and glassy phosphates with NASICON-type chemistry

High microwave susceptibility of NaH2PO4 . 2H(2)O has been discovered, This hydrated acid phosphate of sodium can be heated upto 1000 K or more when exposed to 2.45 GHz microwaves. Using this, a novel microwave-assisted preparation of a number of important crystalline and glassy materials with NASICON-type chemistry has been accomplished in less than 8 min which is only a fraction of the time required for conventional synthetic procedures, The present single-shot approach to the preparation of phosphates is attractive in terms of its simplicity, rapidity, and general applicability, A ''step-ladder'' heating mechanism has been proposed to account for the high microwave absorbing ability of NaH2PO4 . 2H(2)O.

Microwave spectrum and structure of C(6)H(5)CCH center dot center dot center dot H(2)S complex

Rotational spectra of C(6)H(5)CCH center dot center dot center dot H(2)S, C(6)H(5)CCH center dot center dot center dot H(2)(34)S, C(6)H(5)CCH center dot center dot center dot HDS, C(6)H(5)CCH center dot center dot center dot D(2)S and C(6) H(5)CCD center dot center dot center dot H(2)S complexes have been observed using a pulsed nozzle Fourier transform microwave spectrometer. The observed spectrum is consistent with a structure in which hydrogen sulfide is located over the phenyl ring pi cloud and the distance between the centers of masses of the two monomers is 3.74 +/- 0.01 angstrom. In the complex, the H(2)S unit is shifted from the phenyl ring center towards the acetylene group. The vibrationally averaged structure has an effective Cs symmetry. Ab initio calculations were performed at MP2/aug-cc-pVDZ level of theory to locate the possible geometries of the complex. The calculations reveal the experimentally observed structure to be more stable than a coplanar arrangement of the monomers, which was observed for the C(6)H(5)CCH center dot center dot center dot H(2)O complex. Atoms in molecule theoretical analysis shows the presence of S-H center dot center dot center dot pi hydrogen bond. For the parent isotopologue, each transition frequency was found to split into two resulting from an interchange of the equivalent hydrogens of H(2)S unit in the complex. (C) 2011 Elsevier Inc. All rights reserved.

Microwave spectroscopic and theoretical studies on the phenylacetylene center dot center dot center dot H(2)O complex: C-H center dot center dot center dot O and O-H center dot center dot center dot pi hydrogen bonds as equal partners

Rotational spectra of five isotopologues of the title complex, C(6)H(5)CCH center dot center dot center dot H(2)O, C(6)H(5)CCH center dot center dot center dot HOD, C(6)H(5)CCH center dot center dot center dot D(2)O, C(6)H(5)CCH center dot center dot center dot H(2)(18)O and C(6)H(5)CCD center dot center dot center dot H(2)O, were measured and analyzed. The parent isotopologue is an asymmetric top with kappa = -0.73. The complex is effectively planar (ab inertial plane) and both `a' and `b' dipole transitions have been observed but no c dipole transition could be seen. All the transitions of the parent complex are split into two resulting from an internal motion interchanging the two H atoms in H(2)O. This is confirmed by the absence of such doubling for the C(6)H(5)CCH center dot center dot center dot HOD complex and a significant reduction in the splitting for the D(2)O analog. The rotational spectra, unambiguously, reveal a structure in which H(2)O has both O-H center dot center dot center dot pi (pi cloud of acetylene moiety) and C-H center dot center dot center dot O (ortho C-H group of phenylacetylene) interactions. This is in agreement with the structure deduced by IR-UV double resonance studies (Singh et al., J. Phys. Chem. A, 2008, 112, 3360) and also with the global minimum predicted by advanced electronic structure theory calculations (Sedlack et al., J. Phys. Chem. A, 2009, 113, 6620). Atoms in Molecule (AIM) theoretical analysis of the complex reveals the presence of both O-H center dot center dot center dot pi and C-H center dot center dot center dot O hydrogen bonds. More interestingly, based on the electron densities at the bond critical points, this analysis suggests that both these interactions are equally strong. Moreover, the presence of both these interactions leads to significant deviation from linearity of both hydrogen bonds.

Synthesis, structure and magnetic properties of the polyoxovanadate cluster Zn-2(NH2(CH2)(2)NH2)(5)]{Zn(NH2(CH2)(2)NH2)(2)}(2){V18O42(H2O)\ ]center dot xH(2)O (x similar to 12), possessing a layered structure

A hydrothermal reaction of a mixture of ZnCl2, V2O5, ethylenediamine and water gave rise to a layered poly oxovanadate material. clusters. These clusters, with all the vanadium ions in the +4 state, are connected together through Zn(NH2(CH2)(2)NH2)(2) linkers forming a two-dimensional structure. The layers are also separated by distorted trigonal bipyramidal [Zn-2(NH2(CH2)(2)NH2)(5)] complexes. The Structure, thus, presents a dual role for the Zn-ethylenediamine complex. The magnetic susceptibility studies indicate that the interactions between the V centres in I are predominantly antiferromagnetic in nature and the compound shows highly frustrated behaviour. The magnetic properties are compared to the theoretical calculations based oil the Heisenberg model, in addition to correlating to the structure. Crystal data for the complexes are presented.

Synthesis and electrical properties of the (PVA)(0.7)(Kl)(0.3)center dot xH(2)SO(4) (0 <= x <= 5) polymer electrolytes and their performance in a primary Zn/MnO2 battery

Solid acid polymer electrolytes (SAPE) were synthesised using polyvinyl alcohol, potassium iodide and sulphuric acid in different molar ratios by solution cast technique. The temperature dependent nature of electrical conductivity and the impedance of the polymer electrolytes were determined along with the associated activation energy. The electrical conductivity at room temperature was found to be strongly depended on the amorphous nature of the polymers and H2SO4 concentration. The ac (100 Hz to 10 MHz) and dc conductivities of the polymer electrolytes with different H2SO4 concentrations were analyzed. A maximum dc conductivity of 1.05 x 10(-3) S cm(-1) has been achieved at ambient temperature for electrolytes containing 5 M H2SO4. The frequency and temperature dependent dielectric and electrical modulus properties of the SAPE were studied. The charge transport in the present polymer electrolyte was obtained using Wagner's polarization technique, which demonstrated the charge transport to be mainly due to ions. Using these solid acid polymer electrolytes novel Zn/SAPE/MnO2 solid state batteries were fabricated and their discharge capacity was calculated. An open circuit voltage of 1.758V was obtained for 5 M H2SO4 based Zn/SAPE/MnO2 battery. (C) 2010 Elsevier Ltd. All rights reserved.

H-1 MAS NMR study of protonic conduction in layered HNbWO6 center dot xH(2)O (x=1.5, 0.5)

H-1 Magic Angle Spinning (MAS) NMR of layered HNbWO6 . xH(2)O (x = 1.5, 0.5) is carried out at room temperature and at various spinning speeds (1-12 kHz). Results on the fully hydrated sample (x = 1.5) are consistent with the model of diffusion of H3O+ ions within the layers. In the partially dehydrated sample (x = 0.5) an exchange between the distinctly present cage protons and H3O+ protons leads to protonic conduction.

Synthesis of acicular hydrogoethite (alpha-FeOOH center dot xH(2)O; 0.1 < x < 0.22) particles using morphology controlling cationic additives and magnetic properties of maghemite derived from hydrogoethite

A method for the preparation of acicular hydrogoethite (alpha -FeOOH.xH(2)O, 0.1 < x < 0.22) particles of 0.3-1 mm length has been optimized by air oxidation of Fe( II) hydroxide gel precipitated from aqueous (NH4)(2)Fe(SO4)(2) solutions containing 0.005-0.02 atom% of cationic Pt, Pd or Rh additives as morphology controlling agents. Hydrogoethite particles are evolved from the amorphous ferrous hydroxide gel by heterogeneous nucleation and growth. Preferential adsorption of additives on certain crystallographic planes thereby retarding the growth in the perpendicular direction, allows the particles to acquire acicular shapes with high aspect ratios of 8-15. Synthetic hydrogoethite showed a mass loss of about 14% at similar to 280 degreesC, revealing the presence of strongly coordinated water of hydration in the interior of the goethite crystallites. As evident from IR spectra, excess H2O molecules (0.1- 0.22 per formula unit) are located in the strands of channels formed in between the double ribbons of FeO6 octahedra running parallel to the c- axis. Hydrogoethite particles constituted of multicrystallites are formed with Pt as additive, whereas single crystallite particles are obtained with Pd (or Rh). For both dehydroxylation as well as H-2 reduction, a lower reaction temperature (similar to 220 degreesC) was observed for the former (Pt treated) compared to the latter (Pd or Rh) (similar to 260 degreesC). Acicular magnetite (Fe3O4) was prepared either by reducing hydrogoethite (magnetite route) or dehydroxylating hydrogoethite to hematite and then reducing it to magnetite (hematite- magnetite route). According to TEM studies, preferential dehydroxylation of hydrogoethite along < 010 > leads to microporous hematite. Maghemite (gamma -Fe2O3 (-) (delta), 0 < < 0.25) was obtained by reoxidation of magnetite. The micropores are retained during the topotactic transformation to magnetite and finally to maghemite, whereas cylindrical mesopores are formed due to rearrangement of the oxygen sublattice from hexagonal to cubic close packing during the conversion of hydrogoethite to magnetite and then to maghemite. Accordingly, three different types of maghemite particles are realized: strongly oriented multicrystalline particles, single crystalline acicular particles with micropores or crystallites having mesopores. Higher values of saturation magnetization ((s) = 74 emu g(-1)) and coercivity (H-c = 320 Oe) are obtained for single crystalline mesoporous particles. In the other cases, the smaller size of particles and larger distribution of micropores decreases sigma (s) considerably ( < 60 emu g(-1)) due to relaxation effects of spins on the surface atoms as revealed by Mossbauer spectroscopy.

Am unexpected entry into the silver(I) chemistry of diphosphazane ligands: Crystal and molecular structures of [Ag{Ph2PN(Pr-i)PPh2}(CF3SO3)](2), [Ag{Ph2PN(Pr-i)PPh(OC6H3Me2-2,6)}(2)]PF6, and [Ag-3(mu-Cl)(2){Ph2PN(R)PPh2}(3)]PF6 (R = H, Pr-i)

Mononuclear, binuclear and trinuclear silver(l) complexes were obtained unexpectedly while probing the reactivity of diphosphazane ligands of the type X2PN(Pr-i)PXY towards the ruthenium-based precursor Ru(bipy)(2)Cl-2 center dot 2H(2)O, in the presence of a silver salt as a chloride scavenger. Subsequently, the reactions of AgX [X = Cl, NO3 or CF3SO3] with Ph2PN(R)PPh(Y) [R = H, Y = Ph; R = Pr-i, Y = Ph or OC6H3Me2-2,6] in a 1: 1 or 1:2 molar ratio have been investigated. Mononuclear or binuclear Ag(I) complexes containing either chelating or bridging diphosphazane ligands are obtained. Trinuclear silver(l) complexes are accessible by the treatment of diphosphazane ligands, Ph2PN(R)PPh2 [R = H, Pr-i] with AgCl using piperidine as the solvent. In the presence of a suitable chloride donor species, the mononuclear and binuclear complexes of Ph2PN(Pr-i)PPh2 are transformed slowly to the trinuclear complex [Ag-3(mu-Cl)(2){Ph2PN(Pr-i)PPh2}(3)]X, over a period 20 h. The structures of representative complexes have been confirmed by X-ray crystallography and the salient structural features are discussed

Stepwise Crystallization: Illustrative Examples of the Use of Metalloligands Cu-6(mna)(6)](6-) and (Ag-6(Hmna)(2)(mna)(4)](4-) (H(2)mna=2-Mercapto Nicotinic Acid) in the Formation of Heterometallic Two- and Three-Dimensional Assemblies with brucite, pcu, and sql Topologies

Three new inorganic coordination polymers, {Mn(H2O)(6)]-Mn-2(H2O)(6)](Cu-6(mna)(6)]center dot 6H(2)O}, 1, {Mn-4(OH)(2)(H2O)(10)] (Cu-6(mna)6]center dot 8H(2)O}, 2, and {Mn-2(H2O)(5)]Ag-6(Hmna)(2)(mna)(4)]center dot 20H(2)O}, 3, have been synthesized at room temperature through a sequential crystallization route. In addition, we have also prepared and characterized the molecular precursor Cu-6(Hmna)(6)]. Compounds 1 and 3 have a two-dimensional structure, whereas 2 has a three-dimensional structure. The formation of 2 has been achieved by minor modification in the synthetic composition, suggesting the subtle relationship between the reactant composition and the structure. The hexanudear copper and silver duster cores have Cu center dot center dot center dot Cu and Ag center dot center dot center dot Ag distances close to the sum of the van der Waals radii of Cu1+ and Ag1+, respectively. The connectivity between Cu-6(mna)(6)](6-) cluster units and Mn2+ ions gives rise to a brucite related layer in 1 and a pcu-net in 2. The Ag-6(Hmna)(2)(mna)(4)](4-) cluster in 3, on the other hand, forms a sql-net with Mn2+. Compound 1 exhibits an interesting and reversible hydrochromic behavior, changing from pale yellow to red, on heating at 70 degrees C or treatment under a vacuum. Electron paramagnetic resonance studies indicate no change in the valence states, suggesting the color change could be due to changes in the coordination environment only. The magnetic studies indicate weak antiferromagnetic behavior. Proton conductivity studies indicate moderate proton migrations in 1 and 3. The present study dearly establishes sequential crystallization as an important pathway for the synthesis of heterometallic coordination polymers.

Self-assembly of three new coordination complexes: Formation of 2-D square grid, 1-D chain and tape structures

Three distinct coordination complexes, viz., [Co(imi)(2)(tmb)(2)] (1) [where imi = imidazole], {[Ni(tmb)(2)(H2O)(3)]center dot 2H(2)O}(n) (2) and [Cu-2(mu-tmb)(4)(CH3OH)(2)] (3), have been synthesized hydrothermally by the reactions of metal acetates,2,4,6-trimethylbenzoic acid (Htmb) and with or without appropriate amine. The Ni analogue of 1 and the Co analogue of 2 have also been synthesized. X-ray single-crystal diffraction suggests that complex 1 represents discrete mononuclear species and complex 2 represents a 1D chain coordination polymer in which the Ni(H) ions are connected by the bridging water molecules. Complex 3 represents a neutral dinuclear complex. In 1, the central metal ions are associated by the carboxylate moiety and imidazole ligands, whereas the central metal atom is coordinated to the carboxylate moiety and the respective solvent molecules in 2 and 3. In 3, the four 2,4,6-trimethylbenzoate moieties act as a bridge connecting two copper (11) ions and the 0 atoms of methanol coord geometry, with the methanol molecule at the apical position. In all the three structures the central metal atom sits on a crystallographic inversion centre. In all the cases, the coordination entities are further organized via hydrogen bonding interactions to generate multifarious supramolecular networks. Complexes 1, 2 and 3 have also been characterized by spectroscopic (UV/Vis and IR) and thermal analysis (TGA). In addition, the complexes were found to exhibit antimicrobial activity. The magnetic susceptibility measurements, measured from 8 to 300 K, revealed antiferromagnetic interactions between the Co(II) ions in compound 1 and the Ni(II) ions in la, respectively.

Time- and Temperature-Dependent Study in the Three-Component Zinc-Triazolate-Oxybis(benzoate) System: Stabilization of New Topologies

Three new three-dimensional zinc-triazolate-oxybis(benzoate) compounds. [{Zn-3(H2O)(2)}{C12H8O(COO)(2)}(2)-{C2H2N3}(2)]center dot 2H(2)O(I), [Zn-7{C12H8O(COO)(2)}(4){C2H2N3}(6)]center dot H2O, (II), and[{Zn-5(OH)(2)}{C12H8O(COO)(2)}(3){C2H2N3}(2)] (III), synthesized by a hydrothermal reaction of a mixture of Zn(OAc)(2)center dot 2H(2)O, 4,4'-oxybis(benzoic acid), 1,2,4-triazole, NaOH, and water. Compound I has an interpenetrated diamond structure and II and III have pillared-layer related structures. The formation of a hydrated phase (I) at low temperature and a completely dehydrated phase (III) at high temperature suggests the importance of thermodynamic factors in the formation of three compounds. Transformation studies of I in the presence of water shows the formation of a simple Zn-OBA compound, [Zn(OBA)(H2O)] (IV), at 150 and 180 degrees C and compound III at 200 degrees C. The compounds have been characterized by single-crystal X-ray diffraction, powder X-ray diffraction. thermogravimetric analysis, IR, and photoluminescence studies.