High-Tc superconductivity in the Er---Ba---Cu---O and related systems

ErBa2Cu3O7 and Er0.5Y0.5Ba2Cu3O7 are both high-Tc superconductors attaining zero resistance above 80 K. Preliminary studies indicate that Yb1−xYxBa2Cu3O7 also exhibits zero resistance above 77 K.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

High-temperature superconductivity in the 100 K region in perovskite-related oxides of the Ln-Ba-Cu-O (Ln=Y or La) system

Oxides of the Y-Ba-Cu-O system are found to show onset of superconductivity in the 100–120 K region.

Hydrothermal preparation of Ba(Ti,Zr)O3 fine powders

Fine powders consisting of aggregated submicron crystallites of Ba(Ti,Zr)O3 in the complete range of Ti/Zr ratios are prepared at 85–130°C by hydrothermal method, starting from TiO2 + ZrO2 · xH2O mixed gel and Ba(OH)2 solution. The products obtained below 110°C incorporate considerable amounts of H2O and OH− within the lattice. As-prepared BaTiO3 is cubic and converts to tetragonal phase after the heat treatment at 1200°C, accompanied by the loss of residual hydroxyl ions. TEM investgations of the growth features show a transformation of the gel to the crystallite. Ba2+ ions entering the gel produce chemical changes within the gel, followed by dehydration, resulting in a cubic perovskite phase irrespective of Ti/Zr. The sintering properties of these powders to fine-grained, high density ceramics and their dielectric properties are presented.

Hydrothermal synthesis of Ba(Ti, Sn)O3 fine powders and dielectric properties of the corresponding ceramics

Fine powders of submicron-sized crystallites of BaTiO3 were prepared at 85–130°C by the hydrothermal method, starting from TiO2.ξH2O gel and Ba(OH)2 solution. The products obtained below 110°C incorporated considerable amounts of H2O and OH− in the lattice. As-prepared BaTiO3 is cubic and converts to the tetragonal phase after heat treatment at 1200°C, accompanied by the loss of residual OH− ions. Hydrothermal reaction of SnO2.ξH2O gel with Ba(OH)2 at 150–260°C gives rise to the hydrated phase, BaSn(OH)6.3H2O, due to the amphoteric nature of SnO2.ξH2O which stabilises Sn(OH)62− anions in basic media. On heating in air or releasing the pressure in situ at 260°C, BaSn(OH)6.3H2O converts to BaSnO3 through an intermediate, BaSnO(OH)4. Solid solutions of Ba(Ti,Sn)O3 are directly formed from (TiO2 + SnO2)..ξH2O gel up to 35 mol% SnO2. At higher Sn contents, the hydrothermal products are mixtures of BaSn(OH)6.3H2O and BaTiO3, which on annealing at 1000°C result in monophasic Ba(Ti,Sn)O3. The sintering characteristics and the dielectric properties of the ceramics prepared out of these fine powders are presented. The dielectric properties of fine-grained Ba(Ti,Sn)O3 ceramics are explained on the basis of the prevailing diffuse phase transition behaviour.

TlCaBa2Cu2O7: The 1122 (90 K) superconductor in the new Tl(Ca,Ba)n+1CunO2n+3 seriesstar, open

The 1122 (n=2) member of the Tl(Ca,Ba)n+1CunO2n+3 series containing a single Tl-O layer is shown to be associated with a Tc of 90 K. This value of Tc is significantly lower than that of the 2122 phase (Tcnot, vert, similar110 K) with two Tl-O layers.

Precipitation of rutile and anatase (Tio12) fine powders and their conversion to MTiO3 (M = Ba, Sr, Ca) by the hydrothermal method

Fine powders of TiO2 (rutile) with high degree of crystallinity are formed from aqueous titanium oxychloride solution under hydrothermal conditions at 160–230°C and 15–100 kg/cm2 for 1–2 hours. The anatase phase is produced from the same medium when sulfate ion impurity is present, with Image . Both these fine powders are converted to BaTiO3, SrTiO3 or CaTiO3 when suspended in Ba(OH)2 or Sr(OH)2 solution or in an aqueous slurry of carbonate-free CaO with Image , at 180–280°C and 12–65 kg/cm2 for 4–8 hours. The resulting fine powders contain monocrystallites of the perovskite phase with 0.1–1.5 μm particle size.

Separation of sulfur-containing components of transfer ribonucleic acid on Bio-Gel P-2 and Sephadex G-10 columns

S-Labeled nucleosides of E. coli tRNA and some of the derivatives of thionucleosides were separated on Bio-Gel P-2 and Sephadex G-10 columns employing buffers of low salt concentration and high pH.

Highly biocompatible and water-dispersible, amine functionalized magnetite nanoparticles, prepared by a low temperature, air-assisted polyol process: a new platform for bio-separation and diagnostics

A low temperature polyol process, based on glycolaldehyde mediated partial reduction of FeCl3 center dot 6H(2)O at 120 degrees C in the presence of sodium acetate as an alkali source and 2,2'-(ethylenedioxy)-bis-(ethylamine) as an electrostatic stabilizer has been used for the gram-scale preparation of biocompatible, water-dispersible, amine functionalized magnetite nanoparticles (MNPs) with an average diameter of 6 +/- 0.75 nm. With a reasonably high magnetization (37.8 e.m.u.) and amine groups on the outer surface of the nanoparticles, we demonstrated the magnetic separation and concentration implications of these ultrasmall particles in immunoassay. MRI studies indicated that these nanoparticles had the desired relaxivity for T-2 contrast enhancement in vivo. In vitro biocompatibility, cell uptake and MR imaging studies established that these nanoparticles were safe in clinical dosages and by virtue of their ultrasmall sizes and positively charged surfaces could be easily internalized by cancer cells. All these positive attributes make these functional nanoparticles a promising platform for further in vitro and in vivo evaluations.

Infra-red spectra of crystalline chloroacetates of Cu, Ca, Sr, Ba and Pb

The infra-red spectra of Cu, Ca, Sr, Ba and Pb chloroacetates were studied in order to investigate the effect of co-ordination on the vibration spectra of the ligand. The shifts of the symmetric and antisymmetric COO− vibrational frequencies indicate a bridged structure as the most probable one for the complexes investigated. No linear relationship between the shifts of the COO− stretching frequencies and E/r (where E is the electron excitation energy and r the ionic radius) was observed. No systematic mass effect on these COO− frequencies also could be established.

Dielectric response in pulsed laser ablated (Ba,Sr)TiO3 thin films

The dielectric response of pulsed laser ablated barium strontium titanate thin films were studied as a function of frequency and ambient temperature (from room temperature to 320 degrees C) by employing impedance spectroscopy. Combined modulus and impedance spectroscopic plots were used to study the response of the film, which in general may contain the grain, grain boundary, and the electrode/film interface as capacitive elements. The spectroscopic plots revealed that the major response was due to the grains, while contributions from the grain boundary or the electrode/film interface was negligible. Further observation from the complex impedance plot showed data points lying on a single semicircle, implying the response originated from a single capacitive element corresponding to the bulk grains. Conductivity plots against frequency at different temperatures suggested a response obeying the 'universal power law'. The value of the activation energies computed from the Arrhenius plots of both ac and dc conductivities with 1000/T were 0.97 and 1.04 eV, respectively. This was found to be in excellent agreement with published literature, and was attributed to the motion of oxygen vacancies within the bulk. (C) 2000 American Institute of Physics. [S0021-8979(00)02801-2].

On superconducting Y-Ba-Cu-O films prepared by printing on lumina substrates

This Letter attempts to examine the impact of the chemical interaction of the alumina substrate on the Y-Ba-Cu-O film deposited on it.

Crystal chemistry of a new solid solution in the BaO-Bi2O3-Nb2O5 system: Ba-5x/2-Bi(1-x)5/3Nb5O15

A solid solution of the type Ba5x/2Bi(1-x)5/3Nb5O15 has been identified in the BaO-Bi2O3-Nb2O5 system for the first time. The limits of the solid solution are within the range 0.52 <= x <= 0.80. The compositions x = 0.52, 0.60, 0.72, 0.77, 0.78, and 0.80 were synthesized by the solid-state technique from the starting materials in stoichiometric quantities. The powder X-ray patterns of all the phases in the domain indicate a structural similarity to tetragonal tungsten bronzes (TTBs). The compositions below x = 0.52 and those above x = 0.80 exhibit barium niobate and bismuth niobate impurities, respectively. Single crystals of the composition x = 0.77 were obtained by the melt cooling technique. The crystal structure of Ba3.85/2Bi1.15/3Nb5O15 (x = 0.77) was solved in the tetragonal space group P4bm (No. 100) with a = 12.4938 (14) angstrom, c = 3.9519 (2) A, V = 616.87 (10) angstrom(3), and Z = 2 and was refined to an R index of 0.034. Dielectric measurements on all the phases indicate a typical relaxor behavior with a broad phase transition at T-m approximate to 300 K.