Die Darstellung von Schwefeltetrafluorid aus den Elementen bei tiefer Temperatur in einem inerten Lösungsmittel

Schwefeltetrafluorid läßt sich in reiner Form in einer CCl3F-Lösung durch direkte Fluorierung von elementarem Schwefel bei -78°C in hoher Ausbeute darstellen.

Carbon nanotube mat as substrate for ZnO nanotip field emitters

We have reported the synthesis of ZnO nanotips on a multi walled carbon nanotube (MWCNT) mat by a vapour transport process. This combination of ZnO nanotips and a MWCNT mat exhibit ideal field emission behaviour. The turn on field and threshold field is found to be 0.34 and 1.5 V mu m(-1), respectively. The low threshold field is due to the good adherence of the ZnO nanotips on the MWCNT mat. The field enhancement factor is found to be 5 x 10(2) which is in agreement with the intrinsic field emission factor of ZnO nanotips. The emission current is found to be highly stable even at moderate vacuum.

Effect of magnetic field on Mott's variable-range hopping parameters in multiwall carbon nanotube mat

We report the temperature and magnetic field dependence of the conductivity of multiwall carbon nanotube mat in the temperature range 1.4-150 K and in magnetic fields up to 10 T. It is observed that charge transport in this system is governed by Mott's variable-range hopping of three-dimensional type in the higher temperature range and two-dimensional type in the lower temperature range. Mott's various parameters, such as localization length, hopping length, hopping energy and density of states at the Fermi level are deduced from the variable-range hopping fit. The resistance of the sample decreases with the magnetic field applied in the direction of tube axis of the nanotubes. The magnetic field gives rise to delocalization of states with the well-known consequence of a decrease in Mott's T-0 parameter in variable-range hopping. The application of magnetic field lowers the crossover temperature at which three-dimensional variable-range hopping turns to two-dimensional variable-range hopping. The conductivity on the lower temperature side is governed by the weak localization giving rise to positive magnetoconductance. Finally, a magnetic field-temperature diagram is proposed showing different regions for different kinds of transport mechanism.

Substrate integrated Lead-Carbon hybrid ultracapacitor with flooded, absorbent glass mat and silica-gel electrolyte configurations

Lead-Carbon hybrid ultracapacitors (Pb-C HUCs) with flooded, absorbent-glass-mat (AGM) and silica-gel sulphuric acid electrolyte configurations are developed and performance tested. Pb-C HUCs comprise substrate-integrated PbO2 (SI-PbO2) as positive electrodes and high surface-area carbon with graphite-sheet substrate as negative electrodes. The electrode and silica-gel electrolyte materials are characterized by XRD, XPS, SEM, TEM, Rheometry, BET surface area, and FTIR spectroscopy in conjunction with electrochemistry. Electrochemical performance of SI-PbO2 and carbon electrodes is studied using cyclic voltammetry with constant-current charge and discharge techniques by assembling symmetric electrical-double-layer capacitors and hybrid Pb-C HUCs with a dynamic Pb(porous)/PbSO4 reference electrode. The specific capacitance values for 2 V Pb-C HUCs are found to be 166 F/g, 102 F/g and 152 F/g with a faradaic efficiency of 98%, 92% and 88% for flooded, AGM and gel configurations, respectively.