Evaluation of CaO-CeO2-partially stabilized zirconia thermal barrier coatings

Plasma sprayable powders were prepared from ZrO2-CaO-CeO2 system using an organic binder and coated onto stainless steel substrates previously coated by a bond coat (Ni 22Cr 20Al 1.0Y) using plasma spraying. The coatings exhibited good thermal barrier characteristics and excellent resistance to thermal shock at 1000 degrees C under simulated laboratory conditions (90 half hour cycles without failure) and at 1200 degrees C under accelerated burner rig test conditions (500 2 min cycles without failure). No destabilization of cubic/tetragonal ZrO2 phase fraction occured either during the long hours (45 h cumulative) or the large number of thermal shock tests. Growth of a distinct SiO2 rich region within the ceramic was observed in the specimens thermal shock cycled at 1000 degrees C apart from mild oxidation of the bond coat. The specimens tested at 1200 degrees C had a glassy appearance on the top surface and exhibited severe oxidation of the bond coat at the ceramic-bond coat interface. The glassy appearance of the surface is due to the formation of a liquid silicate layer attributable to the impurity phase present in commercial grade ZrO2 powder. These observations are supported by SEM analysis and quantitative EDAX data.

Rb2Cd3(SO4)(3)(OH)(2)center dot H2O: structural stability at 500 K

The title compound, dirubidium tricadmium tris(sulfate) dihydroxide dihydrate, consists of sheets of CdO6 octahedra and sulfate tetrahedra propagating in the (100) plane, with Rb+ ions in the interlayer positions. It is isostructural with K2Co3(SO4)(3)(OH)(2)(.)2H(2)O.

Solution combustion synthesis of gamma(L)-Bi(2)MoO(6) and photocatalytic activity under solar radiation

The facile method of solution combustion was used to synthesize gamma(L)-Bi(2)MoO(6). The material was crystallized in a purely crystalline orthorhombic phase with sizes varying from 300 to 500 nm. Because the band gap was 2.51 eV, the degradation of wide variety of cationic and anionic dyes was investigated under solar radiation. Despite the low surface area (< 1 m(2)/g) of the synthesized material, gamma(L)-Bi(2)MoO(6) showed high photocatalytic activity under solar radiation due to its electronic and morphological properties. (C) 2011 Elsevier Ltd. All rights reserved.

A 0.5-2.0 GHz injection locked oscillator cascade for parallel wideband RF spectrum sensing

An area-efficient, wideband RF frequency synthesizer, which simultaneously generates multiple local oscillator (LO) signals, is designed. It is suitable for parallel wideband RF spectrum sensing in cognitive radios. The frequency synthesizer consists of an injection locked oscillator cascade (ILOC) where all the LO signals are derived from a single reference oscillator. The ILOC is implemented in a 130-nm technology with an active area of . It generates 4 uniformly spaced LO carrier frequencies from 500 MHz to 2 GHz. This design is the first known implementation of a CMOS based ILOC for wide-band RF spectrum sensing applications.

Influence of deposition time on the properties of electrodeposited Cu(In,Al)Se-2 thin films

Cu(In,Al)Se-2 films are grown using single step electrodeposition technique. The film properties are studied by varying the deposition time from 500 to 2000 s. Peaks corresponding to elemental Se and Cu2Se phase started appearing from 1200 s of deposition. The composition is changed significantly after 1500 S. Se concentration increased from 57 to 68% with the increase in the deposition time. The Cu2Se phase is dominant in the films deposited for a duration of 2000 s and the grain size increased from 1.12 to 2.15 mu m in this film. Raman analysis confirmed the presence of Se and Cu2Se phase in C1200. In C1500 and C2000 the spectra showed prominent mode corresponding to Cu2Se. The thickness of the film increased from 0.85 to 2.3 mu m with the increase in the deposition time. All the films showed p-type conductivity and resistivity reduced with increased thickness. (C) 2015 Elsevier Ltd. All rights reserved.