An electron microscopic study of quasicrystals in a quaternary alloy : Mg32(Al, Zn, Cu)49

The discovery of a solid exhibiting m 3 5 point group symmetry by Shechtman et. al. (l) in a rapidly solidified Al-14at%Mn alloy has activated intensive studies of a new class of solids, termed as quasicrystals (2). While the original discovery reported the existence of quasicrystals in AI-Mn. AI-Fe and AI-Cr alloys, subsequent work has revealed their existence in Mg-Zn-Al(3,4), Mg-A]-Cu(5), AI-Mn-Si(6) and Ti-Ni-V(7) alloys (Table l).

Low temperature crystallographic data on Kevlar 49 fibres

Using X-ray diffraction data, the behaviour of Kevlar 49 fibres at low temperatures, up to -100degreesC, has been analysed. During cooling, the basal plane of the monoclinic unit cell shrinks whereas the c- (unique, chain axis) length is not significantly affected. In contrast, in the return heating cycle to ambient temperature, the basal plane expands and contraction occurs along the chain direction. The unit cell registers a reduction in volume in both the cooling and heating cycles. Conspicuously, after a cycle of cooling and heating, the unit cell does not return to its initial volume. (C) 2003 Kluwer Academic Publishers.

Gd1.96-xYxEu0.04O3 (x=0.0, 0.49, 0.98, 1.47, 1.96 mol%) nanophosphors: Propellant combustion synthesis, structural and luminescence studies

Gd1.96-xYxEu0.04O3 (x = 0.0, 0.49, 0.98, 1.47, 1.96 mol%) nanophosphors were synthesized by propellant combustion method at low temperature (400 degrees C). The powder X-ray diffraction patterns of as formed Gd1.96Eu0.04O3 showed monoclinic phase, however with the addition of yttria it transforms from monoclinic to pure cubic phase. The porous nature increases with increase of yttria content. The particle size was estimated from Scherrer's and W-H plots which was found to be in the range 30-40 nm. These results were in well agreement with transmission electron microscopy studies. The optical band gap energies estimated were found to be in the range 5.32-5.49 eV. PL emission was recorded under 305 nm excitation show an intense emission peak at 611 nm along with other emission peaks at 582, 641 nm. These emission peaks were attributed to the transition of D-5(0) —> F-7(J) (J = 0, 1, 2, 3) of Eu3+ ions. It was observed that PL intensity increases with increase of Y content up to x = 0.98 and thereafter intensity decreases. CIE color co-ordinates indicates that at x = 1.47 an intense red bright color can be achieved, which could find a promising application in flat panel displays. The cubic and monoclinic phases show different thermoluminescence glow peak values measured under identical conditions. The response of the cubic phase to the applied dose showed good linearity, negligible fading, and simple glow curve structure than monoclinic phase indicating that suitability of this phosphor in dosimetric applications. (C) 2014 Elsevier B.V. All rights reserved.