Growth and electron effective mass measurements of strained Si and Si0.94Ge0.06 on relaxed Si0.62Ge0.38 buffers grown by rapid thermal chemical vapor deposition

Abstract: We report the growth and the electron cyclotron resonance measurements of n-type Si/Si0.62Ge0.38 and Si0.94Ge0.06/Si0.62Ge0.38 modulation-doped heterostructures grown by rapid thermal chemical vapor deposition. The strained Si and Si0.94Ge0.06 channels were grown on relaxed Si0.62Ge0.38 buffer layers, which consist of 0.6 mu m uniform Si0.62Ge0.38 layers and 0.5 mu m compositionally graded relaxed SiGe layers from 0 to 38% Ge. The buffer layers were annealed at 800 degrees C for 1 h to obtain complete relaxation. A 75 Angstrom Si(SiGe) channel with a 100 Angstrom spacer and a 300 Angstrom 2 X 10(19) cm(-3) n-type supply layer was grown on the top of the buffer layers. The cross-sectional transmission electron microscope reveals that the dense dislocation network is confined to the buffer layer, and relatively few dislocations terminate on the surface. The plan-view image indicates the threading dislocation density is about 4 X 10(6) cm(-2). The far-infrared measurements of electron cyclotron resonance were performed at 4 K with the magnetic field of 4-8 T. The effective masses determined from the slope of the center frequency of the absorption peak versus applied magnetic field plot are 0.203m(0) and 0.193m(0) for the two dimensional electron gases in the Si and Si0.94Ge0.06 channels, respectively. The Si effective mass is very close to that of a two dimensional electron gas in an Si MOSFET (0.198m(0)). The electron effective mass of Si0.94Ge0.06 is reported for the first time and is about 5% lower than that of pure Si.

Axial binding of 2-methylimidazole to the tetraarylcarboxylatodiruthenium (II, III) core: X-ray crystal structure of [Ru-2(O2CC6H4-p-OMe)(4)(2-mimH)(2)](ClO4). 1.75CH(2)Cl(2).H2O

Diruthenium (II. III) complexes of the type [Ru-2(O2CAr)(4) (2-mimH)(2)](ClO4) (Ar = C6H4-p-X : X=OMe,1, X=Me, 2, 2-mimH=2-methylimidazole) have been isolated from the reaction of Ru2Cl(O2CAr)(4) with 2-mimH in CH2Cl2 followed by the addition of NaClO4. The crystal structure of 1.1.75CH(2)Cl(2).H2O has been determined. The crystal belongs to the monoclinic space group p2(1)/c with the following unit cell dimensions for the C40H40N4O16ClRu2.1.75CH(2)Cl(2).H2O (M = 1237.0) : a = 12.347(3)Angstrom, b = 17.615(5)Angstrom, c = 26.148(2)Angstrom,beta = 92.88(1)degrees. v = 5679(2)Angstrom(3). Z=4, D-c = 1.45 g cm(-3). lambda(Mo-K-alpha) = 0.7107 Angstrom, mu(Mo-K-alpha) = 8.1 cm(-1), T = 293 K, R = 0.0815 (wR(2) = 0.2118) for 5834 reflections with 1 > 2 sigma(I). The complex has a tetracarboxylatodiruthenium (II, III) core and two axially bound 2-methylimidazole ligands. The Ru-Ru bond length is 2.290(1)Angstrom. The Ru-Ru bond order is 2.5 and the complex is three-electron paramagnetic. The complex shows an irreversible Ru-2(II,III)-->Ru-2(Il,II) reduction near -0.2 V vs SCE in CH2Cl2-0. 1 MTBAP. The complexes exemplify the first adduct of the tetracarboxylatodiruthenium (II,III) core having N-donor ligands

Purification and properties of riboflavin-binding protein from the egg white of the duck (Anas platyrhynckos).

Riboflavin-binding protein was purified from the egg white of domestic duck and some of its properties were investigated. The protein was homogeneous by the criteria of gel filtration on Sephadex G-100 and electrophoresis on sodium dodecyl sulphate-polyacrylamide gels, had molecular weight of 36 000 ± 1000 and, unlike the chicken egg white protein (Mr 32 000 ± 2000), was devoid of covalently-bound carbohydrate. It was similar to the chicken riboflavin-binding protein in its behavior on ion-exchange celluloses and affinity to interact with the flavin and its coenzymes, but differed significantly in amino acid composition in that it completely lacked proline and contained less of methionine and arginine. The protein partially cross-reacted with the specific antiserum to chicken riboflavin-binding protein with a spur during immunodiffusion analysis.

Structure of pentacyclo[7.4.2.02,6.06,15.011,14]pentadec-4-ene-7,13-dione, a novel pentacyclic C15 quinane system

C 15H 1602 (a synthetic precursor to dodecahedrane), monoclinic, P21/n, a = 12.171 (5), b = 6.976(5), c = 13.868 (3) A, B = 102.56 (3) ° , Z = 4, D m = 1.30, D c = 1.318 g cm -3, F(000) = 488, g(Mo K¢t) = 0.92 cm- 1. Intensity data were collected on a Nonius CAD-4 diffractometer and the structure was solved by direct methods. Full-matrix least-squares refinement gave R = 0.077 (R w = 0.076) for 1337 observed reflections. All the five-membered rings are cis fused and have envelope (C s symmetry) conformations.

Vibrational analysis of the (B2P{cyrillic}→X2P{cyrillic}) system of NS

A few red degraded bands attributable to NS have been reported earlier by Fowler and Barker, Dressler and Barrow et al, and they occur in the same region (2300 to 2700 Å) as the bands of the known systems (C2∑+-X2P{cyrillic}) and (A2Δ-X2P{cyrillic}). Measurements made on the heads of some of these weak bands led Barrow et al. to believe that these bands may form a system analogous to the β-system of NO and be due to a2P{cyrillic}-2P{cyrillic} transition. The spectrum of NS has now been studied in a little more detail by means of an uncondensed discharge through dry nitrogen and sulphur vapour in the presence of argon and thirty three bands belonging to this system have been recorded in the region 2280 to 2760 Å. It has been found possible to represent the band heads by means of the equation {Mathematical expression}. Taking the lower state doublet interval as 223 cm-1, it is shown that the separation in the upper state is 94 cm-1. The ratio of the force constants in the upper and the ground states is found to be 0·39 and is nearly the same as that in the β-system of NO (0·30). The present vibrational analysis therefore supports the view that these new red degraded bands of NS arise from a (B2P{cyrillic}→X2P{cyrillic}) transition and the observed intensity distribution in the form of a wide parabola is also in qualitative agreement with what is expected from the moderately large Δ re (∼0·12Å) value.

Process-kinetics in facing targets sputtering of multi-component oxide thin films

The kinetics of the processes in facing targets sputtering of multicomponent oxide films is presented. The novel configuration of the process exhibits an enhanced ionization efficiency. Discharge diagnostics performed using optical emission spectroscopy revealed strong dependence of plasma parameters on process conditions. Numerical simulation based on thermalization and diffusion of sputtered atoms has been performed to estimate the transport efficiency in off-axis mode. Composition, structure and epitaxial quality of YBa2Cu3O7-x films prepared was found to be strongly dependent on atomic flux ratios (of Cu/Y and Ba/Y) arriving at the substrate, resputtering effect and phase stability of YBa2Cu3O7-x These studies have been shown to be useful in understanding the complex processes that occur in sputtering of multicomponent films. (C) 1999 Elsevier Science S.A. All rights reserved.

Electron Cyclotron Resonance in Strained Si and Si0.94Ge0.06 Channels on Relaxed Si0.62Ge0.38 Buffers Grown by Rapid Thermal Chemical Vapor Deposition

We report the far-infrared measurements of the electron cyclotron resonance absorption in n-type Si/Si0. 62Ge0.38 and Si0.94Ge0.06 /Si0. 62Ge0.38 modulation- doped heterostructures grown by rapid thermal chemical vapor deposition. The strained Si and Si0.94Ge0.06 channels were grown on relaxed Si0.62Ge0.38 buffer layers, which consist of 0.6 μm uniform Si0.62Ge0.38 layers and 0.5 μm compositionally graded relaxed SiGe layers from 0% Ge to 38 % Ge. The buffer layers were annealed at 800 °C for 1 hr to obtain complete relaxation. The samples had 100 Å spacers and 300 Å 2×1019 cm-3 n-type supply layers on the tops of the 75 Å channels. The far-infrared measurements of electron cyclotron resonance were performed at 4K with the magnetic field of 4 – 8 Tesla. The effective masses determined from the slope of center frequency of absorption peak vs applied magnetic field plot are 0.20 mo and 0.19 mo for the two dimensional electron gases in the Si and Si0.94Ge0.06 channels, respectively. The Si effective mass is very close to that of two dimensional electron gas in Si MOSFET (0.198mo). The electron effective mass of Si0.94Ge0.06 is reported for the first time and about 5 % lower than that of pure Si.

Transport, optical and magnetotransport properties of hetero-epitaxial InAsxSb1−x/GaAs(x0.06) and bulk View the MathML source crystals: experiment and theoretical analysis

We briefly review the growth and structural properties of View the MathML source bulk single crystals and View the MathML source epitaxial films grown on semi-insulating GaAs substrates. Temperature-dependent transport measurements on these samples are then correlated with the information obtained from structural (XRD, TEM, SEM) and optical (FTIR absorption) investigations. The temperature dependence of mobility and the Hall coefficient are theoretically modelled by exactly solving the linearized Boltzmann transport equation by inversion of the collision matrix and the relative role of various scattering mechanisms in limiting the low temperature and View the MathML source mobility is estimated. Finally, the first observation of Shubnikov oscillations in InAsSb is discussed.

Dielectric relaxation, phase transition and Rietveld studies of perovskite Pb0.94Sr0.06](Mn1/3Sb2/3)(0.05)(Zr0.52Ti0.48)(0.95)]O-3 ceramics

The frequency-dependent dielectric relaxation of Pb0.94Sr0.06](Mn1/3Sb2/3)(0.05)(Zr0.52Ti0.48)(0.95)]O-3 ceramics, synthesized in pure perovskite phase by a solid-state reaction technique is investigated in the temperature range from 303 to 773 K by alternating-current impedance spectroscopy. Using Cole-Cole model, an analysis of the imaginary part of the dielectric permittivity with frequency is performed assuming a distribution of relaxation times. The scaling behavior of the imaginary part of the electric modulus suggests that the relaxation describes the same mechanism at various temperatures. The variation of dielectric constant with temperature is explained considering the space-charge polarization. The SEM indicates that the sample has single phase with an average grain size similar to 14.2 mu m. The material exhibits tetragonal structure. A detailed temperature dependent dielectric study at various frequencies has also been performed. (C) 2013 Elsevier B.V. All rights reserved.

Electron Magnetic Resonance Studies of Nanosized Nd0.65Ca0.35 Mn1-xCrxO3 (x=0, 0.06, 0.1) Manganite

We report a systematic investigation of the temperature dependence of electron magnetic resonance (EMR) line width, intensity and resonance field for similar to 25 nm Nd0.65Ca0.35MnO3 (NCMO1), Nd0.65Ca0.35Mn0.94Cr0.06O3 (NCMO2) and Nd0.65Ca0.35Mn0.9Cr0.1O3 (NCMO3) nanoparticles prepared by sol-gel method. The EMR line widths for the three nano-samples differ significantly from one another below a temperature T (min) where the line width has a minimum. T (min) was found to be 130, 100 and 120 K for NCMO1, NCMO2 and NCMO3, respectively. Well above T (min) the line width values for the three samples are close to one another. The sharp upturn of EMR line width below T (min) is attributed to the formation of short range, ferromagnetically ordered clusters. Temperature dependence of EMR intensity shows a residual CO transition in NCMO1 and NCMO2 and a complete disappearance of it in NCMO3. The intensity undergoes significant increase below 120, 80 and 100 K for NCMO1, NCMO2 and NCMO3, respectively, indicating the onset of ferromagnetic transitions. The occurrence of ferromagnetic transition is further confirmed by magnetization hysteresis measurements. The decrease in T (C) in NCMO2 and NCMO3 compared to NCMO1 nanoparticles is understood to be due to the destruction of the double-exchange interaction by chromium doping. The resonance field decreases below the ferromagnetic onset temperatures for all the samples as expected. The combined effects of the reduction in size and of chromium doping in Mn site are discussed.

Investigations into the structural and down-shifting and up-conversion luminescence properties of Ba2Na1-3xErxNb5O15 (0 <= x <= 0.06) nanocrystalline phosphor synthesized via sol-gel route

The present work deals with the structural and efficient down-shifting (DS) and up-conversion (UC) luminescence properties of erbium ion (Er3+) doped nanocrystalline barium sodium niobate (Ba2Na1-3xErxNb5O15, where x = 0, 0.02, 0.04 and 0.06) powders synthesized via novel citrate-based sol-gel route. The monophasic nature of the title compound was confirmed via x-ray powder diffraction followed by FT-IR studies. High-resolution transmission electron microscopy (HRTEM) facilitated the establishment of the nanocrystalline phase and the morphology of the crystallites. The Kubelka-Munk function, based on diffused reflectance studies and carried out on nano-sized crystallites, was employed to obtain the optical band-gap. The synthesized nanophosphor showed efficient DS/PL-photoluminescence and UC luminescence properties, which have not yet been reported so far in this material. The material emits intense DS green emission on excitation with 378 nm radiation. Interestingly, the material gives intense UC emission in the visible region dominated by green emission and relatively weak red emission on 976 nm excitation (NIR laser excitation). Such a dual-mode emitting nanophosphor could be very useful in display devices and for many other applications.