Growth and study of antiferroelectric lead zirconate thin films by pulsed laser ablation

Antiferroelectric lead zirconate (PZ) thin films were deposited by pulsed laser ablation on platinum-coated silicon substrates. Films showed a polycrystalline pervoskite structure upon annealing at 650 degrees C for 5-10 min. Dielectric properties were investigated as a function of temperature and frequency. The dielectric constant of PZ films was 220 at 100 kHz with a dissipation factor of 0.03. The electric field induced transformation from the antiferroelectric phase to the ferroelectric phase was observed through the polarization change, using a Sawyer-Tower circuit. The maximum polarization value obtained was 40 mu C/cm(2). The average fields to excite the ferroelectric state, and to reverse to the antiferroelectric state were 71 and 140 kV/cm, respectively. The field induced switching was also observed through double maxima in capacitance-voltage characteristics. Leakage current was studied in terms of current versus time and current versus voltage measurements. A leakage current density of 5x10(-7) A/cm(2) at 3 V, for a film of 0.7 mu m thickness, was noted at room temperature. The trap mechanism was investigated in detail in lead zirconate thin films based upon a space charge limited conduction mechanism. The films showed a backward switching time of less than 90 ns at room temperature.

Bismuth-doped amorphous-germanium sulfidesemiconductors

A study of the effect of bismuth dopant on the electronic transport properties of the amorphous semiconductors Ge20S80-xBix under high pressure (up to 140 kbar) has been carried out down to liquid-nitrogen temperature. The experiments reveal that the electronic conduction is strongly composition dependent and is thermally activated with a single activation energy at all pressures and for all compositions. A remarkable resemblance between the electronic conduction process, x-ray diffraction studies, and differential thermal analysis results is revealed. It is proposed that the n-type conduction in germanium chalcogenides doped with a large Bi concentration is due to the effect of Bi dopants on the positive correlation energy defects present in germanium chalcogenides. The impurity-induced chemical modification of the network creates a favorable environment for such an interaction.

Information theory and one-dimensional disordered conductors

A novel method is proposed to treat the problem of the random resistance of a strictly one-dimensional conductor with static disorder. It is suggested, for the probability distribution of the transfer matrix of the conductor, the distribution of maximum information-entropy, constrained by the following physical requirements: 1) flux conservation, 2) time-reversal invariance and 3) scaling, with the length of the conductor, of the two lowest cumulants of ζ, where = sh2ζ. The preliminary results discussed in the text are in qualitative agreement with those obtained by sophisticated microscopic theories.

EPR observation of phase transitions in calcium cadmium acetate hexahydrate: Using Mn2+ and Cu2+ ions as probe

Results of temperature dependence of EPR spectra of Mn2+ and Cu2+ ions doped calcium cadmium acetate hexahydrate (CaCd(CH3COO)4•6H2O) have been reported. The investigation has been carried out in the temperature range between room temperature ( 300 K) and liquid nitrogen temperature. A I-order phase transition at 146 ± 0.5 K has been confirmed. In addition a new II-order phase transition at 128 ± 1 K has been detected for the first time. There is evidence of large amplitude hindered rotations of CH3 groups which become frozen at 128 K. The incorporation of Cu2+ and Mn2+ probes at Ca2+ and Cd2+ sites respectively provide evidence that the phase transitions are caused by the molecular rearrangements of the common coordinating acetate groups between Ca2+ and Cd2+ sites. In contradiction to the previous reports of a change of symmetry from tetragonal to orthorhombic below 140 K, the symmetry of the host is concluded to remain tetragonal in all the three observed phases between room temperature and liquid nitrogen temperature.

Geometry Of Proline And Hydroxyproline .1. An Analysis Of X-Ray Crystal-Structure Data

We have carried out an analysis of crystal structure data on prolyl and hydroxyprolyl moieties in small molecules. The flexibility of the pyrrolidine ring due to the pyramidal character of nitrogen has been defined in terms of two projection angles δ1 and δ2. The distribution of these parameters in the crystal structures is found to be consistent with results of the energy calculations carried out on prolyl moieties in our laboratory.

The O-H Raman Frequency in Inorganic Acids

The band characteristic of the OH group has been recorded in the Raman spectra of many hydroxides and alcohols. It has not so far been observed, however, in the case of the stronger acids. Using the improved technique of complementary filters recently developed by Ananthakrishnan1, and giving long exposures varying from six to twelve days, I have succeeded in obtaining spectra with sulphuric acid and crystals of iodic, selenious and telluric acids, in which the band is clearly seen in the 4046 A. excitation. Table 1 gives the frequency shifts. The value for boric acid is taken from Ananthakrishnan's paper2.

Spray erosion studies on pressed soil blocks

Erosion resistance of pressed soil blocks used for wall construction is discussed. The spray erosion test using a standardized shower spray is discussed. Spray erosion behaviour of pressed soil blocks made out of five different soils is presented. Results of laboratory and field tests are compared. Effect of clay content of the soil and density of the pressed soil block on erosion are discussed. Also the effect of water-proof coatings on erosion of soil blocks is presented. Erosion resistance of soil blocks stabilized with organic (jaggery syrup and starch) or inorganic binders is also discussed.

Counterclockwise exhumation of a hot orogen: The Paleoproterozoic ultrahigh-temperature granulites in the North China Craton

Regional metamorphic belts provide important constraints on the plate tectonic architecture of orogens. We report here a detailed petrologic examination of the sapphirine-bearing ultra-high temperature (UHT) granulites from the Jining Complex within the Khondalite Belt of the North China Craton (NCC). These granulites carry diagnostic UHT assemblages and their microstructures provide robust evidence to trace the prograde, peak and retrograde metamorphic evolution. The P–T conditions of the granulites estimated from XMgGrt(Mg/Fe + Mg) − XMgSpr isopleth calculations indicate temperature above 970 °C and pressures close to 7 kbar. We present phase diagrams based on thermodynamic computations to evaluate the mineral assemblages and microstructures and trace the metamorphic trajectory of the rocks. The evolution from Spl–Qtz–Ilm–Crd–Grt–Sil to Spr–Qtz–Crd–Opx–Ilm marks the prograde stage. The Spl–Qtz assemblage appears on the low-pressure side of the P–T space with Spr–Qtz stable at the high-pressure side, possibly representing an increase in pressure corresponding to compression. The spectacular development of sapphirine rims around spinel enclosed in quartz supports this inference. An evaluation of the key UHT assemblages based on model proportion calculation suggests a counterclockwise P–T path. With few exceptions, granulite-facies rocks developed along collisional metamorphic zones have generally been characterized by clockwise exhumation trajectories. Recent evaluation of the P–T paths of metamorphic rocks developed within collisional orogens indicates that in many cases the exhumation trajectories follow the model subduction geotherm, in accordance with a tectonic model in which the metamorphic rocks are subducted and exhumed along a plate boundary. The timing of UHT metamorphism in the NCC (c. 1.92 Ga) coincides with the assembly of the NCC within the Paleoproterozoic Columbia supercontinent, a process that would have involved subduction of passive margins sediments and closure of the intervening ocean. Thus, the counterclockwise P–T path obtained in this study correlates well with a tectonic model involving subduction and final collisional suturing, with the UHT granulites representing the core of the hot or ultra-hot orogen developed during Columbia amalgamation.

Studies on the purification of banana polyphenoloxidase

Studies on the extractability of polyphenoloxidase (PPO) from the pulp of five banana cultivars revealed a varietal difference in the nature of binding of the PPO in the cell, with the enzyme being entirely in the soluble fraction in one and partly associated with the cell wall in others, necessitating use of a detergent to release it from the latter. Partial purification by acetone precipitation and chromatography using a DEAE-cellulose column yielded two major fractions DE-I and DE-II with purifications of 4- and 16·3-fold and activity recoveries of 38·2 and 43·3% respectively. Further gel filtration of the two fractions on a Sephadex G-100 column improved the purifications to 44- and 50-fold respectively with full activity recovery. Polyacrylamide gel electrophoretic studies showed the two fractions to be composed of isoenzymes differing in pattern. The purified enzyme showed maximum absorption at 275 nm.

Molecular Dynamics in [(CH8)aN]z Cd14 A Proton Magnetic Relaxation Study

second moment measurements are carried out on [(CH,),N], CdI, in the temperature range 77 to 400 K. The results are interpreted based on a molecular dynamical model of randomly reorienting methyl groups and isotropically tumbling tetramethyl ammonium group. The relaxation data show contributions from spin-rotation interaction at high temperatures and presence of inequivalent methyl groups. The correlation times and associated activation energies, connected with this model, are calculated from the data. The structure in the absorption line and in the free-induction decay signal at 77 K indicates the possibility of tunnelling motion of the methyl groups. Im Temperaturbereich 77 bis 400 K werden an [(CH,),N],CdI, Protonen-Spin-Gitter-Relaxationsexperimente (bei Larmorfrequenzen von 10,20 und 30 MHz) und Messungen des zweiten Moments durchgefiihrt. Die Ergebnisse werden an Hand eines molekularen dynamischen Modells sich statistisch umorientierender Methylgruppen und isotrop taumelnder Tetramethyl-Ammoniumgruppen interpretiert. Die Relaxationswerte zeigen Beitriige von Spin-Rotations-Wechselwirkung bei hohen Temperaturen und die Anwesenheit von inaquivalenten Methylgruppen. Die Korrelationszeiten und verknupften Aktivierungsenergien, die mit diesem Model1 verbunden sind, werden am den Werten berechnet. Die Struktur in der Absorptionslinie und im Abklingsignal der freien Induktion bei 77 K zeigt die Moglichkeit einer Tunnelbewegung der Methylgruppen.

Impression creep behaviour of magnesium alloy-based hybrid composites in the transverse direction

The creep behaviour of a creep-resistant AE42 magnesium alloy reinforced with Saffil short fibres and SiC particulates in various combinations has been investigated in the transverse direction, i.e., the plane containing random fibre orientation was perpendicular to the loading direction, in the temperature range of 175-300 degrees C at the stress levels ranging from 60 to 140 MPa using impression creep test technique. Normal creep behaviour, i.e., strain rate decreasing with strain and then reaching a steady state, is observed at 175 degrees C at all the stresses employed, and up to 80 MPa stress at 240 degrees C. A reverse creep behaviour, i.e., strain rate increasing with strain, then reaching a steady state and then decreasing, is observed above 80 MPa stress at 240 degrees C and at all the stress levels at 300 degrees C. This pattern remains the same for all the composites employed. The reverse creep behaviour is found to be associated with fibre breakage. The apparent stress exponent is found to be very high for all the composites. However, after taking the threshold stress into account, the true stress exponent is found to range between 4 and 7, which suggests viscous glide and dislocation climb being the dominant creep mechanisms. The apparent activation energy Q(C) was not calculated due to insufficient data at any stress level either for normal or reverse creep behaviour. The creep resistance of the hybrid composites is found to be comparable to that of the composite reinforced with 20% Saffil short fibres alone at all the temperatures and stress levels investigated. The creep rate of the composites in the transverse direction is found to be higher than the creep rate in the longitudinal direction reported in a previous paper.

The rα structure, chemical shift anisotropy, and the abnormal orientation of methyldichlorophosphine from the NMR spectrum

NMR studies of methyldichlorophosphine have been undertaken in the nematic phase of mixed liquid crystals of opposite diamagnetic anisotropies. The rα structure is derived. The proton chemical-shift anisotropy has been determined from the studies without the use of a reference compound and without a change of experimental conditions. It is shown that the molecule orients in the liquid crystal with positive diamagnetic anisotropy in such a way that the C3 symmetry axis of the CH3P moiety is preferentially aligned perpendicular to the direction of the magnetic field, unlike other similar systems. This is interpreted in terms of the formation of a weak solvent-solute molecular complex. The heteronuclear indirect spin-spin coupling constants are determined. The sign of the two-bond JPH is found to be positive.

Penetration Rate Effect on Miniature Cone Tip Resistance for Different Cohesionless Materials

Cone penetrometer tests were carried out in a 140 mm diameter triaxial chamber by using a miniature cone of diameter 19.5 mm. The rate of cone penetration was varied from 0.01 mm/s to 0.1 mm/s. Tests were performed in (i) clean sand, (ii) silty sand, and (iii) sand added with fly ash. Two different effective vertical pressures (sigma(nu)), 100 kPa and 300 kPa, were employed. It was noted that for clean and silty sand, the effect of penetration rate on the ultimate tip resistance (q(cu)) of the cone was found to remain only marginal. On the other hand, for sand added with 30% fly ash, the variation in q(cu) values with penetration rate was found to become quite significant. The effect of penetratio rate on q(cu) in all the cases was found to increase with a decrease in the rate of cone penetration. It was noted that with an increase in sigma(nu), the effect of penetration rate on q(cu) was found to become smaller. The effect of the cone penetration rate on q(cu) generally reduces with an increase in the relative density of the material.